Method for the preparation of thermoplastic resin compositions
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1995-11-29
•
Granted: 1997-02-18
•
Expires: 2015-11-29
Abstract
Abstract A method for preparing a thermoplastic resin composition, said method comprising hot-kneading, in the absence of a radical-generating catalyst, (A) 100 parts by weight of a thermoplastic resin; and (B) 0.1 to 200 parts by weight of an alkenyl-functional polyorganosiloxane filled with amorphous silica micropowder, wherein the weight ratio of said silica micropowder to said alkenyl-functional polyorganosiloxane is 0.01:100 to 50:100, whereby the polyorganosiloxane of component (B) is chemically bonded to resin (A).
Inventors
- 👤 Haruhiko Furukawa
- 👤 Akihiro Nakamura
- 👤 Akihiko Shirahata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:16
CPC Classifications
C; C08; C08G; C08G77/00; C08G77/42; C08G77/442; C08G81/00; C08G81/02; C08G81/024
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
83 words
A method for preparing a thermoplastic resin composition, said method comprising hot-kneading, in the absence of a radical-generating catalyst, (A) 100 parts by weight of a thermoplastic resin derived from at least one vinylic monomer ; and (B) 0.1 to 200 parts by weight of an alkenyl-functional polyorganosiloxane filled with amorphous silica micropowder, wherein the weight ratio of said silica micropowder to said alkenyl-functional polyorganosiloxane is 0.01:100 to 50:100, whereby said polyorganosiloxane of component (B) becomes chemically bonded to said thermoplastic resin (A).
Claim 2
Independent Claim
83 words
A method for preparing a thermoplastic resin composition, said method comprising hot-kneading, in the absence of a radical-generating catalyst, (A) 100 parts by weight of a thermoplastic resin derived from at least one vinylic monomer ; and (B) 0.1 to 200 parts by weight of an alkenyl-functional polyorganosiloxane filled with amorphous silica micropowder, wherein the weight ratio of said silica micropowder to said alkenyl-functional polyorganosiloxane is 0.01:100 to 50:100, whereby said polyorganosiloxane of component (B) becomes chemically bonded to said thermoplastic resin (A).
Claim 3
Dependent Claim
27 words
The method according to claim 1, wherein at least 50 weight percent of said alkenyl-functional polyorganosiloxane in component (B) is chemically bonded to said thermoplastic resin (A).
Claim 4
Dependent Claim
34 words
The method according to claim 1, wherein said alkenyl-functional polyorganosiloxane in component (B) contains ≦50,000 parts per million by weight of a low molecular weight siloxane having a vapor pressure≧10 mmHg at 200° C.
Claim 5
Dependent Claim
24 words
The method according to claim 1, wherein said alkenyl-functional polyorganosiloxane in component (B) has a viscosity of at least 1,000,000 centistokes at 25° C.
Claim 6
Dependent Claim
21 words
The method according to claim 1, wherein said thermoplastic resin (A) is a homopolymer or copolymer derived from a vinylic monomer.
Claim 7
Dependent Claim
60 words
The method according to claim 1, wherein said thermoplastic resin (A) is selected from the group consisting of polyethylene, polypropylene, polymethylpentene, polyvinyl acetate, polyvinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride, polystyrene, polymethyl methacrylate, polyethyl methacrylate, polybutyl methacrylate, polymethyl acrylate, polyethyl acrylate, polybutyl acrylate, ethylene-propylene copolymer, ethylene-vinyl acetate copolymer, ethylene-vinyl chloride copolymer, ethylene-methyl methacrylate copolymer, styrene-acrylonitrile copolymer and styrene-acrylonitrile-butadiene copolymer.
Claim 8
Dependent Claim
25 words
The method according to claim 2, wherein the viscosity of said alkenyl-functional polyorganosiloxane in component (B) is at least 1 million centistokes at 25° C.
Claim 9
Dependent Claim
31 words
The method according to claim 7, wherein the alkenyl radicals of said alkenyl-functional polyorganosiloxane in component (B) are selected from the group consisting of vinyl, propenyl, butenyl, pentenyl, hexenyl and decenyl.
Claim 10
Dependent Claim
41 words
The method according to claim 8, wherein said alkenyl-functional polyorganosiloxane in component (B) is selected from the group consisting of dimethylvinylsiloxy-endblocked polydimethylsiloxanes, dimethylvinylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymers, trimethylsiloxy-endblocked polymethylvinylsiloxanes, trimethylsiloxy-endblocked dimethylsiloxane-methylvinylsiloxane copolymers, dimethylhexenylsiloxy-endblocked polydimethylsiloxanes, dimethylhexenylsiloxy-endblocked dimethylsiloxane-methylhexenylsiloxane copolymers, trimethylsiloxy-endblocked polymethylhexenylsiloxanes and trimethylsiloxy-endblocked dimethylsiloxane-methylhexenylsiloxane copolymers.
Claim 11
Dependent Claim
30 words
The method according to claim 1, wherein the diameter of said silica particles is≦50 microns and the specific surface area of said silica is at least 50 m 2 /g.
Claim 12
Dependent Claim
31 words
The method according to claim 10, wherein 0.1 to 30 parts by weight of said silica are used for each 100 parts by weight of said alkenyl-functional polyorganosiloxane in component (B).
Claim 13
Dependent Claim
30 words
The method according to claim 2, wherein the diameter of said silica particles is≦50 microns and the specific surface area of said silica is at least 50 m 2 /g.
Claim 14
Dependent Claim
31 words
The method according to claim 12, wherein 0.1 to 30 parts by weight of said silica are used for each 100 parts by weight of said alkenyl-functional polyorganosiloxane in component (B).
Claim 15
Dependent Claim
30 words
The method according to claim 5, wherein the diameter of said silica particles is≦50 microns and the specific surface area of said silica is at least 50 m 2 /g.
Claim 16
Dependent Claim
30 words
The method according to claim 14, wherein 0.1 to parts by weight of said silica are used for each 100 parts by weight of said alkenyl-functional polyorganosiloxane in component (B).
Claim 17
Dependent Claim
21 words
The method according to claim 1, wherein the hot-kneading is carried out at a temperature of 160° C. to 260° C.
Claim 18
Dependent Claim
21 words
The method according to claim 2, wherein the hot-kneading is carried out at a temperature of 160° C. to 260° C.
Claim 19
Dependent Claim
21 words
The method according to claim 4, wherein the hot-kneading is carried out at a temperature of 160° C. to 260° C.
Claim 20
Dependent Claim
21 words
The method according to claim 5, wherein the hot-kneading is carried out at a temperature of 160° C. to 260° C.
Claim 21
Dependent Claim
21 words
The method according to claim 8, wherein the hot-kneading is carried out at a temperature of 160° C. to 260° C.
References Cited (Backward Citations)
US2888419A
Cited
US3865897A
Cited
US4196731A
Cited
US4252915A
Cited
US4273691A
Cited
JPH0616824A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-02-18 | 2000-08-19 | 2001-02-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-02-18 | 2004-08-19 | 2005-02-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-02-18 | 2008-08-19 | 2009-02-18 | $7700.00 | Window Closed / Lapsed |