Laser machining of ceramic cores
Assignee: Honeywell International Inc
•
Filing: 1993-11-23
•
Granted: 1995-11-14
•
Expires: 2013-11-23
Abstract
Abstract A method is disclosed for producing a hollow airfoil, specifically, a blade or vane for a gas turbine engine, which is formed with a complex interior for cooling purposes. Broadly, the method comprises the steps of molding a green ceramic core having outer surfaces generally contoured to produce the intended interior surfaces of the completed airfoil, heating the green ceramic core to a sufficient extent to produce a fired core, and operating on the fired core with a laser to modify the characteristics of the fired core. Use of the laser enables the formation of detailed features having a transverse dimension less than approximately 0.020 inches. Specific operations may include labeling, trimming, cutting, drilling either by punching or trepanning, etching or milling, and glazing or strengthening. In another embodiment of the invention, a layer is produced on the core surface having a very high surface energy to promote the flow of the casting alloy around the core within the mold.
Inventors
- 👤 Michael S. Muntner
- 👤 James S. Perron
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 05:32
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/80; B; B22; B22C; B22C9/00; B22C9/02; B22C9/04; B22C9/10; B22C9/18; B23; B23K; B23K26/00; B23K26/0006; B23K26/36; B23K26/361; B23K26/40; B28; B28B; B28B11/00; B28B11/04; B28B11/08; B28B11/12; C04B41/0036; C04B41/009; B23K2103/00; B23K2103/50; B23K2103/52; C04B2111/00; C04B2111/00474; C04B2111/00939
Claims Analysis
Total Claims: 64
Claim 1
Independent Claim
69 words
A method of producing a core for making a hollow blade comprising the steps of: (a) molding a green ceramic core having outer surfaces generally contoured to produce the intended interior surfaces of the completed blade; (b) heating the green ceramic core to a sufficient extent to produce a fired core; and (c) operating on the fired core with a laser to modify the characteristics of the fired core.
Claim 2
Independent Claim
69 words
A method of producing a core for making a hollow blade comprising the steps of: (a) molding a green ceramic core having outer surfaces generally contoured to produce the intended interior surfaces of the completed blade; (b) heating the green ceramic core to a sufficient extent to produce a fired core; and (c) operating on the fired core with a laser to modify the characteristics of the fired core.
Claim 3
Dependent Claim
42 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (c) includes the step of: (d) applying the laser in such a manner that the outer surface of the fired core is smoothened.
Claim 4
Dependent Claim
48 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (c) includes the step of: (d) applying the laser to the surface of the fired core in such a manner that the outer surface of the core is strengthened.
Claim 5
Dependent Claim
86 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (a) includes the steps of: (d) positioning opposed mating core dies into juxtaposed relationship such that mutually opposed faying surfaces are proximately engaged; and (e) injecting ceramic material into the cavity defined by opposed core dies; and wherein step (c) includes the step of: (f) directing the laser to remove excessive amounts of fired core material which intrudes between the mutually opposed faying surfaces during step (e).
Claim 6
Dependent Claim
41 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (c) includes the step of: (d) cutting detailed features into the outer surfaces of the fired core by means of the laser.
Claim 7
Dependent Claim
37 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (c) includes the step of: (d) using the laser to mill the outer surfaces of the fired core.
Claim 8
Dependent Claim
44 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (c) includes the step of: (d) using the laser to heat localized outer surfaces of the fired core to a temperature at which glazing occurs.
Claim 9
Dependent Claim
59 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (a) includes the step of: (d) providing temporary tie bar means for core stability during step (b); and wherein step (c) includes the step of: (d) directing the laser to remove the temporary tie bar means from the fired core.
Claim 10
Dependent Claim
55 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (c) includes the step of: (d) forming indicia on the outer surfaces of the fired core which will subsequently, upon completion of a molding process, be x-ray readable on the interior surfaces of the completed blade.
Claim 11
Dependent Claim
48 words
A method of producing a core for making a hollow blade as set forth in claim 9 wherein step (d) includes the step of: (e) operating the laser at a level of power such that the laser beam only superficially ablates the surface of the fired ceramic core.
Claim 12
Dependent Claim
40 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (c) includes the step of: (d) drilling holes into the outer surfaces of the fired core by means of the laser.
Claim 13
Dependent Claim
51 words
A method of producing a core for making a hollow blade as set forth in claim 11 wherein step (d) includes the step of: (e) punching holes into the outer surfaces of the fired core by centering the axis of the laser beam on the axis of the hole being formed.
Claim 14
Dependent Claim
78 words
A method of producing a core for making a hollow blade as set forth in claim 11 wherein step (d) includes the step of: (e) using the laser to cut at least one disk having a desired diameter out of the outer surfaces of the fired core by directing the axis of the laser beam transverse to the plane of the outer surfaces at a plurality of locations substantially equidistant from the axis of the disk being removed.
Claim 15
Dependent Claim
62 words
A method of producing a core for making a hollow blade as set forth in claim 11 wherein step (d) includes the step of: (e) using the laser to cut out of the outer surface of the fired core a disk having an irregular boundary by directing the axis of the laser beam transverse to the plane of the outer surface thereof.
Claim 16
Dependent Claim
67 words
A method of producing a core for making a hollow blade as set forth in claim 1 including the steps, after step (a) and before step (b), of: (d) ejecting the green ceramic core from the core mold; (e) placing the green ceramic core on refractory supporting means; and (f) introducing the green ceramic core and refractory supporting means to the interior of a high temperature kiln.
Claim 17
Dependent Claim
62 words
A method of producing a core for making a hollow blade as set forth in claim 15 including the steps, after step (b), of: (g) removing the fired core from the kiln and from the refractory supporting means; (h) placing the fired core on refractory supporting means; (i) holding the fired core stationary on the refractory supporting means while performing step (c).
Claim 18
Dependent Claim
46 words
A method of producing a core for making a hollow blade as set forth in claim 1 wherein step (c) includes the step of: (d) operating the laser to form specific detailed features on the fired core desired for the interior passages of the completed blade.
Claim 19
Dependent Claim
51 words
A method of producing a core for making a hollow blade as set forth in claim 17 wherein step (d) includes the step of: (e) operating the laser with a level of power adequate for melting and vaporizing the fired ceramic core so as to produce the specific detailed features desired.
Claim 20
Dependent Claim
32 words
A method of producing a core for making a hollow blade as set forth in claim 17 wherein the transverse dimension of the specific detailed features is less than approximately 0.020 inches.
Claim 21
Dependent Claim
91 words
A method of producing a core for making a hollow blade as set forth in claim 17 including the steps of: (e) depositing a catalyst onto the surface of the fired core; and (f) after step (e), immersing the fired core with the catalyst surface thereon into a heated solution of nickel salts to thereby form an electroless nickel coating on the surfaces of the core; and (g) withdrawing the fired core from the heated solution when a sufficient thickness of the electroless nickel has been deposited on the surfaces thereof.
Claim 22
Dependent Claim
54 words
A method of producing a core for making a hollow blade as set forth in claim 20 wherein the wetting material is a metallo-organic compound containing at least one metal having a high melting point selected from the group consisting of: copper, silver, gold, iron, ruthenium, osmium cobalt, rhodium, iridium, nickel, palladium, and platinum.
Claim 23
Dependent Claim
64 words
A method of producing a core for making a hollow blade as set forth in claim 17 wherein the transverse dimension of the specific detailed features is less than approximately 0.020 inches; and including the step of: (d) applying to the surface of the fired core a coating of a wetting material having a surface energy in excess of approximately 750 dynes per centimeter.
Claim 24
Dependent Claim
26 words
A method of producing a core for making a hollow blade as set forth in claim 22 wherein step (d) is performed by an electroplating process.
Claim 25
Dependent Claim
28 words
A method of producing a core for making a hollow blade as set forth in claim 22 wherein step (d) is performed by a chemical vapor deposition process.
Claim 26
Dependent Claim
28 words
A method of producing a core for making a hollow blade as set forth in claim 22 wherein step (d) is performed by a physical vapor deposition process.
Claim 27
Dependent Claim
83 words
A method of producing a core for making a hollow blade as set forth in claim 22 wherein step (d) includes the step of: (e) applying to the surface of the fired core by an ion sputtering process a coating of a material selected from the group consisting of titanium diboride and titanium carbide; wherein step (c) includes the step of: (d) operating the laser to form specific detailed features on the fired core desired for the interior passages of the completed blade.
Claim 28
Dependent Claim
54 words
A method of producing a core for making a hollow blade as set forth in claim 22 wherein the wetting material is a metallo-organic compound containing at least one metal having a high melting point selected from the group consisting of: copper, silver, gold; iron, ruthenium, osmium, cobalt, rhodium, iridium, nickel, palladium, and platinum.
Claim 29
Dependent Claim
68 words
A method of producing a core for making a hollow blade as set forth in claim 27 wherein step (d) includes the steps of: (e) heating the fired core with the wetting material thereon to a temperature in the range of approximately 400° C. to 600° C. to drive off the organic compound thereby leaving only the high temperature metal on the outer surface of the fired core.
Claim 30
Dependent Claim
27 words
A method of producing a core for making a hollow blade as set forth in claim 28 wherein steps (d) and (e) are performed at least twice.
Claim 31
Dependent Claim
48 words
A method of producing a core for making a hollow blade as set forth in claim 28 including the step of: (f) after steps (d) and (e), immersing the fired core into an electroless nickel bath to form a nickel coating onto the outermost surface of the core.
Claim 32
Independent Claim
243 words
A method of making a hollow blade comprising the steps of: (a) molding a green ceramic core having outer surfaces generally contoured to produce the intended interior surfaces of the completed blade; (b) heating the green ceramic core to a sufficient extent to produce a fired core; (c) operating on the fired core with a laser to modify the characteristics of the fired core; (d) inserting the modified fired core into a wax injection mold having the negative contour of a desired blade; (e) injecting molten wax into the wax injection mold to form a wax mold/core combination; (f) removing the wax mold/core combination from the wax injection mold; (g) generously coating the wax mold/core combination with a ceramic slurry; (h) causing the ceramic slurry applied in step (g) to harden so as to form an outer shell; (h) heating the outer shell to melt the wax of the wax mold/core combination within the interior of the outer shell; (i) draining off the melted wax from the interior of the outer shell; (j) pouring molten alloy into the interior of the outer shell to thereby fill the cavity defined by the interior surfaces of the outer shell and the surfaces of the fired core; (k) allowing the alloy to solidify to form a casting having a desired external surface with the desired contour; and (l) leaching out the fired core from the interior of the casting substantially resulting in the desired hollow blade.
Claim 33
Independent Claim
243 words
A method of making a hollow blade comprising the steps of: (a) molding a green ceramic core having outer surfaces generally contoured to produce the intended interior surfaces of the completed blade; (b) heating the green ceramic core to a sufficient extent to produce a fired core; (c) operating on the fired core with a laser to modify the characteristics of the fired core; (d) inserting the modified fired core into a wax injection mold having the negative contour of a desired blade; (e) injecting molten wax into the wax injection mold to form a wax mold/core combination; (f) removing the wax mold/core combination from the wax injection mold; (g) generously coating the wax mold/core combination with a ceramic slurry; (h) causing the ceramic slurry applied in step (g) to harden so as to form an outer shell; (h) heating the outer shell to melt the wax of the wax mold/core combination within the interior of the outer shell; (i) draining off the melted wax from the interior of the outer shell; (j) pouring molten alloy into the interior of the outer shell to thereby fill the cavity defined by the interior surfaces of the outer shell and the surfaces of the fired core; (k) allowing the alloy to solidify to form a casting having a desired external surface with the desired contour; and (l) leaching out the fired core from the interior of the casting substantially resulting in the desired hollow blade.
Claim 34
Dependent Claim
37 words
A method of making a hollow blade as set forth in claim 31 wherein step (c) includes the step of: (d) operating the laser in such a manner that the surface of the fired core is smoothened.
Claim 35
Dependent Claim
46 words
A method of making a hollow blade as set forth in claim 31 wherein step (c) includes the step of: (d) directing the beam of the laser to the surface of the fired core in such a manner that the surface of the core is strengthened.
Claim 36
Dependent Claim
82 words
A method of making a hollow blade as set forth in claim 31 wherein step (a) includes the steps of: (d) positioning opposed mating core dies into juxtaposed relationship such that mutually opposed faying surfaces are proximately engaged; and (e) injecting ceramic material into the cavity defined by opposed core dies; and wherein step (c) includes the step of: (f) directing the laser to remove excessive amounts of fired core material which intrudes between the mutually opposed faying surfaces during step (e).
Claim 37
Dependent Claim
37 words
A method of making a hollow blade as set forth in claim 31 wherein step (c) includes the step of: (d) cutting detailed features into the outer surfaces of the fired core by means of the laser.
Claim 38
Dependent Claim
33 words
A method of making a hollow blade as set forth in claim 31 wherein step (c) includes the step of: (d) using the laser to mill the outer surfaces of the fired core.
Claim 39
Dependent Claim
40 words
A method of making a hollow blade as set forth in claim 31 wherein step (c) includes the step of: (d) using the laser to heat localized outer surfaces of the fired core to a temperature at which glazing occurs.
Claim 40
Dependent Claim
55 words
A method of making a hollow blade as set forth in claim 31 wherein step (a) includes the step of: (d) providing temporary tie bar means for core stability during step (b); and wherein step (c) includes the step of: (d) directing the laser to remove the temporary tie bar means from the fired core.
Claim 41
Dependent Claim
47 words
A method of making a hollow blade as set forth in claim 32 wherein step (d) includes the step of: (e) operating the laser with a level of power adequate for melting and vaporizing the fired ceramic core so as to produce the specific detailed features desired.
Claim 42
Dependent Claim
27 words
A method of making a hollow blade as set forth in claim 39 wherein the laser used in steps (c) and (d) is a CO 2 laser.
Claim 43
Dependent Claim
51 words
A method of making a hollow blade as set forth in claim 31 wherein step (c) includes the step of: (d) forming indicia on the outer surfaces of the fired core which will subsequently, upon completion of a molding process, be x-ray readable on the interior surfaces of the completed blade.
Claim 44
Dependent Claim
45 words
A method of making a hollow blade as set forth in claim 41 wherein step (d) includes the step of: (e) operating the laser at a level of power such that the laser beam therefrom only superficially ablates the surface of the fired ceramic core.
Claim 45
Dependent Claim
26 words
A method of making a hollow blade as set forth in claim 42 wherein the laser used in steps (c) and (e) is a YAG laser.
Claim 46
Dependent Claim
36 words
A method of making a hollow blade as set forth in claim 31 wherein step (c) includes the step of: (d) drilling holes into the outer surfaces of the fired core by means of the laser.
Claim 47
Dependent Claim
47 words
A method of making a hollow blade as set forth in claim 44 wherein step (d) includes the step of: (e) punching holes into the outer surfaces of the fired core by centering the axis of the laser beam on the axis of the hole being formed.
Claim 48
Dependent Claim
74 words
A method of making a hollow blade as set forth in claim 44 wherein step (d) includes the step of: (e) using the laser to cut at least one disk having a desired diameter out of the outer surfaces of the fired core by directing the axis of the laser beam transverse to the plane of the outer surfaces at a plurality of locations substantially equidistant from the axis of the disk being removed.
Claim 49
Dependent Claim
58 words
A method of making a hollow blade as set forth in claim 44 wherein step (d) includes the step of: (e) using the laser to cut out of the outer surface of the fired core a disk having an irregular boundary by directing the axis of the laser beam transverse to the plane of the outer surface thereof.
Claim 50
Dependent Claim
63 words
A method of making a hollow blade as set forth in claim 31 including the steps, after step (a) and before step (b), of: (d) ejecting the green ceramic core from the core mold; (e) placing the green ceramic core on refractory supporting means; and (f) introducing the green ceramic core and refractory supporting means to the interior of a high temperature kiln.
Claim 51
Dependent Claim
58 words
A method of making a hollow blade as set forth in claim 48 including the steps, after step (b), of: (g) removing the fired core from the kiln and from the refractory supporting means; (h) placing the fired core on refractory supporting means; (i) holding the fired core stationary on the refractory supporting means while performing step (c).
Claim 52
Dependent Claim
42 words
A method of making a hollow blade as set forth in claim 31 wherein step (c) includes the step of: (d) operating the laser to form specific detailed features on the fired core desired for the interior passages of the completed blade.
Claim 53
Dependent Claim
28 words
A method of making a hollow blade as set forth in claim 50 wherein the transverse dimension of the specific detailed features is less than approximately 0.020 inches.
Claim 54
Dependent Claim
87 words
A method of making a hollow blade as set forth in claim 50 including the steps of: (e) depositing a catalyst onto the surface of the fired core; and (f) after step (e), immersing the fired core with the catalyst surface thereon into a heated solution of nickel salts to thereby form an electroless nickel coating on the surfaces of the core; and (g) withdrawing the fired core from the heated solution when a sufficient thickness of the electroless nickel has been deposited on the surfaces thereof.
Claim 55
Dependent Claim
50 words
A method of making a hollow blade as set forth in claim 52 wherein the wetting material is a metallo-organic compound containing at least one metal having a high melting point selected from the group consisting of: copper, silver, gold, iron, ruthenium, osmium, cobalt, rhodium, iridium, nickel, palladium, and platinum.
Claim 56
Dependent Claim
60 words
A method of making a hollow blade as set forth in claim 50 wherein the transverse dimension of the specific detailed features is less than approximately 0.020 inches; and including the step of: (d) applying to the surface of the fired core a coating of a wetting material having a surface energy in excess of approximately 750 dynes per centimeter.
Claim 57
Dependent Claim
22 words
A method of making a hollow blade as set forth in claim 54 wherein step (d) is performed by an electroplating process.
Claim 58
Dependent Claim
24 words
A method of making a hollow blade as set forth in claim 54 wherein step (d) is performed by a chemical vapor deposition process.
Claim 59
Dependent Claim
24 words
A method of making a hollow blade as set forth in claim 54 wherein step (d) is performed by a physical vapor deposition process.
Claim 60
Dependent Claim
50 words
A method of making a hollow blade as set forth in claim 54 wherein step (d) includes the step of: (e) applying to the surface of the fired core by an ion sputtering process a coating of a material selected from the group consisting of titanium diboride and titanium carbide.
Claim 61
Dependent Claim
50 words
A method of making a hollow blade as set forth in claim 54 wherein the wetting material is a metallo-organic compound containing at least one metal having a high melting point selected from the group consisting of: copper, silver, gold; iron, ruthenium, osomium; cobalt, rhodium, iridium nickel, palladium, and platinum.
Claim 62
Dependent Claim
68 words
A method of producing a core for making a hollow blade as set forth in claim 59 wherein step (d) includes the steps of; (e) heating the fired core with the wetting material thereon to a temperature in the range of approximately 400° C. to 600° C. to drive off the organic compound thereby leaving only the high temperature metal on the outer surface of the fired core.
Claim 63
Dependent Claim
27 words
A method of producing a core for making a hollow blade as set forth in claim 60 wherein steps (d) and (e) are performed at least twice.
Claim 64
Dependent Claim
44 words
A method of making a hollow blade as set forth in claim 60 including the step of: (f) after steps (d) and (e), immersing the fired core into an electroless nickel bath to form a nickel coating onto the outermost surface of the core.
References Cited (Backward Citations)
JPS4913695A
Cited
US4322601A
Cited
US4401876A
Cited
US4455893A
Cited
US4606747A
Cited
US4475027A
Cited
US4467172A
Cited
US4986664A
Cited
US4842782A
Cited
US4952789A
Cited
US4914270A
Cited
US4978830A
Cited
US4970600A
Cited
US5295530A
Cited
US5329985A
Cited
US5296308A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-11-13 | 1999-05-15 | 1999-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-11-13 | 2003-05-15 | 2003-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-11-13 | 2007-05-15 | 2007-11-14 | $7700.00 | Window Closed / Lapsed |