Method of fabricating high voltage silicon carbide MESFETs
Assignee: Intellectual Ventures Holding 81 LLC
•
Filing: 1994-12-13
•
Granted: 1995-10-17
•
Expires: 2014-12-13
Abstract
Abstract A high voltage silicon carbide MESFET includes an electric field equalizing region in a monocrystalline silicon carbide substrate at a face thereof, which extends between the drain and gate of the MESFET and between the source and gate of the MESFET. The region equalizes the electric field between the drain and gate and between the source and gate to thereby increase the breakdown voltage of the silicon carbide MESFET. The first and second electric field equalizing regions are preferably amorphous silicon carbide regions in the monocrystalline silicon carbide substrate. The amorphous regions are preferably formed by performing a shallow ion implantation of electrically inactive ions such as argon, using the source and drain electrodes and the metal gate as a mask, at a sufficient dose and energy to amorphize the substrate face. A third amorphous silicon carbide region may be formed at the face, adjacent and surrounding the MESFET to provide edge termination and isolation of the MESFET. The third amorphous, silicon carbide region may be formed during the same shallow implant described above or may be formed in a separate deep implant. The lateral silicon carbide MESFET may be formed in an epitaxial region of second conductivity type on a substrate of first conductivity type, or in an implanted region of second conductivity type in a substrate of first conductivity type.
Inventors
- 👤 Bantval J. Baliga
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:29
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/118; H10D12/00; H10D12/01; H10D12/031; H10D30/00; H10D30/01; H10D30/061; H10D30/80; H10D30/87; H10D62/00; H10D62/10; H10D62/13; H10D62/149; H10D62/161; H10D62/80; H10D62/83; H10D62/832; H10D62/8325; Y; Y10; Y10S; Y10S438/00; Y10S438/931
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
60 words
A method of fabricating a silicon carbide field effect transistor, comprising the steps of: forming spaced apart source and drain regions in a fact of a monocrystalline silicon carbide substrate, and a gate on said face between said spaced apart source and drain regions; and amorphizing said monocrystalline silicon carbide substrate, at said face, between said drain and said gate.
Claim 2
Independent Claim
60 words
A method of fabricating a silicon carbide field effect transistor, comprising the steps of: forming spaced apart source and drain regions in a fact of a monocrystalline silicon carbide substrate, and a gate on said face between said spaced apart source and drain regions; and amorphizing said monocrystalline silicon carbide substrate, at said face, between said drain and said gate.
Claim 3
Dependent Claim
30 words
A method according to claim 1 wherein said amorphizing step further comprises the step of amorphizing said monocrystalline silicon carbide substrate, at said face, between said source and said gate.
Claim 4
Dependent Claim
35 words
A method according to claim 2 wherein said amorphizing step further comprises the step of amorphizing said monocrystalline silicon carbide substrate, at said face, adjacent and surrounding said source and drain regions and said gate.
Claim 5
Dependent Claim
27 words
A method according to claim 1 wherein said amorphizing step comprises the step of implanting electrically inactive ions into said face, between said drain and said gate.
Claim 6
Dependent Claim
45 words
A method according to claim 3 wherein said amorphizing step comprises the step of implanting electrically inactive ions into said face, between said drain and said gate, between said source and said gate, and adjacent and surrounding said source and drain regions and said gate.
Claim 7
Dependent Claim
20 words
A method according to claim 5 wherein said implanting electrically inactive ions step comprises the step of implanting argon ions.
Claim 8
Dependent Claim
27 words
A method according to claim 1 wherein said gate forming step comprises the step of forming a metal gate directly on said face, to provide a MESFET.
Claim 9
Dependent Claim
83 words
A method according to claim 1 wherein said forming step further comprises the step of: forming a source electrode on said face electrically contacting said source region, and a drain electrode on said face electrically contacting said drain region, said source electrode, said drain electrode and said gate all comprising titanium, such that said source electrode and said drain electrode form ohmic contacts with said source region and said drain region, respectively, and said metal gate forms a rectifying contact with said face.
Claim 10
Dependent Claim
52 words
A method according to claim 1 wherein comprises the steps of: forming a blanket titanium layer on said face; and patterning said blanket titanium layer to define a source electrode on said face, electrically contacting said source region, a drain electrode on said face, electrically contacting said drain region, and said gate.
Claim 11
Dependent Claim
58 words
A method according to claim 1 wherein said forming step is preceded by the step of doping said monocrystalline silicon carbide substrate at a predetermined dopant charge at said face, said predetermined dopant charge being equal to the product of the dielectric constant of said monocrystalline silicon carbide substrate and the breakdown electric field strength of silicon carbide.
Claim 12
Independent Claim
145 words
A method of forming a silicon carbide MESFET comprising the steps of: epitaxially forming a second monocrystalline silicon carbide region of second conductivity type on a first monocrystalline silicon carbide region of first conductivity type, said second monocrystalline silicon carbide region having a face opposite said first monocrystalline silicon carbide region; forming spaced apart source and drain regions in said second monocrystalline silicon carbide region, extending to said face; forming source and drain electrodes on said face, electrically contacting said source and drain regions respectively, and a metal gate directly on said face between said spaced apart source and drain regions; and amorphizing said face between said source electrode and said metal gate, between said drain electrode and said metal gate, and adjacent and surrounding said MESFET extending from said face, through said second monocrystalline silicon carbide region and into first monocrystalline silicon carbide region.
Claim 13
Independent Claim
145 words
A method of forming a silicon carbide MESFET comprising the steps of: epitaxially forming a second monocrystalline silicon carbide region of second conductivity type on a first monocrystalline silicon carbide region of first conductivity type, said second monocrystalline silicon carbide region having a face opposite said first monocrystalline silicon carbide region; forming spaced apart source and drain regions in said second monocrystalline silicon carbide region, extending to said face; forming source and drain electrodes on said face, electrically contacting said source and drain regions respectively, and a metal gate directly on said face between said spaced apart source and drain regions; and amorphizing said face between said source electrode and said metal gate, between said drain electrode and said metal gate, and adjacent and surrounding said MESFET extending from said face, through said second monocrystalline silicon carbide region and into first monocrystalline silicon carbide region.
Claim 14
Dependent Claim
68 words
A method according to claim 11 wherein said epitaxially forming step comprises the steps of: epitaxially forming a first monocrystalline silicon carbide portion of said first conductivity type on a monocrystalline silicon carbide substrate of said first conductivity type, said substrate being more highly doped than said first portion; and epitaxially forming said second monocrystalline silicon carbide region on said first monocrystalline silicon carbide portion, opposite said substrate.
Claim 15
Dependent Claim
80 words
A method according to claim 11 wherein said amorphizing step comprises the step of implanting electrically inactive ions into said face between said source electrode and said metal gate, between said drain electrode and said metal gate, and adjacent and surrounding said MESFET extending from said face, through said second monocrystalline silicon carbide region and into first monocrystalline silicon carbide region, at an energy and dose which is sufficient to amorphize said second monocrystalline silicon carbide region, at said face.
Claim 16
Dependent Claim
36 words
A method according to claim 13 wherein said implanting step comprises implanting argon ions into said face at an energy of about 30 keV and a dose of at least about 10 15 /cm 2 .
Claim 17
Dependent Claim
47 words
A method according to claim 11 wherein said step of forming source and drain electrodes and a metal gate comprises the steps of: forming a blanket metal layer on said face: and patterning said blanket layer to define said source and drain electrodes and said metal gate.
Claim 18
Dependent Claim
105 words
A method according to claim 15 wherein said amorphizing step comprises the steps of: masking said MESFET; performing a deep implant of electrically inactive ions at an energy and a dose which is sufficient to amorphize said second monocrystalline silicon carbide region adjacent and surrounding said MESFET extending from said face, through said second monocrystalline silicon carbide region and into first monocrystalline silicon carbide region; and performing a blanket shallow implant of electrically inactive ions at an energy and a dose which is sufficient to amorphize said face between said source electrode and said metal gate, and between said drain electrode and said metal gate.
Claim 19
Dependent Claim
55 words
A method according to claim 15 wherein said blanket metal layer forming step comprises the step of blanket forming a titanium layer, such that the patterned source electrode and drain electrode form ohmic contacts with said source region and said drain region, respectively, and the patterned metal gate forms a rectifying contact with said face.
Claim 20
Dependent Claim
56 words
A method according to claim 11 wherein said epitaxially forming step comprises the step of epitaxially forming said second monocrystalline silicon carbide region with a predetermined dopant charge, said predetermined dopant charge being equal to the product of the dielectric constant of said monocrystalline silicon carbide substrate and the breakdown electric field strength of silicon carbide.
Claim 21
Independent Claim
180 words
A method of fabricating a silicon carbide MESFET comprising the steps of: performing a masked implantation of ions of a second conductivity type into a face of a first monocrystalline silicon carbide region of first conductivity type, to form a second monocrystalline silicon carbide region of second conductivity type in said first monocrystalline silicon carbide region, at a face thereof, said second monocrystalline silicon carbide region defining a junction with said first monocrystalline silicon carbide region, said junction extending adjacent said face; forming spaced apart source and drain regions in said second monocrystalline silicon carbide region, extending to said face; forming source and drain electrodes on said face, electrically contacting said source and drain regions respectively, and a metal gate directly on said face between said spaced apart source and drain regions; and amorphizing said face between said source electrode and said metal gate, between said drain electrode and said metal gate, and adjacent and surrounding said MESFET extending from said second monocrystalline silicon carbide region, across said junction and to said first monocrystalline silicon carbide region at said face.
Claim 22
Independent Claim
180 words
A method of fabricating a silicon carbide MESFET comprising the steps of: performing a masked implantation of ions of a second conductivity type into a face of a first monocrystalline silicon carbide region of first conductivity type, to form a second monocrystalline silicon carbide region of second conductivity type in said first monocrystalline silicon carbide region, at a face thereof, said second monocrystalline silicon carbide region defining a junction with said first monocrystalline silicon carbide region, said junction extending adjacent said face; forming spaced apart source and drain regions in said second monocrystalline silicon carbide region, extending to said face; forming source and drain electrodes on said face, electrically contacting said source and drain regions respectively, and a metal gate directly on said face between said spaced apart source and drain regions; and amorphizing said face between said source electrode and said metal gate, between said drain electrode and said metal gate, and adjacent and surrounding said MESFET extending from said second monocrystalline silicon carbide region, across said junction and to said first monocrystalline silicon carbide region at said face.
Claim 23
Dependent Claim
115 words
A method according to claim 19 wherein said masked implantation performing step comprises the steps of: epitaxially forming a first monocrystalline silicon carbide portion of said first conductivity type on a monocrystalline silicon carbide substrate of said first conductivity type, said substrate being more highly doped than said first portion; and performing a masked implantation of ions of said second conductivity type into said first monocrystalline silicon carbide region portion, to form said second monocrystalline silicon carbide region of second conductivity type in said first monocrystalline silicon carbide portion, at a face thereof, said second monocrystalline silicon carbide region defining a junction with said first monocrystalline silicon carbide portion, said junction extending adjacent said face.
Claim 24
Dependent Claim
84 words
A method according to claim 20 wherein said amorphizing step comprises the step of implanting electrically inactive ions into said face between said source electrode and said metal gate, between said drain electrode and said metal gate, and adjacent and surrounding said MESFET, extending from said second monocrystalline silicon carbide region, across said junction and to said first monocrystalline silicon carbide region at said face, at an energy and dose which is sufficient to amorphize said second monocrystalline silicon carbide region, at said face.
Claim 25
Dependent Claim
36 words
A method according to claim 21 wherein said implanting step comprises implanting argon ions into said face at an energy of about 30 keV and a dose of at least about 10 15 /cm 2 .
Claim 26
Dependent Claim
45 words
A method according to claim 19 wherein said source and drain electrode and metal gate forming step comprises the steps of: forming a blanket metal layer on said face: and patterning said blanket layer to define said source and drain electrodes and said metal gate.
Claim 27
Dependent Claim
78 words
A method according to claim 23 wherein said amorphizing step comprises the step of: performing a blanket shallow implant of electrically inactive ions at an energy and a dose which is sufficient to amorphize said face between said source electrode and said metal gate, between said drain electrode and said metal gate and surrounding said MESFET extending from said second monocrystalline silicon carbide region, across said junction and to said first monocrystalline silicon carbide region at said face.
Claim 28
Dependent Claim
55 words
A method according to claim 24 wherein said blanket metal layer forming step comprises the step of blanket forming a titanium layer, such that the patterned source electrode and drain electrode form ohmic contacts with said source region and said drain region, respectively, and the patterned metal gate forms a rectifying contact with said face.
Claim 29
Dependent Claim
71 words
A method according to claim 19 wherein said step of performing a masked implantation of ions of a second conductivity type comprises the step of performing a masked implantation of ions of a second conductivity type with ions of a predetermined dopant charge, said predetermined dopant charge being equal to the product of the dielectric constant of said monocrystalline silicon carbide substrate and the breakdown electric field strength of silicon carbide.
References Cited (Backward Citations)
US5170231A
Cited
US5270244A
Cited
US5318915A
Cited
US5322802A
Cited
US5378642A
Cited
US5397717A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-10-16 | 1999-04-17 | 1999-10-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-10-16 | 2003-04-17 | 2003-10-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-10-16 | 2007-04-17 | 2007-10-17 | $7700.00 | Window Closed / Lapsed |