Method for forming porous composites as a low dielectric constant layer with varying porosity distribution electronics applications
Assignee: Texas Instruments Inc
•
Filing: 1994-06-07
•
Granted: 1996-02-27
•
Expires: 2014-06-07
Abstract
Abstract This invention provides a process for making a semiconductor device with reduced capacitance between adjacent conductors. This process can include applying and gelling one or more solutions between and over conductors 24 and drying the wet gel to create at least porous dielectric sublayers 28 and 29. By varying the composition of the solutions, gelling conditions, drying temperature, composition of the solvents in the wet gel, or a combination of these approaches, the porosity of the sublayers may be tailored individually. A non-porous dielectric layer 30 may be formed over porous layer 28, which may complete an interlayer dielectric. A novel process for creating the porous dielectric layer is disclosed, which can be completed at vacuum or ambient pressures, yet results in porosity, pore size, and shrinkage of the dielectric during drying comparable to that previously attainable only by drying gels at supercritical pressure.
Inventors
- 👤 Bruce E. Gnade
- 👤 Chih-Chen Cho
- 👤 Douglas M. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 21:15
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/65; H10P14/6516; H10P14/6529; H10P14/6534; H10P14/6546; H10P14/6548; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/072; H10W20/40; H10W20/45; H10W20/46; H10W20/48; H10W20/495; H10P14/63; H10P14/6326; H10P14/6342; H10P14/66; H10P14/665; H10P14/668; H10P14/6681; H10P14/6684; H10P14/6686; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
128 words
A method of forming a porous dielectric on a semiconductor device comprising: (a) providing a patterned layer formed on a substrate; (b) providing a solution capable of forming a wet gel; (c) coating said substrate with said solution; (d) gelling said solution to form a wet gel on said substrate, said wet gel containing pores arranged in an open-pored structure; and (e) drying said wet gel in a controlled manner which produces a porous dielectric layer with at least two vertically separated regions of porosity, pairs of said regions which share a common transition region differing in porosity by at least 20%, said porous dielectric having average pore diameters of less than 80 nm, whereby the incorporation of extremely porous sublayers into said porous dielectric layer is facilitated.
Claim 2
Independent Claim
128 words
A method of forming a porous dielectric on a semiconductor device comprising: (a) providing a patterned layer formed on a substrate; (b) providing a solution capable of forming a wet gel; (c) coating said substrate with said solution; (d) gelling said solution to form a wet gel on said substrate, said wet gel containing pores arranged in an open-pored structure; and (e) drying said wet gel in a controlled manner which produces a porous dielectric layer with at least two vertically separated regions of porosity, pairs of said regions which share a common transition region differing in porosity by at least 20%, said porous dielectric having average pore diameters of less than 80 nm, whereby the incorporation of extremely porous sublayers into said porous dielectric layer is facilitated.
Claim 3
Dependent Claim
79 words
The method of claim 1, wherein said drying in a controlled manner step comprises: (a) adjusting the pore fluid contained in said wet gel to a desired mixture of at least two solvents, said solvents differing in volatility; and (b) controlling evaporation of said solvents such that the ratio of the solvents present in said wet gel changes during said drying step, whereby an effective variation in porosity is achieved in substantially the vertical cross-section of said porous dielectric.
Claim 4
Dependent Claim
52 words
The method of claim 1, wherein said drying in a controlled manner step comprises varying the temperature of the pore fluid contained in said wet gel to alter the surface tension of said pore fluid, whereby an effective variation in porosity is achieved in substantially the vertical cross-section of said porous dielectric.
Claim 5
Dependent Claim
39 words
The method of claim 1, further comprising after gelling step, replacing at least 30% of reactive groups on the surface of said pores with substantially stable surface groups, whereby shrinkage of said gel during said drying step is controlled.
Claim 6
Dependent Claim
36 words
The method of claim 1, wherein said patterned layer comprises conductors constructed from materials selected from the group consisting of: aluminum, copper, titanium, platinum, gold, tungsten, polysilicon, tantalum, nickel, TiN, TiSi 2 , and combinations thereof.
Claim 7
Dependent Claim
16 words
The method of claim 5, wherein said patterned layer further comprises at least one dielectric sublayer.
Claim 8
Independent Claim
161 words
A method of forming a porous dielectric on a semiconductor device comprising: (a) providing a patterned layer formed on a substrate; (b) providing first and second solutions capable of forming a wet gel; (c) coating said substrate with said first solution; (d) gelling said first solution to form a first wet gel on said substrate, said first wet gel containing pores arranged in an open-pored structure and a first porosity; (e) coating said substrate with said second solution; (f) gelling said second solution to form a second wet gel contacting said first wet gel, said second wet gel containing pores arranged in an open-pored structure and a second porosity, said first and second porosities differing by at least 20%; and (g) drying said first and second wet gels to produce a porous dielectric layer, said porous dielectric having average pore diameters of less than 80 nm, whereby the incorporation of extremely porous layered regions into said porous dielectric layer is facilitated.
Claim 9
Independent Claim
161 words
A method of forming a porous dielectric on a semiconductor device comprising: (a) providing a patterned layer formed on a substrate; (b) providing first and second solutions capable of forming a wet gel; (c) coating said substrate with said first solution; (d) gelling said first solution to form a first wet gel on said substrate, said first wet gel containing pores arranged in an open-pored structure and a first porosity; (e) coating said substrate with said second solution; (f) gelling said second solution to form a second wet gel contacting said first wet gel, said second wet gel containing pores arranged in an open-pored structure and a second porosity, said first and second porosities differing by at least 20%; and (g) drying said first and second wet gels to produce a porous dielectric layer, said porous dielectric having average pore diameters of less than 80 nm, whereby the incorporation of extremely porous layered regions into said porous dielectric layer is facilitated.
Claim 10
Dependent Claim
43 words
The method of claim 7, further comprising replacing at least 30% of reactive groups on the surface of said pores of said first wet gel with substantially stable surface groups, whereby shrinkage of said first wet gel during said drying step is controlled.
Claim 11
Dependent Claim
43 words
The method of claim 7, further comprising replacing at least 30% of reactive groups on the surface of said pores of said second wet gel with substantially stable surface groups, whereby shrinkage of said second wet gel during said drying step is controlled.
Claim 12
Dependent Claim
43 words
The method of claim 7, wherein said first wet gel forms a first porous dielectric sublayer with a porosity greater than 50%, and said second wet gel forms a second porous dielectric sublayer with a porosity in the range of 15% to 50%.
Claim 13
Dependent Claim
86 words
The method of claim 7, further comprising: (a) providing a third solution capable of forming a wet gel; (b) after said gelling said second solution step, coating said substrate with said third solution and gelling said third solution to form a third wet gel contacting said second wet gel, said third wet gel containing pores arranged in an open-pored structure and a third porosity, said second and third porosities differing by at least 20%; and (c) during said drying step, also drying said third wet gel.
Claim 14
Dependent Claim
45 words
The method of claim 11, wherein said first and third wet gels form first and third porous dielectric sublayers with porosities in the range of 15% to 50%, and said second wet gel forms a second porous dielectric sublayer with a porosity greater than 50%.
References Cited (Backward Citations)
US4652467A
Cited
US5103288A
Cited
JPH0259452A
Cited
US4987101A
Cited
JPH03109236A
Cited
US5155576A
Cited
JPH05339020A
Cited
US5393712A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-02-26 | 1999-08-28 | 2000-02-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-02-26 | 2003-08-28 | 2004-02-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-02-26 | 2007-08-28 | 2008-02-27 | $7700.00 | Window Closed / Lapsed |