Abstract
Abstract A method is disclosed for forming dual damascene interconnections in semiconductor chips through the use of opposite type two-layered photoresist process. A silicon substrate is provided having a composite layer comprising a first layer of dielectric separated from a second layer of dielectric by an intervening intermediate layer of silicon nitride. Then, a layer of positive (P-type) chemical amplification resist (CAR) is deposited over the composite dielectric layer. The P-type resist is next line patterned by exposing and developing it through a dark field mask. This is followed by cross-linking the remaining P-type resist by performing a hard-bake. An opposite polarity, namely, a negative (N-type) CAR is next formed over the opposite P-type resist, and hole patterned through a clear field mask. Because of cross-linking, the P-type resist is not affected during hole patterning of the opposite N-type resist. The hole pattern is next transferred by dry etching into the top dielectric layer and then into the intervening silicon nitride layer in the composite layer. The line pattern in the P-type CAR layer is etched into the top dielectric layer at the same time the hole pattern is transferred from the top dielectric layer into the bottom dielectric layer by the same etching process. The photoresist layers are then removed and the dual damascene structure thusly formed is filled with metal forming the line trench and hole interconnection on the semiconductor substrate.
Inventors
- 👤 Chang-Ming Dai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 00:00
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/081; H10W20/084; H10W20/087; H10P; H10P76/00; H10P76/20; H10P76/204; H10P76/2041; H10W20/088
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
283 words
A method of dual damascene patterning through the use of opposed two-layered photoresist process comprising the steps of: providing a substrate having a composite layer of insulation deposited thereon whereby said composite layer comprises a first layer of dielectric separated from a second layer of dielectric by an intervening intermediate layer of dielectric; forming a first photoresist layer on said composite layer of dielectric insulation; hole patterning said first photoresist layer by exposing and wet developing said first photoresist layer using a first mask; cross-linking said first photoresist layer; forming a second photoresist layer on said first photoresist layer; line patterning said second photoresist layer by exposing and wet developing said second photoresist layer using a second mask; etching said second layer of dielectric underlying said first layer of photoresist using said patterned layer of first photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said second layer of dielectric; etching said intermediate layer of dielectric underlying said second layer of dielectric using said first layer of photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said intermediate layer of dielectric; etching said second layer of photoresist to extend downward said line pattern until second layer of dielectric is reached; etching said composite layer of insulation thereby transferring said line pattern in said first layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a hole; removing said layers of photoresist; and depositing metal into said line trench and said hole to form a dual damascene structure.
Claim 2
Independent Claim
283 words
A method of dual damascene patterning through the use of opposed two-layered photoresist process comprising the steps of: providing a substrate having a composite layer of insulation deposited thereon whereby said composite layer comprises a first layer of dielectric separated from a second layer of dielectric by an intervening intermediate layer of dielectric; forming a first photoresist layer on said composite layer of dielectric insulation; hole patterning said first photoresist layer by exposing and wet developing said first photoresist layer using a first mask; cross-linking said first photoresist layer; forming a second photoresist layer on said first photoresist layer; line patterning said second photoresist layer by exposing and wet developing said second photoresist layer using a second mask; etching said second layer of dielectric underlying said first layer of photoresist using said patterned layer of first photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said second layer of dielectric; etching said intermediate layer of dielectric underlying said second layer of dielectric using said first layer of photoresist as a mask thereby transferring said hole pattern in said layer of photoresist into said intermediate layer of dielectric; etching said second layer of photoresist to extend downward said line pattern until second layer of dielectric is reached; etching said composite layer of insulation thereby transferring said line pattern in said first layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a hole; removing said layers of photoresist; and depositing metal into said line trench and said hole to form a dual damascene structure.
Claim 3
Dependent Claim
19 words
The method of claim 1, wherein said composite layer of insulation is planarized by means of chemical-mechanical polishing (CMP).
Claim 4
Dependent Claim
29 words
The method of claim 1, wherein said first layer of dielectric of said composite layer is phosphosilicate glass (PSG) having a thickness between about 0.3 to 0.7 micrometers (μm).
Claim 5
Dependent Claim
25 words
The method of claim 1, wherein said intermediate layer of dielectric is silicon nitride (SiN) having a thickness between about 500 to 2000 angstroms (Å).
Claim 6
Dependent Claim
29 words
The method of claim 1, wherein said second layer of dielectric of said composite layer is phosphosilicate glass (PSG) having a thickness between about 0.3 to 0.7 micrometers (μm).
Claim 7
Dependent Claim
25 words
The method of claim 1, wherein said first layer of photoresist is a positive chemical amplification resist (CAR) with a photo acid generator (PAG) component.
Claim 8
Dependent Claim
20 words
The method of claim 1, wherein said first layer of photoresist has a thickness between about 0.40 to 0.90 μm.
Claim 9
Dependent Claim
18 words
The method of claim 1, wherein said first mask has positive resist hole patterns with dark field reticle.
Claim 10
Dependent Claim
31 words
The method of claim 1, wherein said wet developing said first photoresist layer is accomplished with a recipe comprising 2.38% TMAH developer solution stream puddled for about 45 to 70 seconds.
Claim 11
Dependent Claim
34 words
The method of claim 1, wherein said cross-linking said first photoresist layer is accomplished with a hard bake at a temperature between about 110° to 130° C. for between about 0.5 to 2 minutes.
Claim 12
Dependent Claim
26 words
The method of claim 1, wherein said second layer of photoresist is a negative type chemical amplification resist (CAR) with a photo acid generator (PAG) component.
Claim 13
Dependent Claim
20 words
The method of claim 1, wherein said second layer of photoresist has a thickness between about 0.40 to 0.90 μm.
Claim 14
Dependent Claim
18 words
The method of claim 1, wherein said second mask has negative resist line patterns with clear field reticle.
Claim 15
Dependent Claim
31 words
The method of claim 1, wherein said wet developing said second photoresist layer is accomplished with a recipe comprising 2.38% TMAH developer solution stream puddled for about 45 to 70 seconds.
Claim 16
Dependent Claim
88 words
The method of claim 1, wherein said etching said second layer of dielectric underlying said first layer of photoresist using said patterned first layer of photoresist as a mask thereby transferring said hole pattern in said first layer of photoresist into said second layer of dielectric is accomplished with etch recipe comprising gases Ar, CHF 3 and C 4 F 8 at a flow rate between about 50 to 150 sccm, 10 to 50 sccm, and 0 to 22 sccm, respectively, and used in a HDP oxide etcher.
Claim 17
Dependent Claim
83 words
The method of claim 1, wherein said etching said intermediate layer of dielectric underlying said second layer of dielectric using said first layer of photoresist as a mask thereby transferring said hole pattern in said first layer of photoresist into said intermediate layer of dielectric is accomplished by using etch recipe comprising gases Ar, CHF 3 and CF 4 at a flow rate between about 50 to 150, 0 to 100 and 0 to 50 sccm, respectively, and used in a nitride etcher.
Claim 18
Dependent Claim
65 words
The method of claim 1, wherein said etching of said second layer of photoresist to extend downward said line pattern until said second layer of dielectric is reached is accomplished with recipe comprising gases O 2 , He and CF 4 at a flow rate between about 10 to 250 sccm, 40 to 80 sccm, and 0 to 50 sccm, respectively, in a resist etcher.
Claim 19
Dependent Claim
96 words
The method of claim 1, wherein etching said composite layer of insulation thereby transferring said line pattern in said layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a contact hole is accomplished with etch recipe comprising gases Ar, CHF 3 and C 4 F 8 at a flow rate between about 50 to 150 sccm, 10 to 150 sccm, and 0 to 22 sccm, respectively, in a HDP oxide etcher.
Claim 20
Dependent Claim
41 words
The method of claim 1, wherein said removing said layer of photoresist is accomplished by O 2 plasma ashing and then wet stripping said photoresist by using H 2 SO 4 , H 2 O 2 and NH 4 OH solutions.
Claim 21
Dependent Claim
20 words
The method of claim 1, wherein said metal deposited to form a dual damascene structure is copper or aluminum-copper alloy.
Claim 22
Independent Claim
205 words
A method of dual damascene patterning through the use of opposed two-layered photoresist process comprising the steps of: providing a substrate having a composite layer of insulation deposited thereon whereby said composite layer comprises a top layer of dielectric separated from a bottom layer of dielectric by an intervening intermediate layer of dielectric; forming a layer of positive (P-type) chemical amplification resist (CAR) on said composite layer; hole patterning said layer of P-type CAR using a dark-field mask; cross-linking said layer of P-type CAR; forming a layer of negative (N-type) chemical amplification resist (CAR) on said layer of opposite P-type CAR; line patterning said layer of N-type photoresist using a clear-field mask; transferring said hole pattern in said layer of P-type CAR into said top and intermediate layers of said composite layer of insulation by etching; transferring said line pattern in said layer of N-type CAR into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form an interconnect hole; removing said layers of photoresist; and depositing metal into said trench and said hole to form a dual damascene structure and planarizing said composite layer.
Claim 23
Independent Claim
205 words
A method of dual damascene patterning through the use of opposed two-layered photoresist process comprising the steps of: providing a substrate having a composite layer of insulation deposited thereon whereby said composite layer comprises a top layer of dielectric separated from a bottom layer of dielectric by an intervening intermediate layer of dielectric; forming a layer of positive (P-type) chemical amplification resist (CAR) on said composite layer; hole patterning said layer of P-type CAR using a dark-field mask; cross-linking said layer of P-type CAR; forming a layer of negative (N-type) chemical amplification resist (CAR) on said layer of opposite P-type CAR; line patterning said layer of N-type photoresist using a clear-field mask; transferring said hole pattern in said layer of P-type CAR into said top and intermediate layers of said composite layer of insulation by etching; transferring said line pattern in said layer of N-type CAR into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form an interconnect hole; removing said layers of photoresist; and depositing metal into said trench and said hole to form a dual damascene structure and planarizing said composite layer.
Claim 24
Dependent Claim
13 words
The method of claim 21, wherein said composite layer is phosphosilicate glass (PSG).
Claim 25
Dependent Claim
28 words
The method of claim 21, wherein said intermediate layer of said composite layer of insulation is silicon nitride with a thickness between about 500 to 2000 angstroms (Å).
Claim 26
Dependent Claim
45 words
The method of claim 21, wherein said hole patterning said layer of P-type CAR is accomplished with a recipe comprising an energy exposure between about 10 to 80 millijoules (mj)/cm 2 and stream puddling in a 2.38% TMAH solution for about 40 to 70 seconds.
Claim 27
Dependent Claim
31 words
The method of claim 21, wherein said cross-linking is accomplished with a recipe comprising hard-baking between about 110° to 130° C. for about 30 to 120 seconds on a proximity hot-plate.
Claim 28
Dependent Claim
45 words
The method of claim 21, wherein said line patterning said layer of N-type CAR is accomplished with a recipe comprising an energy exposure between about 10 to 80 milijoules (mj)/cm 2 and stream puddling in a 2.38% TMAH solution for about 40 to 70 seconds.
Claim 29
Dependent Claim
93 words
The method of claim 21, wherein said transferring said line pattern in said layer of photoresist into said second layer of dielectric to form a line trench, and simultaneously transferring said hole pattern in said intermediate layer of dielectric into said first layer of dielectric to form a interconnect hole is accomplished with an etch recipe comprising gases Ar, CHF 3 and C 4 F 8 at a flow rate between about 50 to 150 sccm, 10 to 150 sccm, and 0 to 22 sccm, respectively, and used in a HDP oxide etcher.
Claim 30
Dependent Claim
20 words
The method of claim 21, wherein said metal deposited to form a dual damascene structure is copper or aluminum-copper alloy.
References Cited (Backward Citations)
US5427649A
Cited
US5378649A
Cited
US5635423A
Cited
US5529953A
Cited
US5602423A
Cited
US5614765A
Cited
US5686354A
Cited
US5691238A
Cited
US5602053A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-03-01 | 2002-08-31 | 2003-03-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-03-01 | 2006-08-31 | 2007-03-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-03-01 | 2010-08-31 | 2011-03-02 | $7700.00 | Window Closed / Lapsed |