Encapsulation of nanoclusters in dried gel materials via an inverse micelle/sol gel synthesis
Assignee: National Technology and Engineering Solutions of Sandia LLC
•
Filing: 1996-06-11
•
Granted: 1998-09-29
•
Expires: 2016-06-11
Abstract
Abstract A dried gel material sterically entrapping nanoclusters of a catalytically active material and a process to make the material via an inverse micelle/sol-gel synthesis. A surfactant is mixed with an apolar solvent to form an inverse micelle solution. A salt of a catalytically active material, such as gold chloride, is added along with a silica gel precursor to the solution to form a mixture. To the mixture are then added a reducing agent for the purpose of reducing the gold in the gold chloride to atomic gold to form the nanoclusters and a condensing agent to form the gel which sterically entraps the nanoclusters. The nanoclusters are normally in the average size range of from 5-10 nm in diameter with a monodisperse size distribution.
Inventors
- 👤 Anthony Martino
- 👤 Stacey A. Yamanaka
- 👤 Jeffrey S. Kawola
- 👤 Steven K. Showalter
- 👤 Douglas A. Loy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:55
CPC Classifications
B; B01; B01J; B01J13/00; B01J13/02; B01J13/0052; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2989; Y10T428/2991; Y10T428/2993
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
108 words
A method to encapsulate a substance as a nanocluster having a size of from about 1-20 nm in a dried gel material comprising: combining a surfactant with an apolar solvent to form an inverse micelle mixture; adding a salt of the substance to the inverse micelle mixture and mixing to solubilize the salt in the mixture; adding a gel precursor solution and a reducing agent to the mixture to form a colloidal suspension of the substance in the mixture; adding a condensing agent to the mixture to form a gel; and aging and drying the gel which contains nanoclusters of the substance to form the dried gel material.
Claim 2
Independent Claim
108 words
A method to encapsulate a substance as a nanocluster having a size of from about 1-20 nm in a dried gel material comprising: combining a surfactant with an apolar solvent to form an inverse micelle mixture; adding a salt of the substance to the inverse micelle mixture and mixing to solubilize the salt in the mixture; adding a gel precursor solution and a reducing agent to the mixture to form a colloidal suspension of the substance in the mixture; adding a condensing agent to the mixture to form a gel; and aging and drying the gel which contains nanoclusters of the substance to form the dried gel material.
Claim 3
Dependent Claim
40 words
The method of claim 1 wherein the substance is selected from the group consisting of Au, Ag, Pd, Pt, Rh, Fe, Ni, bimetallic combinations of these metals, Fe-based compounds, Ni-based compounds, CdS, MoS 2 and FeS 2 and combinations thereof.
Claim 4
Dependent Claim
12 words
The method of claim 1 wherein the surfactant is a cationic surfactant.
Claim 5
Dependent Claim
14 words
The method of claim 3 wherein the surfactant is a quaternary ammonium salt surfactant.
Claim 6
Dependent Claim
14 words
The method of claim 1 wherein the surfactant is didodecyldimethylammonium bromide or dilauryldimethylammonium chloride.
Claim 7
Dependent Claim
25 words
The method of claim 1 wherein the apolar solvent is selected from the group consisting of cyclohexane, liquid alkane, and aromatic hydrocarbons and combinations thereof.
Claim 8
Dependent Claim
46 words
The method of claim 1 wherein the gel precusor solution is selected from the group consisting of solutions of tetramethoxysilane, tetraethoxysilane, polydiethoxysilane, octyl polysilsesquioxane, hexyl polysilsesquioxane, alumina-based gel precursors, titanium dioxide-based gel precursors, zirconium dioxide-based gel precursors, partially hydrolyzed versions of the preceding, and combinations thereof.
Claim 9
Dependent Claim
16 words
The method of claim 1 wherein the gel precursor solution is a silica-based gel precursor solution.
Claim 10
Dependent Claim
18 words
The method of claim 1 wherein the average size of the nanoclusters is less than about 10 nm.
Claim 11
Dependent Claim
20 words
The method of claim 9 wherein the average size of the nanoclusters is between about 5 and about 10 nm.
Claim 12
Independent Claim
132 words
A method to encapsulate a catalytically active metal or metal compound as a nanocluster having a monodisperse size distribution with an average size of from about 1-10 nm in a dried gel material comprising: combining a quaternary ammonium salt surfactant with an apolar solvent to form an inverse micelle mixture; adding a salt of the metal or metal compound to the inverse micelle mixture and mixing to solubilize the salt in the mixture; adding a silica gel precursor solution and a reducing agent to the mixture to form a colloidal suspension of the metal or metal compound in the mixture; adding a condensing agent to the mixture to form a gel; and aging and drying the gel which contains nanoclusters of the metal or metal compound to form the dried gel material.
Claim 13
Independent Claim
132 words
A method to encapsulate a catalytically active metal or metal compound as a nanocluster having a monodisperse size distribution with an average size of from about 1-10 nm in a dried gel material comprising: combining a quaternary ammonium salt surfactant with an apolar solvent to form an inverse micelle mixture; adding a salt of the metal or metal compound to the inverse micelle mixture and mixing to solubilize the salt in the mixture; adding a silica gel precursor solution and a reducing agent to the mixture to form a colloidal suspension of the metal or metal compound in the mixture; adding a condensing agent to the mixture to form a gel; and aging and drying the gel which contains nanoclusters of the metal or metal compound to form the dried gel material.
Claim 14
Dependent Claim
28 words
The method of claim 11 wherein the metal is gold, the apolar solvent is toluene, and the silica gel precursor solution is a solution of tetraethoxysilane and water.
Claim 15
Dependent Claim
16 words
The method of claim 11 wherein the dried gel material is an aerogel or a xerogel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-09-28 | 2002-03-30 | 2002-09-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-09-28 | 2006-03-30 | 2006-09-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-09-28 | 2010-03-30 | 2010-09-29 | $7700.00 | Window Closed / Lapsed |