Method for forming supported thin layers of non-evaporable getter material and getter devices formed thereby
Assignee: SAES Getters SpA
•
Filing: 1997-05-13
•
Granted: 1999-03-16
•
Expires: 2017-05-13
Abstract
Abstract A method for forming a supported thin layer of non-evaporable getter (NEG) material and a getter device formed thereby are provided. A suspension comprised of non-evaporable getter (NEG) material particles in a dispersing medium is prepared. The NEG material particles in the suspension have a particle size not greater than about 150 μm. The dispersing medium has an aqueous, alcoholic, or hydroalcoholic base and contains not more than about 1 wt % of organic compounds having a boiling temperature of at least about 250° C. The ratio of the weight of the NEG material particles to the weight of the dispersing medium is between about 4:1 and about 1:1. A layer of the suspension is deposited on a carrier by a serigraphic technique. Next, the deposited layer is dried to evaporate volatile components of the dispersing medium and thereby form a dried deposit. Finally, the dried deposit is sintered under vacuum at a temperature between about 800° C. and 1000° C. with a surface of the dried deposit covered with a refractory material to inhibit scaling. Getter devices formed in accordance with this method also are provided.
Inventors
- 👤 Alessio Corazza
- 👤 Claudio Boffito
- 👤 Alessandro Gallitognotta
- 👤 Richard C. Kullberg
- 👤 Michael L. Ferris
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:44
CPC Classifications
H; H01; H01J; H01J7/00; H01J7/14; H01J7/18; H01J7/183
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
181 words
A method for forming a supported thin layer of getter material, comprising: preparing at least one suspension comprised of non-evaporable getter (NEG) material particles in a dispersing medium, said non-evaporable getter (NEG) particles having a particle size not greater than about 150 μm, said dispersing medium having an aqueous, alcoholic, or hydroalcoholic base and containing not more than about 1 wt % of organic compounds having a boiling temperature of at least about 250° C., wherein a ratio of a weight of said NEG material particles to a weight of said dispersing medium is between about 4:1 and about 1:1; depositing at least one layer of said suspension on a carrier by a serigraphic technique; drying said at least one deposited layer to evaporate volatile components of said dispersing medium and thereby form a dried deposit; and sintering said dried deposit under vacuum at a temperature between about 800° C. and 1000° C. with a surface of said dried deposit covered with a refractory material to inhibit scaling, whereby a layer comprised of NEG material supported on said carrier is obtained.
Claim 2
Independent Claim
181 words
A method for forming a supported thin layer of getter material, comprising: preparing at least one suspension comprised of non-evaporable getter (NEG) material particles in a dispersing medium, said non-evaporable getter (NEG) particles having a particle size not greater than about 150 μm, said dispersing medium having an aqueous, alcoholic, or hydroalcoholic base and containing not more than about 1 wt % of organic compounds having a boiling temperature of at least about 250° C., wherein a ratio of a weight of said NEG material particles to a weight of said dispersing medium is between about 4:1 and about 1:1; depositing at least one layer of said suspension on a carrier by a serigraphic technique; drying said at least one deposited layer to evaporate volatile components of said dispersing medium and thereby form a dried deposit; and sintering said dried deposit under vacuum at a temperature between about 800° C. and 1000° C. with a surface of said dried deposit covered with a refractory material to inhibit scaling, whereby a layer comprised of NEG material supported on said carrier is obtained.
Claim 3
Dependent Claim
34 words
The method of claim 1, wherein the NEG material is comprised of a metal selected from the group consisting of Zr, Ti, Nb, Ta, V, and alloys thereof with one or more other metals.
Claim 4
Dependent Claim
31 words
The method of claim 2, wherein the NEG material is comprised of an alloy having a composition of 70 wt % Zr, 24.6 wt % V, and 5.4 wt % Fe.
Claim 5
Dependent Claim
27 words
The method of claim 2, wherein the NEG material is comprised of an alloy having a composition of 84 wt % Zr and 16 wt % Al.
Claim 6
Dependent Claim
17 words
The method of claim 2, wherein the NEG material is comprised of a Zr 2 Fe compound.
Claim 7
Dependent Claim
17 words
The method of claim 2, wherein the NEG material is comprised of a Zr 2 Ni compound.
Claim 8
Dependent Claim
22 words
The method of claim 1, wherein the NEG material particles have a particle size between about 5 μm and about 70 μm.
Claim 9
Dependent Claim
30 words
The method of claim 1, wherein the dispersing medium contains not more than about 0.8 wt % of organic compounds having a boiling temperature of at least about 250° C.
Claim 10
Dependent Claim
30 words
The method of claim 1, wherein the ratio of the weight of the NEG material particles to the weight of the dispersing medium is between about 2.5:1 and about 1.5:1.
Claim 11
Dependent Claim
29 words
The method of claim 1, wherein the carrier is comprised of a metal selected from the group consisting of steel, titanium, nickel-plated iron, constantan, nickel/chromium alloys, and nickel/iron alloys.
Claim 12
Dependent Claim
20 words
The method of claim 10, wherein the metal carrier has a thickness between about 20 μm and about 1 mm.
Claim 13
Dependent Claim
16 words
The method of claim 1, wherein sintering occurs at a residual pressure lower than 0.1 mbar.
Claim 14
Dependent Claim
29 words
The method of claim 1, wherein the layer comprised of NEG material is cut along one or more lines passing through one or more deposit zones using a laser.
Claim 15
Dependent Claim
19 words
The method of claim 1, wherein at least two layers of different materials are deposited by the serigraphic technique.
Claim 16
Dependent Claim
23 words
The method of claim 14, wherein at least one layer is comprised of a material having a sintering temperature below about 850° C.
Claim 17
Dependent Claim
17 words
The method of claim 14, wherein at least one layer includes a plurality of discrete deposit zones.
References Cited (Backward Citations)
US3652317A
Cited
US3856709A
Cited
US3975304A
Cited
US4628198A
Cited
US5523165A
Cited
WO1995023425A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-03-15 | 2002-09-14 | 2003-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-03-15 | 2006-09-14 | 2007-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-03-15 | 2010-09-14 | 2011-03-16 | $7700.00 | Window Closed / Lapsed |