Template type cavity-formation device for low temperature cofired ceramic (LTCC) sheets
Assignee: Northrop Grumman Corp
•
Filing: 1996-11-20
•
Granted: 1999-01-05
•
Expires: 2016-11-20
Abstract
Abstract A cavity pattern for a laminated structure such as a substrate for integrated circuitry is formed in a sheet of unfired low temperature cofired ceramic (LTCC) material also known as "green" tape. One sheet at a time is placed in a flexible ram forming die including a resilient rubber pressure pad and a template including the pattern to be formed in the sheet. A pair of outer pressure plates hold the pressure pad and template in place. When a sheet of unfired LTCC material is placed between the pressure pad and template and pressurization is applied to the outer plates, extrusion of the rubber material through the template causes the tape to be sheared off at the edges of the holes in the template, thus effectively cutting the required pattern in the sheet. Following pressurization, the sheet now with the pattern cut therein is removed from the die and the residual tape cut-outs are subsequently removed from the template by a vacuum.
Inventors
- 👤 Alex Bailey
- 👤 Ronnie Starling
- 👤 John Chino
- 👤 Tapan Gupta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 16:16
CPC Classifications
B; B28; B28B; B28B11/00; B28B11/12; H; H10; H10W; H10W99/00; H05; H05K; H05K3/00; H05K3/0011; H05K3/0014; H05K3/0044; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T156/1056; Y10T156/1062
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
173 words
A method of forming one or more openings in a sheet of low temperature cofired ceramic (LTCC) material which corresponds to a cavity pattern produced when a plurality of said sheets are subsequently laminated together, comprising the step of: placing a sheet of unfired LTCC material between an extrudable body of elastic material located on a first pressure plate and a template located on a second pressure plate and having one or more openings corresponding to said cavity pattern; bringing the pressure plates together and applying a pressure at least on said first pressure plate and extruding said elastic material of said body through said one or more openings in said template, thereby shearing the LTCC material along the edges of said one or more openings and cutting the cavity pattern in the sheet of LTCC material; removing the pressure from said first pressure plate and separating the pressure plates; and removing the sheet of LTCC material with the cavity pattern formed therein from between said body of elastic material and said template.
Claim 2
Independent Claim
173 words
A method of forming one or more openings in a sheet of low temperature cofired ceramic (LTCC) material which corresponds to a cavity pattern produced when a plurality of said sheets are subsequently laminated together, comprising the step of: placing a sheet of unfired LTCC material between an extrudable body of elastic material located on a first pressure plate and a template located on a second pressure plate and having one or more openings corresponding to said cavity pattern; bringing the pressure plates together and applying a pressure at least on said first pressure plate and extruding said elastic material of said body through said one or more openings in said template, thereby shearing the LTCC material along the edges of said one or more openings and cutting the cavity pattern in the sheet of LTCC material; removing the pressure from said first pressure plate and separating the pressure plates; and removing the sheet of LTCC material with the cavity pattern formed therein from between said body of elastic material and said template.
Claim 3
Dependent Claim
26 words
The method as defined by claim 1 and additionally including the step of removing residual LTCC material from said one or more openings in said template.
Claim 4
Dependent Claim
16 words
The method as defined by claim 2 wherein said step of removing comprises removing by vacuum.
Claim 5
Dependent Claim
17 words
The method of claim 1 wherein said pressure is between about 20 psi and about 100 psi.
Claim 6
Dependent Claim
18 words
The method of claim 1 and additionally including the step of fabricating a cavity pattern in said template.
Claim 7
Dependent Claim
20 words
The method of claim 5 wherein said step of fabricating comprises mechanically routing said cavity pattern in a polyimide template.
Claim 8
Dependent Claim
20 words
The method of claim 5 wherein said step of fabricating comprises machining said cavity pattern in a stainless steel template.
Claim 9
Dependent Claim
21 words
The method of claim 5 wherein said step of fabricating comprises chemically etching said cavity pattern in a stainless steel template.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-01-04 | 2002-07-06 | 2003-01-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-01-04 | 2006-07-06 | 2007-01-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-01-04 | 2010-07-06 | 2011-01-05 | $7700.00 | Window Closed / Lapsed |