Conductive polyurethane foam compositions and method for producing same
Assignee: FXI Inc
•
Filing: 1995-06-07
•
Granted: 1996-10-22
•
Expires: 2015-06-07
Abstract
Abstract The present invention relates to three-dimensional expanded polyurethane foam materials, such as flexible reticulated polyurethane foam compositions, that are electrically conductive and have antistatic properties. More specifically, the invention relates to a polyurethane foam having long-lasting and reliable electrical conductivity characteristics and a volume resistivity of approximately 10 12 ohm·cm or less at ambient room temperature (about 70° F.). This foam is produced by combining conventional polyurethane foam-forming reactants and an effective amount of an antistatic agent such as tetracyanoquinodimethane (TCNQ) or sodium perchlorate under foam-forming conditions. In one preferred embodiment, the conductive foam is subsequently reticulated by momentary exposure to a flame front.
Inventors
- 👤 Sharon A. Free
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 10:44
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/0066; C08J9/0014; C08J9/0028; H; H01; H01B; H01B1/00; H01B1/20; C08J2375/00; C08J2375/04
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
32 words
A three dimensional electrically conductive plastic foam structure comprising a polyurethane foam containing an effective amount for lowering the volume resistivity of said foam of an antistatic agent consisting essentially of tetracyanoquinodimethane.
Claim 2
Dependent Claim
32 words
A three dimensional electrically conductive plastic foam structure comprising a polyurethane foam containing an effective amount for lowering the volume resistivity of said foam of an antistatic agent consisting essentially of tetracyanoquinodimethane.
Claim 3
Dependent Claim
43 words
A three dimensional electrically conductive structure according to claim 1, wherein said structure is prepared by reacting a polyol and an isocyanate and comprises 0.08 to 0.20 parts per hundred parts by weight of said polyol of said tetracyanoquinodimethane as said antistatic agent.
Claim 4
Dependent Claim
19 words
A three dimensional electrically conductive structure according to claim 1, wherein said polyurethane foam comprises a reticulated polyurethane foam.
Claim 5
Dependent Claim
41 words
A three dimensional electrically conductive structure according to claim 1, wherein said polyurethane foam is formed from at least one polyol and at least one isocyanate and further wherein said antistatic agent is tetracyanoquinodimethane which is dissolved in a suitable solvent.
Claim 6
Dependent Claim
53 words
A three dimensional electrically conductive structure according to claim 1, wherein said polyurethane foam is formed from a reaction mixture containing at least one polyol and at least one isocyanate and further wherein said antistatic agent is tetracyanoquinodimethane which is not dissolved in a solvent but is added directly to the reaction mixture.
Claim 7
Dependent Claim
30 words
A three dimensional electrically conductive structure according to claim 2, wherein said polyurethane foam contains 0.08 to 0.15 parts per hundred parts by weight of said polyol of said tetracyanoquinodimethane.
Claim 8
Dependent Claim
30 words
A three dimensional electrically conductive structure according to claim 2, wherein said polyurethane foam contains 0.10 to 0.15 parts per hundred parts by weight of said polyol of said tetracyanoquinodimethane.
Claim 9
Dependent Claim
56 words
A three dimensional electrically conductive structure having a volume resistivity at about 70° F. of less than 10 12 ohm·cm, comprising a polyurethane foam containing an effective amount for reducing the electrical resistivity of said foam to less than 10 12 ohm·cm of an antistatic agent consisting essentially of tetracyanoquinodimethane incorporated into said foam in situ.
Claim 10
Dependent Claim
56 words
A three dimensional electrically conductive structure having a volume resistivity at about 70° F. of less than 10 12 ohm·cm, comprising a polyurethane foam containing an effective amount for reducing the electrical resistivity of said foam to less than 10 12 ohm·cm of an antistatic agent consisting essentially of tetracyanoquinodimethane incorporated into said foam in situ.
Claim 11
Dependent Claim
29 words
A three dimensional electrically conductive structure according to claim 8, wherein said antistatic agent is tetracyanoquinodimethane which is present in an amount of from about 0.08 to 0.20 php.
Claim 12
Independent Claim
52 words
A method of preparing an electrically conductive polyurethane foam composition which comprises reacting, under foam forming conditions, at least one polyester or polyether polyol with an isocyanate compound in the presence of an effective amount for lowering the electrical resistance of said polyurethane foam of an antistatic agent consisting essentially of tetracyanoquinodimethane.
Claim 13
Independent Claim
52 words
A method of preparing an electrically conductive polyurethane foam composition which comprises reacting, under foam forming conditions, at least one polyester or polyether polyol with an isocyanate compound in the presence of an effective amount for lowering the electrical resistance of said polyurethane foam of an antistatic agent consisting essentially of tetracyanoquinodimethane.
Claim 14
Dependent Claim
26 words
A method according to claim 10, wherein said electrically conductive polyurethane foam has an electrical resistivity of less than 10 12 ohm·cm at about 70° F.
Claim 15
Dependent Claim
30 words
A method according to claim 10, wherein said antistatic agent is tetracyanoquinodimethane and the amount of said tetracyanoquinodimethane in said polyurethane foam composition is from about 0.08 to 0.20 php.
References Cited (Backward Citations)
US5180755A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-10-22 | 2000-04-22 | 2000-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-10-22 | 2004-04-22 | 2004-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-10-22 | 2008-04-22 | 2008-10-22 | $7700.00 | Window Closed / Lapsed |