Abstract
Abstract There is disclosed an efficient, cost effective production method to bond layers of electronic devices into an integral stack, or for joining electronic devices to other devices or substrates with use of an adhesive material, preferably an appropriate polyimide, to provide, in effect, a two-stage bonding process. In the first stage, the electronic device is coated, preferably at the wafer level, with a liquid solution of the adhesive material, the coated device is heated to remove solvent, forming a dry adhesive coating of sufficient thickness to fill all spaces between metal traces on the electronic device. Coated wafers can be stacked and bonded, or preferably diced to yield individual chips, which are cut and stacked in a suitable fixture, and heat and pressure are applied in a second stage, to cause viscous flow of the adhesive, filling all voids, and to cure the adhesive, creating an integral, adhesively bonded stack. The adhesive selected for use in the process is one which can be dried to a solvent free layer, which has good B stage properties, exhibits viscous flow at temperatures below its curing temperature, and which is substantially free of volatile release during curing to form a substantially void-free adhesive bond having high film strength, high adhesion, chemical resistance and good dielectric properties.
Inventors
- 👤 Angel A. Pepe
- 👤 David M. Reinker
- 👤 Paul Wojtuszewski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:19
CPC Classifications
B; B32; B32B; B32B7/00; B32B7/04; B32B7/12; B32B25/00; B32B25/04; B32B25/20; B32B27/00; B32B27/28; B32B27/281; B32B37/00; B32B37/12; B32B37/14; B32B37/15; B32B37/153; B32B2379/00; B32B2379/08; B32B2457/00; B32B2457/08; B32B2553/00; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T156/1062; Y10T156/1075; Y10T156/1089; Y10T156/1092; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49126
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
257 words
In a method for fabrication of a high-density electronic package wherein a plurality of electronic device layers, which in raw form comprise a plurality of electronic devices arrayed on an electronic device wafer, are separated as individual devices from the wafer, stacked and adhesively bonded together into a layered stack by a lamination step including the application of heat and compression to the stack, the improvement comprising: a. applying an adhesive material to at least one surface of said wafer to obtain a wafer having a substantially dry, solvent-free coating of adhesive material thereon; b. separating said wafer having said coating of adhesive material into a plurality of discrete, individual electronic devices of substantially equal size; c. stacking said plurality of electronic devices to form a non-integral stack of layers of electronic devices said coating of adhesive material at the interface between adjacent layers of electronic devices; d. applying heat and compressive loading to said non-integral stack in a progressive manner to provide viscous flow conditions of heat and pressure sufficient to soften said coatings of adhesive material and cause said coatings to undergo viscous flow sufficient to fill any non-planar irregularities at the interfaces between adjacent electronic device layers and to extrude from between said adjacent layers, thereby reducing the thicknesses of said adhesive layers and adhesive curing conditions sufficient to cure said adhesive layers into adhesive bonds between said adjacent layers; and e. cooling said stack and releasing said compressive pressure to obtain said high-density electronic package of a plurality of integral, electronic device layers.
Claim 2
Dependent Claim
257 words
In a method for fabrication of a high-density electronic package wherein a plurality of electronic device layers, which in raw form comprise a plurality of electronic devices arrayed on an electronic device wafer, are separated as individual devices from the wafer, stacked and adhesively bonded together into a layered stack by a lamination step including the application of heat and compression to the stack, the improvement comprising: a. applying an adhesive material to at least one surface of said wafer to obtain a wafer having a substantially dry, solvent-free coating of adhesive material thereon; b. separating said wafer having said coating of adhesive material into a plurality of discrete, individual electronic devices of substantially equal size; c. stacking said plurality of electronic devices to form a non-integral stack of layers of electronic devices said coating of adhesive material at the interface between adjacent layers of electronic devices; d. applying heat and compressive loading to said non-integral stack in a progressive manner to provide viscous flow conditions of heat and pressure sufficient to soften said coatings of adhesive material and cause said coatings to undergo viscous flow sufficient to fill any non-planar irregularities at the interfaces between adjacent electronic device layers and to extrude from between said adjacent layers, thereby reducing the thicknesses of said adhesive layers and adhesive curing conditions sufficient to cure said adhesive layers into adhesive bonds between said adjacent layers; and e. cooling said stack and releasing said compressive pressure to obtain said high-density electronic package of a plurality of integral, electronic device layers.
Claim 3
Dependent Claim
17 words
The method for fabrication of claim 1 wherein said adhesive material is a fully imidized oligomeric, isoimide.
Claim 4
Dependent Claim
14 words
The method for fabrication of claim 2 wherein said imide is a thermosetting polyimide.
Claim 5
Dependent Claim
25 words
The method for fabrication of claim 3 wherein said adhesive curing conditions include heating to an adhesive curing temperature from 300° C. to 400° C.
Claim 6
Dependent Claim
27 words
The method for fabrication of claim 4 wherein said polyimide is applied to said wafer as a solution in a volatile solvent to obtain a liquid-adhesive-coated wafer.
Claim 7
Dependent Claim
30 words
The method for fabrication of claim 5 including the step of removing said volatile solvent by drying said liquid-adhesive-coated wafer to obtain a wafer having a dry, solvent-free adhesive coating.
Claim 8
Dependent Claim
36 words
The method of claim 6 wherein said solvent is removed by vaporization under sufficiently reduced pressure to permit complete removal of said solvent at evaporation temperatures less than the adhesive curing temperature of said adhesive material.
Claim 9
Dependent Claim
14 words
The method for fabrication of claim 7 wherein said reduced pressure is subatmospheric pressure.
Claim 10
Dependent Claim
25 words
The method for fabrication of claim 1 including the step of reducing the thickness of said wafer prior to the application of said adhesive material.
Claim 11
Dependent Claim
28 words
The method for fabrication of claim 1 wherein said stack is cooled to below the glass transition temperature of said adhesive material prior to releasing said compressive pressure.
Claim 12
Dependent Claim
37 words
The method for fabrication of claim 1 including the steps of applying layers of metal leads to connect terminals at preselected locations on the front surface of said wafer prior to the application of said adhesive material.
Claim 13
Independent Claim
231 words
The method for fabrication of a high density electronic package comprising a stack of a plurality of electronic device layers laminated together with adhesive bonds which comprises: a. the step of coating semiconductor wafers of electronic chips that have surfaces with non-planar irregularities with an adhesive material having the properties of forming a dry, solvent-free, non-tacky coating which when heated exhibits viscous flow at an intermediate temperature and cures into an adhesive bond at a more elevated curing temperature without releasing volatiles during curing; b. separating from said coating step wafers having substantially dry, solvent-free coatings of adhesive material thereon; c. subsequently treating said adhesive coated wafers by the steps of dicing and forming stacks of layers of said electronic devices with said adhesive coatings at the interfaces between adjacent layers of said electronic devices, and heating under compression said stacks in a progressive manner comprising an initial step at said intermediate temperature and sufficient pressure to cause said adhesive coatings to undergo viscous flow and fill said non-planar irregularities of said surfaces and to extrude from between said adjacent layers, and a final adhesive coating curing step at said more elevated temperature sufficient to cure said adhesive coatings to bonds cementing said layers into coherent stacks; and d. cooling said stacks and releasing said compressive pressure to obtain high-density electronic packages, each comprising a plurality of integral, electronic device layers.
Claim 14
Independent Claim
231 words
The method for fabrication of a high density electronic package comprising a stack of a plurality of electronic device layers laminated together with adhesive bonds which comprises: a. the step of coating semiconductor wafers of electronic chips that have surfaces with non-planar irregularities with an adhesive material having the properties of forming a dry, solvent-free, non-tacky coating which when heated exhibits viscous flow at an intermediate temperature and cures into an adhesive bond at a more elevated curing temperature without releasing volatiles during curing; b. separating from said coating step wafers having substantially dry, solvent-free coatings of adhesive material thereon; c. subsequently treating said adhesive coated wafers by the steps of dicing and forming stacks of layers of said electronic devices with said adhesive coatings at the interfaces between adjacent layers of said electronic devices, and heating under compression said stacks in a progressive manner comprising an initial step at said intermediate temperature and sufficient pressure to cause said adhesive coatings to undergo viscous flow and fill said non-planar irregularities of said surfaces and to extrude from between said adjacent layers, and a final adhesive coating curing step at said more elevated temperature sufficient to cure said adhesive coatings to bonds cementing said layers into coherent stacks; and d. cooling said stacks and releasing said compressive pressure to obtain high-density electronic packages, each comprising a plurality of integral, electronic device layers.
Claim 15
Dependent Claim
17 words
The method for fabrication of claim 12 wherein said adhesive material is a fully imidized oligomeric, iso-imide.
Claim 16
Dependent Claim
14 words
The method for fabrication of claim 13 wherein said imide is a thermosetting polyimide.
Claim 17
Dependent Claim
19 words
The method for fabrication of claim 14 wherein said more elevated temperature is from 300° C. to 400° C.
Claim 18
Dependent Claim
27 words
The method for fabrication of claim 14 wherein said polyimide is applied to said wafer as a solution in a volatile solvent to obtain a liquid-adhesive-coated wafer.
Claim 19
Dependent Claim
30 words
The method for fabrication of claim 16 including the step of removing said volatile solvent by drying said liquid-adhesive-coated wafer to obtain a wafer having a dry, solvent-free adhesive coating.
Claim 20
Dependent Claim
36 words
The method of claim 17 wherein said solvent is removed by vaporization under sufficiently reduced pressure to permit complete removal of said solvent at evaporation temperatures less than the adhesive curing temperature of said adhesive material.
Claim 21
Dependent Claim
14 words
The method for fabrication of claim 18 wherein said reduced pressure is subatmospheric pressure.
Claim 22
Dependent Claim
25 words
The method for fabrication of claim 12 including the step of reducing the thickness of said wafer prior to the application of said adhesive material.
Claim 23
Dependent Claim
28 words
The method for fabrication of claim 12 wherein said stack is cooled to below the glass transition temperature of said adhesive material prior to releasing said compressive pressure.
Claim 24
Dependent Claim
37 words
The method for fabrication of claim 12 including the steps of applying layers of metal leads to connect terminals at preselected locations on the front surface of said wafer prior to the application of said adhesive material.
Claim 25
Dependent Claim
30 words
The method for fabrication of claim 12 wherein said step of dicing is performed on said wafers prior to said steps of stacking and heating said electronic devices under compression.
References Cited (Backward Citations)
US4617160A
Cited
US4880486A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-06-02 | 2000-12-02 | 2001-06-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-06-02 | 2004-12-02 | 2005-06-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-06-02 | 2008-12-02 | 2009-06-03 | $7700.00 | Window Closed / Lapsed |