Dual phase and hybrid phase shifting mask fabrication using a surface etch monitoring technique
Assignee: International Business Machines Corp
•
Filing: 1994-04-28
•
Granted: 1995-11-14
•
Expires: 2014-04-28
Abstract
Abstract A subtractive method for making a Levenson type lithographic phase shift mask using a sacrificial etch monitor film in which some of the monitor film is left standing on the opaque portions of the mask. The monitor film otherwise is consumed when it is simultaneously etched with selected portions of the mask substrate to produce recesses of desired depth in the substrate. The etching is stopped upon detecting that the etched monitor film is completely consumed. The technique also is adapted for the fabrication of a RIM type lithographic phase shift mask combined with the Levenson type phase shift mask in the same mask. The technique further is adapted to include 90 degree shift transitions at the end of the Levenson line-space pairs of the mask. The monitor film left standing on the opaque portions of the mask provides self-aligned phase error correction to offset sidewall scattering in the Levenson type mask.
Inventors
- 👤 Jonathan D. Chapple-Sokol
- 👤 Louis L.-C. Hsu
- 👤 Paul J.-M. Tsang
- 👤 Chi-Min Yuan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 22:28
CPC Classifications
G; G03; G03F; G03F1/00; G03F1/26; G03F1/30; G03F1/28
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
94 words
A method for making a lithographic phase shift mask comprising providing a substrate, placing opaque material in a pattern over said substrate, mounting a sacrificial etch monitor first film solely on said opaque material, masking selected portions of said first film, in a first etching step, simultaneously etching said first film where unmasked and the exposed portions of said substrate until said unmasked first film is entirely removed, comprising, detecting when said unmasked film is entirely removed and, stopping said etching thereupon, said masked film remaining on said material when said etching is stopped.
Claim 2
Independent Claim
94 words
A method for making a lithographic phase shift mask comprising providing a substrate, placing opaque material in a pattern over said substrate, mounting a sacrificial etch monitor first film solely on said opaque material, masking selected portions of said first film, in a first etching step, simultaneously etching said first film where unmasked and the exposed portions of said substrate until said unmasked first film is entirely removed, comprising, detecting when said unmasked film is entirely removed and, stopping said etching thereupon, said masked film remaining on said material when said etching is stopped.
Claim 3
Dependent Claim
47 words
The method defined in claim 1 and further including placing a second film on and between said first film of a successive pair of said patterned opaque material, and directionally etching said second film to produce sidewalls on said successive pair prior to said simultaneously etching step.
Claim 4
Dependent Claim
18 words
The method defined in claim 2 and further including removing said sidewalls subsequent to said simultaneously etching step.
Claim 5
Dependent Claim
42 words
The method defined in claim 1 and further comprising removing said masking of said selected portions of said first film, and in a second etching step, simultaneously etching said selected portions of said first film and the exposed portions of said substrate.
Claim 6
Dependent Claim
55 words
The method defined in claim 4 and further including placing a third film between said substrate and said material, selectively removing first portions of said third film prior to said first etching step, and selectively removing second portions of said third film subsequent to said first etching step but prior to said second etching step.
Claim 7
Dependent Claim
48 words
The method defined in claim 4 and further including placing a third film between said substrate and said material, selectively removing first portions of said third film prior to said first etching step, and selectively removing second portions of said third film subsequent to said second etching step.
Claim 8
Dependent Claim
47 words
The method in claim 4 wherein the thickness of said first film is selected such that when it is simultaneously etched with said substrate, the substrate will be etched to a depth equal to π/2 phase shift at the moment that said first film is completely removed.
Claim 9
Dependent Claim
47 words
The method in claim 1 wherein the thickness of said first film is selected such that when it is simultaneously etched with said substrate, the substrate will be etched to a depth equal to π phase shift at the moment that said first film is completely removed.
Claim 10
Dependent Claim
24 words
The method in claim 1 wherein said detecting step comprises using laser interferometer end point detection on a dedicated portion of said first film.
Claim 11
Dependent Claim
38 words
The method defined in claim 1 wherein said masked film remaining on said material when said etching is stopped is located adjacent sidewalls of the phase shift mask openings whereby phase error caused by sidewall scattering is corrected.
References Cited (Backward Citations)
US4496425A
Cited
US4722878A
Cited
US4780382A
Cited
US4902899A
Cited
US5030316A
Cited
US4937129A
Cited
US4927485A
Cited
US5200796A
Cited
US5024726A
Cited
US5170217A
Cited
US5100503A
Cited
US5225035A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-11-13 | 1999-05-15 | 1999-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-11-13 | 2003-05-15 | 2003-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-11-13 | 2007-05-15 | 2007-11-14 | $7700.00 | Window Closed / Lapsed |