Surface-coated vessel and process for producing same
Assignee: Mitsui Chemicals Inc
•
Filing: 1996-01-29
•
Granted: 1997-12-02
•
Expires: 2016-01-29
Abstract
Abstract PCT No. PCT/JP96/00163 Sec. 371 Date Sep. 20, 1996 Sec. 102(e) Date Sep. 20, 1996 PCT Filed Jan. 29, 1996 PCT Pub. No. WO96/23842 PCT Pub. Date Aug. 8, 1996A surface-coated vessel or a surface-coated product having a hard coating layer is obtained, by coating a substrate of, for example, resin product with a resin composition for hard coating which comprises (a) a poly[(meth)acryloyloxyalkyl](iso)cyanurate represented by the following general formula (1) or (2): <IMAGE> (1) <IMAGE> (2) wherein X1, X2 and X3 are each an acryloyl group, methacryloyl group, hydrogen atom or an alkyl group, with a proviso that at least two of them are (meth)acryloyl groups, and R1, R2 and R3 are each an oxyalkylene group or a polyoxyalkylene group; (b) a poly(meth)acrylated polyoxyalkane polyol; (c) a photopolymerization initiator consisting of 2-methyl-1-[4-(methylthio)phenyl]-2-morpholino-1-propanone; (d) a photopolymerization initiator based on thioxanthone; (e) a UV-absorber based on monohydroxybenzophenone; (f) an organic solvent. Such surface-coated products and vessels have a hard coat which is more excellent than that of the prior art especially in the curing characteristics, such as the rate of curing etc., as well as in the coating properties, such as surface hardness, fastness to scratch and abrasion, flexibility, surface gloss, heat resistance, fastness to solvents and to alkali, weather resistance and tight adhesion onto substrates, so that they can constitute reclamable coated products in a form of, for example, returnable bottles.
Inventors
- 👤 Hajime Inagaki
- 👤 Koji Yoshii
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:46
CPC Classifications
G; G06; G06K; G06K7/00; G06K7/10; G06K7/10544; G06K7/10554; G06K7/10594; G06K7/10683; G06K7/10693; C; C08; C08F; C08F222/00; C08F222/10; C08F222/1006; C08F222/106; C09; C09D; C09D4/00; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
265 words
A surface-coated vessel in which a hard coating layer improved in surface hardness, wear resistance, alkali resistance and weather resistance is formed over the outer surface of a vessel made of a resin based on polyester, said coating layer being obtained from a resin composition which comprises (a) a poly((meth)acryloyloxyalkyl) (iso)cyanurate represented by the following general formula (1) or (2): ##STR3## wherein X 1 , X 2 and X 3 are each an acryloyl group, methacryloyl group, hydrogen atom or an alkyl group, with a proviso that at least two of them are (meth)acryloyl groups, and R 1 , R 2 and R 3 are each an oxyalkylene group or a polyoxyalkylene group; (b) a poly(meth)acrylated polyoxyalkane polyol having in the molecule at least one ether bond and at least three hydroxy groups, in the range from 5 to 300 parts per 100 parts by weight of said component (a); (c) a photopolymerization initiator consisting of 2-methyl-1-(4-(methylthio)phenyl)-2-morpholino-1-propanone in the range from 0.01 to 20 parts per 100 parts by weight of the sum of the above two components (a) and (b); (d) a photopolymerization initiator based on thioxanthone in the range from 0.001 to 5 parts per 100 parts by weight of the sum of the components (a) and (b); (e) a UV-absorber based on monohydroxybenzophenone in the range from 0.01 to 20 parts per 100 parts by weight of the sum of the components (a) and (b); and (f) an organic solvent in the range from 5 to 2,000 parts per 100 parts by weight of the sum of the components (a) and (b).
Claim 2
Dependent Claim
265 words
A surface-coated vessel in which a hard coating layer improved in surface hardness, wear resistance, alkali resistance and weather resistance is formed over the outer surface of a vessel made of a resin based on polyester, said coating layer being obtained from a resin composition which comprises (a) a poly((meth)acryloyloxyalkyl) (iso)cyanurate represented by the following general formula (1) or (2): ##STR3## wherein X 1 , X 2 and X 3 are each an acryloyl group, methacryloyl group, hydrogen atom or an alkyl group, with a proviso that at least two of them are (meth)acryloyl groups, and R 1 , R 2 and R 3 are each an oxyalkylene group or a polyoxyalkylene group; (b) a poly(meth)acrylated polyoxyalkane polyol having in the molecule at least one ether bond and at least three hydroxy groups, in the range from 5 to 300 parts per 100 parts by weight of said component (a); (c) a photopolymerization initiator consisting of 2-methyl-1-(4-(methylthio)phenyl)-2-morpholino-1-propanone in the range from 0.01 to 20 parts per 100 parts by weight of the sum of the above two components (a) and (b); (d) a photopolymerization initiator based on thioxanthone in the range from 0.001 to 5 parts per 100 parts by weight of the sum of the components (a) and (b); (e) a UV-absorber based on monohydroxybenzophenone in the range from 0.01 to 20 parts per 100 parts by weight of the sum of the components (a) and (b); and (f) an organic solvent in the range from 5 to 2,000 parts per 100 parts by weight of the sum of the components (a) and (b).
Claim 3
Dependent Claim
18 words
A surface-coated vessel according to claim 1, wherein the resin based on polyester consists essentially of polyethylene terephthalate.
Claim 4
Dependent Claim
16 words
A surface-coated vessel according to claim 1 or 2, wherein the vessel is a returnable bottle.
Claim 5
Dependent Claim
264 words
A process for producing a surface-coated vessel improved in surface hardness, wear resistance, alkali resistance and weather resistance comprising the process step of coating the outer surface of a vessel made of a resin based on polyester with a resin composition for hard coating which comprises (a) a poly((meth)acryloyloxyalkyl) (iso)cyanurate represented by the following general formula (1) or (2): ##STR4## wherein X 1 , X 2 and X 3 are each an acryloyl group, methacryloyl group, hydrogen atom or an alkyl group, with a proviso that at least two of them are (meth)acryloyl groups, and R 1 , R 2 and R 3 are each an oxyalkylene group or a polyoxyalkylene group; (b) a poly(meth)acrylated polyoxyalkane polyol having in the molecule at least one ether bond and at least three hydroxy groups, in the range from 5 to 300 parts per 100 parts by weight of said component (a); (c) a photopolymerization initiator consisting of 2-methyl-1-(4-(methylthio)phenyl)-2-morpholino-1-propanone in the range from 0.01 to 20 parts per 100 parts by weight of the sum of the above two components (a) and (b); (d) a photopolymerization initiator based on thioxanthone in the range from 0.001 to 5 parts per 100 parts by weight of the sum of the components (a) and (b); (e) a UV-absorber based on monohydroxybenzophenone in the range from 0.01 to 20 parts per 100 parts by weight of the sum of the components (a) and (b); and (f) an organic solvent in the range from 5 to 2,000 parts per 100 parts by weight of the sum of the components (a) and (b).
Claim 6
Dependent Claim
264 words
A process for producing a surface-coated vessel improved in surface hardness, wear resistance, alkali resistance and weather resistance comprising the process step of coating the outer surface of a vessel made of a resin based on polyester with a resin composition for hard coating which comprises (a) a poly((meth)acryloyloxyalkyl) (iso)cyanurate represented by the following general formula (1) or (2): ##STR4## wherein X 1 , X 2 and X 3 are each an acryloyl group, methacryloyl group, hydrogen atom or an alkyl group, with a proviso that at least two of them are (meth)acryloyl groups, and R 1 , R 2 and R 3 are each an oxyalkylene group or a polyoxyalkylene group; (b) a poly(meth)acrylated polyoxyalkane polyol having in the molecule at least one ether bond and at least three hydroxy groups, in the range from 5 to 300 parts per 100 parts by weight of said component (a); (c) a photopolymerization initiator consisting of 2-methyl-1-(4-(methylthio)phenyl)-2-morpholino-1-propanone in the range from 0.01 to 20 parts per 100 parts by weight of the sum of the above two components (a) and (b); (d) a photopolymerization initiator based on thioxanthone in the range from 0.001 to 5 parts per 100 parts by weight of the sum of the components (a) and (b); (e) a UV-absorber based on monohydroxybenzophenone in the range from 0.01 to 20 parts per 100 parts by weight of the sum of the components (a) and (b); and (f) an organic solvent in the range from 5 to 2,000 parts per 100 parts by weight of the sum of the components (a) and (b).
Claim 7
Dependent Claim
26 words
A process according to claim 4, wherein the vessel is coated with the resin composition so as to reach a coating layer thickness of 0.5-50 μm.
Claim 8
Dependent Claim
26 words
A process according to claim 4 or 5, wherein a UV-exposure is incorporated so as to reach a cumulative exposure intensity of 500-5,000 mJ/cm 2 .
Claim 9
Dependent Claim
28 words
A process according to claim 4 or 5, wherein the coating step comprises applying the resin composition onto the outer surface of the vessel while rotating the vessel.
Claim 10
Dependent Claim
35 words
A process according to claim 4 or 5, wherein it comprises a further step of drying the coating layer at a temperature below the glass transition temperature of the polyester resin while rotating the vessel.
Claim 11
Dependent Claim
37 words
A process according to claim 4 or 5, wherein it comprises a further step of forming a hard coat by hardening the coating layer by irradiating the coating layer with a UV ray while rotating the vessel.
Claim 12
Dependent Claim
32 words
A process according to claim 4 or 5, wherein the coating step comprises applying the resin composition onto the outer surface of the vessel while rotating the vessel around a horizontal axis.
Claim 13
Dependent Claim
38 words
A process according to claim 4 or 5, which comprises a further step of drying the coating layer at a temperature below the glass transition temperature of the polyester resin while rotating the vessel around a horizontal axis.
Claim 14
Dependent Claim
40 words
A process according to claim 4 or 5, which comprises a further step of forming a hard coat by hardening the coating layer by irradiating the coating layer with a UV ray while rotating the vessel around a horizontal axis.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-12-01 | 2001-06-02 | 2001-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-12-01 | 2005-06-02 | 2005-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-12-01 | 2009-06-02 | 2009-12-02 | $7700.00 | Window Closed / Lapsed |