Method of forming an electrically conductive polymer bump over an aluminum electrode
Assignee: NXP USA Inc
•
Filing: 1995-07-24
•
Granted: 1997-10-07
•
Expires: 2015-07-24
Abstract
Abstract A method of forming an electrically conductive polymer bump (22) over an aluminum electrode (21) produces low contact resistance for an interconnect structure (24). Aluminum oxide is first removed from the aluminum electrode (21). Tiron and palladium are subsequently bonded to the fresh surface of the aluminum electrode (21). Finally, the electrically conductive polymer bump (22) is formed over the aluminum electrode (21). The Tiron and palladium improve the electrical contact between the conductive polymer bump (22) and the aluminum electrode (21) thereby reducing the contact resistance. The Tiron also inhibits corrosion of the aluminum electrode (21) and enhances the conductivity by catalytically shrinking the cyanate ester conductive bump.
Inventors
- 👤 William H. Lytle
- 👤 Treliant Fang
- 👤 Jong-Kai Lin
- 👤 Ravinder K. Sharma
- 👤 Naresh C. Saha
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:02
CPC Classifications
H; H10; H10W; H10W72/00; H10W72/01; H10W72/012; H10W72/019; H10W72/20; H10W72/251; H10W72/90; H10W72/921; H10W72/923; H10W72/951; H10W72/952
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
85 words
A method of forming an electrically conductive polymer bump over an aluminum electrode, the method comprising: providing a substrate; disposing an aluminum layer over the substrate; patterning the aluminum layer to form the aluminum electrode; etching the aluminum electrode with an etchant to remove aluminum oxide from the aluminum electrode; immersing the substrate in aqueous solutions of a chelate and metallic ions; rinsing the substrate; drying the substrate; forming the electrically conductive polymer bump over the aluminum electrode; and curing the electrically conductive polymer bump.
Claim 2
Independent Claim
85 words
A method of forming an electrically conductive polymer bump over an aluminum electrode, the method comprising: providing a substrate; disposing an aluminum layer over the substrate; patterning the aluminum layer to form the aluminum electrode; etching the aluminum electrode with an etchant to remove aluminum oxide from the aluminum electrode; immersing the substrate in aqueous solutions of a chelate and metallic ions; rinsing the substrate; drying the substrate; forming the electrically conductive polymer bump over the aluminum electrode; and curing the electrically conductive polymer bump.
Claim 3
Dependent Claim
31 words
The method according to claim 1, further comprising selecting the substrate from the group consisting of silicon, silicon germanium, gallium arsenide, indium phosphide, printed wiring boards, organic substrates, and inorganic substrates.
Claim 4
Dependent Claim
24 words
The method according to claim 1, further comprising providing less than five percent copper and less than three percent silicon in the aluminum layer.
Claim 5
Dependent Claim
30 words
The method according to claim 1, further selecting the etchant from the group consisting of alkali metal hydroxides, phosphoric acid, and other non-oxidizing acids having a pKa less than five.
Claim 6
Dependent Claim
36 words
The method according to claim 1, wherein the immersing step further comprises first immersing the substrate in a first aqueous solution of Tiron and then immersing the substrate in a second aqueous solution of palladium salts.
Claim 7
Dependent Claim
35 words
The method according to claim 1, wherein the immersing step further comprises first immersing the substrate in a first aqueous solution of palladium and then immersing the substrate in a second aqueous solution of Tiron.
Claim 8
Dependent Claim
20 words
The method according to claim 1, wherein the immersing step comprises immersing the substrate in aqueous solutions which are buffered.
Claim 9
Dependent Claim
23 words
The method according to claim 1, further comprising selecting the electrically conductive polymer bump from the group consisting of epoxy and cyanate ester.
Claim 10
Independent Claim
76 words
A method of forming a conductive bump over an aluminum pad, the method comprising: providing a substrate having the aluminum pad; removing aluminum oxide from the aluminum pad; exposing the aluminum pad to an aqueous solution having metallic ions and to an aqueous solution having a chemical with a formation constant with aluminum greater than formation constant of aluminum with hydroxide; rinsing the substrate; drying the substrate; and forming the conductive bump over the aluminum pad.
Claim 11
Independent Claim
76 words
A method of forming a conductive bump over an aluminum pad, the method comprising: providing a substrate having the aluminum pad; removing aluminum oxide from the aluminum pad; exposing the aluminum pad to an aqueous solution having metallic ions and to an aqueous solution having a chemical with a formation constant with aluminum greater than formation constant of aluminum with hydroxide; rinsing the substrate; drying the substrate; and forming the conductive bump over the aluminum pad.
Claim 12
Dependent Claim
27 words
The method according to claim 9, further providing an aluminum pad having less than five percent copper and less than three percent silicon for the aluminum pad.
Claim 13
Dependent Claim
44 words
The method according to claim 9, further providing an additional aqueous solution to remove the aluminum oxide and further selecting the additional aqueous solution from the group consisting of alkali metal hydroxides, phosphoric acid, and other non-oxidizing acids having a pKa less than five.
Claim 14
Dependent Claim
36 words
The method according to claim 9, further comprising selecting the metallic ions from the group consisting of palladium, silver, copper, zinc, gold, tin, iridium, and other metallic ions with reduction potentials greater than approximately -0.77 volts.
Claim 15
Dependent Claim
19 words
The method according to claim 9, further providing an acidic aqueous solution for the aqueous solution having metallic ions.
Claim 16
Dependent Claim
37 words
The method according to claim 9, further comprising selecting the chemical from the group consisting of Tiron, 5-sulfosalicylic acid, pyrocatechol-3,5 sulfonic acid, salicylic acid, and other complexing agents having a log K 1 with aluminum greater 9.27.
Claim 17
Dependent Claim
22 words
The method according to claim 9, further providing a chelation agent in an alkaline condition for the aqueous solution having the chemical.
Claim 18
Dependent Claim
20 words
The method according to claim 9, wherein the forming step further comprises dispensing the conductive bump over the aluminum pad.
Claim 19
Dependent Claim
23 words
The method according to claim 9, wherein the forming step further comprises using cyanate ester filled with metallic particles for the conductive bump.
Claim 20
Dependent Claim
18 words
The method according to claim 9, wherein the forming step further comprises using epoxy for the conductive bump.
Claim 21
Independent Claim
64 words
A method of forming a conductive layer over an aluminum layer, the method comprising: providing a substrate having the aluminum layer; etching aluminum oxide off of the aluminum layer; dipping the aluminum layer into an acidic aqueous solution of palladium salts; rinsing the substrate with deionized water; blow drying the substrate with an inert gas; and providing the conductive layer over the aluminum layer.
Claim 22
Independent Claim
64 words
A method of forming a conductive layer over an aluminum layer, the method comprising: providing a substrate having the aluminum layer; etching aluminum oxide off of the aluminum layer; dipping the aluminum layer into an acidic aqueous solution of palladium salts; rinsing the substrate with deionized water; blow drying the substrate with an inert gas; and providing the conductive layer over the aluminum layer.
Claim 23
Dependent Claim
32 words
The method according to claim 19, further providing phosphoric acid for the etching step and further comprising dipping the aluminum layer into an alkaline aqueous Tiron solution prior to the rinsing step.
References Cited (Backward Citations)
US5055356A
Cited
US5074947A
Cited
US5196371A
Cited
US5130052A
Cited
US5565378A
Cited
US5583073A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-10-06 | 2001-04-07 | 2001-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-10-06 | 2005-04-07 | 2005-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-10-06 | 2009-04-07 | 2009-10-07 | $7700.00 | Window Closed / Lapsed |