Assignee: GlobalFoundries Singapore Pte Ltd
•
Filing: 1997-01-27
•
Granted: 1998-08-04
•
Expires: 2017-01-27
Abstract
Abstract The present invention provides a method of fabricating a field oxide layer having a reduced bird's beak using a nitride foot 70 and a first field oxide region 80A as a N 2 implant mask. The N 2 implant suppresses oxide growth around the perimeter of the field oxide and reduces the bird's beak. A pad oxide layer 20 and a first nitride layer 30 are formed over a substrate. The first nitride layer is partially etched back forming a residual first nitride layer in the areas where the field oxide will be formed. A polysilicon spacer is formed on the sidewalls of the first nitride layer and over a portion of the residual first nitride layer. The residual first nitride layer 31 is etched using the spacer 60 as an etch mask forming a nitride foot 70. The substrate is thermally oxidized in the field oxide area using the first nitride layer and the foot 60 as an oxidation barrier forming a first field oxide layer 80A having a bird's beak 85. Nitrogen ions are then implanted into the bird beak region 90 forming a nitrogen implanted bird's beak region 90. The substrate is thermally oxidized forming a second field oxide layer 80B wherein the bird's beak is reduced due to the nitrogen implant. In other embodiments, the first field oxide layer is removed and a recessed second field oxide layer 82 is formed (with and without the foot 70).
Inventors
- 👤 Igor V. Peidous
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:31
CPC Classifications
H; H10; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/10; H10W10/13
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
219 words
A method of fabricating a field oxide layer having a reduced bird's beak length and height using a nitride foot and a local nitrogen implant, comprising the steps of: a) forming a pad oxide layer over a semiconductor substrate; said substrate having a field isolation area where a first field oxide layer and a second field oxide layer will be formed; b) forming a first nitride layer over said pad oxide layer; c) partially etching said first nitride layer over said field isolation area forming a residual first nitride layer over said field oxide area and forming sidewalls of said first nitride layer; d) forming a spacer on said sidewalls of said first nitride layer; e) etching said residual first nitride layer using said spacer as an etch mask forming a foot composed of said residual first nitride layer under said spacer; f) removing said spacer; g) thermally oxidizing said substrate in said field oxide area using said first nitride layer and said foot as an oxidation barrier forming a first field oxide layer, said substrate having bird's beak regions around the perimeter of said first field oxide layer; and h) implanting nitrogen ions into said bird beak region using said first field oxide layer as a implant mask, forming a nitrogen implanted bird's beak region in said substrate.
Claim 2
Independent Claim
219 words
A method of fabricating a field oxide layer having a reduced bird's beak length and height using a nitride foot and a local nitrogen implant, comprising the steps of: a) forming a pad oxide layer over a semiconductor substrate; said substrate having a field isolation area where a first field oxide layer and a second field oxide layer will be formed; b) forming a first nitride layer over said pad oxide layer; c) partially etching said first nitride layer over said field isolation area forming a residual first nitride layer over said field oxide area and forming sidewalls of said first nitride layer; d) forming a spacer on said sidewalls of said first nitride layer; e) etching said residual first nitride layer using said spacer as an etch mask forming a foot composed of said residual first nitride layer under said spacer; f) removing said spacer; g) thermally oxidizing said substrate in said field oxide area using said first nitride layer and said foot as an oxidation barrier forming a first field oxide layer, said substrate having bird's beak regions around the perimeter of said first field oxide layer; and h) implanting nitrogen ions into said bird beak region using said first field oxide layer as a implant mask, forming a nitrogen implanted bird's beak region in said substrate.
Claim 3
Dependent Claim
39 words
The method of claim 1 which further includes: a) thermally oxidizing said substrate forming a second field oxide layer wherein said nitrogen implanted bird's beak region retards oxide growth in said bird's beak region thereby reducing bird's beak growth.
Claim 4
Dependent Claim
43 words
The method of claim 1 which further includes: a) removing said foot; b) thermally oxidizing said substrate forming a second field oxide layer wherein said nitrogen implanted bird's beak region retards oxide growth in said bird's beak region thereby reducing bird's beak growth.
Claim 5
Dependent Claim
49 words
The method of claim 1 which further includes: a) removing said foot and first field oxide layer; b) thermally oxidizing said substrate forming a second recessed field oxide layer wherein said nitrogen implanted bird's beak region retards oxide growth in said bird's beak region thereby reducing bird's beak growth.
Claim 6
Dependent Claim
47 words
The method of claim 1 which further includes: a) removing said first field oxide layer; b) thermally oxidizing said substrate forming a second recessed field oxide layer wherein said nitrogen implanted bird's beak region retards oxide growth in said bird's beak region thereby reducing bird's beak growth.
Claim 7
Dependent Claim
26 words
The method of claim 1 wherein said pad oxide layer composed of silicon oxide having thickness in a range of between about 100 and 300 Å.
Claim 8
Dependent Claim
23 words
The method of claim 1 wherein said first nitride layer has a thickness in a range of between about 140 and 200 nm.
Claim 9
Dependent Claim
21 words
The method of claim 1 wherein said spacer has a thickness in a range of between about 0.05 and 0.2 μm.
Claim 10
Dependent Claim
34 words
The method of claim 1 wherein said foot having a height in a range of between about 100 and 600 Å and a length in a range of between about 0.1 and 0.15 μm.
Claim 11
Dependent Claim
45 words
The method of claim 1 wherein the energy of the nitrogen implantation is insufficient for the ion penetration thorough said first nitride layer and said first field oxide layer outside of said bird's beak region, but high enough to nitrogen dope said bird's beak region.
Claim 12
Dependent Claim
24 words
The method of claim 1 wherein said nitride layer is composed of a material selected from the group consisting of silicon nitride and oxynitride.
Claim 13
Dependent Claim
24 words
The method of claim 2 wherein said second field oxide layer has a thickness in a range of between about 3000 and 5000 Å.
Claim 14
Dependent Claim
76 words
The method of claim 1 wherein said nitrogen implanted bird's beak region has N 2 concentration in a range of between about 1E18 and 1E21 atoms/cm 3 and said nitrogen implanted bird's beak region extends from the substrate surface to a depth below the substrate surface in a range of between about 0.5 and 0.15 μm and said nitrogen implanted bird's beak region has a width in a range of between about 0.05 and 0.2 μm.
Claim 15
Independent Claim
300 words
A method of fabricating a field oxide layer having a reduced bird's beak length and height using a nitride foot and a local nitrogen implant, comprising the steps of: a) forming a pad oxide layer over a semiconductor substrate; said substrate having a field isolation area where a first and second field oxide layer will be formed; b) forming a first nitride layer over said pad oxide layer; c) partially etching said first nitride layer over said field isolation area forming a residual first nitride layer over said field oxide area and forming sidewalls of said first nitride layer; d) depositing a dielectric layer over said first nitride layer and said residual nitride layer; e) anisotropically etching said dielectric layer forming a spacer on said sidewalls of said first nitride layer; f) etching said residual first nitride layer using said spacer as an etch mask forming a foot composed of said residual nitride layer under said spacer; said foot having a length in a range of between about 0.1 and 0.15 μm; g) removing said spacer; h) thermally oxidizing said substrate in said field oxide area using said first nitride layer and said foot as an oxidation barrier forming said first field oxide layer, said substrate having bird's beak regions around the perimeter of said first field oxide layer; said first field oxide layer having a thickness in a range of between about 1200 and 2200 Å; and i) implanting nitrogen ions into said bird beak region using said first field oxide layer as a implant mask, forming a nitrogen implanted bird's beak region; the energy of the nitrogen implantation is insufficient for the ion penetration thorough said first nitride layer and said first field oxide layer, but sufficient to nitrogen dope the outer perimeter of the field isolation area.
Claim 16
Independent Claim
300 words
A method of fabricating a field oxide layer having a reduced bird's beak length and height using a nitride foot and a local nitrogen implant, comprising the steps of: a) forming a pad oxide layer over a semiconductor substrate; said substrate having a field isolation area where a first and second field oxide layer will be formed; b) forming a first nitride layer over said pad oxide layer; c) partially etching said first nitride layer over said field isolation area forming a residual first nitride layer over said field oxide area and forming sidewalls of said first nitride layer; d) depositing a dielectric layer over said first nitride layer and said residual nitride layer; e) anisotropically etching said dielectric layer forming a spacer on said sidewalls of said first nitride layer; f) etching said residual first nitride layer using said spacer as an etch mask forming a foot composed of said residual nitride layer under said spacer; said foot having a length in a range of between about 0.1 and 0.15 μm; g) removing said spacer; h) thermally oxidizing said substrate in said field oxide area using said first nitride layer and said foot as an oxidation barrier forming said first field oxide layer, said substrate having bird's beak regions around the perimeter of said first field oxide layer; said first field oxide layer having a thickness in a range of between about 1200 and 2200 Å; and i) implanting nitrogen ions into said bird beak region using said first field oxide layer as a implant mask, forming a nitrogen implanted bird's beak region; the energy of the nitrogen implantation is insufficient for the ion penetration thorough said first nitride layer and said first field oxide layer, but sufficient to nitrogen dope the outer perimeter of the field isolation area.
Claim 17
Dependent Claim
39 words
The method of claim 14 which further includes: a) thermally oxidizing said substrate forming said second field oxide layer wherein said nitrogen implanted bird's beak region retards oxide growth in said bird's beak region thereby reducing bird's beak growth.
Claim 18
Dependent Claim
43 words
The method of claim 14 which further includes: a) removing said foot; b) thermally oxidizing said substrate forming said second field oxide layer wherein said nitrogen implanted bird's beak region retards oxide growth in said bird's beak region thereby reducing bird's beak growth.
Claim 19
Dependent Claim
49 words
The method of claim 14 which further includes: a) removing said foot and first field oxide layer; b) thermally oxidizing said substrate forming said second recessed field oxide layer wherein said nitrogen implanted bird's beak region retards oxide growth in said bird's beak region thereby reducing bird's beak growth.
Claim 20
Dependent Claim
47 words
The method of claim 14 which further includes: a) removing said first field oxide layer; b) thermally oxidizing said substrate forming said second recessed field oxide layer wherein said nitrogen implanted bird's beak region retards oxide growth in said bird's beak region thereby reducing bird's beak growth.
Claim 21
Dependent Claim
77 words
The method of claim 14 wherein said nitrogen implanted bird's beak region has N 2 concentration in a range of between about 1E18 and 1E21 atoms/cm 3 , and said nitrogen implanted bird's beak region extends from the substrate surface to a depth below the substrate surface in a range of between about 0.5 and 0.15 μm and said nitrogen implanted bird's beak region has a width in a range of between about 0.05 and 0.2 μm.
References Cited (Backward Citations)
JPS63300526A
Cited
US5173444A
Cited
US5229318A
Cited
US5399520A
Cited
US5308787A
Cited
US5472906A
Cited
US5470783A
Cited
US5468657A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-08-03 | 2002-02-02 | 2002-08-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-08-03 | 2006-02-02 | 2006-08-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-08-03 | 2010-02-02 | 2010-08-04 | $7700.00 | Window Closed / Lapsed |