Method for fabricating optical quality molds with precision microfeatures
Assignee: Avago Technologies International Sales Pte Ltd
•
Filing: 1994-12-02
•
Granted: 1996-11-19
•
Expires: 2014-12-02
Abstract
Abstract Optical quality molds and mold inserts include an optically flat substrate, a layer of material applied to the substrate and one or more depressions in a predetermined pattern formed in the layer of material applied to the substrate. The depth of the depressions are precisely determined by the thickness of the layer applied to the substrate. By contacting the mold with resin in a fluid state, a component is fabricated having microfeatures formed monolithically thereon.
Inventors
- 👤 Ken M. Takahashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:28
CPC Classifications
B; B29; B29C; B29C33/00; G; G02; G02F; G02F1/00; G02F1/01; G02F1/13; G02F1/133; G02F1/1333; G02F1/1339; G02F1/13394; B29C33/42; B29C33/38; B29C33/3842; G02F1/133305; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24777; Y10T428/24802; Y10T428/249921; Y10T428/249953; Y10T428/249978; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/31504
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
129 words
A method for making a flat panel display from a polymeric resin, the flat panel display having microfeatures monolithically formed thereon, the method comprising: providing a mold including an optically fiat substrate, a layer of metal applied to the substrate and one or more depressions in a predetermined pattern etched in the layer of metal applied to the substrate, portions of the optically flat substrate being exposed in the one or more depressions; contacting the mold with a polymeric resin in a fluid state such that the resin substantially fills the depressions and contacts exposed portions of the optically flat substrate; hardening the polymeric resin to form a component of a flat panel display having microfeatures monolithically formed thereon; and removing the flat panel display component from the mold.
Claim 2
Independent Claim
129 words
A method for making a flat panel display from a polymeric resin, the flat panel display having microfeatures monolithically formed thereon, the method comprising: providing a mold including an optically fiat substrate, a layer of metal applied to the substrate and one or more depressions in a predetermined pattern etched in the layer of metal applied to the substrate, portions of the optically flat substrate being exposed in the one or more depressions; contacting the mold with a polymeric resin in a fluid state such that the resin substantially fills the depressions and contacts exposed portions of the optically flat substrate; hardening the polymeric resin to form a component of a flat panel display having microfeatures monolithically formed thereon; and removing the flat panel display component from the mold.
Claim 3
Dependent Claim
49 words
A method as in claim 1, wherein the step of contacting the mold with a polymeric resin in a fluid state comprises contacting the mold with a composition selected from the group consisting of solutions of polymers in one or more solvents, molten thermoplastic polymers and uncured thermosetting polymers.
Claim 4
Dependent Claim
31 words
A method as in claim 1, wherein the step of providing a mold comprises forming a predetermined pattern of depressions having a maximum depth of about 0.1 to about 50 μm.
Claim 5
Dependent Claim
34 words
A method as in claim 1, wherein the step of providing a mold comprises forming an optically flat substrate by replicating an optically flat surface by applying a metal to the optically flat surface.
Claim 6
Dependent Claim
25 words
A method as in claim 4, wherein the metal is applied to the optically flat surface to a thickness of at least about 2 mils.
Claim 7
Dependent Claim
21 words
A method as in claim 4, wherein nickel is the metal applied to the optically flat surface to form the substrate.
Claim 8
Dependent Claim
26 words
A method as in claim 7, wherein the metal applied to the substrate is selected from the group consisting of chromium, copper, aluminum, titanium and molybdenum.
Claim 9
Dependent Claim
26 words
A method as in claim 7, wherein the metal is applied to the substrate to a thickness ranging from about 0.1 μm to about 50 μm.
Claim 10
Dependent Claim
44 words
A method as in claim 7, wherein the step of providing a mold further comprises applying and patterning a masking layer on the metal layer applied to the substrate and etching the layer applied to the substrate to form the predetermined pattern of depressions.
Claim 11
Dependent Claim
47 words
A method as in claim 1, wherein the step of providing a mold further comprises applying an upper layer of material to the layer of metal applied to the substrate, the upper layer having a different chemical composition than the layer of metal applied to the substrate.
Claim 12
Dependent Claim
26 words
A method as in claim 10, wherein the upper layer is made from a metal selected from the group consisting of titanium, aluminum, molybdenum and nickel.
Claim 13
Dependent Claim
45 words
A method as in claim 10, wherein the step of providing a mold further comprises applying and patterning a masking layer on the upper layer and etching the upper layer and the metal layer applied to the substrate to form the predetermined pattern of depressions.
Claim 14
Dependent Claim
15 words
A method as in claim 12, wherein the etching produces depressions having tapered side walls.
Claim 15
Dependent Claim
23 words
A method as in claim 12, further comprising the step of removing the masking layer prior to contacting the mold with polymeric resin.
Claim 16
Dependent Claim
23 words
A method as in claim 12, further comprising the step of removing the upper layer prior to contacting the mold with polymeric resin.
Claim 17
Independent Claim
180 words
A method for making a resinous fiat panel display from a polymeric resin, the resinous fiat panel display having microfeatures monolithically formed thereon, the method comprising: a) providing a substrate having an optically flat surface; b) depositing at least one layer of at least one etchable metal onto the optically flat surface of the substrate; then c) depositing a masking layer onto said at least one layer of at least one etchable metal; d) photolithographically forming a predetermined pattern in said masking layer to provide at least one exposed area of the at least one etchable metal; e) etching the at least one exposed area of the at least one etchable metal to form at least one depression wherein the optically flat surface of the substrate is exposed for contact with a molding material; f) removing the masking layer; g) contacting the exposed optically flat surface of the substrate with a polymeric resin in a fluid state such that the resin substantially fills the at least one depression; h) hardening the polymeric resin; and i) removing the hardened polymeric resin.
Claim 18
Independent Claim
180 words
A method for making a resinous fiat panel display from a polymeric resin, the resinous fiat panel display having microfeatures monolithically formed thereon, the method comprising: a) providing a substrate having an optically flat surface; b) depositing at least one layer of at least one etchable metal onto the optically flat surface of the substrate; then c) depositing a masking layer onto said at least one layer of at least one etchable metal; d) photolithographically forming a predetermined pattern in said masking layer to provide at least one exposed area of the at least one etchable metal; e) etching the at least one exposed area of the at least one etchable metal to form at least one depression wherein the optically flat surface of the substrate is exposed for contact with a molding material; f) removing the masking layer; g) contacting the exposed optically flat surface of the substrate with a polymeric resin in a fluid state such that the resin substantially fills the at least one depression; h) hardening the polymeric resin; and i) removing the hardened polymeric resin.
Claim 19
Dependent Claim
41 words
The method of claim 16 wherein said step of providing a substrate having an optically flat surface comprises providing an optically flat plate, depositing a metal onto the optically flat plate, and removing the metal to replicate the optically flat surface.
Claim 20
Dependent Claim
65 words
The method of claim 16 wherein said step of depositing at least one etchable metal comprises depositing a first layer of first etchable metal onto the optically flat surface of the substrate, then depositing a second layer of second etchable metal onto the first layer of first etchable metal, the second etchable metal having a higher etch rate than that of the first etchable metal.
References Cited (Backward Citations)
US4144300A
Cited
US4325779A
Cited
US4832790A
Cited
US5007984A
Cited
US5389313A
Cited
US5013494A
Cited
US5071597A
Cited
US5245454A
Cited
US5288591A
Cited
US5348616A
Cited
US5298117A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-11-19 | 2000-05-20 | 2000-11-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-11-19 | 2004-05-20 | 2004-11-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-11-19 | 2008-05-20 | 2008-11-19 | $7700.00 | Window Closed / Lapsed |