Method of etching a trench into a semiconductor substrate
Assignee: NXP USA Inc
•
Filing: 1995-12-21
•
Granted: 1999-03-16
•
Expires: 2015-12-21
Abstract
Abstract Trench structures (12,32,35,46) are formed in single crystal silicon substrates (10,30) that have either a (110) or (112) orientation. A selective wet etch solution is used that removes only the exposed portions of the single crystal silicon substrates (10,30) that are in the (110) or (112) crystal planes. The trench structures (12,32,35,46) are defined by the {111} crystal planes in the single crystal silicon substrate (10,30) that are exposed during the selective wet etch process. Trench structures (32,35) can be formed on both sides of a single crystal silicon substrate (30) to form an opening (34). Opening (34) can be used as an alignment mark to align front side processing to backside and vice versa. Trench structures can also be use to form a microstructure (41,61) for a sensor (40,60).
Inventors
- 👤 Herng-Der Chiou
- 👤 Ping-Chang Lue
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:37
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/69; H10P50/691; H10P50/693; Y; Y10; Y10S; Y10S438/00; Y10S438/928; Y10S438/973
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
111 words
A method for etching a semiconductor substrate, the method comprising the steps of: providing a semiconductor substrate having a top surface and a bottom surface, wherein the top surface is of a (110) crystal plane orientation; disposing a masking layer overlying the top surface of the semiconductor substrate; removing a portion of the masking layer to provide an exposed portion of the top surface, the exposed portion of the top surface having a width; and etching the exposed portion of the top surface of the semiconductor substrate along a <110> direction thereby forming a trench, the trench extending from the top surface and comprising two parallel planes along a <111> direction.
Claim 2
Independent Claim
111 words
A method for etching a semiconductor substrate, the method comprising the steps of: providing a semiconductor substrate having a top surface and a bottom surface, wherein the top surface is of a (110) crystal plane orientation; disposing a masking layer overlying the top surface of the semiconductor substrate; removing a portion of the masking layer to provide an exposed portion of the top surface, the exposed portion of the top surface having a width; and etching the exposed portion of the top surface of the semiconductor substrate along a <110> direction thereby forming a trench, the trench extending from the top surface and comprising two parallel planes along a <111> direction.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein the width of the trench extending from the top surface is about 0.1 microns to 100 microns.
Claim 4
Dependent Claim
88 words
The method of claim 1 further comprising the steps of: disposing a masking layer on the bottom surface of the semiconductor substrate; removing a portion of the masking layer on the bottom surface to provide an exposed portion of the bottom surface, the exposed portion of the bottom surface having a width; and etching the semiconductor substrate from the bottom surface along the <110> direction such that a trench is formed, the second trench extending from the bottom surface and comprising two parallel planes along a <111> direction.
Claim 5
Dependent Claim
38 words
The method of claim 3 wherein the step of etching the semiconductor substrate continues until the trench extending from the bottom surface intersects the trench extending from the top surface to provide an opening through the semiconductor substrate.
Claim 6
Dependent Claim
32 words
The method of claim 4 wherein the step of disposing the masking layer on the bottom surface occurs simultaneously with disposing the masking layer overlying the top surface of the semiconductor substrate.
Claim 7
Dependent Claim
27 words
The method of claim 1 wherein the step of providing the semiconductor substrate includes providing a single crystal silicon substrate having a flat along a <111> direction.
Claim 8
Dependent Claim
38 words
The method of claim 1 wherein the step of disposing the masking layer overlying the top surface of the semiconductor substrate includes disposing a material selected from the group consisting of silicon, oxide, nitride, silicon dioxide, and photoresist.
Claim 9
Dependent Claim
37 words
The method of claim 1 wherein the step of etching the semiconductor substrate uses a solution comprising a chemical selected from the group consisting of cesium hydroxide, tetramethylammoniumhydroxide, potassium hydroxide, ethylenediamine pyrocatechol, lithium hydroxide, and sodium hydroxide.
Claim 10
Independent Claim
213 words
A method for forming a semiconductor device, the method comprising the steps of: providing a single crystal silicon substrate having a top surface and a bottom surface, wherein the single crystal silicon substrate is of a (110) crystal plane orientation; forming a masking layer on the top surface and the bottom surface of the single crystal silicon substrate; patterning the masking layer to provide an exposed portion of the top surface and an exposed portion of the bottom surface of the single crystal silicon substrate; etching the single crystal silicon substrate from the top surface and the bottom surface along a <110> direction such that (111) crystal planes of the single crystal silicon substrate are exposed so that a trench is formed on both the top surface and the bottom surface of the single crystal silicon substrate, the trench on the top surface and the trench on the bottom surface comprising parallel planes along a <111> direction; bonding a substrate to the single crystal silicon substrate; and etching the single crystal silicon substrate from the top surface along the <110> direction such that (111) crystal planes of the single crystal silicon substrate are exposed so that the trench from the top surface intersects the trench on the bottom surface to provide a microstructure.
Claim 11
Independent Claim
213 words
A method for forming a semiconductor device, the method comprising the steps of: providing a single crystal silicon substrate having a top surface and a bottom surface, wherein the single crystal silicon substrate is of a (110) crystal plane orientation; forming a masking layer on the top surface and the bottom surface of the single crystal silicon substrate; patterning the masking layer to provide an exposed portion of the top surface and an exposed portion of the bottom surface of the single crystal silicon substrate; etching the single crystal silicon substrate from the top surface and the bottom surface along a <110> direction such that (111) crystal planes of the single crystal silicon substrate are exposed so that a trench is formed on both the top surface and the bottom surface of the single crystal silicon substrate, the trench on the top surface and the trench on the bottom surface comprising parallel planes along a <111> direction; bonding a substrate to the single crystal silicon substrate; and etching the single crystal silicon substrate from the top surface along the <110> direction such that (111) crystal planes of the single crystal silicon substrate are exposed so that the trench from the top surface intersects the trench on the bottom surface to provide a microstructure.
Claim 12
Dependent Claim
29 words
The method of claim 9 wherein the step of providing the single crystal silicon substrate includes providing a single crystal silicon substrate having a flat along a <111> direction.
Claim 13
Dependent Claim
34 words
The method of claim 9 wherein the step of forming the masking layer includes forming a masking layer comprising a material selected from the group consisting of silicon, silicon dioxide, oxide, nitride, or photoresist.
Claim 14
Dependent Claim
47 words
The method of claim 9 wherein the step of patterning the masking layer comprises the steps of: depositing a layer of photoresist onto the masking layer; patterning the layer of photoresist to expose a portion of the masking layer; and etching the portion of the masking layer.
Claim 15
Dependent Claim
39 words
The method of claim 9 wherein the step of etching the single crystal silicon substrate uses a solution comprising a chemical selected from the group consisting of tetramethylammoniumhydroxide, cesium hydroxide, potassium hydroxide, ethylenediamine pyrocatechol, lithium hydroxide, and sodium hydroxide.
Claim 16
Dependent Claim
34 words
The method of claim 9 further comprising the steps of: patterning the masking layer to provide an exposed portion of the microstructure; and etching the exposed portion of the microstructure to form a hinge.
Claim 17
Dependent Claim
38 words
The method of claim 14 wherein the step of etching the exposed portion of the microstructure forms a hinge on the top surface of the single crystal silicon substrate at an angle of about 70.53° with the microstructure.
Claim 18
Dependent Claim
38 words
The method of claim 9 further comprising the step of forming an additional trench structure in the top surface of the single crystal silicon substrate at an angle of about 70.53° to the microstructure of the semiconductor device.
Claim 19
Independent Claim
132 words
A method for etching a semiconductor substrate, the method comprising the steps of: providing a single crystal silicon substrate having a top surface and a bottom surface, wherein the top surface is of a (112) crystal plane orientation; disposing a masking layer on the top surface of the single crystal silicon substrate; removing a portion of the masking layer to provide an exposed portion of the top surface, the exposed portion of the top surface having a width; and etching the single crystal silicon substrate from the top surface along a <112> direction such that (111) crystal planes of the single crystal silicon substrate are exposed so that a trench extending from the top surface is formed, the trench comprising two parallel planes along a <111> direction and separated by a distance.
Claim 20
Independent Claim
132 words
A method for etching a semiconductor substrate, the method comprising the steps of: providing a single crystal silicon substrate having a top surface and a bottom surface, wherein the top surface is of a (112) crystal plane orientation; disposing a masking layer on the top surface of the single crystal silicon substrate; removing a portion of the masking layer to provide an exposed portion of the top surface, the exposed portion of the top surface having a width; and etching the single crystal silicon substrate from the top surface along a <112> direction such that (111) crystal planes of the single crystal silicon substrate are exposed so that a trench extending from the top surface is formed, the trench comprising two parallel planes along a <111> direction and separated by a distance.
Claim 21
Dependent Claim
23 words
The method of claim 17 wherein the width of the trench extending from the top surface is about 0.1 microns to 100 microns.
Claim 22
Dependent Claim
98 words
The method of claim 17 further comprising the steps of: disposing a masking layer on the bottom surface of single crystal silicon substrate; removing a portion of the masking layer on the bottom surface to provide an exposed portion of the bottom surface; and etching the single crystal silicon substrate from the bottom surface along the <112> direction such that (111) crystal planes of the single crystal silicon substrate are exposed so that a trench extending from the bottom surface is formed, the trench extending from the bottom surface and comprising two parallel planes along a <111> direction.
Claim 23
Dependent Claim
42 words
The method of claim 19 wherein the step of etching the single crystal silicon substrate continues until the trench extending from the bottom surface intersects the trench extending from the top surface to provide an opening through the single crystal silicon substrate.
Claim 24
Dependent Claim
42 words
The method of claim 19 wherein the step of disposing the masking layer on the top surface of the single crystal silicon substrate includes disposing a masking layer comprising a material selected from the group consisting of silicon, oxide, nitride, and photoresist.
Claim 25
Dependent Claim
39 words
The method of claim 19 wherein the step of etching the single crystal silicon substrate uses a solution comprising a chemical selected from the group consisting of cesium hydroxide, tetramethylammoniumhydroxide, potassium hydroxide, ethylenediamine pyrocatechol, lithium hydroxide, and sodium hydroxide.
References Cited (Backward Citations)
DE3215411A1
Cited
US4867842A
Cited
JPS6070186A
Cited
US5336634A
Cited
US5207866A
Cited
WO1994012886A1
Cited
US5484507A
Cited
US5698063A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-03-15 | 2002-09-14 | 2003-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-03-15 | 2006-09-14 | 2007-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-03-15 | 2010-09-14 | 2011-03-16 | $7700.00 | Window Closed / Lapsed |