Electrically conductive silicone elastomer compositions, methods for manufacturing semiconductor devices, and semiconductor devices
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1997-04-21
•
Granted: 1999-02-16
•
Expires: 2017-04-21
Abstract
Abstract A hydrosilylation curable electrically conductive silicone elastomer composition containing an acrylic functional group-containing organopolysiloxane such that when the composition is used to adhere a semiconductor chip to a substrate and the composition is then irradiated with a high energy beam, the exposed periphery of the composition cures to the extent that migration of low molecular weight silicone species from the composition, both before and during the hydrosilyation reaction, is minimized. A method for manufacturing a semiconductor device having improved reliability in which, during adhesion of a semiconductor chip to the substrate, package, etc., by means of this composition, decreases in wire bondability to the semiconductor chip or lead frame and adhesion defects between the semiconductor chip, substrate, package, or lead frame and the sealing resin can be inhibited. A semiconductor device manufactured by this method which has improved reliability.
Inventors
- 👤 Katsutoshi Mine
- 👤 Osamu Mitani
- 👤 Kazumi Nakayoshi
- 👤 Rikako Tazawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 23:10
CPC Classifications
C; C09; C09J; C09J183/00; C09J183/04; C08; C08L; C08L83/00; C08L83/04; C08L83/06; C09J183/06; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/20; C08L2666/00; C08L2666/28; H; H10; H10W; H10W72/00; H10W72/851; H10W72/874; H10W72/884; H10W74/00; H10W90/00; H10W90/701; H10W90/731; H10W90/736; H10W90/751; H10W90/756
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
180 words
An electrically conductive silicone elastomer composition, comprising: (A) 100 parts by weight of an organopolysiloxane consisting essentially of (a) 5-95% by weight of an acrylic functional group-containing organopolysiloxane having an average of at least two silicon-bonded acrylic groups per molecule having the formula: ##STR23## wherein R 1 is a hydrogen atom or a monovalent hydrocarbon group, R 2 is a hydrogen atom or a monovalent hydrocarbon group, and R 3 is a divalent hydrocarbon group having 1-10 carbon atoms; and (b) 95-5% by weight of an alkenyl group-containing organopolysiloxane having an average of at least two silicon-bonded alkenyl groups per molecule; (B) a silicon-bonded hydrogen atom-containing organopolysiloxane having an average of at least two silicon-bonded hydrogen atoms per molecule, in a quanity sufficient to provide 0.5 to 20 moles of silicon-bonded hydrogen atoms in component (B) per mole of silicon-bonded alkenyl group in component (b); (C) 50-2,000 parts by weight of an electrically conductive filler; (D) 0.1-20 parts by weight of a photosensitizer; and (E) a platinum catalyst, in a sufficient quantity to cure the electrically conductive silicone elastomer composition.
Claim 2
Dependent Claim
180 words
An electrically conductive silicone elastomer composition, comprising: (A) 100 parts by weight of an organopolysiloxane consisting essentially of (a) 5-95% by weight of an acrylic functional group-containing organopolysiloxane having an average of at least two silicon-bonded acrylic groups per molecule having the formula: ##STR23## wherein R 1 is a hydrogen atom or a monovalent hydrocarbon group, R 2 is a hydrogen atom or a monovalent hydrocarbon group, and R 3 is a divalent hydrocarbon group having 1-10 carbon atoms; and (b) 95-5% by weight of an alkenyl group-containing organopolysiloxane having an average of at least two silicon-bonded alkenyl groups per molecule; (B) a silicon-bonded hydrogen atom-containing organopolysiloxane having an average of at least two silicon-bonded hydrogen atoms per molecule, in a quanity sufficient to provide 0.5 to 20 moles of silicon-bonded hydrogen atoms in component (B) per mole of silicon-bonded alkenyl group in component (b); (C) 50-2,000 parts by weight of an electrically conductive filler; (D) 0.1-20 parts by weight of a photosensitizer; and (E) a platinum catalyst, in a sufficient quantity to cure the electrically conductive silicone elastomer composition.
Claim 3
Dependent Claim
169 words
An electrically conductive silicone elastomer composition, comprising (A') 100 parts by weight of an alkenyl group-containing organopolysiloxane having an average of at least two silicon-bonded alkenyl groups per molecule; (B') a silicon bonded hydrogen atom-containing organopolysiloxane having an average of at least two silicon-bonded hydrogen atoms per molecule; in an amount sufficient to provide 0.5-20 moles of silicon-bonded hydrogen atoms in component (B') per mole of silicon-bonded alkenyl group in component (A'); (C) 50-2,000 parts by weight of an electrically conductive filler; (D) 0.1-20 parts by weight of a photosensitizer; and (E) a platinum catalyst, in an amount sufficient to cure the electrically conductive silicone elastomer composition; wherein at least one component selected from components (A') or (B') contains an average of at least two silicon-bonded acrylic groups per molecule having the formula ##STR24## wherein R 1 is a hydrogen atom or a monovalent hydrocarbon group, R 2 is a hydrogen atom or a monovalent hydrocarbon group, and R 3 is a divalent hydrocarbon group having 1-10 carbon atoms.
Claim 4
Dependent Claim
169 words
An electrically conductive silicone elastomer composition, comprising (A') 100 parts by weight of an alkenyl group-containing organopolysiloxane having an average of at least two silicon-bonded alkenyl groups per molecule; (B') a silicon bonded hydrogen atom-containing organopolysiloxane having an average of at least two silicon-bonded hydrogen atoms per molecule; in an amount sufficient to provide 0.5-20 moles of silicon-bonded hydrogen atoms in component (B') per mole of silicon-bonded alkenyl group in component (A'); (C) 50-2,000 parts by weight of an electrically conductive filler; (D) 0.1-20 parts by weight of a photosensitizer; and (E) a platinum catalyst, in an amount sufficient to cure the electrically conductive silicone elastomer composition; wherein at least one component selected from components (A') or (B') contains an average of at least two silicon-bonded acrylic groups per molecule having the formula ##STR24## wherein R 1 is a hydrogen atom or a monovalent hydrocarbon group, R 2 is a hydrogen atom or a monovalent hydrocarbon group, and R 3 is a divalent hydrocarbon group having 1-10 carbon atoms.
Claim 5
Dependent Claim
175 words
A product obtained from incipient materials: (A) 100 parts by weight of an organopolysiloxane consisting essentially of (a) 5-95% by weight of an acrylic functional group-containing organopolysiloxane having an average of at least two silicon-bonded acrylic groups per molecule having the formula: ##STR25## wherein R 1 is a hydrogen atom or a monovalent hydrocarbon group, R 2 is a hydrogen atom or a monovalent hydrocarbon group, and R 3 is a divalent hydrocarbon group having 1-10 carbon atoms; and (b) 95-5% by weight of an alkenyl group-containing organopolysiloxane having an average of at least two silicon-bonded alkenyl groups per molecule; (B) a silicon-bonded hydrogen atom-containing organopolysiloxane having an average of at least two silicon-bonded hydrogen atoms per molecule, in a quanity sufficient to provide 0.5 to 20 moles of silicon-bonded hydrogen atoms in component (B) per mole of silicon-bonded alkenyl group in component (b); (C) 50-2,000 parts by weight of an electrically conductive filler; (D) 0.1-20 parts by weight of a photosensitizer; and (E) a platinum catalyst, in a sufficient quantity to cure the product.
Claim 6
Dependent Claim
175 words
A product obtained from incipient materials: (A) 100 parts by weight of an organopolysiloxane consisting essentially of (a) 5-95% by weight of an acrylic functional group-containing organopolysiloxane having an average of at least two silicon-bonded acrylic groups per molecule having the formula: ##STR25## wherein R 1 is a hydrogen atom or a monovalent hydrocarbon group, R 2 is a hydrogen atom or a monovalent hydrocarbon group, and R 3 is a divalent hydrocarbon group having 1-10 carbon atoms; and (b) 95-5% by weight of an alkenyl group-containing organopolysiloxane having an average of at least two silicon-bonded alkenyl groups per molecule; (B) a silicon-bonded hydrogen atom-containing organopolysiloxane having an average of at least two silicon-bonded hydrogen atoms per molecule, in a quanity sufficient to provide 0.5 to 20 moles of silicon-bonded hydrogen atoms in component (B) per mole of silicon-bonded alkenyl group in component (b); (C) 50-2,000 parts by weight of an electrically conductive filler; (D) 0.1-20 parts by weight of a photosensitizer; and (E) a platinum catalyst, in a sufficient quantity to cure the product.
Claim 7
Dependent Claim
163 words
A product obtained from incipient materials: (A') 100 parts by weight of an alkenyl group-containing organopolysiloxane having an averaage of at least two silicon-bonded alkenyl groups per molecule; (B') a silicon bonded hydrogen atom-containing organopolysiloxane having an average of at least two silicon-bonded hydrogen atoms per molecule; in an amount sufficient to provide 0.5-20 moles of silicon-bonded hydrogen atoms in component (B') per mole of silicon-bonded alkenyl group in component (A'); (C) 50-2,000 parts by weight of an electrically conductive filler; (D) 0.1-20 parts by weight of a photosensitizer; and (E) a platinum catalyst, in an amount sufficient to cure the product; wherein at least one component selected from components (A') or (B') contains an average of at least two silicon-bonded acrylic groups per molecule having the formula ##STR26## wherein R 1 is a hydrogen atom or a monovalent hydrocarbon group, R.sup. is a hydrogen atom or a monovalent hydrocarbon group, and R 3 is a divalent hydrocarbon group having 1-10 carbon atoms.
Claim 8
Dependent Claim
163 words
A product obtained from incipient materials: (A') 100 parts by weight of an alkenyl group-containing organopolysiloxane having an averaage of at least two silicon-bonded alkenyl groups per molecule; (B') a silicon bonded hydrogen atom-containing organopolysiloxane having an average of at least two silicon-bonded hydrogen atoms per molecule; in an amount sufficient to provide 0.5-20 moles of silicon-bonded hydrogen atoms in component (B') per mole of silicon-bonded alkenyl group in component (A'); (C) 50-2,000 parts by weight of an electrically conductive filler; (D) 0.1-20 parts by weight of a photosensitizer; and (E) a platinum catalyst, in an amount sufficient to cure the product; wherein at least one component selected from components (A') or (B') contains an average of at least two silicon-bonded acrylic groups per molecule having the formula ##STR26## wherein R 1 is a hydrogen atom or a monovalent hydrocarbon group, R.sup. is a hydrogen atom or a monovalent hydrocarbon group, and R 3 is a divalent hydrocarbon group having 1-10 carbon atoms.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-02-15 | 2002-08-17 | 2003-02-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-02-15 | 2006-08-17 | 2007-02-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-02-15 | 2010-08-17 | 2011-02-16 | $7700.00 | Window Closed / Lapsed |