Porous carbonaceous material and a method for producing the same
Assignee: Osaka Gas Co Ltd
•
Filing: 1994-11-01
•
Granted: 1997-07-15
•
Expires: 2014-11-01
Abstract
Abstract A slurry containing a precursor fiber convertible to carbon fiber and/or a carbon fiber and, based on 100 parts by weight of the fiber, 10 to 300 parts by weight of a thermosetting resin, e.g. phenol resin, is processed into a random web. This web may contain a pitch or an organic granular material. The web is hot-pressed between a pair of belts while curing of the resin is inhibited to prepare a prepreg sheet. This sheet is disposed, leaving a clearance, in a mold having ribs on a molding surface and heated over the melting point of the resin for expansion and complete cure to provide a porous composite sheet equipped with grooves. This porous composite sheet is carbonized or graphitized to produce a porous carbonaceous material for use as a fuel cell electrode material and so on. This porous carbonaceous material has high homogeneity, gas permeability, electrical conductivity, heat conductivity and mechanical strength.
Inventors
- 👤 Hiroyuki Tajiri
- 👤 Yoshiteru Nakagawa
- 👤 Yoshiaki Iwaya
- 👤 Yoshiharu Tanaka
- 👤 Keiichi Asami
- 👤 Katsuyuki Touma
- 👤 Shinji Okumura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 00:01
CPC Classifications
D; D01; D01F; D01F9/00; D01F9/08; D01F9/12; D01F9/14; D01F9/145; C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/522; C04B35/528; C04B35/532; C04B35/622; C04B35/626; C04B35/62605; C04B35/6269; C04B35/71; C04B35/78; C04B35/80; C04B35/83; C04B38/00; C04B38/0022; D01F9/16; D01F9/20; D01F9/21; D01F9/22; D01F9/24; H; H01; H01M; H01M4/00; H01M4/02; H01M4/64; H01M4/66; H01M4/663; H01M4/86; H01M4/96; C04B2111/00; C04B2111/00474; C04B2111/00853; C04B2201/00; C04B2235/00; C04B2235/02; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/524; C04B2235/5248; C04B2235/5252; C04B2235/526; C04B2235/5264; C04B2235/60; C04B2235/602; C04B2235/70; C04B2235/96; C04B2235/9607; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y02E60/30; Y02E60/50; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24562; Y10T428/2457; Y10T428/24744
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
74 words
A process for producing a porous composite sheet which comprises hot-pressing a random web comprising a precursor fiber convertible to carbon fiber and/or a carbon fiber and a carbonizable or graphitizable thermosetting resin while curing of said resin is inhibited to provide a prepreg sheet; and heating said prepreg sheet at a temperature of the melting point of said thermosetting resin or more under no load, for expansion and complete cure of said resin.
Claim 2
Dependent Claim
74 words
A process for producing a porous composite sheet which comprises hot-pressing a random web comprising a precursor fiber convertible to carbon fiber and/or a carbon fiber and a carbonizable or graphitizable thermosetting resin while curing of said resin is inhibited to provide a prepreg sheet; and heating said prepreg sheet at a temperature of the melting point of said thermosetting resin or more under no load, for expansion and complete cure of said resin.
Claim 3
Dependent Claim
68 words
The process for producing a porous composite sheet as claimed in claim 1, wherein one or more plies of said web is hot-pressed at a temperature of 70° to 280° C. under pressure without complete curing of said resin to provide a prepreg sheet and the resulting prepreg sheet is heated again at a temperature of 150° to 250° C. for expansion and complete cure of said resin.
Claim 4
Dependent Claim
31 words
The process for producing a porous composite sheet as claimed in claim 1, wherein said hot-pressing of a web into a sheet is carried out using a pair of endless belts.
Claim 5
Dependent Claim
57 words
The process for producing a porous composite sheet as claimed in claim 2, wherein said hot-pressing of a web into a sheet is performed at a temperature of 70° to 170° C. and a pressure of 2 to 50 kg/cm 2 to provide a prepreg sheet having a bulk density of 0.8 to 1.5 g/cm 3 .
Claim 6
Dependent Claim
54 words
The process for producing a porous composite sheet as claimed in claim 1, wherein said hot-pressing of a web into a sheet is carried out at 170° to 250° C. and a pressure of 2 to 50 kg/cm 2 provide a prepreg sheet having a bulk density of 0.6 to 1.0 g/cm 3 .
Claim 7
Dependent Claim
46 words
The process for producing a porous composite sheet as claimed in claim 4, wherein said prepreg sheet is disposed in a mold, leaving a clearance, and heated at a temperature over the melting point of said thermosetting resin for expansion and complete cure of the resin.
Claim 8
Dependent Claim
44 words
The process for producing a porous composite sheet as claimed in claim 4, wherein said prepreg sheet is disposed, leaving a clearance, in a mold having flat opposed molding surfaces and heated at 150° to 250° C. for expansion and cure of said resin.
Claim 9
Dependent Claim
67 words
The process for producing a porous composite sheet as claimed in claim 4, wherein said prepreg sheet is disposed, leaving a clearance, in a mold comprising at least one pair of opposed surfaces defining a molding compartment, at least one of said opposed surfaces being provided with a plurality of rib-shaped projections, and heated at 150° to 250° C. for expansion and complete cure of said resin.
Claim 10
Dependent Claim
126 words
A process for producing a porous composite sheet which comprises hot-pressing one or more plies of a web wherein a prepreg sheet is disposed in a first mold comprising at least one pair of opposed surfaces defining a molding compartment, at least one of said opposed surfaces being provided with grooves, under heating at 80° to 200° to provide a ribbed sheet and disposing said ribbed sheet, leaving a clearance, in a second mold comprising at least one pair of opposed surfaces defining a molding compartment, at least one of said opposed surfaces being provided with grooves larger than the grooves of said first mold, and heating said ribbed sheet at a temperature of 150° to 250° C. for expansion and complete cure of said resin.
Claim 11
Dependent Claim
126 words
A process for producing a porous composite sheet which comprises hot-pressing one or more plies of a web wherein a prepreg sheet is disposed in a first mold comprising at least one pair of opposed surfaces defining a molding compartment, at least one of said opposed surfaces being provided with grooves, under heating at 80° to 200° to provide a ribbed sheet and disposing said ribbed sheet, leaving a clearance, in a second mold comprising at least one pair of opposed surfaces defining a molding compartment, at least one of said opposed surfaces being provided with grooves larger than the grooves of said first mold, and heating said ribbed sheet at a temperature of 150° to 250° C. for expansion and complete cure of said resin.
Claim 12
Dependent Claim
35 words
The process for producing porous composite sheet as claimed in claim 6, wherein said prepreg sheet is disposed in said mold, leaving a clearance corresponding to 0.1 to 4 times the thickness of said sheet.
Claim 13
Dependent Claim
35 words
The process for producing a porous composite sheet as claimed in claim 6, wherein said prepreg sheet in said mold is heated at 150° to 250° C. for expansion and complete cure of the resin.
Claim 14
Dependent Claim
33 words
The process for producing a porous composite sheet as claimed in claim 1, wherein said web contains at least the carbon fiber of said precursor fiber convertible to carbon fiber and carbon fiber.
Claim 15
Dependent Claim
37 words
The process for producing a porous composite sheet as claimed in claim 1, wherein said web contains said precursor fiber convertible to carbon fiber and carbon fiber in a ratio of 10/90 to 90/10 (% by weight).
Claim 16
Dependent Claim
30 words
The process for producing a porous composite sheet as claimed in claim 1, wherein said thermosetting resin is a resin having a carbonization yield of 40 to 75% by weight.
Claim 17
Dependent Claim
21 words
The process for producing a porous composite sheet as claimed in claim 1, wherein said thermosetting resin is a phenolic resin.
Claim 18
Dependent Claim
47 words
The process for producing a porous composite sheet as claimed in claim 1, wherein said web to be hot-pressed comprises a precursor fiber convertible to carbon fiber and/or a carbon fiber, a thermosetting resin with a carbonization yield of 40 to 75 weight %, and a pitch.
Claim 19
Dependent Claim
49 words
The process for producing a porous composite sheet as claimed in claim 1, wherein said web to be hot-pressed comprises 10 to 300 parts by weight of a thermosetting resin and 10 to 300 parts by weight of a pitch relative to 100 parts by weight of the fiber.
Claim 20
Dependent Claim
32 words
The process for producing a porous composite sheet as claimed in claim 16, wherein the pitch component of said web to be hot-pressed has a softening point of 150° to 400° C.
Claim 21
Dependent Claim
29 words
The process for producing a porous composite sheet as claimed in claim 1, wherein said web to be hot-pressed further contains an organic granular material as a pore-forming agent.
Claim 22
Dependent Claim
30 words
The process for producing a porous composite sheet as claimed in claim 19, wherein the organic granular material contained in the web to be hot-pressed is a cured thermosetting resin.
Claim 23
Dependent Claim
41 words
The process for producing a porous composite sheet as claimed in claim 19, wherein a web containing an organic granular material composed of a pitch and a resin with a carbonization yield of not greater than 30% by weight is hot-pressed.
Claim 24
Dependent Claim
32 words
The process for producing a porous composite sheet as claimed in claim 21, wherein the amount of the pitch based on the whole organic granular material is 10 to 75% by weight.
Claim 25
Dependent Claim
39 words
The process for producing a porous composite sheet as claimed in claim 18, wherein a web containing 10 to 500 parts by weight of said organic granular material relative to 100 parts by weight of the fiber is hot-pressed.
Claim 26
Dependent Claim
146 words
A process for producing a porous composite sheet as claimed in claim 1, which comprises a prepreg-forming step of hot-pressing a web including a fiber component comprising at least the carbon fiber of said precursor fiber convertible to carbon fiber and said carbon fiber and, based on 100 parts by weight of said fiber component, 20 to 250 parts by weight of a carbonizable or graphitizable thermosetting resin, 0 to 250 parts by weight of a pitch having a softening point of 200° to 400° C. and 0 to 300 parts by weight of an organic granular material as a pore-forming agent using a pair of endless belts at a temperature of 70° to 280° C. to provide a prepreg sheet, and an expansion-curing step of heating said prepreg sheet at a temperature of 150° to 250° C. for expansion and complete cure of the resin.
Claim 27
Dependent Claim
66 words
The process for producing a porous composite sheet as claimed in claim 24, wherein the hot-pressing of the web is carried out at 170° to 280° C. in the prepreg-forming step to inhibit curing of said thermosetting resin and the prepreg sheet thus obtained is heated at 150° to 250° C. under no load for expansion and complete cure of the resin in the expansion-curing step.
Claim 28
Dependent Claim
123 words
The process for producing a porous composite sheet as claimed in claim 24, wherein the hot-pressing of said web in the hot-pressing step is carried out using a metal mold optionally having groove-like recesses on one of its molding surfaces at a temperature of 80° to 200° C. and a pressure of 2 to 1000 kg/cm 2 while curing of the thermosetting resin is inhibited and the expansion and cure of the resulting prepreg sheet in the expansion-curing step is carried out by disposing said sheet, leaving a clearance, in a metal mold optionally having groove-shaped recesses on one of its molding surfaces and heating the sheet at a temperature of 150° to 250° C. for expansion and complete cure of the resin.
Claim 29
Dependent Claim
84 words
A process of producing a porous carbonaceous material which comprises hot-pressing at least one of a random web comprising a precursor fiber convertible to carbon fiber and/or a carbon fiber and a carbonizable or graphitizable thermosetting resin while curing of said resin is inhibited to provide a prepreg sheet, heating the prepreg sheet at a temperature over the melting temperature of said resin under no load, for expansion and complete cure of the resin, and either carbonizing or graphitizing the resultant porous composite sheet.
Claim 30
Dependent Claim
84 words
A process of producing a porous carbonaceous material which comprises hot-pressing at least one of a random web comprising a precursor fiber convertible to carbon fiber and/or a carbon fiber and a carbonizable or graphitizable thermosetting resin while curing of said resin is inhibited to provide a prepreg sheet, heating the prepreg sheet at a temperature over the melting temperature of said resin under no load, for expansion and complete cure of the resin, and either carbonizing or graphitizing the resultant porous composite sheet.
Claim 31
Dependent Claim
28 words
The process for producing a porous carbonaceous material as claimed in claim 27 wherein said porous composite sheet is calcined at a temperature of 1000° to 3300° C.
Claim 32
Dependent Claim
167 words
A process for manufacturing a porous carbon which comprises a step of hot-pressing at least one ply of a random web comprising a fiber component composed of a precursor fiber convertible to carbon fiber and/or a carbon fiber and, based on 100 parts by weight of said fiber component, 15 to 275 parts by weight of a carbonizable or graphitizable thermosetting resin with a carbonization yield of 50 to 75% by weight, 0 to 250 parts by weight of a pitch with a carbonization yield of not less than 50% by weight, and 0 to 250 parts by weight of an organic granular material with a mean particle diameter of 0.1 to 500 μM while curing of said thermosetting resin is inhibited to provide a prepreg sheet; a step of heating said prepreg sheet at a temperature over the melting temperature of said resin under no load for expansion and complete cure of the resin; and a step of carbonizing or graphitizing the resultant porous composite sheet.
Claim 33
Dependent Claim
167 words
A process for manufacturing a porous carbon which comprises a step of hot-pressing at least one ply of a random web comprising a fiber component composed of a precursor fiber convertible to carbon fiber and/or a carbon fiber and, based on 100 parts by weight of said fiber component, 15 to 275 parts by weight of a carbonizable or graphitizable thermosetting resin with a carbonization yield of 50 to 75% by weight, 0 to 250 parts by weight of a pitch with a carbonization yield of not less than 50% by weight, and 0 to 250 parts by weight of an organic granular material with a mean particle diameter of 0.1 to 500 μM while curing of said thermosetting resin is inhibited to provide a prepreg sheet; a step of heating said prepreg sheet at a temperature over the melting temperature of said resin under no load for expansion and complete cure of the resin; and a step of carbonizing or graphitizing the resultant porous composite sheet.
Claim 34
Dependent Claim
75 words
A porous composite sheet which is prepared by a process comprising hot-pressing a random web comprising a precursor fiber convertible to carbon fiber and/or a carbon fiber and a carbonizable or graphitizable thermosetting resin while curing of said resin is inhibited to provide a prepreg sheet; and heating said prepreg sheet at a temperature of the melting point of said thermosetting resin or more under no load, for expansion and complete cure of said resin.
Claim 35
Dependent Claim
75 words
A porous composite sheet which is prepared by a process comprising hot-pressing a random web comprising a precursor fiber convertible to carbon fiber and/or a carbon fiber and a carbonizable or graphitizable thermosetting resin while curing of said resin is inhibited to provide a prepreg sheet; and heating said prepreg sheet at a temperature of the melting point of said thermosetting resin or more under no load, for expansion and complete cure of said resin.
Claim 36
Dependent Claim
85 words
A porous carbonaceous material which is prepared by a process comprising hot-pressing at least one of a random web comprising a precursor fiber convertible to carbon fiber and/or a carbon fiber and a carbonizable or graphitizable thermosetting resin while curing of said resin is inhibited to provide a prepreg sheet, heating the prepreg sheet at a temperature over the melting temperature of said resin under no load for expansion and complete cure of the resin, and either carbonizing or graphitizing the resultant porous composite sheet.
Claim 37
Dependent Claim
85 words
A porous carbonaceous material which is prepared by a process comprising hot-pressing at least one of a random web comprising a precursor fiber convertible to carbon fiber and/or a carbon fiber and a carbonizable or graphitizable thermosetting resin while curing of said resin is inhibited to provide a prepreg sheet, heating the prepreg sheet at a temperature over the melting temperature of said resin under no load for expansion and complete cure of the resin, and either carbonizing or graphitizing the resultant porous composite sheet.
Claim 38
Dependent Claim
169 words
A porous carbonaceous material which is prepared by a process comprising a step of hot-pressing at least one ply of a random web comprising a fiber component composed of a precursor fiber convertible to carbon fiber and/or a carbon fiber and, based on 100 parts by weight of said fiber component, 15 to 275 parts by weight of a carbonizable or graphitizable thermosetting resin with a carbonization yield of 50 to 75% by weight, 0 to 250 parts by weight of a pitch with a carbonization yield of not less than 50% by weight, and 0 to 250 parts by weight of an organic granular material with a mean particle diameter of 0.1 to 500 μm while curing of said thermosetting resin is inhibited to provide a prepreg sheet; a step of heating said prepreg sheet at a temperature over the melting temperature of said resin under no load for expansion and complete cure of the resin; and a step of carbonizing or graphitizing the resultant porous composite sheet.
Claim 39
Dependent Claim
169 words
A porous carbonaceous material which is prepared by a process comprising a step of hot-pressing at least one ply of a random web comprising a fiber component composed of a precursor fiber convertible to carbon fiber and/or a carbon fiber and, based on 100 parts by weight of said fiber component, 15 to 275 parts by weight of a carbonizable or graphitizable thermosetting resin with a carbonization yield of 50 to 75% by weight, 0 to 250 parts by weight of a pitch with a carbonization yield of not less than 50% by weight, and 0 to 250 parts by weight of an organic granular material with a mean particle diameter of 0.1 to 500 μm while curing of said thermosetting resin is inhibited to provide a prepreg sheet; a step of heating said prepreg sheet at a temperature over the melting temperature of said resin under no load for expansion and complete cure of the resin; and a step of carbonizing or graphitizing the resultant porous composite sheet.
Claim 40
Dependent Claim
148 words
A porous carbonaceous material which is prepared by a process comprising hot-pressing one or more plies of a web wherein a prepreg sheet is disposed in a first mold comprising at least one pair of opposed surfaces defining a molding compartment, at least one of said opposed surfaces defining a molding compartment, at least one of said opposed surfaces being provided with grooves, under heating at 80° to 200° C. to provide a ribbed sheet and disposing said ribbed sheet, leaving a clearance, in a second mold comprising at least one pair of opposed surfaces defining a molding compartment, at least one of said opposed surfaces being provided with grooves larger than the grooves of said first mold, heating said ribbed sheet at a temperature of 150° to 250° C. for expansion and complete cure of said resin, and either carbonizing or graphitizing the resultant porous composite sheet.
Claim 41
Dependent Claim
148 words
A porous carbonaceous material which is prepared by a process comprising hot-pressing one or more plies of a web wherein a prepreg sheet is disposed in a first mold comprising at least one pair of opposed surfaces defining a molding compartment, at least one of said opposed surfaces defining a molding compartment, at least one of said opposed surfaces being provided with grooves, under heating at 80° to 200° C. to provide a ribbed sheet and disposing said ribbed sheet, leaving a clearance, in a second mold comprising at least one pair of opposed surfaces defining a molding compartment, at least one of said opposed surfaces being provided with grooves larger than the grooves of said first mold, heating said ribbed sheet at a temperature of 150° to 250° C. for expansion and complete cure of said resin, and either carbonizing or graphitizing the resultant porous composite sheet.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-07-14 | 2001-01-13 | 2001-07-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-07-14 | 2005-01-13 | 2005-07-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-07-14 | 2009-01-13 | 2009-07-15 | $7700.00 | Window Closed / Lapsed |