Method to produce flexible ceramic thermal protection system resistant to high aeroacoustic noise

Claim 1

A method of producing a three dimensional angle interlock ceramic fabric structure which is stable to high aeroacoustic noise of about 170 decibels and to high temperatures up to about 2500° F., which method comprises: (a) obtaining multiple separate strands of a ceramic fiber or ceramic tow suitable for weaving having multiple warp fibers and multiple fill fibers; (b) utilizing a modified fly-shuttle loom or a rapier shuttleless loom which has nip rolls, a modified fabric advancement mechanism, and at least eight harnesses in conjunction with a Dobby pattern chain; (c) utilizing sufficient heddles for each warp fiber and a reed which accommodates about 168 ends per inch for a given fabric width wherein a multilayered top fabric, rib fabric, and a single layered bottom fabric are each woven of high temperature ceramic fibers with a separate shuttle; (d) drawing the warp sheets into the loom through a series of tensioning bars and into each respective harness for each fabric; (e) utilizing an additional roller system to drive extra length of a rib fiber into the loom; (f) translating a warp and fill fiber sequence into a Dobby pattern chain which chain utilizes bars and pegs wherein each bar represents one fill fiber insertion and each peg indicates a lifting of a specific harness; (g) weaving the fiber in a particular direction such that the Dobby mechanism reads one pattern bar instructing the loom to raise or lower one or more harnesses creating a shed opening; (h) conveying a shuttle through the shed opening and dispensing a fill yarn in one direction into a specific location; (i) locking the fill yarn in place as the harness achieves its highest or lowest position which creates the next shed sequence, concurrently the reed pushes back the fill fiber into place and moves to its original back most position; (j) utilizing the same shuttle to traverse the created fabric in a direction which is opposite to the direction in step (h) dispensing another fill yarn in the newly formed shed opening; (k) interconnecting said rib fabric at locations on said top and bottom fibers designated as nodes; (l) repeating steps (g), (h), (i), (j) and (k) as needed to create three dimensional angular triangular prism or trapezoidal prism volumes defined by flutes formed at a 90° angle to the direction of the fiber weaving; (m) filling said three-dimensional prism volume with insulation of heat resistant ceramic fibers to create a formed structure; and (n) cleaning said formed structure at temperatures between about 800° F. and 2000° F.

Claim 2

A method of producing a three dimensional angle interlock ceramic fabric structure which is stable to high aeroacoustic noise of about 170 decibels and to high temperatures up to about 2500° F., which method comprises: (a) obtaining multiple separate strands of a ceramic fiber or ceramic tow suitable for weaving having multiple warp fibers and multiple fill fibers; (b) utilizing a modified fly-shuttle loom or a rapier shuttleless loom which has nip rolls, a modified fabric advancement mechanism, and at least eight harnesses in conjunction with a Dobby pattern chain; (c) utilizing sufficient heddles for each warp fiber and a reed which accommodates about 168 ends per inch for a given fabric width wherein a multilayered top fabric, rib fabric, and a single layered bottom fabric are each woven of high temperature ceramic fibers with a separate shuttle; (d) drawing the warp sheets into the loom through a series of tensioning bars and into each respective harness for each fabric; (e) utilizing an additional roller system to drive extra length of a rib fiber into the loom; (f) translating a warp and fill fiber sequence into a Dobby pattern chain which chain utilizes bars and pegs wherein each bar represents one fill fiber insertion and each peg indicates a lifting of a specific harness; (g) weaving the fiber in a particular direction such that the Dobby mechanism reads one pattern bar instructing the loom to raise or lower one or more harnesses creating a shed opening; (h) conveying a shuttle through the shed opening and dispensing a fill yarn in one direction into a specific location; (i) locking the fill yarn in place as the harness achieves its highest or lowest position which creates the next shed sequence, concurrently the reed pushes back the fill fiber into place and moves to its original back most position; (j) utilizing the same shuttle to traverse the created fabric in a direction which is opposite to the direction in step (h) dispensing another fill yarn in the newly formed shed opening; (k) interconnecting said rib fabric at locations on said top and bottom fibers designated as nodes; (l) repeating steps (g), (h), (i), (j) and (k) as needed to create three dimensional angular triangular prism or trapezoidal prism volumes defined by flutes formed at a 90° angle to the direction of the fiber weaving; (m) filling said three-dimensional prism volume with insulation of heat resistant ceramic fibers to create a formed structure; and (n) cleaning said formed structure at temperatures between about 800° F. and 2000° F.