US5587231A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Syntactic foam core material and method of manufacture
Assignee: TALC Ltd
•
Filing: 1994-07-29
•
Granted: 1996-12-24
•
Expires: 2014-07-29
Abstract
Abstract A syntactic structural foam product in flat sheet form or curved three-dimensional form adaptable to such uses as a light weight structural core for composite laminates, is made of a mixture of hollow ceramic microspheres and dry resin powder, of either thermosetting or a high-temperature thermoplastic resin, distributed in the interstices of the mass of microspheres for integration of the mixture into desired form upon heating and cooling. Resin powder collected as a waste by-product from resin coating materials can be recycled in the production of the desired product. The foam product is produced by first intermixing the microspheres and powdered resin by physical agitation of the mixture and depositing the mixture as a layer over a surface having a release agent thereover within a dimension defining region between boundary members and then supplying heat with or without pressure to the layer at a temperature and for a time period sufficient to effect a melting of the resin powder and thereafter cooling the resin in a hardened condition to integrate the mixture into the product desired after which the product is withdrawn from the forming zone. Reinforcing elements such as glass or carbon fibers can be selectively included in the mixture for predeterminable desired physical and mechanical properties.
Inventors
- 👤 Charles L. Mereer
- 👤 Thomas E. Philipps
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:15
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/18; B32B3/00; B32B3/26; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/08; B29C70/086; B29C70/58; B29C70/66; B29D; B29D99/00; B29D99/001; B32B27/00; B32B27/18; B32B27/20; B32B27/42; B32B37/00; B32B37/04; B32B9/00; B32B9/005; B32B9/04; B32B9/046; C; C08; C08J; C08J9/00; C08J9/0085; C08J9/32; B29K; B29K2105/00; B29K2105/06; B29K2105/16; B29K2105/165; B32B2262/00; B32B2262/10; B32B2262/101; B32B2262/106; B32B2305/00; B32B2305/30; B32B2307/00; B32B2307/70; B32B2307/72; B32B2315/00; B32B2315/08; B32B2315/085; B32B2361/00; Y; Y10; Y10S; Y10S264/00; Y10S264/06; Y10S264/07; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1043; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249971; Y10T428/249972; Y10T428/249974; Y10T428/249986; Y10T428/26; Y10T428/269; Y10T442/00; Y10T442/60; Y10T442/647; Y10T442/652; Y10T442/653
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
168 words
A syntactic foam core material adaptable to providing a low density rigid foam core layer for composite layered sandwich structures comprising a layer of hollow ceramic microspheres, dry resin powder particles finer in dimension than the diameter of said microspheres thoroughly intermixed with said layer of microspheres to provide a uniform mixture of said powder particles and microspheres, said microspheres being present in said mixture in a percentage by volume amount of at least 60%, said mixture of microspheres and resin powder having been processed through a cycle of heat melting and setting of said resin particles in interbonded relationship with said microspheres, said resin particles being present in quantity to interbond said mixture into an integrated rigid syntactic foam layer while leaving void spaces within said layer upon setting of said melted resin, said rigid foam layer having a density less than 25 pounds per cubic foot, said layer having opposite major surfaces for combination with layers of material on opposite sides thereof in layered sandwich structures.
Claim 2
Dependent Claim
168 words
A syntactic foam core material adaptable to providing a low density rigid foam core layer for composite layered sandwich structures comprising a layer of hollow ceramic microspheres, dry resin powder particles finer in dimension than the diameter of said microspheres thoroughly intermixed with said layer of microspheres to provide a uniform mixture of said powder particles and microspheres, said microspheres being present in said mixture in a percentage by volume amount of at least 60%, said mixture of microspheres and resin powder having been processed through a cycle of heat melting and setting of said resin particles in interbonded relationship with said microspheres, said resin particles being present in quantity to interbond said mixture into an integrated rigid syntactic foam layer while leaving void spaces within said layer upon setting of said melted resin, said rigid foam layer having a density less than 25 pounds per cubic foot, said layer having opposite major surfaces for combination with layers of material on opposite sides thereof in layered sandwich structures.
Claim 3
Dependent Claim
42 words
A syntactic foam core material as set forth in claim 1 in which said microspheres are glass microspheres and said core material includes reinforcing elements in the form of fibers intermixed throughout and interbonded with said mixture of glass microspheres and resin.
Claim 4
Dependent Claim
20 words
A syntactic foam core material as set forth in claim 2 in which the reinforcing elements are of glass fibers.
Claim 5
Dependent Claim
22 words
A syntactic foam core material as set forth in claim 3 in which said reinforcing elements are fibers of chopped glass strands.
Claim 6
Dependent Claim
26 words
A syntactic foam core material as set forth in claim 2 in which the reinforcing elements are fibers in the form of a mat of fibers.
Claim 7
Dependent Claim
19 words
A syntactic foam core material as set forth in claim 2 in which the reinforcing elements are carbon fibers.
Claim 8
Dependent Claim
40 words
A syntactic foam core material as set forth in claims 1 in which the diameter of the microspheres is in the order of 170 microns and the size of the resin powder particles is in the order of 20 microns.
Claim 9
Dependent Claim
19 words
A syntactic foam core material as set forth in claim 1 wherein said powdered resin is a phenolic resin.
Claim 10
Dependent Claim
28 words
A syntactic foam core material as set forth in claim 8 in which hexamethylenetetramine is present as a catalyst to enhance adhesion of said resin to said microspheres.
Claim 11
Dependent Claim
27 words
A syntactic foam core material as set forth in claim 1 in sheet form in which said resin powder particles have a dimension less than 50 microns.
Claim 12
Dependent Claim
140 words
A syntactic foam material for producing a light weight rigid layer for multilayered composite articles comprising a mass of hollow microspheres of glass in a layer, particles of a dry powdered resin distributed throughout said mass of hollow microspheres, said particles being finer in dimension than the dimension of said microspheres, said particles of powdered resin being present in said material in an amount to effect an interbonding of the combination in integrated relation in a rigid layer with void spaces in said layer upon heat cycling and setting of said resin powder, said microspheres being present, in said material in a percentage by volume amount of at least 60%, said rigid layer having a density less than 25 pounds per cubic foot and having opposite major surfaces for accommodation of surfaces of adjacent layers in said multilayered composite articles.
Claim 13
Dependent Claim
140 words
A syntactic foam material for producing a light weight rigid layer for multilayered composite articles comprising a mass of hollow microspheres of glass in a layer, particles of a dry powdered resin distributed throughout said mass of hollow microspheres, said particles being finer in dimension than the dimension of said microspheres, said particles of powdered resin being present in said material in an amount to effect an interbonding of the combination in integrated relation in a rigid layer with void spaces in said layer upon heat cycling and setting of said resin powder, said microspheres being present, in said material in a percentage by volume amount of at least 60%, said rigid layer having a density less than 25 pounds per cubic foot and having opposite major surfaces for accommodation of surfaces of adjacent layers in said multilayered composite articles.
References Cited (Backward Citations)
US2806509A
Cited
US3855160A
Cited
US4144372A
Cited
US4025686A
Cited
US4193829A
Cited
US4132755A
Cited
US4178406A
Cited
US4201823A
Cited
US4917945A
Cited
US4861649A
Cited
US5030488A
Cited
US5219629A
Cited
US5034256A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-12-24 | 2000-06-24 | 2000-12-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-12-24 | 2004-06-24 | 2004-12-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-12-24 | 2008-06-24 | 2008-12-24 | $7700.00 | Window Closed / Lapsed |