Method for producing a hydrogenated vertical-cavity surface-emitting laser
Assignee: Electronics and Telecommunications Research Institute
•
Filing: 1997-04-25
•
Granted: 1998-06-30
•
Expires: 2017-04-25
Abstract
Abstract A method for producing a vertical-cavity surface-emitting laser, includes the steps of: forming a bottom mirror layer, an active layer and a top mirror layer on a semiconductor substrate; forming an antireflection layer on a rear surface of the semiconductor substrate; selectively etching peripheral portions of the antireflection layer to form a first electrode; defining laser emission portions through etching processing; forming a hydrogenated barrier over an entire surface of the resultant structure; forming a post; forming a passivation layer through the hydrogenating of the exposed top mirror layer and the portions of the active layer; forming a planarization film after the partial exposure of the top mirror and forming a second electrode pad to which the exposed top mirror layer contacts.
Inventors
- 👤 Hye-Yong Chu
- 👤 Byueng-Su Yoo
- 👤 Hyo-Hoon Park
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:06
CPC Classifications
H; H01; H01S; H01S5/00; H01S5/10; H01S5/18; H01S5/183; H01S5/18308; H01S5/02; H01S5/028; H01S5/0282; H01S5/20; H01S5/2054; H01S5/2059; H01S5/40; H01S5/42; H01S5/423
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
239 words
A method for producing a vertical-cavity surface-emitting laser comprising the steps of: sequentially forming a bottom mirror layer, an active layer and a top mirror layer on a compound semiconductor substrate; forming an antireflection layer on a rear surface of the compound semiconductor substrate; selectively etching predetermined peripheral portions of the antireflection layer, and then forming a first electrode; forming a first photoresist pattern on a surface of the top mirror layer to define laser emission portions, and removing the first photoresist pattern after selectively etching portions of the top mirror layer by using the first photoresist pattern as a mask; forming a protection layer for hydrogenation barrier over an entire surface of the resultant structure; forming a second photoresist pattern on a surface of the protection layer for hydrogenation barrier of a post, and removing the second photoresist pattern after selectively etching the hydrogenated barrier, the top mirror layer and portions of the active layer by using the second photoresist pattern as a mask; forming a passivation layer through the hydrogenating of the exposed top mirror layer and the portions of the active layer; exposing the top mirror layer by etching the protection layer for hydrogenation barrier over the surface of the post; forming a planarization layer over an entire surface of the resultant structure, and exposing the top mirror layer on the post; and forming a second electrode pad to which the exposed top mirror layer contacts.
Claim 2
Independent Claim
239 words
A method for producing a vertical-cavity surface-emitting laser comprising the steps of: sequentially forming a bottom mirror layer, an active layer and a top mirror layer on a compound semiconductor substrate; forming an antireflection layer on a rear surface of the compound semiconductor substrate; selectively etching predetermined peripheral portions of the antireflection layer, and then forming a first electrode; forming a first photoresist pattern on a surface of the top mirror layer to define laser emission portions, and removing the first photoresist pattern after selectively etching portions of the top mirror layer by using the first photoresist pattern as a mask; forming a protection layer for hydrogenation barrier over an entire surface of the resultant structure; forming a second photoresist pattern on a surface of the protection layer for hydrogenation barrier of a post, and removing the second photoresist pattern after selectively etching the hydrogenated barrier, the top mirror layer and portions of the active layer by using the second photoresist pattern as a mask; forming a passivation layer through the hydrogenating of the exposed top mirror layer and the portions of the active layer; exposing the top mirror layer by etching the protection layer for hydrogenation barrier over the surface of the post; forming a planarization layer over an entire surface of the resultant structure, and exposing the top mirror layer on the post; and forming a second electrode pad to which the exposed top mirror layer contacts.
Claim 3
Dependent Claim
16 words
The method as defined in claim 1, wherein the planarization film comprises a layer of polyimide.
Claim 4
Dependent Claim
19 words
The method as defined in claim 1, wherein the hydrogenated barrier comprises one of silicon-oxide layer or silicon-nitride layer.
Claim 5
Dependent Claim
20 words
The method as defined in claim 1, wherein the passivation layer has a thickness of around 0.5 to 20 micrometer.
Claim 6
Dependent Claim
31 words
The method as defined in claim 4, wherein the step of hydrogenating is performed at the atmosphere of hydrogen plasma having a pressure of about 10 -4 Torr to 1 Torr.
Claim 7
Dependent Claim
23 words
The method as defined in claim 5, wherein the step of hydrogenating is performed at temperature of around 250 to 500 degree celsius.
Claim 8
Dependent Claim
20 words
The method as defined in claim 6, wherein the step of hydrogenating is performed for about 0.5 to 2 hours.
References Cited (Backward Citations)
US5115442A
Cited
US5416044A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-29 | 2001-12-29 | 2002-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-29 | 2005-12-29 | 2006-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-29 | 2009-12-29 | 2010-06-30 | $7700.00 | Window Closed / Lapsed |