US5830531A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Coated tool with increased service life
Assignee: Oerlikon Surface Solutions AG Pfaeffikon
•
Filing: 1997-09-29
•
Granted: 1998-11-03
•
Expires: 2017-09-29
Abstract
Abstract A tool with at least one area which is to be exposed to wear, is coated in a vacuum process with a first hard coating lying directly on the tool material and a superimposed exterior friction reducing layer over the hard coating. The grain size of the hard and friction reducing layers has a linear average width of less than 1 mu m.
Inventors
- 👤 Erich Bergmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 11:12
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/0635; C23C14/0641; C23C14/0664; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
123 words
A method of treating a tool body having at least one area to be exposed to wear, comprising: coating the one area to be exposed to wear with at least one hard layer lying directly on the tool body, the coating step taking place in a vacuum process; and superimposing on the hard layer, an exterior friction reducing layer using physical vapor deposition in the vacuum process, the friction reducing layer being a mixture of metal carbide and carbon and being formed to be free of any halide, the grain size of the hard layer and the friction reducing layer being a linear average width of less than 1 μm, the friction reducing layer also having a lower thickness than the hard layer.
Claim 2
Independent Claim
123 words
A method of treating a tool body having at least one area to be exposed to wear, comprising: coating the one area to be exposed to wear with at least one hard layer lying directly on the tool body, the coating step taking place in a vacuum process; and superimposing on the hard layer, an exterior friction reducing layer using physical vapor deposition in the vacuum process, the friction reducing layer being a mixture of metal carbide and carbon and being formed to be free of any halide, the grain size of the hard layer and the friction reducing layer being a linear average width of less than 1 μm, the friction reducing layer also having a lower thickness than the hard layer.
Claim 3
Dependent Claim
55 words
A method according to claim 1 including conducting the coating step and the superimposing step so that the coating on the at least one area of the tool which is to be exposed to wear consists essentially of the at least one hard layer and the at least one superimposed exterior friction reducing layer only.
Claim 4
Dependent Claim
33 words
A method according to claim 1 including coating the at least one area to be exposed to wear so that the hard layer has a compressive internal stress of more than 0.2 Gigapascal.
Claim 5
Dependent Claim
25 words
A method according to claim 3 wherein the superimposing step superimposes the friction reducing layer to have a thickness of about 0.12 to 1.6 μm.
Claim 6
Dependent Claim
55 words
A method according to claim 4 including coating the hard layer so that the hard layer consists essentially of at least one of a carbide; a nitride; or a carbonitride of titanium, hafnium or zirconium; or alloys thereof with other materials; and wherein the friction reducing layer consists essentially of one of CrC/C or WC/C.
Claim 7
Dependent Claim
26 words
A method according to claim 1 wherein the friction reducing layer is superimposed on the hard layer to about 1/3 the thickness of the hard layer.
Claim 8
Dependent Claim
19 words
A method according to claim 6 wherein the hard layer is coated to be about 1.1 to 8 μm.
Claim 9
Dependent Claim
18 words
A method according to claim 1 wherein the physical vapor deposition is sputtering for the friction reducing layer.
Claim 10
Dependent Claim
12 words
A method according to claim 8 wherein the sputtering is cathode sputtering.
References Cited (Backward Citations)
US4992153A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-11-02 | 2002-05-04 | 2002-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-11-02 | 2006-05-04 | 2006-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-11-02 | 2010-05-04 | 2010-11-03 | $7700.00 | Window Closed / Lapsed |