Trans 1,4-butadiene/isoprene copolymers and tire with tread thereof
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1997-07-18
•
Granted: 1998-12-01
•
Expires: 2017-07-18
Abstract
Abstract Trans 1,4-copolymers of butadiene and isoprene are provided as blends with other elastomers, including partial replacement of natural cis 1,4-polyisoprene in elastomer compositions. Pneumatic rubber tires with components composed of such elastomer blends, including tire treads, are also included.
Inventors
- 👤 Paul Harry Sandstrom
- 👤 Wen-Liang Hsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 19:26
CPC Classifications
C; C08; C08L; C08L7/00; C08F; C08F236/00; C08F236/02; C08F236/04; C08L9/00; C08L9/06; C08K; C08K3/00; C08K3/34; C08K3/36; Y; Y10; Y10S; Y10S152/00; Y10S152/905
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
94 words
A rubber composition comprised of, based upon 100 parts by weight rubber (phr), (A) about 2 to about 20 phr of a trans 1,4-copolymer of isoprene and butadiene containing about 20 to about 80 percent units derived from isoprene and having a Tg within a range of about -70° C. to about -80° C.; and, correspondingly, (B) about 80 to about 98 phr of at least one other elastomer selected from homopolymers and copolymers of isoprene and 1,3-butadiene and copolymers of isoprene and/or 1,3-butadiene with a vinyl aromatic hydrocarbon selected from styrene and alpha-methylstyrene.
Claim 2
Dependent Claim
94 words
A rubber composition comprised of, based upon 100 parts by weight rubber (phr), (A) about 2 to about 20 phr of a trans 1,4-copolymer of isoprene and butadiene containing about 20 to about 80 percent units derived from isoprene and having a Tg within a range of about -70° C. to about -80° C.; and, correspondingly, (B) about 80 to about 98 phr of at least one other elastomer selected from homopolymers and copolymers of isoprene and 1,3-butadiene and copolymers of isoprene and/or 1,3-butadiene with a vinyl aromatic hydrocarbon selected from styrene and alpha-methylstyrene.
Claim 3
Dependent Claim
63 words
The rubber composition of claim 1 wherein said 1,4-trans copolymer of isoprene and butadiene is characterized by having about 75 to about 98 percent of its repeat units of a trans 1,4-isomeric structure, about 2 to about 18 percent of its repeat units of a cis 1,4-isomeric structure and about 2 to about 18 percent of its repeat units of a vinyl 1,2-structure.
Claim 4
Dependent Claim
80 words
The rubber composition of claim 1 which contains about 20 to about 120 phr of rubber reinforcing carbon black and precipitated silica; wherein said carbon black is present in an amount of about 5 to about 80 phr and the silica is present in an amount of about 15 to about 55, phr, together with a coupler for said silica having a moiety reactive with silanol groups on the surface of said silica and another moiety interactive with said elastomer(s).
Claim 5
Dependent Claim
80 words
The rubber composition of claim 2 which contains about 20 to about 120 phr of rubber reinforcing carbon black and precipitated silica; wherein said carbon black is present in an amount of about 5 to about 80 phr and the silica is present in an amount of about 15 to about 55 phr, together with a coupler for said silica having a moiety reactive with silanol groups on the surface of said silica and another moiety interactive with said elastomer(s).
Claim 6
Dependent Claim
49 words
The rubber composition of claim 3 wherein said silica coupler is a bis(trialkoxysilylalkyl) polysulfide which contains from two to about 8, with an average of about 2.3 to about 4, sulfur atoms in its polysulfidic bridge and where said alkyl groups are selected from methyl, ethyl and propyl radicals.
Claim 7
Dependent Claim
49 words
The rubber composition of claim 5 wherein said silica coupler is a bis(trialkoxysilylalkyl) polysulfide which contains from two to about 8, with an average of about 2.3 to about 4, sulfur atoms in its polysulfidic bridge and where said alkyl groups are selected from methyl, ethyl and propyl radicals.
Claim 8
Dependent Claim
49 words
The rubber composition of claim 4 wherein said silica coupler is a bis(trialkoxysilylalkyl) polysulfide which contains from two to about 8, with an average of about 2.3 to about 4, sulfur atoms in its polysulfidic bridge and where said alkyl groups are selected from methyl, ethyl and propyl radicals.
Claim 9
Dependent Claim
11 words
A tire having a tread of the composition of claim 1.
Claim 10
Dependent Claim
11 words
A tire having a tread of the composition of claim 2.
Claim 11
Dependent Claim
11 words
A tire having a tread of the composition of claim 3.
Claim 12
Dependent Claim
11 words
A tire having a tread of the composition of claim 5.
Claim 13
Dependent Claim
11 words
A tire having a tread of the composition of claim 4.
Claim 14
Dependent Claim
11 words
A tire having a tread of the composition of claim 5.
Claim 15
Dependent Claim
11 words
A tire having a tread of the composition of claim 6.
Claim 16
Dependent Claim
11 words
A tire having a tread of the composition of claim 7.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-30 | 2002-06-01 | 2002-12-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-30 | 2006-06-01 | 2006-12-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-30 | 2010-06-01 | 2010-12-01 | $7700.00 | Window Closed / Lapsed |