Abstract
Abstract A semiconductor fabrication technique is provided for producing a low resistivity polycide. Polycide resistivity is lowered by minimizing areas where the polycide is unduly thin. By preparing the polysilicon upper surface prior to polycide formation thereon, the polysilicon surface can grow polycide at a uniform rate across the entire polysilicon surface. The polysilicon surface is prepared by either restricting doping atoms at grain boundary locations at the polysilicon surface, or by disrupting the grain boundaries by ion implanting that surface. In either instance, a properly prepared polysilicon surface greatly enhances the conductivity of polycide grown thereon.
Inventors
- 👤 Effiong E. Ibok
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:35
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/0131; Y; Y10; Y10S; Y10S438/00; Y10S438/974
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
92 words
A method for producing a low resistivity polycide, comprising: depositing a layer of polysilicon upon one surface of a silicon substrate; doping said layer of polysilicon with a first impurity species to form a doped layer of polysilicon; removing select portions of said doped layer of polysilicon to present a polysilicon gate structure having an upper surface; implanting said upper surface with ions at an energy level sufficient to amorphize the upper surface of said polysilicon gate structure; and forming a silicide upon the amorphized upper surface of said polysilicon gate structure.
Claim 2
Independent Claim
92 words
A method for producing a low resistivity polycide, comprising: depositing a layer of polysilicon upon one surface of a silicon substrate; doping said layer of polysilicon with a first impurity species to form a doped layer of polysilicon; removing select portions of said doped layer of polysilicon to present a polysilicon gate structure having an upper surface; implanting said upper surface with ions at an energy level sufficient to amorphize the upper surface of said polysilicon gate structure; and forming a silicide upon the amorphized upper surface of said polysilicon gate structure.
Claim 3
Dependent Claim
19 words
The method as recited in claim 1, wherein said depositing comprises chemical vapor depositing polysilicon from a silane source.
Claim 4
Dependent Claim
28 words
The method as recited in claim 1, wherein said doping comprises placing said layer of polysilicon in a heated diffusion chamber containing atoms of the first impurity species.
Claim 5
Dependent Claim
33 words
The method as recited in claim 1, wherein said doping said layer of polysilicon with a first impurity species is to a concentration level of 1×10 19 to 1×10 21 atoms/cm 3 .
Claim 6
Dependent Claim
18 words
The method as recited in claim 1, wherein said removing comprises anisotropically etching the doped layer of polysilicon.
Claim 7
Dependent Claim
28 words
The method as recited in claim 1, wherein said amorphizing comprises implanting ions of a second impurity species to a concentration level less than said first impurity species.
Claim 8
Dependent Claim
36 words
The method as recited in claim 6, wherein said implanting step comprises injecting ions into the upper surface of said polysilicon gate structure to a concentration peak density less than 0.1 μm below said upper surface.
Claim 9
Dependent Claim
64 words
The method as recited in claim 1, wherein said forming step comprises: depositing a refractory metal upon the upper surface of said polysilicon; and heating the deposited refractory metal to cause portions of the refractory metal to react with the upper surface of said polysilicon, and leaving non-reacted portions of the deposited refractory metal; and removing the non-reacted portions, of the deposited refractory metal.
Claim 10
Dependent Claim
27 words
The method as recited in claim 1, wherein the silicide in combination with the polysilicon gate structure form a polycide having a resistivity less than 90 μΩ-cm.
Claim 11
Independent Claim
90 words
A method for producing low resistivity polycide, comprising: depositing a first layer of polysilicon upon one surface of a silicon substrate; doping said first layer of polysilicon with a first impurity species; growing an oxide to form a grown oxide upon the first layer of polysilicon; depositing a second layer of undoped polysilicon upon the grown oxide to form a stacked polysilicon structure; removing select portions of said first and second layers of polysilicon; and forming a silicide upon an upper surface of the remaining said second layer of polysilicon.
Claim 12
Independent Claim
90 words
A method for producing low resistivity polycide, comprising: depositing a first layer of polysilicon upon one surface of a silicon substrate; doping said first layer of polysilicon with a first impurity species; growing an oxide to form a grown oxide upon the first layer of polysilicon; depositing a second layer of undoped polysilicon upon the grown oxide to form a stacked polysilicon structure; removing select portions of said first and second layers of polysilicon; and forming a silicide upon an upper surface of the remaining said second layer of polysilicon.
Claim 13
Dependent Claim
35 words
The method as recited in claim 10, wherein said depositing a first layer and said depositing a second layer each comprise chemical vapor depositing respective first and second layers of polysilicon from a silane source.
Claim 14
Dependent Claim
29 words
The method as recited in claim 10, wherein said doping comprises placing said first layer of polysilicon in a heated diffusion chamber containing atoms of the first impurity species.
Claim 15
Dependent Claim
33 words
The method as recited in claim 10, wherein said doping said layer of polysilicon with a first impurity species is to a concentration level of 1×10 19 to 1×10 21 atoms/cm 3 .
Claim 16
Dependent Claim
34 words
The method as recited in claim 10, wherein said removing comprises anisotropically etching said first layer of polysilicon, said layer of oxide and said second layer of polysilicon using a single lithography masking step.
Claim 17
Dependent Claim
62 words
The method as recited in claim 10, wherein said forming comprises: depositing a refractory metal upon the upper surface of the remaining said second layer of polysilicon; and heating the deposited refractory metal to cause portions of the refractory metal to react with the upper surface of said second layer of polysilicon; and removing the non-reacted portions of the deposited refractory metal.
Claim 18
Dependent Claim
26 words
The method as recited in claim 10, further comprising amorphizing the upper surface of said second layer of polysilicon after said removing and before said forming.
Claim 19
Dependent Claim
56 words
The method as recited in claim 10, further comprising ion implanting the upper surface of said second layer with ion beam energy sufficient to displace, within 0.1 μm of the upper surface of said second layer, an amount of atoms per unit volume therein which is more than half the atomic density of total atoms therein.
Claim 20
Dependent Claim
53 words
The method as recited in claim 10, further comprising ion implanting the upper surface of said second layer with ion beam energy sufficient to displace, within 0.1 μm of the upper surface of said second layer, an amount of atoms per unit volume therein which approaches the atomic density of total atoms therein.
Claim 21
Independent Claim
206 words
A method for producing a polycide having a resistivity of less than 12 μΩ-cm, comprising: depositing a first layer of polysilicon upon one surface of a silicon substrate; doping said first layer of polysilicon with a first impurity species; growing an oxide to form a grown oxide upon the first layer of polysilicon; depositing a second layer of polysilicon having an upper surface upon the grown oxide to form a stacked polysilicon structure; removing select portions of said first and second layers of polysilicon to form respective remaining first and second layers of polysilicon, wherein the remaining second layer has an upper surface; implanting ions into the upper surface of said second layer with ion beam energy sufficient to displace, within 0.1 μm of the upper surface of said second layer, an amount of atoms per unit volume therein which is more than half the atomic density of total atoms therein; depositing a layer of titanium upon the upper surface of the remaining second layer of polysilicon; heating the layer of titanium to cause portions of the titanium to react with the upper surface of said second layer of polysilicon, leaving non-reacted portions of the deposited titanium; and removing the non-reacted portions of the deposited titanium.
Claim 22
Independent Claim
206 words
A method for producing a polycide having a resistivity of less than 12 μΩ-cm, comprising: depositing a first layer of polysilicon upon one surface of a silicon substrate; doping said first layer of polysilicon with a first impurity species; growing an oxide to form a grown oxide upon the first layer of polysilicon; depositing a second layer of polysilicon having an upper surface upon the grown oxide to form a stacked polysilicon structure; removing select portions of said first and second layers of polysilicon to form respective remaining first and second layers of polysilicon, wherein the remaining second layer has an upper surface; implanting ions into the upper surface of said second layer with ion beam energy sufficient to displace, within 0.1 μm of the upper surface of said second layer, an amount of atoms per unit volume therein which is more than half the atomic density of total atoms therein; depositing a layer of titanium upon the upper surface of the remaining second layer of polysilicon; heating the layer of titanium to cause portions of the titanium to react with the upper surface of said second layer of polysilicon, leaving non-reacted portions of the deposited titanium; and removing the non-reacted portions of the deposited titanium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-01-26 | 2001-07-28 | 2002-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-01-26 | 2005-07-28 | 2006-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-01-26 | 2009-07-28 | 2010-01-27 | $7700.00 | Window Closed / Lapsed |