US5635315A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Phase shift mask and phase shift mask blank
Assignee: Hoya Corp
•
Filing: 1995-06-21
•
Granted: 1997-06-03
•
Expires: 2015-06-21
Abstract
Abstract A phase shift mask comprises a transparent substrate (1) provided with a mask pattern formed by a light transmitting portion (4) for transmitting effective light beams having an intensity which substantially contributes to exposure and a light translucent portion (2) for transmitting ineffective light beams having an intensity which does not substantially contribute to exposure. The light translucent portion (2) is for phase shifting the ineffective light beams transmitted therethrough to make the ineffective light beams be different in phase from the effective light beams transmitted through the light transmitting portion (4) that the effective and the ineffective light beams passing through an area in the vicinity of a boundary between the light transmitting portion (4) and the light translucent portion (2) cancel each other so as to assure an excellent contrast at the boundary. The light translucent portion (2) comprises a thin film made of a material containing oxygen, metal, and silicon as main components.
Inventors
- 👤 Masaru Mitsui
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 05:57
CPC Classifications
G; G03; G03F; G03F1/00; G03F1/26; G03F1/32
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
111 words
A phase shift mask comprising a transparent substrate transparent to an exposure light beam and a translucent portion selectively deposited on the transparent substrate with a transparent portion left on the transparent substrate and with a boundary left between the translucent and the transparent portions, the exposure light beam being canceled in phase in an area adjacent to the boundary between the translucent and the transparent portions when the exposure light beam passes through the translucent and the transparent portions, said translucent portion being formed by: a thin film which comprises, as main components, oxygen, metal, and silicon, wherein said thin film comprises 35 to 60 at % of oxygen therein.
Claim 2
Dependent Claim
111 words
A phase shift mask comprising a transparent substrate transparent to an exposure light beam and a translucent portion selectively deposited on the transparent substrate with a transparent portion left on the transparent substrate and with a boundary left between the translucent and the transparent portions, the exposure light beam being canceled in phase in an area adjacent to the boundary between the translucent and the transparent portions when the exposure light beam passes through the translucent and the transparent portions, said translucent portion being formed by: a thin film which comprises, as main components, oxygen, metal, and silicon, wherein said thin film comprises 35 to 60 at % of oxygen therein.
Claim 3
Dependent Claim
22 words
A phase shift mask as claimed in claim 1, wherein the metal and the silicon are included in the form of silicide.
Claim 4
Dependent Claim
116 words
A phase shift mask comprising a transparent substrate transparent to an exposure light beam and a translucent portion selectively deposited on the transparent substrate with a transparent portion left on the transparent substrate and with a boundary left between the translucent and the transparent portions, the exposure light beam being canceled in phase in an area adjacent to the boundary between the translucent and the transparent portions when the exposure light beam passes through the translucent and the transparent portions, said translucent portion being formed by: a thin film which comprises, as main components, oxygen, nitrogen, metal, and silicon and wherein a ratio of nitrogen to the oxygen falls within a range between 0.2 and 0.5.
Claim 5
Dependent Claim
116 words
A phase shift mask comprising a transparent substrate transparent to an exposure light beam and a translucent portion selectively deposited on the transparent substrate with a transparent portion left on the transparent substrate and with a boundary left between the translucent and the transparent portions, the exposure light beam being canceled in phase in an area adjacent to the boundary between the translucent and the transparent portions when the exposure light beam passes through the translucent and the transparent portions, said translucent portion being formed by: a thin film which comprises, as main components, oxygen, nitrogen, metal, and silicon and wherein a ratio of nitrogen to the oxygen falls within a range between 0.2 and 0.5.
Claim 6
Dependent Claim
57 words
A phase shift mask as claimed in claim 3, the thin film having a thickness, a back surface attached to the substrate, and a front surface opposite to the back surface, wherein an amount of the oxygen is decreased along a direction of the thickness from the back surface of the thin film to the front surface.
Claim 7
Dependent Claim
22 words
A phase shift mask as claimed in claim 4, wherein the metal and the silicon are included in the form of silicide.
Claim 8
Dependent Claim
22 words
A phase shift mask as claimed in claim 3, wherein the thin film comprises 35 to 60 at % of the oxygen.
Claim 9
Dependent Claim
55 words
A phase shift mask blank comprising a transparent substrate transparent to an exposure light beam and a translucent layer deposited on the transparent substrate, said translucent layer being formed by: a thin film which comprises, as main components, oxygen, metal, and silicon and which further comprises 35 to 60 at % of the oxygen therein.
Claim 10
Dependent Claim
55 words
A phase shift mask blank comprising a transparent substrate transparent to an exposure light beam and a translucent layer deposited on the transparent substrate, said translucent layer being formed by: a thin film which comprises, as main components, oxygen, metal, and silicon and which further comprises 35 to 60 at % of the oxygen therein.
Claim 11
Dependent Claim
15 words
A phase shift mask blank as claimed in claim 7, wherein the metal is molybdenum.
Claim 12
Dependent Claim
23 words
A phase shift mask blank as claimed in claim 7, wherein the metal and the silicon are included in the form of silicide.
Claim 13
Dependent Claim
60 words
A phase shift mask blank comprising a transparent substrate transparent to an exposure light beam and a translucent layer deposited on the transparent substrate, said translucent layer being formed by: a thin film which comprises, as main components, oxygen, nitrogen, metal, and silicon and wherein a ratio of nitrogen to the oxygen falls within a range between 0.2 and 0.5.
Claim 14
Dependent Claim
60 words
A phase shift mask blank comprising a transparent substrate transparent to an exposure light beam and a translucent layer deposited on the transparent substrate, said translucent layer being formed by: a thin film which comprises, as main components, oxygen, nitrogen, metal, and silicon and wherein a ratio of nitrogen to the oxygen falls within a range between 0.2 and 0.5.
Claim 15
Dependent Claim
15 words
A phase shift mask blank as claimed in claim 10, wherein the metal is molybdenum.
Claim 16
Dependent Claim
23 words
A phase shift mask blank as claimed in claim 10, wherein the metal and the silicon are included in the form of silicide.
Claim 17
Dependent Claim
25 words
A phase shift mask blank as claimed in claim 10, wherein the thin film further comprises 35 to 60 at % of the oxygen therein.
Claim 18
Independent Claim
71 words
A method of manufacturing a phase shift mask, comprising the steps of: preparing a substrate transparent to an exposure light beam; depositing, on the substrate, a light translucent layer which comprises metal, oxygen, and silicon to form a phase shift mask blank so that the light translucent layer includes 35 to 60 at % of the oxygen; and forming a pattern on the phase shift mask blank by a photolithography technique.
Claim 19
Independent Claim
71 words
A method of manufacturing a phase shift mask, comprising the steps of: preparing a substrate transparent to an exposure light beam; depositing, on the substrate, a light translucent layer which comprises metal, oxygen, and silicon to form a phase shift mask blank so that the light translucent layer includes 35 to 60 at % of the oxygen; and forming a pattern on the phase shift mask blank by a photolithography technique.
Claim 20
Dependent Claim
40 words
A method as claimed in claim 14, wherein said thin film further comprises nitrogen, the translucent layer depositing step being carried out so that the ratio of the nitrogen to the oxygen falls within a range between 0.2 and 0.5.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-06-02 | 2000-12-02 | 2001-06-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-06-02 | 2004-12-02 | 2005-06-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-06-02 | 2008-12-02 | 2009-06-03 | $7700.00 | Window Closed / Lapsed |