Method of making high density ROM, without using a code implant
Assignee: United Microelectronics Corp
•
Filing: 1995-01-19
•
Granted: 1996-01-02
•
Expires: 2015-01-19
Abstract
Abstract A method of fabricating read only memory, (ROM), devices has been developed. This process is accomplished using self-alignment of buried N+ bit lines. Thick field oxides are used for isolation purposes. The programmable cell is obtained by growing a gate oxide in a region in which the thick field oxide has been removed. The non-programmable cells contain thick gate oxides. Polysilicon gate structures are processed to function as the word lines.
Inventors
- 👤 Chen-Chung Hsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:34
CPC Classifications
H; H10; H10B; H10B20/00; H10B20/27; H10B20/30; H10B20/36; H10B20/367
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
150 words
A method of fabricating a read only memory, (ROM), cell on a semiconductor substrate comprising the steps of: forming a field oxide pattern on specific regions of said substrate, while leaving exposed silicon on remaining regions of said substrate; ion implanting first conductivity imparting dopants into said exposed silicon regions; growing an oxide on said exposed, ion implanted silicon regions; photolithography to expose a specific field oxide region; removal of oxide from said specific field oxide region, to leave bare silicon; growing a gate oxide on said bare silicon; depositing a polysilicon layer on said gate oxide, on said field oxide regions, and on said oxide, grown on said exposed, ion implanted silicon; ion implanting a first conductivity imparting dopant into said polysilicon layer; and patterning to form polysilicon gate structures on said gate oxide, on said field oxide, and on said oxide, grown from said exposed, ion implanted silicon.
Claim 2
Independent Claim
150 words
A method of fabricating a read only memory, (ROM), cell on a semiconductor substrate comprising the steps of: forming a field oxide pattern on specific regions of said substrate, while leaving exposed silicon on remaining regions of said substrate; ion implanting first conductivity imparting dopants into said exposed silicon regions; growing an oxide on said exposed, ion implanted silicon regions; photolithography to expose a specific field oxide region; removal of oxide from said specific field oxide region, to leave bare silicon; growing a gate oxide on said bare silicon; depositing a polysilicon layer on said gate oxide, on said field oxide regions, and on said oxide, grown on said exposed, ion implanted silicon; ion implanting a first conductivity imparting dopant into said polysilicon layer; and patterning to form polysilicon gate structures on said gate oxide, on said field oxide, and on said oxide, grown from said exposed, ion implanted silicon.
Claim 3
Dependent Claim
30 words
The method of claim 1, wherein said field oxide is grown at a temperature between about 800° to 950° C., to a thickness of between about 4000 to 6000 Angstroms.
Claim 4
Dependent Claim
26 words
The method of claim 1, wherein said first conductivity imparting dopants are ion implanted into said exposed silicon regions, self aligned to said field oxide regions.
Claim 5
Dependent Claim
55 words
The method of claim 1, wherein said first conductivity imparting dopants are arsenic, ion implanted at an energy between about 50 to 100 Kev., at a dose between about 1E14 to 1E16 atoms/cm2, and phosphorous, ion implanted at an energy between about 20 to 60 Kev., at a dose between about 1E14 to 1E16 atoms/cm2.
Claim 6
Dependent Claim
36 words
The method of claim 1, wherein said oxide, is grown on said exposed, ion implanted silicon regions, at a temperature of between about 900° to 1000° C., to a thickness between about 500 to 1000 Angstroms.
Claim 7
Dependent Claim
17 words
The method of claim 1, wherein said specific field oxide region is removed using buffered hydrofluoric acid.
Claim 8
Dependent Claim
40 words
The method of claim 1, wherein said gate oxide is grown in the area where said specific field oxide region was removed, at a temperature between about 800° to 1000° C., to a thickness of between 100 to 300 Angstroms.
Claim 9
Dependent Claim
20 words
The method of claim 1, wherein said polysilicon layer is deposited to a thickness between about 1000 to 3000 Angstroms.
Claim 10
Dependent Claim
33 words
The method of claim 1, wherein said first conductivity imparting dopant is phosphorous, ion implanted at an energy between about 30 to 80 Kev., at a dose between about 1E14 to 1E16 atoms/cm2.
Claim 11
Dependent Claim
36 words
The method of claim 1, wherein said polysilicon gate structures are formed, by anisotropic reactive ion etching, on said gate oxide, on said field oxide, and on said oxide grown from said exposed, ion implanted silicon.
Claim 12
Independent Claim
159 words
A method of fabricating a read only memory, (ROM), cell on a semiconductor substrate comprising the steps of: forming a field oxide pattern on specific regions of said substrate, while leaving exposed silicon on remaining regions of said substrate; ion implanting first conductivity imparting dopants into said exposed silicon regions to form buried bit lines of the ROM cell; growing an oxide on said buried bit line regions; photolithography to expose a specific field oxide region; removal of oxide from said specific field oxide region, to leave bare silicon; growing a gate oxide on said bare silicon; depositing a polysilicon layer on said gate oxide, on said field oxide regions, and on said oxide over said buried bit line regions; ion implanting a first conductivity imparting dopant into said polysilicon layer; and patterning said polysilicon layer to form word lines, on said gate oxide, on said field oxide regions, and on said oxide over said buried bit line regions.
Claim 13
Independent Claim
159 words
A method of fabricating a read only memory, (ROM), cell on a semiconductor substrate comprising the steps of: forming a field oxide pattern on specific regions of said substrate, while leaving exposed silicon on remaining regions of said substrate; ion implanting first conductivity imparting dopants into said exposed silicon regions to form buried bit lines of the ROM cell; growing an oxide on said buried bit line regions; photolithography to expose a specific field oxide region; removal of oxide from said specific field oxide region, to leave bare silicon; growing a gate oxide on said bare silicon; depositing a polysilicon layer on said gate oxide, on said field oxide regions, and on said oxide over said buried bit line regions; ion implanting a first conductivity imparting dopant into said polysilicon layer; and patterning said polysilicon layer to form word lines, on said gate oxide, on said field oxide regions, and on said oxide over said buried bit line regions.
Claim 14
Dependent Claim
29 words
The method of claim 11, wherein said field oxide is grown at a temperature between about 850° to 950° C., to a thickness between about 4000 to 6000 Angstroms.
Claim 15
Dependent Claim
32 words
The method of claim 11, wherein said buried bit line regions are self aligned to said field oxide regions, by ion implanting said first conductivity imparting dopants into said exposed silicon region.
Claim 16
Dependent Claim
55 words
The method of claim 11, wherein said first conductivity imparting dopants are arsenic, ion implanted at an energy between about 50 to 100 Kev., at a dose between about 1E14 to 1E16 atoms/cm2, and phosphorous, ion implanted at an energy between about 20 to 60 Kev., at a dose between about 1E14 to 1E16 atoms/cm2.
Claim 17
Dependent Claim
35 words
The method of claim 11, wherein an oxide is grown on said buried bit line regions, at a temperature between about 900° to 1000° C., to a thickness of between about 500 to 1000 Angstroms.
Claim 18
Dependent Claim
17 words
The method of claim 11, wherein said specific field oxide region is removed using buffered hydrofluoric acid.
Claim 19
Dependent Claim
40 words
The method of claim 11, wherein said gate oxide is grown, in the area where said specific field oxide region was removed, at a temperature between about 800° to 1000° C., to a thickness between about 100 to 300 Angstroms.
Claim 20
Dependent Claim
20 words
The method of claim 11, wherein said polysilicon layer is deposited to a thickness between about 1000 to 3000 Angstroms.
Claim 21
Dependent Claim
33 words
The method of claim 11, wherein said first conductivity imparting dopant is phosphorous, ion implanted at an energy between about 30 to 80 Kev., at a dose between about 1E14 to 1E16 atoms/cm2.
Claim 22
Dependent Claim
20 words
The method of claim 11, wherein said word lines are formed by anisotropic reactive ion etching of said polysilicon layer.
References Cited (Backward Citations)
US4648937A
Cited
US5108937A
Cited
US5342796A
Cited
US5236853A
Cited
US5306657A
Cited
US5308777A
Cited
US5393704A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-01-01 | 1999-07-03 | 2000-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-01-01 | 2003-07-03 | 2004-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-01-01 | 2007-07-03 | 2008-01-02 | $7700.00 | Window Closed / Lapsed |