Production of supported particulate catalyst suitable for use in a vapor phase reactor
Assignee: Philip Morris Products Inc
•
Filing: 1993-01-12
•
Granted: 1995-08-29
•
Expires: 2013-01-12
Abstract
Abstract An improved technique is provided for the expeditious formation of a supported catalyst suitable for use in a vapor phase chemical reaction wherein the catalyst is provided as discrete particles. The support need not be capable of withstanding a highly elevated temperature, and may simply be paper or any other readily available material. A layer of deformable adhesive (preferably an organic adhesive) is provided as a liquid or paste on the surface of the support. Particles of a preformed activated catalyst are dispersed on the outer surface of the adhesive so that only a minor portion of the surfaces of the particles is embedded therein. Next the adhesive is solidified under appropriate conditions while maintaining the exposure of a major portion of the surfaces of the solid preformed catalytic particles to the atmosphere. Throughout the formation process the catalytic activity of the exposed surfaces of the catalytic particles remains substantially unaltered. In preferred embodiments the preformed activated catalyst is capable of accelerating the transformation of carbon monoxide to carbon dioxide (e.g., is a mixed transition metal oxide catalyst) and the resulting supported particulate catalyst is incorporated in a cigarette filter or in a room air purification system.
Inventors
- 👤 Robert L. Augustine
- 👤 Setrak K. Tanielyan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:38
CPC Classifications
B; B01; B01J; B01J37/00; B01J37/02; B01J37/0215; B01J37/0217; A; A24; A24D; A24D3/00; A24D3/06; A24D3/16; B01J2219/00; B01J2219/32; B01J2219/322; B01J2219/32279; B01J2219/324; B01J2219/32466
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
166 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor comprising: (a) applying a layer of an adhesive to at least a portion of the surface of a solid paper support, (b) dispersing solid particles of a preformed catalyst on the outer surface of said layer of adhesive present on said solid support whereby a portion of the surfaces of said solid preformed catalytic particles is embedded in said layer of adhesive while a portion of the surfaces of said solid preformed catalytic particles remains exposed to the ambient atmosphere without any substantial loss of catalytic activity, and (c) solidifying said adhesive layer through the utilization of conditions which do not substantially alter the catalytic activity of said exposed surfaces of said preformed solid particles and cause said adhesive to secure said preformed solid catalytic particles to said solid support while maintaining the exposure of a portion of the surfaces of said solid preformed catalytic particles to the ambient atmosphere.
Claim 2
Dependent Claim
166 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor comprising: (a) applying a layer of an adhesive to at least a portion of the surface of a solid paper support, (b) dispersing solid particles of a preformed catalyst on the outer surface of said layer of adhesive present on said solid support whereby a portion of the surfaces of said solid preformed catalytic particles is embedded in said layer of adhesive while a portion of the surfaces of said solid preformed catalytic particles remains exposed to the ambient atmosphere without any substantial loss of catalytic activity, and (c) solidifying said adhesive layer through the utilization of conditions which do not substantially alter the catalytic activity of said exposed surfaces of said preformed solid particles and cause said adhesive to secure said preformed solid catalytic particles to said solid support while maintaining the exposure of a portion of the surfaces of said solid preformed catalytic particles to the ambient atmosphere.
Claim 3
Dependent Claim
39 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein said layer of adhesive is applied in step (a) in a thickness of approximately 0.05 to 0.5 mm.
Claim 4
Dependent Claim
27 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein a adhesive is an organic adhesive.
Claim 5
Dependent Claim
27 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 3 wherein said organic adhesive is polymer based.
Claim 6
Dependent Claim
29 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 3 wherein said organic adhesive is a styrene-butadiene rubber adhesive.
Claim 7
Dependent Claim
38 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein said particles of a preformed catalyst have an average particle size of approximately 8 to 250 mesh.
Claim 8
Dependent Claim
34 words
A process for forming a said supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein the solid particles of said preformed catalyst comprise transition metal oxide catalyst.
Claim 9
Dependent Claim
59 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein the solid particles of said preformed catalyst comprise a plurality of metal oxide layers wherein the metal oxides are selected from the group consisting of oxides of titanium, chromium, iron, cobalt, nickel, copper, zinc, molybdenum, tungsten, and tin.
Claim 10
Dependent Claim
39 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein during step (c) said solidifying of said adhesive layer is carried out at a temperature below 100° C.
Claim 11
Dependent Claim
37 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein during step (c) said solidifying of said adhesive layer is carried out at substantially room temperature.
Claim 12
Dependent Claim
35 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein during step (c) said solidifying of said adhesive is accomplished through a chemical reaction.
Claim 13
Dependent Claim
41 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein during step (c) said solidifying of said adhesive is accomplished through the volatilization of a solvent component of said adhesive.
Claim 14
Dependent Claim
44 words
A process for forming a supported particulate catalyst suitable for use in a vapor phase reactor according to claim 1 wherein following step (c) at least 60 percent of the surface area of said secured solid preformed catalytic particles remains exposed to ambient conditions.
Claim 15
Dependent Claim
97 words
A supported particulate catalyst suitable for use in a vapor phase reactor comprising: (a) a solid paper support, (b) a layer of a solidified adhesive secured to at least a portion of the surface of said solid support, and (c) solid particles of preformed catalyst secured to said solid support through the action of said adhesive wherein a portion of the surfaces of said solid preformed catalytic particles is embedded in the outer surface of said layer of adhesive and a portion of the surfaces of said solid preformed catalytic particles is exposed to the ambient atmosphere.
Claim 16
Dependent Claim
97 words
A supported particulate catalyst suitable for use in a vapor phase reactor comprising: (a) a solid paper support, (b) a layer of a solidified adhesive secured to at least a portion of the surface of said solid support, and (c) solid particles of preformed catalyst secured to said solid support through the action of said adhesive wherein a portion of the surfaces of said solid preformed catalytic particles is embedded in the outer surface of said layer of adhesive and a portion of the surfaces of said solid preformed catalytic particles is exposed to the ambient atmosphere.
Claim 17
Dependent Claim
30 words
A supported particulate catalyst suitable for use in a vapor phase reactor according to claim 15 wherein said layer of adhesive has a thickness of approximately 0.05 to 0.5 mm.
Claim 18
Dependent Claim
24 words
A supported particulate catalyst suitable for use in a vapor phase reactor according to claim 14 wherein said solidified adhesive is an organic adhesive.
Claim 19
Dependent Claim
24 words
A supported particulate catalyst suitable for use in a vapor phase reactor according to claim 16 wherein said solidified organic adhesive is polymer based.
Claim 20
Dependent Claim
26 words
A supported particulate catalyst suitable for use in a vapor phase reactor according to claim 16 wherein said solidified organic adhesive is a styrene-butadiene robber adhesive.
Claim 21
Dependent Claim
32 words
A supported particulate catalyst suitable for use in a vapor phase reactor according to claim 14 wherein said solid preformed catalyst has a average particle size of approximately 8 to 250 mesh.
Claim 22
Dependent Claim
29 words
A supported particulate catalyst suitable for use in a vapor phase reactor according to claim 14 wherein the solid particles of said preformed catalyst comprise transition metal oxide catalyst.
Claim 23
Dependent Claim
55 words
A supported particulate catalyst suitable for use in a vapor phase reactor according to claim 14 wherein the solid particles of said preformed catalyst comprise a plurality of metal oxide layers wherein the metal oxides are selected from the group consisting of oxides of titanium, chromium, iron, cobalt, nickel, copper, zinc, molybdenum, tungsten, and tin.
Claim 24
Dependent Claim
37 words
A supported particulate catalyst suitable for use in a vapor phase reactor according to claim 14 wherein at least 60 percent of the surface area of said secured solid preformed catalytic particles is exposed to ambient conditions.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-08-28 | 1999-02-27 | 1999-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-08-28 | 2003-02-27 | 2003-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-08-28 | 2007-02-27 | 2007-08-29 | $7700.00 | Window Closed / Lapsed |