Assignee: NEC Corp
•
Filing: 1997-01-13
•
Granted: 1998-12-01
•
Expires: 2017-01-13
Abstract
Abstract A crystal growth method for growing on a gallium arsenide (GaAs) substrate a gallium nitride (GaN) film which is good in surface flatness and superior in crystallinity. According to the method, a GaAs substrate having a surface which is inclined with respect to the GaAs(100) face is used. The inclination angle of the substrate surface is larger than 0 degree but smaller than 35 degrees with respect to the GaAs(100) face. The inclination direction of the substrate surface is within a range of an angular range from the 0,0,1! direction of GaAs to the 0,-1,0! direction past the 0,-1,1! direction and angles less than 5 degrees on opposite sides of the angular range around an 1,0,0! direction of gallium arsenide taken as an axis, or within another range crystallographically equivalent to the range. The GaN layer is formed on the surface of the GaAs substrate preferably by hydride vapor deposition method.
Inventors
- 👤 Akitaka Kimura
- 👤 Haruo Sunakawa
- 👤 Masaaki Nido
- 👤 Atsushi Yamaguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:34
CPC Classifications
C; C30; C30B; C30B25/00; C30B25/02; C30B25/18; C30B29/00; C30B29/10; C30B29/40; C30B29/403; C30B29/406
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
138 words
A crystal growth method for forming a gallium nitride (GaN) film on a gallium arsenide (GaAs) substrate, comprising the steps of; providing a gallium arsenide substrate having a surface which is inclined with respect to a GaAs(100) face, an inclination angle of the surface being larger than 0 degree but smaller than 35 degrees with respect to the GaAs(100) face, and an inclination direction of the surface being within a range of an angular range from a 0,0,1! direction of gallium arsenide to a 0,-1,0! direction of gallium arsenide past a 0,-1,1! direction of gallium arsenide and angles less than 5 degrees on opposite sides of the angular range around an 1,0,0! direction of gallium arsenide taken as an axis, or within another range crystallographically equivalent to the range; and growing a gallium nitride layer on the surface.
Claim 2
Dependent Claim
138 words
A crystal growth method for forming a gallium nitride (GaN) film on a gallium arsenide (GaAs) substrate, comprising the steps of; providing a gallium arsenide substrate having a surface which is inclined with respect to a GaAs(100) face, an inclination angle of the surface being larger than 0 degree but smaller than 35 degrees with respect to the GaAs(100) face, and an inclination direction of the surface being within a range of an angular range from a 0,0,1! direction of gallium arsenide to a 0,-1,0! direction of gallium arsenide past a 0,-1,1! direction of gallium arsenide and angles less than 5 degrees on opposite sides of the angular range around an 1,0,0! direction of gallium arsenide taken as an axis, or within another range crystallographically equivalent to the range; and growing a gallium nitride layer on the surface.
Claim 3
Dependent Claim
24 words
The crystal growth method according to claim 1, wherein the gallium nitride layer is grown on the surface by a hydride vapor deposition method.
Claim 4
Dependent Claim
42 words
The crystal growth method according to claim 1, wherein the inclination direction of the surface is within an angular range from the 0,0,1! direction to the 0,-1,0! direction past the 0,-1,1! direction or within a range crystallographically equivalent to the angular range.
Claim 5
Dependent Claim
60 words
The crystal growth method according to claim 1, wherein the inclination angle of the surface is equal to or larger than 8 degrees but equal to or smaller than 18 degrees with respect to the GaAs(100) face, and the inclination direction of the surface is within a range of less that 5 degrees on opposite sides of the 0,-1,1! direction.
Claim 6
Dependent Claim
24 words
The crystal growth method according to claim 4, wherein the gallium nitride layer is formed on the surface by a hydride vapor deposition method.
Claim 7
Dependent Claim
37 words
The crystal growth method according to claim 4, wherein the inclination angle of the surface is equal to or larger than 10 degrees but equal to or smaller than 16 degrees with respect to the GaAs(100) face.
Claim 8
Dependent Claim
71 words
The crystal growth method according to claim 1, wherein the inclination direction of the surface is equal to or larger than 3 degrees but equal to or smaller than 7 degrees with respect to the GaAs(100) face and the inclination direction of the surface is within a range of less than 5 degrees on opposite sides of a 0,1,0! direction of gallium arsenide around the 1,0,0! direction taken as an axis.
Claim 9
Dependent Claim
24 words
The crystal growth method according to claim 7, wherein the gallium nitride layer is grown on the surface by a hydride vapor deposition method.
Claim 10
Dependent Claim
19 words
The crystal growth method according to claim 1, wherein the gallium arsenide substrate is doped with chromium oxide (CrO).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-30 | 2002-06-01 | 2002-12-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-30 | 2006-06-01 | 2006-12-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-30 | 2010-06-01 | 2010-12-01 | $7700.00 | Window Closed / Lapsed |