Prevention of groove tip deformation in brightness enhancement film
Assignee: 3M Co
•
Filing: 1995-02-03
•
Granted: 1997-05-06
•
Expires: 2015-02-03
Abstract
Abstract A method of producing a microstructure bearing article that includes the steps of molding the microstructure on the base, curing the resin that forms the microstructure, and heat treating the microstructure. The heat treating is performed at a temperature that is at least equal to a normal glass transition temperature of the resin. The heat treating raises the glass transition temperature of the resulting polymer above approximately 333° K. such that groove tip impression is reduced. Such articles are useful in backlit displays which are useful in computers and the like.
Inventors
- 👤 Todd R. Williams
- 👤 Daniel J. Kingston
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:46
CPC Classifications
G; G02; G02B; G02B5/00; G02B5/04; G02B5/045; B; B29; B29D; B29D11/00; G02B5/12; G02B5/122; G02B5/124; B29K; B29K2995/00; B29K2995/0037; B29K2995/0087; G02B6/00; G02B6/0001
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
84 words
A method of improving groove tip impression resistance in a microstructure bearing article, the method comprising: forming a desired microstructure in a first layer on a base from an oligomeric resin; curing the resin of the first layer; and heat treating the first layer at a temperature that is at least equal to a normal glass transition temperature of the resin, the heat treating raising the glass transition temperature of the resulting polymer above about 333° K. such that groove tip impression is reduced.
Claim 2
Independent Claim
84 words
A method of improving groove tip impression resistance in a microstructure bearing article, the method comprising: forming a desired microstructure in a first layer on a base from an oligomeric resin; curing the resin of the first layer; and heat treating the first layer at a temperature that is at least equal to a normal glass transition temperature of the resin, the heat treating raising the glass transition temperature of the resulting polymer above about 333° K. such that groove tip impression is reduced.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein the microstructure has adjacent polymeric tips and grooves, and the tips have an included angle in the approximate range of 70° to 120°.
Claim 4
Dependent Claim
18 words
The method of claim 2 wherein the included angle is in the approximate range of 80° to 100°.
Claim 5
Dependent Claim
17 words
The method of claim 1 wherein the curing step is performed prior to the heat treating step.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein the curing step and the heat treating step are performed simultaneously.
Claim 7
Dependent Claim
11 words
The method of claim 1 wherein the oligomeric resin is crosslinkable.
Claim 8
Dependent Claim
43 words
The method of claim 6 further comprising the step of adding crosslinking agents to the oligomeric resin to facilitate the raising of the glass transition temperature of the resulting polymer above the normal glass transition temperature such that groove tip impression is reduced.
Claim 9
Dependent Claim
12 words
The method of claim 6 wherein crosslinking is initiated by ultraviolet radiation.
Claim 10
Dependent Claim
31 words
The method of claim 1 wherein the heat treating is performed at a temperature that is at least 10 degrees Kelvin greater than the normal glass transition temperature of the resin.
Claim 11
Dependent Claim
31 words
The method of claim 9 wherein the heat treating is performed at a temperature that is at least 20 degrees Kelvin greater than the normal glass transition temperature of the resin.
Claim 12
Dependent Claim
20 words
The method of claim 1 wherein the heat treating reduces groove tip impression penetration to less than 1×10 -4 mm.
Claim 13
Dependent Claim
17 words
The method of claim 1 wherein the base has a sputter etched surface adjacent the first layer.
Claim 14
Dependent Claim
13 words
The method of claim 1 wherein a photoinitiator is used for the curing.
Claim 15
Independent Claim
135 words
A method of forming a microstructure bearing article that exhibits reduced groove tip impression, the method comprising: preparing an oligomeric composition; depositing the oligomeric resin composition onto a master negative microstructured surface or onto a substrate in an amount barely sufficient to fill cavities of the master; filling the cavities by moving a bead of the oligomeric resin composition between the substrate and the master, at least one of which is flexible, the oligomeric resin composition forming the desired microstructure; curing the oligomeric resin that forms the desired microstructure; and heat treating the desired microstructure at a temperature that is at least equal to a normal glass transition temperature of the resin, the heat treating raising the glass transition temperature of the resulting polymer above about 333° K. such that groove tip impression is reduced.
Claim 16
Independent Claim
135 words
A method of forming a microstructure bearing article that exhibits reduced groove tip impression, the method comprising: preparing an oligomeric composition; depositing the oligomeric resin composition onto a master negative microstructured surface or onto a substrate in an amount barely sufficient to fill cavities of the master; filling the cavities by moving a bead of the oligomeric resin composition between the substrate and the master, at least one of which is flexible, the oligomeric resin composition forming the desired microstructure; curing the oligomeric resin that forms the desired microstructure; and heat treating the desired microstructure at a temperature that is at least equal to a normal glass transition temperature of the resin, the heat treating raising the glass transition temperature of the resulting polymer above about 333° K. such that groove tip impression is reduced.
Claim 17
Dependent Claim
31 words
The method of claim 14 wherein the desired microstructure has adjacent polymeric tips and grooves, and wherein the tips have an included angle in the approximate range of 70° to 120°.
Claim 18
Dependent Claim
18 words
The method of claim 15 wherein the included angle is in the approximate range of 80° to 100°.
Claim 19
Dependent Claim
17 words
The method of claim 14 wherein the curing step is performed prior to the heat treating step.
Claim 20
Dependent Claim
17 words
The method of claim 14 wherein the curing step and the heat treating step are performed simultaneously.
Claim 21
Dependent Claim
11 words
The method of claim 14 wherein the oligomeric resin is crosslinkable.
Claim 22
Dependent Claim
47 words
The method of claim 14 and further comprising the step of adding crosslinking agents to the oligomeric composition to facilitate the raising of the glass transition temperature of the resulting polymer above the normal glass transition temperature to a level such that groove tip penetration is reduced.
Claim 23
Dependent Claim
12 words
The method of claim 19 wherein crosslinking is initiated by ultraviolet radiation.
Claim 24
Dependent Claim
31 words
The method of claim 14 wherein the heat treating is performed at a temperature that is at least 10 degrees Kelvin greater than the normal glass transition temperature of the resin.
Claim 25
Dependent Claim
31 words
The method of claim 22 wherein the heat treating is performed at a temperature that is at least 20 degrees Kelvin greater than the normal glass transition temperature of the resin.
Claim 26
Dependent Claim
20 words
The method of claim 14 wherein the heating treating reduces groove tip impression penetration to less than 1×10 -4 mm.
Claim 27
Dependent Claim
13 words
The method of claim 14 wherein a photoinitiator is used for the curing.
Claim 28
Dependent Claim
16 words
The method of claim 14 wherein the substrate has a sputter etched surface adjacent the microstructure.
Claim 29
Dependent Claim
22 words
The method of claim 1 wherein the oligomeric resin provides a cured polymer having a refractive index that is greater than 1.56.
Claim 30
Dependent Claim
22 words
The method of claim 1 wherein the oligomeric resin provides a cured polymer having a refractive index that is greater than 1.58.
Claim 31
Dependent Claim
46 words
The method of claim 1 wherein said oligomeric resin comprises epoxy diacrylate, bromine modified epoxy diacrylate, isobornyl acrylate, methyl methacrylate, cyclohexylchloroacrylate, 2-chlorostyrene, 2,4-dichlorostyrene, styrene, acrylic acid, acrylamide, acrylonitrile, methacrylonitrile, phenoxyethyl acrylate, tribromophenoxyethyl acrylate, benzyl acrylate, alkoxylated epoxy diacrylate, bromine modified alkoxylated epoxy diacrylate or combinations thereof.
References Cited (Backward Citations)
US3935359A
Cited
US4576850A
Cited
US4668558A
Cited
US4582885A
Cited
US4181766A
Cited
US4340276A
Cited
US4262072A
Cited
US4388436A
Cited
US4542449A
Cited
US4973629A
Cited
US5175030A
Cited
US5183597A
Cited
US5229882A
Cited
EP0528645A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-05-05 | 2000-11-04 | 2001-05-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-05-05 | 2004-11-04 | 2005-05-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-05-05 | 2008-11-04 | 2009-05-06 | $7700.00 | Window Closed / Lapsed |