Pre-oxidation of oxide film for chemical decontamination of recirculation piping
Assignee: General Electric Co
•
Filing: 1995-08-29
•
Granted: 1997-04-29
•
Expires: 2015-08-29
Abstract
Abstract A pre-oxidation treatment for decreasing the amount of chromium deposited on out-of-core surfaces such as the internal surfaces of recirculation piping. Hydrogen peroxide is injected into the reactor coolant through the recirculation line during reactor shutdown after H 2 addition has been terminated. A dilute acid solution (e.g., nitric acid) is also injected into the loop to serve as a catalyst to accelerate the oxidation reactions. An appropriate water pH (e.g., in the range of 5-6) is maintained by acid injection. The coolant temperature during shutdown is maintained at approximately 150° C. or lower. The peroxide concentration in the recirculation piping is maintained at approximately 1 ppm or higher as needed. The oxidation process should be allowed to take effect in the proposed temperature range with the recirculation pump in operation for at least a few hours to 24 hours, depending on the temperature and the oxide film thickness. The Cr-enriched oxides can be readily oxidized by the hydrogen peroxide to a soluble chromate under proper conditions. Some of the radioactivities associated with the oxides will then be released into the coolant and consequently removed by the reactor water cleanup system.
Inventors
- 👤 Chien-Chang Lin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 16:29
CPC Classifications
G; G21; G21C; G21C17/00; G21C17/02; G21C17/022; G21C17/0225; G21C19/00; G21C19/28; G21C19/30; Y; Y02; Y02E; Y02E30/00; Y02E30/30
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
106 words
A method for treating a contaminated oxidized surface of a nuclear reactor, comprising the steps of shutting down the reactor and allowing the reactor water that wets said contaminated oxidized surface to cool to a temperature no higher than about 150° C., injecting dilute acid into the reactor water in an amount so that the pH of the reactor water that wets said contaminated oxidized surface is in the range of 5 to 6, and injecting hydrogen peroxide into the reactor water in an amount so that the reactor water that wets said contaminated oxidized surface has a hydrogen peroxide concentration of at least 1 ppm.
Claim 2
Independent Claim
106 words
A method for treating a contaminated oxidized surface of a nuclear reactor, comprising the steps of shutting down the reactor and allowing the reactor water that wets said contaminated oxidized surface to cool to a temperature no higher than about 150° C., injecting dilute acid into the reactor water in an amount so that the pH of the reactor water that wets said contaminated oxidized surface is in the range of 5 to 6, and injecting hydrogen peroxide into the reactor water in an amount so that the reactor water that wets said contaminated oxidized surface has a hydrogen peroxide concentration of at least 1 ppm.
Claim 3
Dependent Claim
19 words
The method as defined in claim 1, wherein said contaminated oxidized surface is an interior surface of recirculation piping.
Claim 4
Dependent Claim
22 words
The method as defined in claim 1, wherein said contaminated oxidized surface is an interior surface of reactor water clean-up system piping.
Claim 5
Dependent Claim
22 words
The method as defined in claim 1, wherein said contaminated oxidized surface is an interior surface of residual heat removal system piping.
Claim 6
Dependent Claim
22 words
The method as defined in claim 1, wherein said contaminated oxidized surface is submerged in reactor water inside a reactor pressure vessel.
Claim 7
Independent Claim
106 words
A method for treating a contaminated oxidized surface of a nuclear reactor, comprising the steps of shutting down the reactor and allowing the reactor water that wets said contaminated oxidized surface to cool to a temperature no higher than about 150°C., injecting dilute acid into the reactor water in an amount so that the pH of the reactor water that wets said contaminated oxidized surface is in the range of 5 to 6, and injecting an oxidizing agent into the reactor water in an amount so that the reactor water that wets said contaminated oxidized surface has an oxidizing agent concentration of at least 1 ppm.
Claim 8
Independent Claim
106 words
A method for treating a contaminated oxidized surface of a nuclear reactor, comprising the steps of shutting down the reactor and allowing the reactor water that wets said contaminated oxidized surface to cool to a temperature no higher than about 150°C., injecting dilute acid into the reactor water in an amount so that the pH of the reactor water that wets said contaminated oxidized surface is in the range of 5 to 6, and injecting an oxidizing agent into the reactor water in an amount so that the reactor water that wets said contaminated oxidized surface has an oxidizing agent concentration of at least 1 ppm.
Claim 9
Dependent Claim
14 words
The method as defined in claim 6, wherein the oxidizing agent is hydrogen peroxide.
Claim 10
Dependent Claim
19 words
The method as defined in claim 6, wherein said contaminated oxidized surface is an interior surface of recirculation piping.
Claim 11
Dependent Claim
22 words
The method as defined in claim 6, wherein said contaminated oxidized surface is an interior surface of reactor water clean-up system piping.
Claim 12
Dependent Claim
22 words
The method as defined in claim 6, wherein said contaminated oxidized surface is an interior surface of residual heat removal system piping.
Claim 13
Dependent Claim
22 words
The method as defined in claim 6, wherein said contaminated oxidized surface is submerged in reactor water inside a reactor pressure vessel.
Claim 14
Independent Claim
128 words
A method for treating recirculation piping of a nuclear reactor having a reactor vessel connected to the recirculation piping by connections, comprising the steps of: shutting down the reactor; closing the connections between the reactor vessel and a section of recirculation piping to be treated connecting one junction of the section of recirculation piping to be treated with another junction of the section of recirculation piping to be treated to form a closed recirculation loop comprising said section of recirculation piping to be treated and excluding the reactor vessel; circulating water through said closed recirculation loop; injecting oxidizing agent and dilute acid into the water circulating in said closed recirculation loop, wherein the amount of dilute acid injected produces a pH in the range of 5 to 6.
Claim 15
Independent Claim
128 words
A method for treating recirculation piping of a nuclear reactor having a reactor vessel connected to the recirculation piping by connections, comprising the steps of: shutting down the reactor; closing the connections between the reactor vessel and a section of recirculation piping to be treated connecting one junction of the section of recirculation piping to be treated with another junction of the section of recirculation piping to be treated to form a closed recirculation loop comprising said section of recirculation piping to be treated and excluding the reactor vessel; circulating water through said closed recirculation loop; injecting oxidizing agent and dilute acid into the water circulating in said closed recirculation loop, wherein the amount of dilute acid injected produces a pH in the range of 5 to 6.
Claim 16
Dependent Claim
38 words
The method as defined in claim 12, wherein the oxidizing agent is hydrogen peroxide injected in an amount sufficient to maintain a hydrogen peroxide concentration of at least approximately 1 ppm in water flowing in said closed loop.
Claim 17
Dependent Claim
26 words
The method as defined in claim 12, wherein the water circulating in said closed loop is diverted to a system which removes radioisotopes from the water.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-04-28 | 2000-10-28 | 2001-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-04-28 | 2004-10-28 | 2005-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-04-28 | 2008-10-28 | 2009-04-29 | $7700.00 | Window Closed / Lapsed |