Abstract
Abstract For the purpose of establishing the manufacturing method to obtain the Fe3B type Fe-Co-B-R-M system high performance resin bonded magnet which possesses improved iHc and (BH)max and can be reliably mass produced, the specific composition of Fe-Co-B-R (Pr, Nd)-M(Ag, Al, Si, Ga, Cu, Au) type molten alloy was rapidly solidified by the melt-quenching or atomization methods, or a combination of the two methods to obtain more than 90% of the solid in an essentially amorphous structure. After the temperature was raised at the rate of 1 DEG DIFFERENCE 15 DEG C./min., the alloy was heat treated at 550 DEG DIFFERENCE 730 DEG C. for 5 minutes DIFFERENCE 6 hours to obtain Fe-rich the boron compound phase, which crystallizes the body centered tetragonal Fe3P type crystalline structure, and the Nd2Fe14B type crystalline structure phase both coexisting as fine crystalline clusters of the average crystalline diameter of 5 nm DIFFERENCE 100 nm. The alloy powder which contains the ferromagnetic phase, where the boron compound phase and the Nd2Fe14B type phase coexist, is combined with resin to produce the high performance resin bonded magnet with iHc>/=3 kOe, Br>/=5 kG, and (BH)max>/=3 MGOe.
Inventors
- 👤 Satoshi Hirosawa
- 👤 Hirokazu Kanekiyo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:52
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/047; H01F1/053; H01F1/055; H01F1/057; H01F1/0571; H01F1/0575; H01F1/0578
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
213 words
A rare earth magnet having a compositional formula of Fe.sub.100-x-y-z Co.sub.x B.sub.y R.sub.z M.sub.w wherein R is at least one of Pr and Nd, M is one or two of Al, Si, Cu, Ga, Ag, and Au, symbols x, y, z and w each indicating a limit of composition range and respectively falling within the ranges of 0.05≦x≦15 at. %, 16≦y≦22 at. %, 3≦z≦6 at. %, and 0.1≦w≦3 at. %, said rare earth magnet including an iron-rich boron compound phase having a body-centered tetragonal Fe 3 B crystalline structure and a phase of Nd 2 Fe 14 B crystalline structure and said rare earth magnet comprising a crystallite aggregate having an average crystalline particle diameter of 5 nm to 100 nm, said crystallite aggregate having been formed by rapidly solidifying a molten alloy by a melt quenching or gas atomizing method to cause substantially more than 90% of the solidified alloy to be amorphous, and heat-treating the rapidly solidifying alloy by raising its temperature from 500° C. at a heating rate of 1°-15° C./min and maintaining a temperature of from 550° C. to 700° C. for a period of from 5 minutes to 360 minutes, the rare earth magnet of which displays magnetic properties of iHc≧3 kOe, Br≧9 kG and (BH) max≧10 MGOe.
Claim 2
Dependent Claim
213 words
A rare earth magnet having a compositional formula of Fe.sub.100-x-y-z Co.sub.x B.sub.y R.sub.z M.sub.w wherein R is at least one of Pr and Nd, M is one or two of Al, Si, Cu, Ga, Ag, and Au, symbols x, y, z and w each indicating a limit of composition range and respectively falling within the ranges of 0.05≦x≦15 at. %, 16≦y≦22 at. %, 3≦z≦6 at. %, and 0.1≦w≦3 at. %, said rare earth magnet including an iron-rich boron compound phase having a body-centered tetragonal Fe 3 B crystalline structure and a phase of Nd 2 Fe 14 B crystalline structure and said rare earth magnet comprising a crystallite aggregate having an average crystalline particle diameter of 5 nm to 100 nm, said crystallite aggregate having been formed by rapidly solidifying a molten alloy by a melt quenching or gas atomizing method to cause substantially more than 90% of the solidified alloy to be amorphous, and heat-treating the rapidly solidifying alloy by raising its temperature from 500° C. at a heating rate of 1°-15° C./min and maintaining a temperature of from 550° C. to 700° C. for a period of from 5 minutes to 360 minutes, the rare earth magnet of which displays magnetic properties of iHc≧3 kOe, Br≧9 kG and (BH) max≧10 MGOe.
Claim 3
Dependent Claim
17 words
The rare earth magnet according to claim 1, wherein said rare earth magnet is a bonded magnet.
Claim 4
Dependent Claim
237 words
A rare earth bonded magnet comprising a mixture of a rare earth magnet alloy powder and a bonding resin, said rare earth magnet alloy powder having a compositional formula of Fe.sub.100-x-y-z Co.sub.x B.sub.y R.sub.z M.sub.w wherein R is at least one of Pr and Nd, M is one or two of Al, Si, Cu, Ga, Ag, and Au, symbols x, y, z and w each indicating a limit of composition range and falling within the ranges of 0.05≦×≦15 at. %, 16≦y≦22 at. % 3≦z≦6 at. %, and 0.1≦w≦3 at. %, and said rare earth magnet alloy powder including an iron rich boron compound phase having a body-centered tetragonal Fe 3 b crystalline structure and a phase of Nd 2 Fe 14 B crystalline structure and said rare earth powder comprising a crystalline aggregate having an average crystalline particle diameter of 5 nm to 100 nm, said crystallite aggregate having been formed by rapidly solidifying a molten alloy by a melt quenching or gas atomizing method to cause substantially more than 90% of the solidified alloy to be amorphous, and heat-treating the rapidly solidifying alloy by raising its temperature from 500° C. at a heating rate of 1°-15° C./min and maintaining a temperature of from 550° C. to 700° C. for a period of from 5 minutes to 360 minutes, the rare earth magnet of which displays magnetic properties of iHc≧3 kOe, Br≧9 kG and (BH) Max≧10 MGOe.
Claim 5
Dependent Claim
237 words
A rare earth bonded magnet comprising a mixture of a rare earth magnet alloy powder and a bonding resin, said rare earth magnet alloy powder having a compositional formula of Fe.sub.100-x-y-z Co.sub.x B.sub.y R.sub.z M.sub.w wherein R is at least one of Pr and Nd, M is one or two of Al, Si, Cu, Ga, Ag, and Au, symbols x, y, z and w each indicating a limit of composition range and falling within the ranges of 0.05≦×≦15 at. %, 16≦y≦22 at. % 3≦z≦6 at. %, and 0.1≦w≦3 at. %, and said rare earth magnet alloy powder including an iron rich boron compound phase having a body-centered tetragonal Fe 3 b crystalline structure and a phase of Nd 2 Fe 14 B crystalline structure and said rare earth powder comprising a crystalline aggregate having an average crystalline particle diameter of 5 nm to 100 nm, said crystallite aggregate having been formed by rapidly solidifying a molten alloy by a melt quenching or gas atomizing method to cause substantially more than 90% of the solidified alloy to be amorphous, and heat-treating the rapidly solidifying alloy by raising its temperature from 500° C. at a heating rate of 1°-15° C./min and maintaining a temperature of from 550° C. to 700° C. for a period of from 5 minutes to 360 minutes, the rare earth magnet of which displays magnetic properties of iHc≧3 kOe, Br≧9 kG and (BH) Max≧10 MGOe.
Claim 6
Dependent Claim
21 words
The rare earth bonded magnet according to claim 3, wherein the powder has been bonded with the resin by compression molding.
Claim 7
Dependent Claim
22 words
The rare earth bonded magnet according to claim 3 comprising the alloy powder in an amount of 70 to 99.5% by weight.
Claim 8
Dependent Claim
22 words
The rare earth bonded magnet according to claim 3, comprising the alloy powder in an amount of 95 to 99.5% by weight.
Claim 9
Dependent Claim
22 words
The rare earth bonded magnet according to claim 3, comprising the alloy powder in an amount of 90 to 99.5% by weight.
Claim 10
Dependent Claim
22 words
The rare earth bonded magnet according to claim 3, comprising the alloy powder in an amount of 96 to 99.5% by weight.
Claim 11
Dependent Claim
21 words
The rare earth bonded magnet according to claim 3, wherein the powder has been bonded with the resin by injection molding.
Claim 12
Dependent Claim
21 words
The rare earth bonded magnet according to claim 3, wherein the powder has been bonded with the resin by extrusion molding.
Claim 13
Dependent Claim
21 words
The rare earth bonded magnet according to claim 3, wherein the powder has been bonded with the resin by roll molding.
Claim 14
Dependent Claim
21 words
The rare earth bonded magnet according to claim 3, wherein the powder has been bonded with the resin by resin impregnation.
References Cited (Backward Citations)
US4402770A
Cited
JPS59229461A
Cited
JPS60162750A
Cited
US4881989A
Cited
US5250206A
Cited
US5395462A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-08-13 | 2000-02-12 | 2000-08-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-08-13 | 2004-02-12 | 2004-08-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-08-13 | 2008-02-12 | 2008-08-13 | $7700.00 | Window Closed / Lapsed |