Method of manufacturing ternary compound thin films
Assignee: Primus Gastronomiebetriebe GmbH
•
Filing: 1995-07-04
•
Granted: 1998-06-30
•
Expires: 2015-07-04
Abstract
Abstract One kind of element belonging to I group or II group and one kind of binary compound including one kind of element belonging to III group and one kind of element selected from the group consisting of S, Se, Te and O are evaporated respectively by means of a vacuum vapor deposition method or molecular beam epitaxial method to produce a ternary compound semiconductor material having a low vapor pressure, and the thus produced ternary compound semiconductor material is deposited on a substrate to form a ternary compound semiconductor thin film. Particularly, when a phosphor thin film for electroluminescence emitting blue light is to be grown, an element Sr and a binary compound Ga 2 S 3 are respectively evaporated by the vacuum evaporation method or molecular beam epitaxial method to deposit a ternary compound semiconductor material SrGa 2 S 4 on a substrate, and at the same time impurity element Ce forming luminescent center is evaporated such that the ternary compound semiconductor material SrGa 2 S 4 is doped with the impurity element.
Inventors
- 👤 Yoji Inoue
- 👤 Katsu Tanaka
- 👤 Shinji Okamoto
- 👤 Kikuo Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:23
CPC Classifications
H; H05; H05B; H05B33/00; H05B33/12; H05B33/22; C; C09; C09K; C09K11/00; C09K11/08; C09K11/62; C09K11/621; C09K11/625; C09K11/77; C09K11/7701; C09K11/7703; C09K11/7715; C09K11/7716; C09K11/7718; C09K11/7728; C09K11/7729; C09K11/7731; C09K11/7743; C09K11/7744; C09K11/7746; C09K11/7759; C09K11/776; C09K11/7761; C23; C23C; C23C14/00; C23C14/06; C23C14/0623; C23C14/08; C30; C30B; C30B23/00; C30B23/02; C30B29/00; C30B29/10; C30B29/46; H05B33/10; H05B33/14; H10; H10D; H10D62/00; H10D62/80; H10P; H10P14/00; H10P14/20; H10P14/22; H10P14/29; H10P14/2901; H10P14/2921; H10P14/2922; H10P14/34; H10P14/3402; H10P14/3436; H10P14/3438; H10P14/3441; H10P14/3446; H10P14/3466
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
102 words
A method of manufacturing a ternary compound semiconductor thin film, characterized in that one kind of element belonging to IB group or IIB group and one kind of binary compound including one kind of element belonging to IIIB group and one kind of element selected from the group consisting of S, Se, Te and O are evaporated respectively by means of a vacuum vapor deposition method or molecular beam epitaxial method to produce a ternary compound semiconductor material having a low vapor pressure, and said ternary compound semiconductor material is deposited on a substrate to form said ternary compound semiconductor thin film.
Claim 2
Independent Claim
102 words
A method of manufacturing a ternary compound semiconductor thin film, characterized in that one kind of element belonging to IB group or IIB group and one kind of binary compound including one kind of element belonging to IIIB group and one kind of element selected from the group consisting of S, Se, Te and O are evaporated respectively by means of a vacuum vapor deposition method or molecular beam epitaxial method to produce a ternary compound semiconductor material having a low vapor pressure, and said ternary compound semiconductor material is deposited on a substrate to form said ternary compound semiconductor thin film.
Claim 3
Independent Claim
159 words
A method of manufacturing a phosphor thin film of a primarily ternary compound semiconductor material, characterized in that one kind of element belonging to IB group or IIB group and one kind of binary compound consisting of one kind of element belonging to the IIIB group and one kind of element selected from the group consisting of S, Se, Te and O are evaporated respectively by means of a vacuum vapor deposition method or molecular beam epitaxial method to produce a ternary compound semiconductor material having a low vapor pressure, the thus produced ternary compound semiconductor material is deposited on a substrate to form a ternary compound semiconductor thin film, and at the same time at least one kind of impurity element or a compound thereof serving as luminescent center is evaporated such that the ternary compound semiconductor thin film is doped with said impurity element to form said phosphor thin film of the primarily ternary compound semiconductor material.
Claim 4
Independent Claim
159 words
A method of manufacturing a phosphor thin film of a primarily ternary compound semiconductor material, characterized in that one kind of element belonging to IB group or IIB group and one kind of binary compound consisting of one kind of element belonging to the IIIB group and one kind of element selected from the group consisting of S, Se, Te and O are evaporated respectively by means of a vacuum vapor deposition method or molecular beam epitaxial method to produce a ternary compound semiconductor material having a low vapor pressure, the thus produced ternary compound semiconductor material is deposited on a substrate to form a ternary compound semiconductor thin film, and at the same time at least one kind of impurity element or a compound thereof serving as luminescent center is evaporated such that the ternary compound semiconductor thin film is doped with said impurity element to form said phosphor thin film of the primarily ternary compound semiconductor material.
Claim 5
Dependent Claim
29 words
A method as claimed in claim 2, characterized in that said element belonging to IIIB group is an element selected from the group consisting of Al, In and Ga.
Claim 6
Dependent Claim
59 words
A method as claimed in claim 2, characterized in that said impurity element serving as luminescent center is an element selected from the group consisting of La, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Tm, Yb, Mn, Ni, Sn, Pb, F, Cl, Br, I, Li, Na, K, Rb, Cs, P, As, Sb, Bi, Sc, Y and O.
Claim 7
Independent Claim
79 words
A method of manufacturing a ternary compound semiconductor thin film, characterized in that only an element Sr and a binary compound Ga 2 S 3 are evaporated by a vacuum vapor deposition method or molecular beam epitaxial method to produce a ternary compound semiconductor material SrGa 2 S 4 having a low vapor pressure, and the thus produced ternary compound semiconductor material is deposited on a substrate to grow a ternary compound semiconductor SrGa 2 S 4 thin film.
Claim 8
Independent Claim
79 words
A method of manufacturing a ternary compound semiconductor thin film, characterized in that only an element Sr and a binary compound Ga 2 S 3 are evaporated by a vacuum vapor deposition method or molecular beam epitaxial method to produce a ternary compound semiconductor material SrGa 2 S 4 having a low vapor pressure, and the thus produced ternary compound semiconductor material is deposited on a substrate to grow a ternary compound semiconductor SrGa 2 S 4 thin film.
Claim 9
Dependent Claim
81 words
A method as claimed in claim 5, characterized in that upon depositing the ternary compound semiconductor thin film on the substrate, a ratio of a vapor pressure of the binary compound Ga 2 S 3 to a vapor pressure of the element Sr (Ga 2 S 3 /Sr) is set to a value within a range from about 15 to about 150, and said substrate is heated to a temperature within a range from about 530° C. to about 605° C.
Claim 10
Independent Claim
170 words
A method of manufacturing an electroluminescent phosphor thin film of a primarily ternary compound semiconductor material, characterized in that only an element Sr and a binary compound Ga 2 S 3 are evaporated by a vacuum vapor deposition method or molecular beam epitaxial method to produce a ternary compound semiconductor material SrGa 2 S 4 having a low vapor pressure, the thus produced ternary compound semiconductor material is deposited on a substrate to grow a ternary compound semiconductor SrGa 2 S 4 thin film, and at the same time a cerium element or a cerium halogenide is evaporated as impurity serving as luminescent center such that the ternary compound semiconductor thin film is doped with said impurity to form said phosphor thin film of the primarily ternary compound semiconductor material, wherein a temperature of the substrate is set to 530-560° C., and a ratio of a vapor pressure of the binary compound Ga 2 S 3 to that of the element Sr(Ga 2 S 3 /Sr) is set to 20-60.
Claim 11
Independent Claim
170 words
A method of manufacturing an electroluminescent phosphor thin film of a primarily ternary compound semiconductor material, characterized in that only an element Sr and a binary compound Ga 2 S 3 are evaporated by a vacuum vapor deposition method or molecular beam epitaxial method to produce a ternary compound semiconductor material SrGa 2 S 4 having a low vapor pressure, the thus produced ternary compound semiconductor material is deposited on a substrate to grow a ternary compound semiconductor SrGa 2 S 4 thin film, and at the same time a cerium element or a cerium halogenide is evaporated as impurity serving as luminescent center such that the ternary compound semiconductor thin film is doped with said impurity to form said phosphor thin film of the primarily ternary compound semiconductor material, wherein a temperature of the substrate is set to 530-560° C., and a ratio of a vapor pressure of the binary compound Ga 2 S 3 to that of the element Sr(Ga 2 S 3 /Sr) is set to 20-60.
Claim 12
Dependent Claim
44 words
A method as claimed in claim 7, characterized in that said cerium or cerium halogenide impurity serving as luminescent center is replaced by a substance selected from the group consisting of Pr, Sm, Eu, fb, Dy, Ho, Er, Tm, Yb, Mn and halogenides thereof.
Claim 13
Dependent Claim
72 words
A method as claimed in claim 7, characterized in that a temperature of the substrate, a ratio of a vapor pressure of the binary compound Ga 2 S 3 to that of the element Sr (Ga 2 S 3 /Sr) and a film growing speed are selected such that an orientation (400) or (800) or (422) of said ternary compound semiconductor material SrGa 2 S 4 exhibits as a main crystal orientation.
Claim 14
Dependent Claim
19 words
A method as claimed in claim 9, characterized in that the film growing speed is set to 10-100 Angstroms/minute.
Claim 15
Dependent Claim
80 words
A method as claimed in claim 7, characterized in that upon depositing said ternary compound semiconductor material SrGa 2 S 4 thin film on the substrate, a substrate having a laminated film of strontium titanate (SrTiO 3 )/silicon nitride (Si 3 N 4 ) or a laminated film of strontium titanate (SrTiO 3 )/aluminum oxide (Al 2 O 3 ) is used such that said ternary compound semiconductor material film is brought into contact with said strontium titanate thin film.
Claim 16
Independent Claim
161 words
A method of manufacturing a phosphor thin film for electroluminescence, characterized in that only an element selected from the group consisting of Ca, Ba and Mg and a binary compound Ga 2 S 3 are evaporated by a vacuum vapor deposition method or a molecular beam epitaxial method to produce a ternary compound semiconductor material CaGa 2 S 4 or BaGa 2 S 4 or MgGa 2 S 4 having a low vapor pressure, the thus produced ternary compound semiconductor material is deposited on a substrate to form a ternary compound semiconductor material thin film, and at the same time an impurity element serving as luminescent center is evaporated such that the ternary compound semiconductor material thin film is doped with said impurity element to form said phosphor thin film for electroluminescence, wherein said impurity element serving as luminescent center is a substance selected from the group consisting of Pr, Sm, Tb, Dy, Ho, Er, Tm, Yb, Mn and halogenides thereof.
Claim 17
Independent Claim
161 words
A method of manufacturing a phosphor thin film for electroluminescence, characterized in that only an element selected from the group consisting of Ca, Ba and Mg and a binary compound Ga 2 S 3 are evaporated by a vacuum vapor deposition method or a molecular beam epitaxial method to produce a ternary compound semiconductor material CaGa 2 S 4 or BaGa 2 S 4 or MgGa 2 S 4 having a low vapor pressure, the thus produced ternary compound semiconductor material is deposited on a substrate to form a ternary compound semiconductor material thin film, and at the same time an impurity element serving as luminescent center is evaporated such that the ternary compound semiconductor material thin film is doped with said impurity element to form said phosphor thin film for electroluminescence, wherein said impurity element serving as luminescent center is a substance selected from the group consisting of Pr, Sm, Tb, Dy, Ho, Er, Tm, Yb, Mn and halogenides thereof.
Claim 18
Dependent Claim
75 words
A method as claimed in claim 12, characterized in that upon depositing said thin film of the ternary compound semiconductor material CaGa 2 S 4 , BaGa 2 S 4 or MgGa 2 S 4 on the substrate, a substrate having a strontium titanate (SrTiO 3 ) thin film formed on a surface thereof is used such that said ternary compound semiconductor material thin film is brought into contact with the strontium titanate thin film.
Claim 19
Independent Claim
165 words
A method of manufacturing a phosphor thin film for electroluminescence, characterized in that only an element selected from the group consisting of Sr, Ca, Ba and Mg and a binary compound Ga 2 Se 3 are evaporated by a vacuum vapor deposition method or a molecular beam epitaxial method to produce a ternary compound semiconductor material SrGa 2 Se 4 or CaGa 2 Se 4 or BaGa 2 Se 4 or MgGa 2 Se 4 having a low vapor pressure, the thus produced ternary compound semiconductor material is deposited on a substrate to form a ternary compound semiconductor material thin film, and at the same time an impurity substance serving as luminescent center is evaporated such that the ternary compound semiconductor material thin film is doped with said impurity substance to form said phosphor thin film for electroluminescence, wherein said impurity substance serving as luminescent center is selected from the group consisting of Pr, Sm, Tb, Dy, Ho, Er, Tm, Yb, Mn and halogenides thereof.
Claim 20
Independent Claim
165 words
A method of manufacturing a phosphor thin film for electroluminescence, characterized in that only an element selected from the group consisting of Sr, Ca, Ba and Mg and a binary compound Ga 2 Se 3 are evaporated by a vacuum vapor deposition method or a molecular beam epitaxial method to produce a ternary compound semiconductor material SrGa 2 Se 4 or CaGa 2 Se 4 or BaGa 2 Se 4 or MgGa 2 Se 4 having a low vapor pressure, the thus produced ternary compound semiconductor material is deposited on a substrate to form a ternary compound semiconductor material thin film, and at the same time an impurity substance serving as luminescent center is evaporated such that the ternary compound semiconductor material thin film is doped with said impurity substance to form said phosphor thin film for electroluminescence, wherein said impurity substance serving as luminescent center is selected from the group consisting of Pr, Sm, Tb, Dy, Ho, Er, Tm, Yb, Mn and halogenides thereof.
Claim 21
Dependent Claim
72 words
A method as claimed in claim 14, characterized in that upon depositing said ternary compound semiconductor material SrGa 2 Se 4 or CaGa 2 Se 4 or BaGa 2 Se 4 or MgGa 2 Se 4 , a substrate having a strontium titanate (SrTiO 3 ) thin film formed on a surface thereof is used such-that said ternary compound semiconductor thin film is brought into contact with said strontium titanate thin film.
References Cited (Backward Citations)
US4770950A
Cited
JPH0265094A
Cited
US5554449A
Cited
JPH02269185A
Cited
JPH04121992A
Cited
JPH0565478A
Cited
US5505986A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-29 | 2001-12-29 | 2002-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-29 | 2005-12-29 | 2006-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-29 | 2009-12-29 | 2010-06-30 | $7700.00 | Window Closed / Lapsed |