Wafer surface temperature control for deposition of thin films
Assignee: Applied Materials Inc
•
Filing: 1996-07-12
•
Granted: 1998-11-10
•
Expires: 2016-07-12
Abstract
Abstract A method for improving the characteristics of deposited thin films by improved control and stabilization of wafer surface temperatures. Further, the invention provides the ability to rapidly change the temperature of the wafer surface without the need to change the temperature of the chamber. The wafer is heated to an operating temperature by conventional means. A gas with high thermal conductivity, such as helium or hydrogen, is passed over the wafer to cool its surface to a desired temperature for the process to be performed. The flow rate is then adjusted to stabilize the temperature of the wafer and reduce surface temperature variations. Processing gases are then introduced into the chamber, and deposition onto the wafer commences. The maintenance of correct wafer surface temperature results in improved step coverage and conformality of the deposited film. Post-deposition steps such as plasma annealing may be performed using a gas compatible with the process at a flow rate which results in a temperature desirable for the post-deposition process.
Inventors
- 👤 Chyi Chern
- 👤 Wei Chen
- 👤 Marvin Liao
- 👤 Jennifer Meng Chu Tseng
- 👤 Mei Chang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:05
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/46; C23C16/463; C23C16/52
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
112 words
A method of processing a substrate in a chamber comprising the sequential steps of: (a) heating the chamber to a first temperature; (b) flowing a cooling gas over a surface of the substrate to cool the surface to a second temperature which is suitable for deposition of a material on the surface and which is less than the first temperature; (c) causing said material to be deposited on the cooled surface; (d) allowing the temperature of the surface of the substrate to increase above the second temperature to a third temperature; and (e) annealing the deposited material at the third temperature by bombarding the deposited material with particles originating from a plasma.
Claim 2
Independent Claim
112 words
A method of processing a substrate in a chamber comprising the sequential steps of: (a) heating the chamber to a first temperature; (b) flowing a cooling gas over a surface of the substrate to cool the surface to a second temperature which is suitable for deposition of a material on the surface and which is less than the first temperature; (c) causing said material to be deposited on the cooled surface; (d) allowing the temperature of the surface of the substrate to increase above the second temperature to a third temperature; and (e) annealing the deposited material at the third temperature by bombarding the deposited material with particles originating from a plasma.
Claim 3
Dependent Claim
36 words
The method of claim 1, further comprising the step of: (a) adjusting the flow of the cooling gas to maintain the temperature of the surface of the substrate at the second temperature for a predetermined time.
Claim 4
Dependent Claim
20 words
The method as recited in claim 1, wherein the third temperature is less than or equal to the first temperature.
Claim 5
Dependent Claim
17 words
The method of claim 3, wherein the first temperature is high enough to support a stable plasma.
Claim 6
Dependent Claim
25 words
The method as recited in claim 1, wherein the cooling gas is one or more of the group consisting of hydrogen, nitrogen, and noble gases.
Claim 7
Dependent Claim
23 words
The method as recited in claim 1, wherein the step of causing a material to be deposited is performed by chemical vapor deposition.
Claim 8
Independent Claim
130 words
A method for increasing step coverage of a trench in an upper surface of a substrate in a chamber at a chamber temperature, comprising the steps of: (a) using a cooling gas to cool the upper surface of the substrate from the chamber temperature to a lower temperature; and (b) depositing a layer in the trench and on the upper surface of the substrate with the upper surface at said lower temperature such that a ratio of the deposition rate of the layer in the trench relative to the deposition rate of the layer on the upper surface is greater than ratios of deposition rates of the layer in the trench to deposition rates of the layer on the upper surface at upper surface temperatures greater than the lower temperature.
Claim 9
Independent Claim
130 words
A method for increasing step coverage of a trench in an upper surface of a substrate in a chamber at a chamber temperature, comprising the steps of: (a) using a cooling gas to cool the upper surface of the substrate from the chamber temperature to a lower temperature; and (b) depositing a layer in the trench and on the upper surface of the substrate with the upper surface at said lower temperature such that a ratio of the deposition rate of the layer in the trench relative to the deposition rate of the layer on the upper surface is greater than ratios of deposition rates of the layer in the trench to deposition rates of the layer on the upper surface at upper surface temperatures greater than the lower temperature.
Claim 10
Dependent Claim
25 words
The method as recited in claim 7, wherein the cooling gas is one or more of the group consisting of hydrogen, nitrogen, and noble gases.
Claim 11
Dependent Claim
38 words
The method as recited in claim 7, further comprising the step of adjusting a flow of the cooling gas to maintain the temperature of the upper surface of the substrate at the lower temperature for a predetermined time.
Claim 12
Dependent Claim
20 words
The method as recited in claim 7, wherein the step of depositing the layer is performed by chemical vapor deposition.
Claim 13
Independent Claim
167 words
A method of decreasing a cycle time in a semiconductor manufacturing cycle, the cycle having steps that are performed on a substrate in a chamber at a chamber temperature, comprising the sequential steps of: (a) performing a first step of the cycle on a surface of the substrate at a first temperature that is substantially equal to the chamber temperature; (b) flowing a cooling gas over the surface of the substrate to cool the surface to a second temperature while maintaining a susceptor upon which the substrate is supported at a temperature that is substantially equal to the chamber temperature; (c) performing a second step of the cycle comprising depositing a material on the cooled surface of the substrate at the second temperature; (d) annealing the deposited material at a third temperature by bombarding the deposited material with particles originating from a plasma, the third temperature being less than or equal to the chamber temperature; and (e) performing one or more remaining steps to complete the cycle.
Claim 14
Independent Claim
167 words
A method of decreasing a cycle time in a semiconductor manufacturing cycle, the cycle having steps that are performed on a substrate in a chamber at a chamber temperature, comprising the sequential steps of: (a) performing a first step of the cycle on a surface of the substrate at a first temperature that is substantially equal to the chamber temperature; (b) flowing a cooling gas over the surface of the substrate to cool the surface to a second temperature while maintaining a susceptor upon which the substrate is supported at a temperature that is substantially equal to the chamber temperature; (c) performing a second step of the cycle comprising depositing a material on the cooled surface of the substrate at the second temperature; (d) annealing the deposited material at a third temperature by bombarding the deposited material with particles originating from a plasma, the third temperature being less than or equal to the chamber temperature; and (e) performing one or more remaining steps to complete the cycle.
Claim 15
Dependent Claim
25 words
The method as recited in claim 11, wherein the cooling gas is one or more of the group consisting of hydrogen, nitrogen, and noble gases.
Claim 16
Dependent Claim
34 words
The method as recited in claim 11, further comprising the step of adjusting the flow of the cooling gas to maintain the temperature of the surface at the second temperature for a predetermined time.
Claim 17
Dependent Claim
20 words
The method as recited in claim 11, wherein at least one of the steps is performed by chemical vapor deposition.
References Cited (Backward Citations)
US5030476A
Cited
US5113929A
Cited
US5124179A
Cited
US5279865A
Cited
US5470619A
Cited
US5576071A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-09 | 2002-05-11 | 2002-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-09 | 2006-05-11 | 2006-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-09 | 2010-05-11 | 2010-11-10 | $7700.00 | Window Closed / Lapsed |