Reinforced carbon composites
Assignee: Fiber Materials Inc
•
Filing: 1990-10-01
•
Granted: 1997-01-28
•
Expires: 2010-10-01
Abstract
Abstract Layered carbon-carbon composites having improved interlaminar tensile strength are disclosed together with a process for making such composites. A metal catalyst is first deposited on a panel comprising a plurality of layers of carbon fiber cloth. The panel is then exposed to a gaseous hydrocarbon in an inert atmosphere at elevated temperature in order to promote the growth of graphite whiskers between the carbon cloth layers.
Inventors
- 👤 James R. Lennox
- 👤 Daniel C. Nelson
- 👤 Roger T. Pepper
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:45
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/83; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24058; Y10T428/24124; Y10T428/24174; Y10T428/30; Y10T442/00; Y10T442/30; Y10T442/3472; Y10T442/3504; Y10T442/3707; Y10T442/3715; Y10T442/60; Y10T442/659
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
94 words
Process for preparing carbon fiber composites comprising: (a) placing multilayered carbon fiber cloth in a nickel nitrate solution under vacuum; (b) removing said cloth from said solution and drying it by heating to about 100° C.; (c) heating said dried cloth to about 600° C. in an inert atmosphere for a time sufficient to reduce the nickel nitrate to nickel; and, (d) contacting said cloth with acetylene while maintaining the temperature at about 600°-800° C. for a period of time sufficient to promote the growth of graphite whiskers between the carbon fiber cloth layers.
Claim 2
Dependent Claim
94 words
Process for preparing carbon fiber composites comprising: (a) placing multilayered carbon fiber cloth in a nickel nitrate solution under vacuum; (b) removing said cloth from said solution and drying it by heating to about 100° C.; (c) heating said dried cloth to about 600° C. in an inert atmosphere for a time sufficient to reduce the nickel nitrate to nickel; and, (d) contacting said cloth with acetylene while maintaining the temperature at about 600°-800° C. for a period of time sufficient to promote the growth of graphite whiskers between the carbon fiber cloth layers.
Claim 3
Dependent Claim
85 words
Process for preparing carbon composites comprising: (a) forming a relatively rigid, porous carbon body having a plurality of carbon layers reinforced with carbon fibers and at least partially impregnated with a subsequently densified and pyrolyzed carbonaceous material; (b) distributing in the pores of said body a metal catalyst capable of initiating the deposition of carbon whiskers from a carbon-containing vapor; and (c) exposing said body to said vapor for a period of time sufficient to promote the growth of graphite whiskers between said carbon layers.
Claim 4
Dependent Claim
85 words
Process for preparing carbon composites comprising: (a) forming a relatively rigid, porous carbon body having a plurality of carbon layers reinforced with carbon fibers and at least partially impregnated with a subsequently densified and pyrolyzed carbonaceous material; (b) distributing in the pores of said body a metal catalyst capable of initiating the deposition of carbon whiskers from a carbon-containing vapor; and (c) exposing said body to said vapor for a period of time sufficient to promote the growth of graphite whiskers between said carbon layers.
Claim 5
Dependent Claim
24 words
The process of claim 2 wherein said metal catalyst is selected from the group consisting essentially of iron, nickel, cobalt, chrome and combinations thereof.
Claim 6
Dependent Claim
22 words
The process of claim 2 wherein said vapor is a hydrocarbon capable of being catalyzed by said catalyst to form carbon whiskers.
Claim 7
Dependent Claim
22 words
The process of claim 4 wherein said vapor is selected from the group consisting essentially of benzene, methane, acetylene and combinations thereof.
Claim 8
Dependent Claim
65 words
The process of claim 2 wherein said metal catalyst is distributed in said body by applying a solution of a soluble compound of said metal catalyst to said panel, said compound being thermally decomposable to said catalyst, and thereafter heating said body containing said compound in an inert atmosphere at elevated temperature for a period of time sufficient to decompose said compound to said catalyst.
Claim 9
Dependent Claim
15 words
The process of claim 6 wherein said solution comprises an aqueous solution of nickel nitrate.
Claim 10
Dependent Claim
39 words
The process of claim 2 wherein said step of forming said body includes a densification step comprising impregnating said body with a pyrolytically carbonizable precursor material and thereafter carbonizing said precursor at an elevated temperature in an inert atmosphere.
Claim 11
Dependent Claim
15 words
The process of claim 8 wherein said densification step is repeated a plurality of times.
References Cited (Backward Citations)
GB1215589A
Cited
GB1254732A
Cited
GB1423240A
Cited
GB1549687A
Cited
GB2002685A
Cited
GB2027418A
Cited
US4328272A
Cited
EP0150566A2
Cited
US4876078A
Cited
GB2199856A
Cited
US5057297A
Cited
US5102647A
Cited
US5039504A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-01-28 | 2000-07-29 | 2001-01-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-01-28 | 2004-07-29 | 2005-01-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-01-28 | 2008-07-29 | 2009-01-28 | $7700.00 | Window Closed / Lapsed |