Sub-micron diffusion area isolation with SI-SEG for a DRAM array

Claim 2

A fabrication process for forming sub-micron diffusion area isolation in a semiconductor device, said process comprising the steps of: forming a native oxide over a silicon substrate; forming a first patterned mask over said native oxide exposing unmasked regions; growing field oxide on said silicon substrate at the unmasked regions; forming a nitride film over said field oxide and said first patterned mask; forming a second patterned mask over said nitride film, thereby exposing spaced apart regions in said nitride film that overlies said field oxide; removing said nitride film and said underlying field oxide at said exposed spaced apart regions and removing a portion of the nitride film residing beneath said second patterned mask, thereby providing exposed field oxide sidewalls; removing an angled upper portion of each said exposed field oxide sidewall along with the corresponding overlying nitride film portion, thereby forming a nitride masking film having sub-micron width that overlies the remaining field oxide at said spaced apart regions; growing silicon by selective epitaxial growth (SEG) in each spaced apart regions, said silicon SEG is grown to approximately the same height of the upper surface of said field oxide; oxidizing the surface of said silicon SEG until the oxide level is approximately even with said nitride masking film, thereby forming a planarized surface; forming a transistor gate over each silicon SEG grown region, said transistor gate being separated from said silicon SEG grown region by a gate oxide; and implanting a conductive dopant into the silicon SEG grown regions left uncovered by said transistor gate, to form diffusion regions therein; whereby an active transistor is formed therefrom.

Claim 3

The process of claim 1, wherein said first patterned mask comprises nitride.

Claim 4

The process of claim 1, wherein said second patterned mask comprises photoresist.

Claim 5

The process of claim 1, wherein said removing the nitride film and the underlying field oxide at said exposed spaced apart regions comprises an isotropic etch.

Claim 6

The process of claim 1, wherein said removing an angled upper portion of each said exposed field oxide sidewall along with the corresponding overlying nitride film portion comprises an isotropic etch.

Claim 7

The process of claim 1, wherein the dopants used for said implanting comprise N-type dopants.

Claim 8

The process of claim 1, wherein the dopants used for said implanting comprise P-type dopants.

Claim 9

The process of claim 6, wherein said N-type dopants comprise arsenic atoms.

Claim 10

The process of claim 7, wherein said P-type dopants comprise boron atoms.

Claim 11

A fabrication process for forming sub-micron diffusion area isolation in a Dynamic Random Access Memory (DRAM) device, said process comprising the steps of: forming a native oxide over a silicon substrate; forming a patterned nitride mask over said native oxide exposing unmasked regions; growing field oxide on said silicon substrate at the unmasked regions; forming a nitride film over said field oxide and said patterned nitride mask; forming a patterned photoresist mask over said nitride film, thereby exposing spaced apart regions in the nitride film that overlies the field oxide; isotropically etching the nitride film and the underlying field oxide at said exposed spaced apart regions, thereby providing exposed field oxide sidewalls and removing a portion of said nitride film that resides beneath the patterned edges of said patterned photoresist mask; performing an isotropic etch on the upper portion of each said exposed field oxide sidewall along with the corresponding overlying nitride film portion, thereby forming a nitride masking film having a sub-micron width that overlies the remaining field oxide at said spaced apart regions; growing silicon SEG in each spaced apart regions, said silicon SEG is grown to approximately the same height as the upper surface of said field oxide; oxidizing the surface of said silicon SEG until the oxide level is approximately even with the surface of said nitride masking film, thereby forming a planarized surface; forming a pair of wordlines over each silicon SEG grown region and a pair of wordlines over each spaced apart areas of field oxide, said pair of wordlines are separated from said silicon SEG grown region by a gate oxide; and implanting a conductive dopant into the silicon SEG grown regions left uncovered by said wordlines, thereby forming diffusion regions therein; whereby an access transistor is formed therefrom.

Claim 12

A fabrication process for forming sub-micron diffusion area isolation in a Dynamic Random Access Memory (DRAM) device, said process comprising the steps of: forming a native oxide over a silicon substrate; forming a patterned nitride mask over said native oxide exposing unmasked regions; growing field oxide on said silicon substrate at the unmasked regions; forming a nitride film over said field oxide and said patterned nitride mask; forming a patterned photoresist mask over said nitride film, thereby exposing spaced apart regions in the nitride film that overlies the field oxide; isotropically etching the nitride film and the underlying field oxide at said exposed spaced apart regions, thereby providing exposed field oxide sidewalls and removing a portion of said nitride film that resides beneath the patterned edges of said patterned photoresist mask; performing an isotropic etch on the upper portion of each said exposed field oxide sidewall along with the corresponding overlying nitride film portion, thereby forming a nitride masking film having a sub-micron width that overlies the remaining field oxide at said spaced apart regions; growing silicon SEG in each spaced apart regions, said silicon SEG is grown to approximately the same height as the upper surface of said field oxide; oxidizing the surface of said silicon SEG until the oxide level is approximately even with the surface of said nitride masking film, thereby forming a planarized surface; forming a pair of wordlines over each silicon SEG grown region and a pair of wordlines over each spaced apart areas of field oxide, said pair of wordlines are separated from said silicon SEG grown region by a gate oxide; and implanting a conductive dopant into the silicon SEG grown regions left uncovered by said wordlines, thereby forming diffusion regions therein; whereby an access transistor is formed therefrom.

Claim 13

The process of claim 10, wherein the dopants used for said implanting comprise N-type dopants.

Claim 14

The process of claim 10, wherein the dopants used for said implanting comprise P-type dopants.

Claim 15

The process of claim 11, wherein said N-type dopants comprise arsenic atoms.

Claim 16

The process of claim 12, wherein said P-type dopants comprise boron atoms.

Claim 17

A fabrication process for a forming storage cell having sub 0.1 micron diffusion area isolation in a Dynamic Random Access Memory (DRAM), said process comprising the steps of: forming a native oxide over a silicon substrate; forming a patterned nitride mask over said native oxide exposing unmasked regions; growing field oxide on said silicon substrate at the unmasked regions; forming a nitride film over said field oxide and said patterned nitride mask; forming a patterned photoresist mask over said nitride film, thereby exposing spaced apart regions in the nitride film that overlies the field oxide; isotropically etching the nitride film and the underlying field oxide at said exposed spaced apart regions, thereby providing exposed field oxide sidewalls and removing a portion of said nitride film that resides beneath the patterned edges of said patterned photoresist mask; performing an isotropic etch on the upper portion of each said exposed field oxide sidewall along with the corresponding overlying nitride film portion, thereby forming a nitride masking film having a sub-micron width that overlies the remaining field oxide at said spaced apart regions; growing silicon SEG in each spaced apart regions, said silicon SEG is grown to approximately the same height as the upper surface of said field oxide; oxidizing the surface of said silicon SEG until the oxide level is approximately even with the surface of said nitride masking film, thereby forming a planarized surface; forming a pair of wordlines over each silicon SEG grown region and a pair of wordlines over each spaced apart areas of field oxide, said pair of wordlines are separated from said silicon SEG grown region by a gate oxide; implanting a conductive dopant into the silicon SEG grown regions left uncovered by said wordlines, thereby forming diffusion regions therein; wherein an access transistor is formed therefrom; forming a storage capacitor that connects to a diffusion region on one side of the access transistors; and connecting a digitline to the diffusion area on the other side of the access transistor.

Claim 18

A fabrication process for a forming storage cell having sub 0.1 micron diffusion area isolation in a Dynamic Random Access Memory (DRAM), said process comprising the steps of: forming a native oxide over a silicon substrate; forming a patterned nitride mask over said native oxide exposing unmasked regions; growing field oxide on said silicon substrate at the unmasked regions; forming a nitride film over said field oxide and said patterned nitride mask; forming a patterned photoresist mask over said nitride film, thereby exposing spaced apart regions in the nitride film that overlies the field oxide; isotropically etching the nitride film and the underlying field oxide at said exposed spaced apart regions, thereby providing exposed field oxide sidewalls and removing a portion of said nitride film that resides beneath the patterned edges of said patterned photoresist mask; performing an isotropic etch on the upper portion of each said exposed field oxide sidewall along with the corresponding overlying nitride film portion, thereby forming a nitride masking film having a sub-micron width that overlies the remaining field oxide at said spaced apart regions; growing silicon SEG in each spaced apart regions, said silicon SEG is grown to approximately the same height as the upper surface of said field oxide; oxidizing the surface of said silicon SEG until the oxide level is approximately even with the surface of said nitride masking film, thereby forming a planarized surface; forming a pair of wordlines over each silicon SEG grown region and a pair of wordlines over each spaced apart areas of field oxide, said pair of wordlines are separated from said silicon SEG grown region by a gate oxide; implanting a conductive dopant into the silicon SEG grown regions left uncovered by said wordlines, thereby forming diffusion regions therein; wherein an access transistor is formed therefrom; forming a storage capacitor that connects to a diffusion region on one side of the access transistors; and connecting a digitline to the diffusion area on the other side of the access transistor.

Claim 19

The process of claim 15, wherein the dopants used for said implanting comprise N-type dopants.

Claim 20

The process of claim 15, wherein the dopants used for said implanting comprise P-type dopants.

Claim 21

The process of claim 16, wherein said N-type dopants comprise arsenic atoms.

Claim 22

The process of claim 17, wherein said P-type dopants comprise boron atoms.

Claim 23

A process for forming diffusion areas and field isolation regions on a silicon substrate, said process comprising the following steps: a) growing a field oxide layer on the surface of said substrate; b) forming a mask pattern which exposes a plurality of spaced-apart regions on the surface of said field oxide layer; c) removing portions of the field oxide layer in the exposed, spaced-apart regions with an isotropic etch so as to leave a cavity in each spaced-apart region, each cavity having as its floor an exposed region of said silicon substrate, and having vertical walls of field oxide; d) angularly chamfering the rim of each cavity with an isotropic etch; and e) filling each cavity with silicon using selective epitaxial growth, and using the floor of each cavity as the seed crystal for such growth.

Claim 24

A process for forming diffusion areas and field isolation regions on a silicon substrate, said process comprising the following steps: a) growing a field oxide layer on the surface of said substrate; b) forming a mask pattern which exposes a plurality of spaced-apart regions on the surface of said field oxide layer; c) removing portions of the field oxide layer in the exposed, spaced-apart regions with an isotropic etch so as to leave a cavity in each spaced-apart region, each cavity having as its floor an exposed region of said silicon substrate, and having vertical walls of field oxide; d) angularly chamfering the rim of each cavity with an isotropic etch; and e) filling each cavity with silicon using selective epitaxial growth, and using the floor of each cavity as the seed crystal for such growth.

Claim 25

The process of claim 20, wherein said step "c" and "d" are performed as an isotropic etch that will create cavities in the field oxide while at the same time chamfer the rim of said cavities.

Claim 26

The process of claim 20, wherein the filling of each cavity is allowed to proceed until the epitaxially-grown silicon has achieved a level greater than the upper surface of the field oxide layer.

Claim 27

The process of claim 22, wherein the exposed upper surface of the epitaxially-grown silicon is oxidized to an extent necessary to make the surface of the unoxidized epitaxially grown silicon equiplanar with the upper surface of the field oxide layer.