Method of making reliable metal leads in high speed LSI semiconductors using thermoconductive layers
Assignee: Texas Instruments Inc
•
Filing: 1994-05-31
•
Granted: 1996-04-23
•
Expires: 2014-05-31
Abstract
Abstract A method for manufacturing semiconductor device having metal leads 14 with improved reliability, and device for same, including metal leads 14 on a substrate 12, a low-dielectric constant material 18 at least between the metal leads 14, and thermoconductive insulating layer 22 deposited on the metal leads 14 and the low-dielectric constant material 18. Heat from the metal leads 14 is transferable to the thermoconductive insulating layer 22, and the thermoconductive insulating layer 22 is capable of dissipating the heat. The low-dielectric constant material 18 has a dielectric constant of less than 3.5. An advantage of the invention is to improve reliability of metal leads for circuits using low-dielectric constant materials.
Inventors
- 👤 Ken Numata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 20:43
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/6336; H10P14/6342; H10P14/65; H10P14/6502; H10P14/6506; H10P14/6516; H10P14/6548; H10P14/66; H10P14/665; H10P14/6924; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/074; H10W20/077; H10W20/40; H10W20/45; H10W20/48; H10W20/495
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
123 words
A method of fabricating metal leads in a semiconductor device, said metal each being resistant to damage due to Joule's heat, said method comprising the steps of: forming at least two metal leads on a substrate, said metal leads having a height-to-width aspect ratio greater than 2; depositing a low-dielectric constant material at least between said metal leads, said low-dielectric constant material having a dielectric constant of less than 3.5; and depositing a thermoconductive insulating layer on at least the tops of said metal leads, said thermoconductive insulating layer comprising at least one of AlN and Si 3 N 4 ; wherein current passing through said metal leads produces said Joule's heat which is transferable to said thermoconductive insulating layer and is dissipatable.
Claim 2
Independent Claim
123 words
A method of fabricating metal leads in a semiconductor device, said metal each being resistant to damage due to Joule's heat, said method comprising the steps of: forming at least two metal leads on a substrate, said metal leads having a height-to-width aspect ratio greater than 2; depositing a low-dielectric constant material at least between said metal leads, said low-dielectric constant material having a dielectric constant of less than 3.5; and depositing a thermoconductive insulating layer on at least the tops of said metal leads, said thermoconductive insulating layer comprising at least one of AlN and Si 3 N 4 ; wherein current passing through said metal leads produces said Joule's heat which is transferable to said thermoconductive insulating layer and is dissipatable.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein said thermoconductive insulating layer comprises AlN.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein the spacing between said metal leads is less than one μm.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein said thermoconductive insulating layer has a thermal conductivity greater than thermal conductivity of said low-dielectric constant material.
Claim 6
Dependent Claim
44 words
The method of claim 1 further comprising the step of depositing a thermoconductive layer on at least said metal leads, after said forming step, wherein said heat from said metal leads is transferred to said thermoconductive layer and then to said thermoconductive insulating layer.
Claim 7
Dependent Claim
47 words
The method of claim 5 further comprising the step of etching said low-dielectric constant material to expose said thermoconductive layer on said metal leads, after said depositing a low-dielectric constant material, and wherein said depositing a low-dielectric constant material is performed over at least said metal leads.
Claim 8
Dependent Claim
19 words
The method of claim 6 wherein a top portion of said thermoconductive layer is removed during said etching step.
Claim 9
Dependent Claim
17 words
The method of claim 6 wherein the spacing between said metal leads is less than one μm.
Claim 10
Independent Claim
134 words
A method of fabricating metal leads in a semiconductor device, said metal leads being resistant to damage due to Joule's heat, said method comprising the steps of: forming at least two metal leads on a substrate, said metal leads having a height-to-width aspect ratio greater than 2; depositing a first thermoconductive layer on at least said metal leads; depositing a low-dielectric constant material on said first thermoconductive layer at least between said metal leads said low-dielectric constant material having a dielectric constant of less than 3.5; and depositing a thermoconductive insulating layer on at least the tops of said metal leads, said thermoconductive insulating layer comprising AlN; wherein current passing through said metal leads produces said Joule's heat which is transferable to said first thermoconductive layer and said thermoconductive insulating layer and is dissipatable.
Claim 11
Independent Claim
134 words
A method of fabricating metal leads in a semiconductor device, said metal leads being resistant to damage due to Joule's heat, said method comprising the steps of: forming at least two metal leads on a substrate, said metal leads having a height-to-width aspect ratio greater than 2; depositing a first thermoconductive layer on at least said metal leads; depositing a low-dielectric constant material on said first thermoconductive layer at least between said metal leads said low-dielectric constant material having a dielectric constant of less than 3.5; and depositing a thermoconductive insulating layer on at least the tops of said metal leads, said thermoconductive insulating layer comprising AlN; wherein current passing through said metal leads produces said Joule's heat which is transferable to said first thermoconductive layer and said thermoconductive insulating layer and is dissipatable.
Claim 12
Dependent Claim
17 words
The method of claim 9 wherein the spacing between said metal leads is less than one μm.
Claim 13
Dependent Claim
22 words
The method of claim 9 wherein said thermoconductive insulating layer has a conductivity greater than the conductivity of said low-dielectric constant material.
Claim 14
Dependent Claim
32 words
The method of claim 9 further comprising the step of etching said low-dielectric constant material to expose said first thermoconductive layer on said metal leads, after said depositing a low-dielectric constant material.
Claim 15
Dependent Claim
20 words
The method of claim 12 wherein a top portion of said first thermoconductive layer is removed during said etching step.
Claim 16
Dependent Claim
17 words
The method of claim 12 wherein the spacing between said metal leads is less than one μm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-04-23 | 1999-10-23 | 2000-04-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-04-23 | 2003-10-23 | 2004-04-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-04-23 | 2007-10-23 | 2008-04-23 | $7700.00 | Window Closed / Lapsed |