Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
135 words
A process for continuously producing a linear lactide copolymer having a weight-average molecular weight of from 20,000 to 400,000 using a continuous reaction apparatus composed of three or more stirred flow reactors connected in series, which process comprises the steps of: continuously feeding from 50 to 98 parts by weight of a lactide and from 2 to 50 parts by weight of a polymer having a hydroxyl group in a molten state or as dissolved in a solvent to the first reactor of said continuous reaction apparatus; and transferring the reaction mixture from said first reactor to the following reactors successively while maintaining the reaction pressure and the reaction temperature in every reactor in the range of from 1 to 5 atm. and of from 140° to 210° C., respectively, to conduct ring opening copolymerization.
Claim 2
Dependent Claim
135 words
A process for continuously producing a linear lactide copolymer having a weight-average molecular weight of from 20,000 to 400,000 using a continuous reaction apparatus composed of three or more stirred flow reactors connected in series, which process comprises the steps of: continuously feeding from 50 to 98 parts by weight of a lactide and from 2 to 50 parts by weight of a polymer having a hydroxyl group in a molten state or as dissolved in a solvent to the first reactor of said continuous reaction apparatus; and transferring the reaction mixture from said first reactor to the following reactors successively while maintaining the reaction pressure and the reaction temperature in every reactor in the range of from 1 to 5 atm. and of from 140° to 210° C., respectively, to conduct ring opening copolymerization.
Claim 3
Dependent Claim
40 words
A process as claimed in claim 1, wherein the rate of polymerization of the lactide in the first reactor is from 30 to 80% and the reaction mixture in that reactor has a viscosity of not higher than 2000 poise.
Claim 4
Dependent Claim
32 words
A process as claimed in claim 1, wherein said polymer having a hydroxyl group is a hydroxyl-terminated polyester having a melting point or a softening point of not higher than 180° C.
Claim 5
Dependent Claim
57 words
A process as claimed in any one of claims 1 to 3, wherein 3 to 30 parts by weight of a solvent having a boiling point of from 70° to 180° C. is used as a reaction solvent per 100 parts by weight of the total amount of the lactide and the polymer having a hydroxyl group.
Claim 6
Dependent Claim
35 words
A process as claimed in any one of claims 1 to 3, wherein a residual lactide and/or a residual solvent in the copolymer obtained after the reaction is/are reduced to 1% by weight or less.
Claim 7
Dependent Claim
83 words
A process as claimed in any one of claims 1 to 3, wherein 3 to 30 parts by weight of a solvent having a boiling point of from 70° to 180° C. is used as a reaction solvent per 100 parts by weight of the total amount of the lactide and the hydroxyl-containing polymer to conduct the ring opening polymerization and, after the reaction, a residual lactide and/or a residual solvent in the copolymer obtained is/are reduced to 1% by weight or less.
Claim 8
Dependent Claim
37 words
A process as claimed in any one of claims 1 to 3, wherein the reaction mixture from the last stirred flow reactor is subjected to further ring opening copolymerization in a reactor equipped with a static mixer.
Claim 9
Dependent Claim
102 words
A process as claimed in any one of claims 1 to 3, wherein from 3 to 30 parts by weight of a solvent having a boiling point of from 70° to 180° C. is used as a reaction solvent per 100 parts by weight of the total amount of the lactide and the hydroxyl-containing polymer to conduct the ring opening copolymerization, the reaction mixture is subjected to further ring opening copolymerization in a reactor equipped with a static mixer, and, after the reaction, a residual lactide and/or a residual solvent in the copolymer obtained is/are reduced to 1% by weight or less.