Inorganic thin film compensator for improved gray scale performance in twisted nematic liquid crystal displays and method of making
Assignee: Teledyne Scientific and Imaging LLC
•
Filing: 1994-09-30
•
Granted: 1997-06-10
•
Expires: 2014-09-30
Abstract
Abstract An optical O-plate compensation device, in accordance with the invention, uses an inorganic thin film which is grown by physical vapor deposition at oblique incidence. The resulting thin film exhibits a biaxial form birefringence and performs, in a liquid crystal display (LCD), in a similar manner to uniaxial films with its extraordinary axis oriented obliquely at about 45 DEG with respect to the surface of the film. The invention makes possible a significant improvement in the gray scale properties and contrast ratios of liquid crystal displays (LCDs) over a wide range of viewing angles.
Inventors
- 👤 William J. Gunning, III
- 👤 Bruce K. Winker
- 👤 Donald B. Taber
- 👤 Paul H. Kobrin
- 👤 James C. Beedy
- 👤 John P. Eblen, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:01
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/225; C23C14/226; G; G02; G02B; G02B5/00; G02B5/30; G02B5/3083; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/1333; G02F1/1335; G02F1/13363; G02F1/133632; G02F1/133636; G02F1/133634; G02F2413/00; G02F2413/10; G02F2413/105
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
89 words
An O-plate compensator for a liquid crystal display, said O-plate compensator comprising a tantalum oxide film having: (a) a tilted-columnar microstructure having a tilt angle of between about 30 degrees and about 60 degrees relative to a surface of said compensator; (b) sufficient thickness to have a positive biaxial optical anisotropy; and (c) wherein at least one of the tilt angle of the tilted-columnar microstructure and the thickness of the tantalum oxide film is selected in order to optimize performance of the liquid crystal display at wide viewing angles.
Claim 2
Dependent Claim
89 words
An O-plate compensator for a liquid crystal display, said O-plate compensator comprising a tantalum oxide film having: (a) a tilted-columnar microstructure having a tilt angle of between about 30 degrees and about 60 degrees relative to a surface of said compensator; (b) sufficient thickness to have a positive biaxial optical anisotropy; and (c) wherein at least one of the tilt angle of the tilted-columnar microstructure and the thickness of the tantalum oxide film is selected in order to optimize performance of the liquid crystal display at wide viewing angles.
Claim 3
Dependent Claim
74 words
An O-plate compensator for a liquid crystal display, said O-plate compensator comprising an obliquely oriented inorganic microstructured film layer having a thickness and a positive optical anisotropy; wherein at least one of the orientation of the inorganic microstructured film layer, the thickness of the inorganic microstructured film layer and the positive optical anisotropy of the inorganic microstructured film are selected in order to optimize performance at wide viewing angles of the liquid crystal display.
Claim 4
Dependent Claim
74 words
An O-plate compensator for a liquid crystal display, said O-plate compensator comprising an obliquely oriented inorganic microstructured film layer having a thickness and a positive optical anisotropy; wherein at least one of the orientation of the inorganic microstructured film layer, the thickness of the inorganic microstructured film layer and the positive optical anisotropy of the inorganic microstructured film are selected in order to optimize performance at wide viewing angles of the liquid crystal display.
Claim 5
Dependent Claim
16 words
The compensator of claim 2, wherein the inorganic microstructured film layer comprises a tilted columnar microstructure.
Claim 6
Dependent Claim
29 words
The compensator of claim 3, wherein said tilted columnar microstructure has a tilt of between about 30 degrees and about 60 degrees relative to a surface of said compensator.
Claim 7
Dependent Claim
15 words
The compensator of claim 2, wherein the inorganic microstructured film layer comprises a metal oxide.
Claim 8
Dependent Claim
13 words
The compensator of claim 5, wherein said metal oxide is a tantalum oxide.
Claim 9
Dependent Claim
128 words
A liquid crystal display for viewing at various angles with respect to a normal axis perpendicular to the display, comprising: (a) a polarizer layer; (b) an analyzer layer; (c) a liquid crystal layer disposed between the polarizer layer and the analyzer layer; (d) a first electrode proximate to a first major surface of the liquid crystal layer; (e) a second electrode proximate to a second major surface of the liquid crystal layer, the first and second electrodes being adapted to apply a voltage across the liquid crystal layer when the electrodes are connected to a source of electrical potential; and (f) an O-plate compensator, disposed between the polarizer layer and the analyzer layer, in accordance with a specified one of claims 1, 2, 3, 4, 5, and 6.
Claim 10
Independent Claim
161 words
A method of manufacturing an O-plate compensator, comprising the steps of: (a) providing a substrate; (b) providing a mask having an aperture; (c) providing a source of an inorganic deposition material comprising tantalum or a tantalum oxide; (d) positioning said substrate and said source on opposite sides of said aperture to provide an oblique deposition angle between said source and said substrate; (e) heating said source in a substantial vacuum to form a vapor; (f) providing an oxygen gas to react with said vapor; (g) applying a combination of a rotation motion, a translation motion, and a nutation motion to said substrate to obtain a substantially uniform thickness and deposition angle over said substrate; (h) controlling one or more of (1) a temperature of said substrate, (2) a rate of deposition on said substrate, and (3) a pressure of said oxygen gas, to obtain a desired refractive index and a desired optical anisotropy; and (i) annealing said inorganic microstructured film layer.
Claim 11
Independent Claim
161 words
A method of manufacturing an O-plate compensator, comprising the steps of: (a) providing a substrate; (b) providing a mask having an aperture; (c) providing a source of an inorganic deposition material comprising tantalum or a tantalum oxide; (d) positioning said substrate and said source on opposite sides of said aperture to provide an oblique deposition angle between said source and said substrate; (e) heating said source in a substantial vacuum to form a vapor; (f) providing an oxygen gas to react with said vapor; (g) applying a combination of a rotation motion, a translation motion, and a nutation motion to said substrate to obtain a substantially uniform thickness and deposition angle over said substrate; (h) controlling one or more of (1) a temperature of said substrate, (2) a rate of deposition on said substrate, and (3) a pressure of said oxygen gas, to obtain a desired refractive index and a desired optical anisotropy; and (i) annealing said inorganic microstructured film layer.
Claim 12
Independent Claim
33 words
A method of manufacturing an O-plate compensator, comprising the steps of: (a) providing a substrate; (b) depositing an inorganic microstructured film layer at an incidence angle oblique to a surface of said substrate.
Claim 13
Independent Claim
33 words
A method of manufacturing an O-plate compensator, comprising the steps of: (a) providing a substrate; (b) depositing an inorganic microstructured film layer at an incidence angle oblique to a surface of said substrate.
Claim 14
Dependent Claim
116 words
The method of claim 9, wherein said step (b) of depositing an inorganic microstructured film layer comprises the substeps of: (1) providing a mask having an aperture; (2) providing a source of an inorganic deposition material; (3) positioning said substrate and said source on opposite sides of said aperture to provide an oblique deposition angle between said source and said substrate; (4) heating or sputtering said source in a substantial vacuum to form a vapor; (5) providing a reactive gas to react with said vapor to form said inorganic microstructured film layer; and (6) applying a relative motion between said substrate and said source to obtain a substantially uniform thickness and deposition angle over said substrate.
Claim 15
Dependent Claim
42 words
The method of claim 10, further comprising the substeps of controlling one or more of (A) a temperature of said substrate, and (B) a rate of deposition of said vapor on said substrate, to obtain a desired refractive index and optical anisotropy.
Claim 16
Dependent Claim
22 words
The method of claim 10, wherein said deposition material is a metal or a metal oxide and said reactive gas comprises oxygen.
Claim 17
Dependent Claim
18 words
The method of claim 12, wherein said metal is tantalum and said metal oxide is a tantalum oxide.
Claim 18
Dependent Claim
26 words
The method of claim 10, further comprising the substep of controlling the pressure of said reactive gas to obtain a desired refractive index and optical anisotropy.
Claim 19
Dependent Claim
33 words
The method of claim 10, wherein said substep (5) of applying a relative motion comprises applying one or more of a rotation motion, a translation motion, and a nutation motion to said substrate.
Claim 20
Independent Claim
26 words
The method of a specified one of claims 9, 10, 11, 12, 13, and 14, further comprising the step of annealing said inorganic microstructured film layer.
Claim 21
Independent Claim
149 words
A method of manufacturing an O-plate compensator, comprising the steps of: (a) providing a substrate; (b) depositing an inorganic microstructured film layer at an incidence angle oblique to a surface of said substrate, wherein the step of depositing an inorganic microstructured film layer comprises the substeps of: (1) providing a mask having an aperture; (2) providing a source of an inorganic deposition material, the deposition material being a metal; (3) positioning said substrate and said source on opposite sides of said aperture to provide an oblique deposition angle between said source and said substrate; (4) heating or sputtering said source in a substantial vacuum to form a vapor; (5) providing a reactive gas to react with said vapor to form said inorganic microstructured film layer; and (6) applying a relative motion between said substrate and said source to obtain a substantially uniform thickness and deposition angle over said substrate.
Claim 22
Independent Claim
149 words
A method of manufacturing an O-plate compensator, comprising the steps of: (a) providing a substrate; (b) depositing an inorganic microstructured film layer at an incidence angle oblique to a surface of said substrate, wherein the step of depositing an inorganic microstructured film layer comprises the substeps of: (1) providing a mask having an aperture; (2) providing a source of an inorganic deposition material, the deposition material being a metal; (3) positioning said substrate and said source on opposite sides of said aperture to provide an oblique deposition angle between said source and said substrate; (4) heating or sputtering said source in a substantial vacuum to form a vapor; (5) providing a reactive gas to react with said vapor to form said inorganic microstructured film layer; and (6) applying a relative motion between said substrate and said source to obtain a substantially uniform thickness and deposition angle over said substrate.
Claim 23
Dependent Claim
42 words
The method of claim 17, further comprising the substeps of controlling one or more of (A) a temperature of said substrate, and (B) a rate of deposition of said vapor on said substrate, to obtain a desired refractive index and optical anisotropy.
Claim 24
Dependent Claim
22 words
The method of claim 17, wherein said deposition material is a metal or a metal oxide and said reactive gas comprises oxygen.
Claim 25
Dependent Claim
18 words
The method of claim 19, wherein said metal is tantalum and said metal oxide is a tantalum oxide.
Claim 26
Dependent Claim
26 words
The method of claim 17, further comprising the substep of controlling the pressure of said reactive gas to obtain a desired refractive index and optical anisotropy.
Claim 27
Dependent Claim
17 words
The method of claim 17, and further comprising the step of annealing said inorganic microstructured film layer.
Claim 28
Independent Claim
150 words
A method of manufacturing an O-plate compensator, comprising the steps of: (a) providing a substrate; (b) depositing an inorganic microstructured film layer at an incidence angle oblique to a surface of said substrate, wherein the step of depositing an inorganic microstructured film layer comprises the substeps of: (1) providing a mask having an aperture; (2) providing a source of an inorganic deposition material; (3) positioning said substrate and said source on opposite sides of said aperture to provide an oblique deposition angle between said source and said substrate; (4) heating or sputtering said source in a substantial vacuum to form a vapor; and (5) applying a relative motion between said substrate and said source to obtain a substantially uniform thickness and deposition angle over said substrate, wherein applying a relative motion comprises applying one or more of a rotation motion, a translation motion, and a nutation motion to said substrate.
Claim 29
Independent Claim
150 words
A method of manufacturing an O-plate compensator, comprising the steps of: (a) providing a substrate; (b) depositing an inorganic microstructured film layer at an incidence angle oblique to a surface of said substrate, wherein the step of depositing an inorganic microstructured film layer comprises the substeps of: (1) providing a mask having an aperture; (2) providing a source of an inorganic deposition material; (3) positioning said substrate and said source on opposite sides of said aperture to provide an oblique deposition angle between said source and said substrate; (4) heating or sputtering said source in a substantial vacuum to form a vapor; and (5) applying a relative motion between said substrate and said source to obtain a substantially uniform thickness and deposition angle over said substrate, wherein applying a relative motion comprises applying one or more of a rotation motion, a translation motion, and a nutation motion to said substrate.
References Cited (Backward Citations)
US4701028A
Cited
US4813768A
Cited
US4874664A
Cited
US5189538A
Cited
US5194975A
Cited
US5305143A
Cited
US5196953A
Cited
EP0576304A1
Cited
US5375006A
Cited
JPH06174920A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-06-09 | 2000-12-09 | 2001-06-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-06-09 | 2004-12-09 | 2005-06-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-06-09 | 2008-12-09 | 2009-06-10 | $7700.00 | Window Closed / Lapsed |