Method for increasing capacitance of an HSG rugged capacitor using a phosphine rich oxidation and subsequent wet etch
Assignee: Micron Technology Inc
•
Filing: 1994-03-11
•
Granted: 1997-12-09
•
Expires: 2014-03-11
Abstract
Abstract A capacitor and method for forming the capacitor having HSG polysilicon with reduced dielectric bridging, increased capacitance, and minimal depletion effects. A first polysilicon layer is deposited and doped with impurities to increase conductivity. A second polysilicon layer is deposited at a temperature adjusted to cause a nucleation of the second polysilicon layer. As a result of the nucleation the second polysilicon layer is altered to resemble hemispherical grains. Next the first and second polysilicon layers are oxidized in an oxygen/phosphine ambient. During the oxidation portions of the first and second polysilicon layers are consumed forming a phosphine rich oxide layer on the surface of the hemispherical grains and in portions of the first polysilicon layer lying between the grains which are reduced in size due to the oxidation. A wet etch is then performed to remove the oxide layer. Phosphorous ions are driven into the hemispherical grains during the oxidation thereby doping the grains. The oxidation is controlled such that the surface area of the hemispherical grains and first polysilicon layer retain a roughened surface area that is at least equal to a surface area of the hemispherical grains prior to the oxidation. The size of the grains decreases and the distance between the grains increases as a result of the oxidation. Following the etch a dielectric layer is deposited to overlie the rough polysilicon. The thickness of the dielectric layer tends to be uniform due to the smaller grains and greater distance between the grains. The process is completed with a deposition of a cell plate layer overlying the dielectric layer. Depletion is reduced or eliminated due to the doping of the grains.
Inventors
- 👤 Thomas A. Figura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:17
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/692; H10D1/711; H10D1/712; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/0698; Y; Y10; Y10S; Y10S438/00; Y10S438/964
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
99 words
A method for forming a capacitor, comprising the following steps: a) forming a polysilicon layer having a hemispherical grained surface; b) oxidizing said polysilicon layer in an ambient comprising oxygen and a dopant to form an oxide layer comprising said dopant, said oxidizing consuming a portion of said polysilicon layer; c) doping said polysilicon layer with said dopant; and d) etching said oxide layer to decrease a size of grains forming said hemispherical grained surface and to increase a distance between said grains, said polysilicon layer forming at least a portion of a storage node plate of said capacitor.
Claim 2
Independent Claim
99 words
A method for forming a capacitor, comprising the following steps: a) forming a polysilicon layer having a hemispherical grained surface; b) oxidizing said polysilicon layer in an ambient comprising oxygen and a dopant to form an oxide layer comprising said dopant, said oxidizing consuming a portion of said polysilicon layer; c) doping said polysilicon layer with said dopant; and d) etching said oxide layer to decrease a size of grains forming said hemispherical grained surface and to increase a distance between said grains, said polysilicon layer forming at least a portion of a storage node plate of said capacitor.
Claim 3
Dependent Claim
34 words
The method as specified in claim 1 further comprising the following steps: a) forming a dielectric layer to overlie said polysilicon layer; and b) forming a cell plate layer to overlie said dielectric layer.
Claim 4
Dependent Claim
22 words
The method as specified in claim 2, further comprising the step of doping said cell plate layer to increase a conductivity thereof.
Claim 5
Dependent Claim
32 words
The method as specified in claim 1, wherein said step of forming said polysilicon layer comprises depositing said polysilicon layer at a temperature and a pressure effecting nucleation of said polysilicon layer.
Claim 6
Dependent Claim
25 words
The method as specified in claim 1, wherein said step of forming said dielectric layer comprises depositing a dielectric material to have a uniform thickness.
Claim 7
Dependent Claim
26 words
The method as specified in claim 1, wherein said step of forming said polysilicon layer comprises forming said polysilicon layer on a doped base polysilicon layer.
Claim 8
Independent Claim
130 words
A method for forming a capacitor comprising the following steps: a) providing a granulated first capacitive plate having a plurality of hemispherical grains on a surface thereof; b) oxidizing a capacitive material comprising said first capacitive plate in an ambient comprising a dopant material and an oxygen source; c) consuming portions of said capacitive material to decrease said size of said grains and to increase a distance between said grains; d) forming an oxide layer comprising said dopant material adjacent to said capacitive material remaining subsequent to said step of oxidizing; e) driving said dopant material into said capacitive material increasing a conductivity thereof; f) removing said oxide layer; g) forming a second capacitive plate; and h) forming a dielectric layer interposed between said first and said second capacitive plates.
Claim 9
Independent Claim
130 words
A method for forming a capacitor comprising the following steps: a) providing a granulated first capacitive plate having a plurality of hemispherical grains on a surface thereof; b) oxidizing a capacitive material comprising said first capacitive plate in an ambient comprising a dopant material and an oxygen source; c) consuming portions of said capacitive material to decrease said size of said grains and to increase a distance between said grains; d) forming an oxide layer comprising said dopant material adjacent to said capacitive material remaining subsequent to said step of oxidizing; e) driving said dopant material into said capacitive material increasing a conductivity thereof; f) removing said oxide layer; g) forming a second capacitive plate; and h) forming a dielectric layer interposed between said first and said second capacitive plates.
Claim 10
Independent Claim
182 words
A method for forming a capacitor, comprising the following steps: a) forming a base layer on a starting surface, said base layer functioning as a storage node plate of said capacitor; b) adjusting a temperature and a pressure of said base layer in order to cause a nucleation of said base layer; c) forming hemispherical grains of said base layer on a surface of said base layer during said step of adjusting; d) oxidizing said base layer in an oxygen ambient comprising dopant ions thereby forming an oxide layer; e) driving said dopant ions into said base layer during said step of oxidizing, said dopant ions increasing a conductivity of said base layer; f) consuming a portion of said base layer during said step of oxidizing thereby decreasing a size of said grains and increasing a distance between said grains; g) removing said oxide layer; h) forming a dielectric layer to overlie said base layer; and i) forming a cell plate layer to overlie said dielectric layer, wherein said base layer, said dielectric layer and said cell plate layer form said capacitor.
Claim 11
Independent Claim
182 words
A method for forming a capacitor, comprising the following steps: a) forming a base layer on a starting surface, said base layer functioning as a storage node plate of said capacitor; b) adjusting a temperature and a pressure of said base layer in order to cause a nucleation of said base layer; c) forming hemispherical grains of said base layer on a surface of said base layer during said step of adjusting; d) oxidizing said base layer in an oxygen ambient comprising dopant ions thereby forming an oxide layer; e) driving said dopant ions into said base layer during said step of oxidizing, said dopant ions increasing a conductivity of said base layer; f) consuming a portion of said base layer during said step of oxidizing thereby decreasing a size of said grains and increasing a distance between said grains; g) removing said oxide layer; h) forming a dielectric layer to overlie said base layer; and i) forming a cell plate layer to overlie said dielectric layer, wherein said base layer, said dielectric layer and said cell plate layer form said capacitor.
Claim 12
Independent Claim
147 words
A method for forming a capacitor comprising the following steps: a) forming a first polysilicon layer on a starting surface; b) forming a second polysilicon layer having hemispherical grains overlying said first polysilicon layer; c) oxidizing at least said second polysilicon layer in an oxygen and phosphorous ambient to form a phosphorous rich oxide layer comprising phosphorous ions, said step of oxidizing consuming a portion of each of said hemispherical grains to decrease a size of said grains and to increase a distance between said grains; d) driving at least a portion of said phosphorous ions into said second polysilicon layer to dope said second polysilicon layer and to increase a conductivity thereof during said step of oxidizing, said first polysilicon layer and said doped second polysilicon layer forming a storage node plate of said capacitor; and (e) etching said oxide layer to remove said oxide layer.
Claim 13
Independent Claim
147 words
A method for forming a capacitor comprising the following steps: a) forming a first polysilicon layer on a starting surface; b) forming a second polysilicon layer having hemispherical grains overlying said first polysilicon layer; c) oxidizing at least said second polysilicon layer in an oxygen and phosphorous ambient to form a phosphorous rich oxide layer comprising phosphorous ions, said step of oxidizing consuming a portion of each of said hemispherical grains to decrease a size of said grains and to increase a distance between said grains; d) driving at least a portion of said phosphorous ions into said second polysilicon layer to dope said second polysilicon layer and to increase a conductivity thereof during said step of oxidizing, said first polysilicon layer and said doped second polysilicon layer forming a storage node plate of said capacitor; and (e) etching said oxide layer to remove said oxide layer.
Claim 14
Dependent Claim
21 words
The method as specified in claim 9, further comprising oxidizing a portion of said first polysilicon layer lying between said grains.
Claim 15
Dependent Claim
34 words
The method as specified in claim 9, further comprising the following steps: a) forming a cell plate layer; and b) forming a dielectric layer interposed between said storage node plate and said cell plate.
Claim 16
Dependent Claim
23 words
The method as specified in claim 11, further comprising doping said cell plate layer and said first polysilicon layer to increase conductivities thereof.
Claim 17
Dependent Claim
32 words
The method as specified in claim 9, wherein said step of forming said second polysilicon layer comprises depositing said second polysilicon layer at a temperature effecting nucleation of said second polysilicon layer.
Claim 18
Dependent Claim
25 words
The method as specified in claim 9, wherein said step of forming said dielectric layer comprises depositing a dielectric material to have a uniform thickness.
Claim 19
Independent Claim
210 words
A method for forming a capacitor, comprising the following steps: a) depositing a first polysilicon layer on a starting surface; b) doping said first polysilicon layer to increase a conductivity thereof; c) depositing a second polysilicon layer to overlie said first polysilicon layer; d) adjusting a temperature and a pressure of said second polysilicon layer during said step of depositing in order to cause a nucleation thereof; e) forming hemispherical grains of said second polysilicon layer during said step of adjusting; f) providing an oxygen and phosphorous ambient; g) oxidizing portions of said first and said second polysilicon layers in said ambient to form an oxide layer comprising phosphorous ions, said oxidizing consuming said portions to decrease a size of said grains and to increase a distance between said grains; h) driving at least a portion of said phosphorous into said second polysilicon layer during said step of oxidizing to increase a conductivity of said second polysilicon layer; i) performing a wet etch to remove said oxide layer; j) forming a dielectric layer to overlie said first and said second polysilicon layers; and k) forming a cell plate layer to overlie said dielectric layer, wherein said first and said second polysilicon layers comprise a storage node plate of said capacitor.
Claim 20
Independent Claim
210 words
A method for forming a capacitor, comprising the following steps: a) depositing a first polysilicon layer on a starting surface; b) doping said first polysilicon layer to increase a conductivity thereof; c) depositing a second polysilicon layer to overlie said first polysilicon layer; d) adjusting a temperature and a pressure of said second polysilicon layer during said step of depositing in order to cause a nucleation thereof; e) forming hemispherical grains of said second polysilicon layer during said step of adjusting; f) providing an oxygen and phosphorous ambient; g) oxidizing portions of said first and said second polysilicon layers in said ambient to form an oxide layer comprising phosphorous ions, said oxidizing consuming said portions to decrease a size of said grains and to increase a distance between said grains; h) driving at least a portion of said phosphorous into said second polysilicon layer during said step of oxidizing to increase a conductivity of said second polysilicon layer; i) performing a wet etch to remove said oxide layer; j) forming a dielectric layer to overlie said first and said second polysilicon layers; and k) forming a cell plate layer to overlie said dielectric layer, wherein said first and said second polysilicon layers comprise a storage node plate of said capacitor.
Claim 21
Dependent Claim
41 words
The method as specified in claim 15, further comprising controlling said step of oxidizing to control a consumption of said first and said second polysilicon layers such that a surface area of said storage node plate is enhanced thereby increasing capacitance.
References Cited (Backward Citations)
US5318920A
Cited
US5372962A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-12-08 | 2001-06-09 | 2001-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-12-08 | 2005-06-09 | 2005-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-12-08 | 2009-06-09 | 2009-12-09 | $7700.00 | Window Closed / Lapsed |