Hotmelt adhesive
Assignee: Henkel AG and Co KGaA
•
Filing: 1992-03-12
•
Granted: 1998-10-27
•
Expires: 2012-03-12
Abstract
Abstract Hot melt adhesives having an "open time" of 10 minutes or longer, preferably more than 1 hour and, more preferably, more than 2 hours for a contact pressure of 5 kg/cm 2 and atmospheric conditions of 25° C./26% relative air humidity are provided. Immediately after the parts to be joined have been pressed together at 18° to 23° C., strengths (initial strengths) of 1 MPa and more and preferably more than 1.5 MPa are obtained. The hot melt adhesive is comprised of 1) a polyester, polyamide, polyethylene/vinyl acetate, or NCO-terminated polyurethane prepolymer which does not crystallize during the open time and 2) a tackifier and/or a plasticizer.
Inventors
- 👤 Hans-Georg Kinzelmann
- 👤 Regina Biele
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:03
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C09; C09J; C09J175/00; C09J175/04; C08G2170/00; C08G2170/20; C08L; C08L2666/00; C08L2666/02; C08L2666/14; C08L2666/22
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
141 words
A process of bonding parts having surfaces to be joined comprising applying a contact hotmelt adhesive as a melt to coat each surface to be joined permitting the applied contact hotmelt adhesive to solidify, fitting the coated surfaces together with pressure without heating wherein the contact hotmelt adhesive comprises: a) 30% to 95% by weight of a polymer selected from the group consisting of polyesters, polyamides and polyethylene/vinyl acetate, and b) at least one member selected from the group consisting of a tackifier softening in a range of 10° C. to 150° C. present in an amount of up to 50% by weight and a plasticizer present in an amount of up to 30% by weight, the contact hotmelt adhesive composition having an open time of at least 10 minutes and wherein the polymer does not crystallize during the open time.
Claim 2
Dependent Claim
141 words
A process of bonding parts having surfaces to be joined comprising applying a contact hotmelt adhesive as a melt to coat each surface to be joined permitting the applied contact hotmelt adhesive to solidify, fitting the coated surfaces together with pressure without heating wherein the contact hotmelt adhesive comprises: a) 30% to 95% by weight of a polymer selected from the group consisting of polyesters, polyamides and polyethylene/vinyl acetate, and b) at least one member selected from the group consisting of a tackifier softening in a range of 10° C. to 150° C. present in an amount of up to 50% by weight and a plasticizer present in an amount of up to 30% by weight, the contact hotmelt adhesive composition having an open time of at least 10 minutes and wherein the polymer does not crystallize during the open time.
Claim 3
Dependent Claim
28 words
The process as claimed in claim 1 wherein said melt is cooled to room temperature over a period of 8 minutes after said applying and before said fitting.
Claim 4
Dependent Claim
23 words
The process of claim 1 wherein the tackifier in the contact hotmelt adhesive has a softening range of 50° C. to 150° C.
Claim 5
Dependent Claim
19 words
The method of claim 1 wherein the contact hotmelt adhesive has an initial strength of at least 1 MPa.
Claim 6
Dependent Claim
31 words
The process of claim 1 wherein the contact hotmelt adhesive has a Shore A hardness at room temperature below 65 and a glass transition temperature between -10° C. to +30° C.
Claim 7
Dependent Claim
41 words
The process of claim 5 wherein the contact hotmelt adhesive has a Shore A hardness at room temperature in the range of from 10 to 60 and a glass transition temperature in the range of from 10° C. to 25° C.
Claim 8
Dependent Claim
27 words
The process of claim 1 wherein the contact hotmelt adhesive contains from 20% to 50% of the tackifier, based on the contact hotmelt adhesive as a whole.
Claim 9
Dependent Claim
25 words
The process of claim 1 wherein the contact hotmelt adhesive contains from 5% to 25% plasticizer, based on the contact hotmelt adhesive as a whole.
Claim 10
Dependent Claim
75 words
The process of claim 1 wherein the contact hotmelt adhesive contains 20% to 50% by weight of a tackifier having a softening range of 10° C. to 150° C. and 5% to 25% by weight of a plasticizer, wherein the contact hotmelt adhesive has an initial strength of at least 1 MPa, a Shore A hardness at room temperature below 65 and a glass transition temperature in the range of -10° C. to +30° C.
Claim 11
Dependent Claim
90 words
A process of bonding comprising applying a contact hotmelt adhesive as a melt to each surface to be joined permitting the applied hotmelt adhesive to solidify, fitting the coated surfaces together with pressure without heating wherein the contact hotmelt adhesive comprises: a) NCO-terminated polyester polyurethane prepolymer, b) a tackifier having a softening range of 40° C. to 150° C. and optionally c) a plasticizer, the contact hotmelt adhesive having an open time of at least 10 minutes, wherein the NCO-terminated polyester polyurethane prepolymer does not crystallize during the open time.
Claim 12
Dependent Claim
90 words
A process of bonding comprising applying a contact hotmelt adhesive as a melt to each surface to be joined permitting the applied hotmelt adhesive to solidify, fitting the coated surfaces together with pressure without heating wherein the contact hotmelt adhesive comprises: a) NCO-terminated polyester polyurethane prepolymer, b) a tackifier having a softening range of 40° C. to 150° C. and optionally c) a plasticizer, the contact hotmelt adhesive having an open time of at least 10 minutes, wherein the NCO-terminated polyester polyurethane prepolymer does not crystallize during the open time.
Claim 13
Dependent Claim
28 words
The process as claimed in claim 10 wherein said melt is cooled to room temperature over a period of 8 minutes after said applying and before said fitting.
Claim 14
Dependent Claim
28 words
The process of claim 10 wherein the tackifier in the contact hotmelt adhesive is a phenolic-modified coumarone/indene resin having a softening range of 55° C. to 105° C.
Claim 15
Dependent Claim
29 words
The process of claim 10 wherein the contact hotmelt adhesive contains from 1% to 50% by weight of the tackifier, based on the contact hotmelt adhesive as a whole.
Claim 16
Dependent Claim
29 words
The process of claim 10 wherein the contact hotmelt adhesive contains from 5% to 30% by weight of the tackifier, based on the contact hotmelt adhesive as a whole.
Claim 17
Dependent Claim
28 words
The process of claim 10 wherein the contact hotmelt adhesive contains up to 25% by weight of the plasticizer, based on the contact hotmelt adhesive as a whole.
Claim 18
Dependent Claim
29 words
The process of claim 10 wherein the contact hotmelt adhesive contains from 1% to 10% by weight of the plasticizer, based on the contact hotmelt adhesive as a whole.
Claim 19
Dependent Claim
19 words
The process of claim 10 wherein the contact hotmelt adhesive has an initial strength of at least 1 MPa.
Claim 20
Dependent Claim
31 words
The process of claim 10 wherein the contact hotmelt adhesive has a Shore A hardness at room temperature below 65 and a glass transition temperature between -10° C. to +30° C.
References Cited (Backward Citations)
US3629360A
Cited
US3832314A
Cited
US3931077A
Cited
US3896069A
Cited
US3991025A
Cited
US4613632A
Cited
DE3236313A1
Cited
US4618651A
Cited
US5284891A
Cited
GB2234516A
Cited
EP0420246A1
Cited
US5518571A
Cited
US5455293A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-10-26 | 2002-04-27 | 2002-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-10-26 | 2006-04-27 | 2006-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-10-26 | 2010-04-27 | 2010-10-27 | $7700.00 | Window Closed / Lapsed |