Method of constructing fully dense metal molds and parts
Assignee: Milwaukee School of Engineering
•
Filing: 1995-01-17
•
Granted: 1996-04-16
•
Expires: 2015-01-17
Abstract
Abstract A method of constructing a fully dense metal part or a metal mold half for mating with another mold half to form a mold for casting multiple parts. Steps include placing a pattern in a tubular mold base, casting a ceramic member onto critical surfaces of the pattern, removing the pattern from the mold base, covering the critical surfaces transferred to the ceramic member with a powdered metal having a melting temperature greater than that of an infiltration metal, placing a quantity of an infiltration metal over the powdered metal, placing the tubular mold base in a furnace at a temperature sufficient to melt the infiltration metal without melting the powdered metal, and removing the ceramic member from the first open end of the tubular mold base to expose the critical surfaces. The quantity of the infiltration metal is sufficient to fill voids between the particles of the powdered metal when the infiltration metal is melted, thereby generating a fully dense metal part. The metal part has the critical surfaces transferred from the ceramic member when the infiltration metal solidifies. The metal powder also acts as a filter to filter out any contamination or oxidized metal within the infiltration metal so that such contamination does not blemish the finished surface of the fully dense metal part.
Inventors
- 👤 James R. Tobin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 21:07
CPC Classifications
B; B22; B22F; B22F5/00; B22F5/007; B22C; B22C9/00; B22C9/02; B22C9/04; B22D; B22D19/00; B22D19/14; B22F2998/00; B33; B33Y; B33Y80/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
253 words
A method of constructing a fully dense mold half comprising the steps of: a) placing a pattern in a tube, said tube having a melting temperature greater than that of an infiltration metal, a first open end, and a second open end, said pattern having critical pattern surfaces facing said first open end; b) casting a ceramic member between said critical pattern surfaces and said first open end of said tube to transfer critical pattern surfaces to said ceramic member, creating critical ceramic surfaces having a shape inverse to said critical pattern surfaces; c) removing said pattern from said second open end of said tube, to expose said critical ceramic surfaces inside said tube; d) covering said critical ceramic surfaces with a powder, said powder comprising particles having a melting temperature greater than that of an infiltration metal; e) placing a quantity of an infiltration metal over said powder, and placing said tube, having said second open end upright, in a furnace at a temperature sufficient to melt said infiltration metal without melting said powder and said tube, said quantity of said infiltration metal being sufficient to fill voids between said particles, thereby generating a fully dense metal mold half, said metal mold half having critical mold surfaces transferred from said ceramic member when said infiltration metal solidifies, said critical mold surfaces having a shape inverse to said critical ceramic surfaces; and f) removing said ceramic member from said first end of said tube, to expose said critical mold surfaces for molding purposes.
Claim 2
Independent Claim
253 words
A method of constructing a fully dense mold half comprising the steps of: a) placing a pattern in a tube, said tube having a melting temperature greater than that of an infiltration metal, a first open end, and a second open end, said pattern having critical pattern surfaces facing said first open end; b) casting a ceramic member between said critical pattern surfaces and said first open end of said tube to transfer critical pattern surfaces to said ceramic member, creating critical ceramic surfaces having a shape inverse to said critical pattern surfaces; c) removing said pattern from said second open end of said tube, to expose said critical ceramic surfaces inside said tube; d) covering said critical ceramic surfaces with a powder, said powder comprising particles having a melting temperature greater than that of an infiltration metal; e) placing a quantity of an infiltration metal over said powder, and placing said tube, having said second open end upright, in a furnace at a temperature sufficient to melt said infiltration metal without melting said powder and said tube, said quantity of said infiltration metal being sufficient to fill voids between said particles, thereby generating a fully dense metal mold half, said metal mold half having critical mold surfaces transferred from said ceramic member when said infiltration metal solidifies, said critical mold surfaces having a shape inverse to said critical ceramic surfaces; and f) removing said ceramic member from said first end of said tube, to expose said critical mold surfaces for molding purposes.
Claim 3
Dependent Claim
27 words
The method of claim 1 wherein said step of removing said pattern comprises burning out said pattern at a temperature below said melting temperature of said tube.
Claim 4
Dependent Claim
60 words
The method of claim 1 further comprising the steps of: g) machining said tube so that a mating mold half may be aligned with said metal mold half in order to east a part; and h) machining a sprue hole through said metal mold half in order to introduce castable material to said critical mold surfaces for casting said part.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein said powder is selected from the group consisting of steel, stainless steel, tungsten, and tungsten carbide.
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein said infiltration metal is selected from the group consisting of copper, copper alloy, and beryllium copper.
Claim 7
Dependent Claim
36 words
The method of claim 1 wherein an insulating material is placed over said quantity of said infiltration metal when said infiltration metal is melted so that said infiltration metal solidifies first at said critical ceramic surfaces.
Claim 8
Dependent Claim
61 words
The method of claim 1 further comprising the step of inserting steel inserts into said powder before melting said quantity of an infiltration metal, said inserts having a melting temperature above that of said furnace temperature, said quantity of an infiltration metal fixedly positioning said inserts when said infiltration metal solidifies in said voids between said particles and around said inserts.
Claim 9
Independent Claim
317 words
A method of constructing a fully dense mold half comprising the steps of: a) placing an epoxy pattern in a tube, said tube having a melting temperature greater than that of an infiltration metal, a first open end, and a second open end, said pattern having critical pattern surfaces facing said first open end; b) casting a ceramic member between said critical pattern surfaces of said pattern and said first open end of said tube to transfer critical pattern surfaces to said ceramic member, creating critical ceramic surfaces having a shape inverse to said critical pattern surfaces; c) burning out said epoxy pattern from said second open end of said tube, thereby exposing said critical ceramic surfaces inside said tube; d) covering said critical ceramic surfaces with a powder, said powder comprising particles having a melting temperature greater than that of an infiltration metal; e) placing a quantity of an infiltration metal over said powder, and placing an insulating material over said quantity of an infiltration metal; f) placing said tube, having said second open end upright, in a hydrogen furnace at about 2100° F., said quantity of an infiltration metal being sufficient to fill voids between said particles of said powder when melted, thereby generating a fully dense metal mold half, said metal mold half having critical mold surfaces transferred from said ceramic member when said quantity of an infiltration metal solidifies, said critical mold surfaces having a shape inverse to said critical ceramic surfaces; g) removing said ceramic member from said first end of said tube, to expose said critical mold surfaces for molding purposes; h) machining said tube so that a mating mold half may be aligned with said metal mold half in order to cast a part; and i) machining a sprue hole through said metal mold half in order to introduce castable material to said critical mold surfaces for casting said part.
Claim 10
Independent Claim
317 words
A method of constructing a fully dense mold half comprising the steps of: a) placing an epoxy pattern in a tube, said tube having a melting temperature greater than that of an infiltration metal, a first open end, and a second open end, said pattern having critical pattern surfaces facing said first open end; b) casting a ceramic member between said critical pattern surfaces of said pattern and said first open end of said tube to transfer critical pattern surfaces to said ceramic member, creating critical ceramic surfaces having a shape inverse to said critical pattern surfaces; c) burning out said epoxy pattern from said second open end of said tube, thereby exposing said critical ceramic surfaces inside said tube; d) covering said critical ceramic surfaces with a powder, said powder comprising particles having a melting temperature greater than that of an infiltration metal; e) placing a quantity of an infiltration metal over said powder, and placing an insulating material over said quantity of an infiltration metal; f) placing said tube, having said second open end upright, in a hydrogen furnace at about 2100° F., said quantity of an infiltration metal being sufficient to fill voids between said particles of said powder when melted, thereby generating a fully dense metal mold half, said metal mold half having critical mold surfaces transferred from said ceramic member when said quantity of an infiltration metal solidifies, said critical mold surfaces having a shape inverse to said critical ceramic surfaces; g) removing said ceramic member from said first end of said tube, to expose said critical mold surfaces for molding purposes; h) machining said tube so that a mating mold half may be aligned with said metal mold half in order to cast a part; and i) machining a sprue hole through said metal mold half in order to introduce castable material to said critical mold surfaces for casting said part.
Claim 11
Dependent Claim
22 words
The method of claim 8 wherein said powder is selected from the group consisting of steel, stainless steel, tungsten, and tungsten carbide.
Claim 12
Dependent Claim
22 words
The method of claim 8 wherein said infiltration metal is selected from the group consisting of copper, copper alloy, and beryllium copper.
Claim 13
Dependent Claim
61 words
The method of claim 8 further comprising the step of inserting steel inserts into said powder before melting said quantity of an infiltration metal, said inserts having a melting temperature above that of said furnace temperature, said quantity of an infiltration metal fixedly positioning said inserts when said infiltration metal solidifies in said voids between said particles and around said inserts.
References Cited (Backward Citations)
US918069A
Cited
US3915699A
Cited
US3751271A
Cited
US3829295A
Cited
US3823002A
Cited
US3929476A
Cited
US3894575A
Cited
US4048709A
Cited
US4327156A
Cited
US5249620A
Cited
JPH02303672A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-04-16 | 1999-10-16 | 2000-04-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-04-16 | 2003-10-16 | 2004-04-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-04-16 | 2007-10-16 | 2008-04-16 | $7700.00 | Window Closed / Lapsed |