Method of annealing film stacks and device having stack produced by same
Assignee: Micron Technology Inc
•
Filing: 1996-07-08
•
Granted: 1998-06-09
•
Expires: 2016-07-08
Abstract
Abstract An annealing method includes providing a wafer having a film stack including at least a flowable film and a semirigid film formed on the flowable film. The film stack is exposed to an initial temperature followed by exposure to an intermediate temperature for an intermediate exposure time period. Then, the film stack is exposed to a final anneal temperature for a final anneal exposure time period. The film stack may include another nonflowable or flowable film formed on the semirigid film. The film stack may be exposed to one or more additional intermediate temperatures for additional intermediate exposure time periods. The film stack may be an oxide/polysilicon/oxide film stack and the oxide films may be doped oxides. A device or wafer having a film stack annealed in accordance with the annealing method is also provided.
Inventors
- 👤 Kenneth Hagen
- 👤 Howard E. Rhodes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:00
CPC Classifications
H; H10; H10P; H10P95/00
Claims Analysis
Total Claims: 33
Claim 1
Independent Claim
68 words
An annealing method comprising the steps of: providing a wafer having a film stack including at least a flowable film and a semirigid film formed on the flowable film; exposing the film stack to an initial temperature; exposing the film stack to an intermediate temperature for an intermediate exposure time period; and exposing the film stack to a final anneal temperature for a final anneal exposure time period.
Claim 2
Dependent Claim
68 words
An annealing method comprising the steps of: providing a wafer having a film stack including at least a flowable film and a semirigid film formed on the flowable film; exposing the film stack to an initial temperature; exposing the film stack to an intermediate temperature for an intermediate exposure time period; and exposing the film stack to a final anneal temperature for a final anneal exposure time period.
Claim 3
Dependent Claim
29 words
The annealing method according to claim 1, further including the step of exposing the film stack to one or more additional intermediate temperatures for additional intermediate exposure time periods.
Claim 4
Dependent Claim
22 words
The annealing method according to claim 2, wherein each additional intermediate temperature is of a temperature higher than the previous intermediate temperature.
Claim 5
Dependent Claim
25 words
The annealing method according to claim 1, wherein the film stack further includes one of a nonflowable or flowable film formed on the semirigid film.
Claim 6
Dependent Claim
84 words
The annealing method according to claim 4, wherein the film stack is an oxide/polysilicon/oxide film stack, and further wherein the intermediate temperature is in the range of about 550° C. to about 1100° C., the intermediate time period is in the range of about 10 seconds to about 60 minutes, the final anneal temperature is in the range of about 700° C. to 1100° C., and the final anneal exposure time period is in the range of about 10 seconds to about 3 hours.
Claim 7
Dependent Claim
68 words
The annealing method according to claim 5, further including the step of exposing the film stack to one or more additional intermediate temperatures for additional intermediate exposure time periods, wherein the one or more additional intermediate temperatures are in the range of about 550° C. to about 1100° C. and the additional intermediate exposure time periods are in the range of about 10 seconds to about 60 minutes.
Claim 8
Dependent Claim
26 words
The annealing method according to claim 1, wherein one or more of the exposing steps are performed using one of rapid thermal processing or furnace processing.
Claim 9
Dependent Claim
58 words
The annealing method according to claim 1, wherein the initial temperature is in a temperature range of about room temperature to about 750° C., the intermediate temperature is in a temperature range of about 550° C. to about 1100° C., and the final anneal temperature is in a temperature range of about 700° C. to about 1100° C.
Claim 10
Dependent Claim
22 words
The annealing method according to claim 1, wherein the final anneal exposure time period is greater than the intermediate exposure time period.
Claim 11
Dependent Claim
84 words
The annealing method according to claim 1, wherein the film stack is an oxide/silicide film stack, and further wherein the intermediate temperature is in the range of about 550° C. to about 1100° C., the intermediate time period is in the range of about 10 seconds to about 60 minutes, the final anneal temperature is in the range of about 700° C. to 1100° C., and the final anneal exposure time period is in the range of about 10 seconds to about 3 hours.
Claim 12
Dependent Claim
68 words
The annealing method according to claim 10, further including the step of exposing the film stack to one or more additional intermediate temperatures for additional intermediate exposure time periods, wherein the one or more additional intermediate temperatures are in the range of about 550° C. to about 1100° C. and the additional intermediate exposure time periods are in the range of about 10 seconds to about 60 minutes.
Claim 13
Dependent Claim
78 words
An annealing method comprising the steps of: providing a wafer having a film stack including: a flowable film; a semirigid film formed on the flowable film; and one of a nonflowable or flowable film formed on the semirigid film; exposing the film stack to an initial temperature; exposing the film stack to an intermediate temperature for an intermediate exposure time period; and exposing the film stack to a final anneal temperature for a final anneal exposure time period.
Claim 14
Dependent Claim
78 words
An annealing method comprising the steps of: providing a wafer having a film stack including: a flowable film; a semirigid film formed on the flowable film; and one of a nonflowable or flowable film formed on the semirigid film; exposing the film stack to an initial temperature; exposing the film stack to an intermediate temperature for an intermediate exposure time period; and exposing the film stack to a final anneal temperature for a final anneal exposure time period.
Claim 15
Dependent Claim
29 words
The annealing method according to claim 12, further including the step of exposing the film stack to one or more additional intermediate temperatures for additional intermediate exposure time periods.
Claim 16
Dependent Claim
22 words
The annealing method according to claim 13, wherein each additional intermediate temperature is of a temperature higher than the previous intermediate temperature.
Claim 17
Dependent Claim
91 words
The annealing method according to claim 14, wherein the film stack is a doped oxide/polysilicon/doped oxide film stack, and further wherein the intermediate temperature is in the range of about 550° C. to about 1100° C., the intermediate time period is in the range of about 10 seconds to about 60 minutes, the one or more additional intermediate temperatures are in the range of about 550° to about 1100° C., and the one or more additional intermediate time periods are in the range of about 10 seconds to about 60 minutes.
Claim 18
Dependent Claim
55 words
The annealing method according to claim 15, wherein the method includes one additional intermediate temperature and additional time period, and further wherein the intermediate temperature is about 700° C., the intermediate time period is about 10 minutes, the additional intermediate temperature is about 750° C., and the additional intermediate time period is about 10 minutes.
Claim 19
Dependent Claim
19 words
The annealing method according to claim 13, wherein the final anneal exposure time period is at least 60 minutes.
Claim 20
Dependent Claim
26 words
The annealing method according to claim 12, wherein one or more of the exposing steps are performed using one of rapid thermal processing or furnace processing.
Claim 21
Dependent Claim
50 words
The annealing method according to claim 18, wherein the performance of the one or more exposing steps includes the step of ramping the temperature from one exposure step to the temperature of the next exposure step at a rate in a range of about 0.01° C./sec to about 200° C./sec.
Claim 22
Dependent Claim
58 words
The annealing method according to claim 12, wherein the initial temperature is in a temperature range of about room temperature to about 750° C., the intermediate temperature is in a temperature range of about 550° C. to about 1100° C., and the final anneal temperature is in a temperature range of about 700° C. to about 1100° C.
Claim 23
Dependent Claim
25 words
The annealing method according to claim 20, wherein the intermediate exposure time period is in a range of about 10 seconds to about 60 minutes.
Claim 24
Dependent Claim
26 words
The annealing method according to claim 20, wherein the final anneal exposure time period is in a range of about 10 seconds to about 3 hours.
Claim 25
Dependent Claim
83 words
An annealing method comprising the steps of: providing a wafer having a film stack including: a first oxide film; a polysilicon film formed on the first oxide film; and a second oxide film formed on the polysilicon film; and exposing the film stack to an initial temperature; exposing the film stack to an intermediate temperature for an intermediate exposure time period; and exposing the film stack to a final anneal temperature higher than the initial temperature for a fmal anneal exposure time period.
Claim 26
Dependent Claim
83 words
An annealing method comprising the steps of: providing a wafer having a film stack including: a first oxide film; a polysilicon film formed on the first oxide film; and a second oxide film formed on the polysilicon film; and exposing the film stack to an initial temperature; exposing the film stack to an intermediate temperature for an intermediate exposure time period; and exposing the film stack to a final anneal temperature higher than the initial temperature for a fmal anneal exposure time period.
Claim 27
Dependent Claim
44 words
The annealing method according claim 23, wherein at least the first oxide film is a film flowable by thermal processing and further wherein the providing of the first oxide layer includes thermal processing of the wafer prior to the forming of the polysilicon film.
Claim 28
Dependent Claim
18 words
The annealing method according claim 24, wherein at least the first oxide film is a doped oxide film.
Claim 29
Dependent Claim
20 words
The annealing method according claim 25, wherein the first oxide film and the second oxide film are doped oxide films.
Claim 30
Dependent Claim
26 words
The annealing method according to claim 23, wherein one or more of the exposing steps are performed using one of rapid thermal processing or furnace processing.
Claim 31
Dependent Claim
50 words
The annealing method according to claim 27, wherein the performance of the one or more exposing steps includes the step of ramping the temperature from one exposure step to the temperature of the next exposure step at a rate in a range of about 0.01° C./sec to about 200° C./sec.
Claim 32
Dependent Claim
63 words
The annealing method according to claim 23, wherein the initial temperature is in a temperature range of about 500° C. to about 700° C., the intermediate temperature is in a temperature range of about 650° C. to about 5° C. below the final anneal temperature, and the final anneal temperature is in a temperature range of about 700° C. to about 1000° C.
Claim 33
Dependent Claim
45 words
The annealing method according to claim 29, wherein the intermediate exposure time period is in a range of about 5 minutes to about 30 minutes and wherein the final anneal exposure time period is in a range of about 10 seconds to about 3 hours.
References Cited (Backward Citations)
US5387557A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-06-08 | 2001-12-08 | 2002-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-06-08 | 2005-12-08 | 2006-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-06-08 | 2009-12-08 | 2010-06-09 | $7700.00 | Window Closed / Lapsed |