Claim 1

Independent Claim 131 words

A process for preparing a ferroelectric composite comprising a sol-gel of a ferroelectric material comprising an oxide of at least two metals, said ferroelectric composite impregnated with a polymer, comprising: (a) providing alcoholates of said at least two metals to form metal alcoholates; (b) combining said metal alcoholates and subjecting them to an equilibration reaction to form an equilibrated metal alcoholate solution; (c) hydrolyzing and condensing said equilibrated metal alcoholate solution by addition of water to form a gel having pores permeated with water and alcohol; (d) removing said water and alcohol from said pores of said gel to leave an aerogel foam; (e) heat-treating said aerogel foam; and (f) filling said pores with said polymer to form said ferroelectric composite, said polymer having a dielectric constant of less than 3.

Claim 2

Dependent Claim 131 words

A process for preparing a ferroelectric composite comprising a sol-gel of a ferroelectric material comprising an oxide of at least two metals, said ferroelectric composite impregnated with a polymer, comprising: (a) providing alcoholates of said at least two metals to form metal alcoholates; (b) combining said metal alcoholates and subjecting them to an equilibration reaction to form an equilibrated metal alcoholate solution; (c) hydrolyzing and condensing said equilibrated metal alcoholate solution by addition of water to form a gel having pores permeated with water and alcohol; (d) removing said water and alcohol from said pores of said gel to leave an aerogel foam; (e) heat-treating said aerogel foam; and (f) filling said pores with said polymer to form said ferroelectric composite, said polymer having a dielectric constant of less than 3.

Claim 3

Dependent Claim 17 words

The process of claim 1 wherein said ferroelectric material comprises a crystalline oxide having a perovskite structure.

Claim 4

Dependent Claim 28 words

The process of claim 2 wherein said ferroelectric material comprises a perovskite selected from the group consisting of BaTiO 3 , SrTiO 3 , and (Ba,Sr)TiO 3 .

Claim 5

Dependent Claim 25 words

The process of claim 3 wherein said metal alcoholates comprise titanium iso-propoxide and the reaction products of barium and 2-methoxyethanol and of strontium and 2-methoxyethanol.

Claim 6

Dependent Claim 25 words

The process of claim 3 wherein said metal alcoholates are equilibrated by refluxing for a period of time ranging from about 2 to 8 hours.

Claim 7

Dependent Claim 34 words

The process of claim 3 wherein said metal alcoholates are hydrolyzed and condensed to form said gel by adding thereto at least a stoichiometric quantity of water, based on the concentration of said metals.

Claim 8

Dependent Claim 206 words

The process of claim 3 wherein said water and alcohol are removed from said pores by a process comprising: (a) extracting said water by immersing said gel in a volume of solvent sufficient to reduce the residual water content to less than 0.1% by weight, in which said solvent is miscible with water and soluble in liquified compressed gas; (b) extracting said solvent by autoclaving in a volume of liquified compressed gas sufficient to reduce the residual content of said solvent to less than 0.1% by weight with said liquified compressed gas at a temperature of 1° to 16° C. below its critical temperature and at a pressure of 70 to 370 pounds per square inch (5 to 26 Kg/cm 2 ) below its critical pressure; (c) heating said liquified compressed gas to a temperature 9° to 29° C. above its critical point, thus generating supercritical fluid at a pressure of about 330 to 930 pounds per square inch (23.2 to 65.4 Kg/cm 2 ) above its critical pressure for about 1 hour; and (d) depressurizing said supercritical fluid at constant temperature to atmospheric pressure over a period of at least 1 hour, thus converting said supercritical fluid into gas, and thereby providing said aerogel foam.

Claim 9

Dependent Claim 20 words

The process of claim 7 wherein said solvent is selected from the group consisting of acetone, methanol, ethanol, and 2-methoxyethanol.

Claim 10

Dependent Claim 25 words

The process of claim 7 wherein said liquefied compressed gas is selected from the group consisting of carbon dioxide, nitrous oxide, sulfur hexafluoride, and trifluoromethane.

Claim 11

Dependent Claim 37 words

The process of claim 3 wherein said crystallinity is induced in said aerogel foam by sintering at a temperature ranging from about 500° to 900° C. for a period of time ranging from 1 to 120 minutes.

Claim 12

Dependent Claim 16 words

The process of claim 1 wherein said pores are filled with said polymer by vacuum impregnation.

Claim 13

Dependent Claim 37 words

The process of claim 11 wherein following said vacuum impregnation, said aerogel is subjected to an inert gas under a pressure ranging from about 100 to 2,500 pounds per square inch (7.03 to 175.8 Kg/cm 2 ).

Claim 14

Dependent Claim 24 words

The process of claim 11 wherein said polymer is selected from the group consisting of polystyrene, polyethylene, polypropylene, fluorinated poly(ethylene-co-propylene), polycarbonate, and polyphenylene oxide.

Claim 15

Dependent Claim 132 words

A process for preparing a ferroelectric composite comprising a sol-gel of a ferroelectric material consisting essentially of (Ba,Sr)TiO 3 impregnated with a polymer, comprising: (a) forming a mixture of titanium iso-propoxide and the reaction products of barium and 2-methoxyethanol and of strontium and 2-methoxyethanol; (b) subjecting said mixture to an equilibration reaction by refluxing said mixture to form an equilibrated metal alcoholate solution; (c) hydrolyzing and condensing said equilibrated metal alcoholate solution with at least a stoichiometric amount of water to form a gel having pores permeated with water and alcohol; (d) removing said water and alcohol from said pores of said gel to leave an aerogel foam; (e) inducing full crystallinity in said aerogel foam by sintering; and (f) vacuum impregnating said pores with said polymer to form said ferroelectric composite.

Claim 16

Dependent Claim 132 words

A process for preparing a ferroelectric composite comprising a sol-gel of a ferroelectric material consisting essentially of (Ba,Sr)TiO 3 impregnated with a polymer, comprising: (a) forming a mixture of titanium iso-propoxide and the reaction products of barium and 2-methoxyethanol and of strontium and 2-methoxyethanol; (b) subjecting said mixture to an equilibration reaction by refluxing said mixture to form an equilibrated metal alcoholate solution; (c) hydrolyzing and condensing said equilibrated metal alcoholate solution with at least a stoichiometric amount of water to form a gel having pores permeated with water and alcohol; (d) removing said water and alcohol from said pores of said gel to leave an aerogel foam; (e) inducing full crystallinity in said aerogel foam by sintering; and (f) vacuum impregnating said pores with said polymer to form said ferroelectric composite.

Claim 17

Dependent Claim 22 words

The process of claim 14 wherein said refluxing is done for a period of time ranging from about 2 to 8 hours.

Claim 18

Dependent Claim 179 words

The process of claim 14 wherein said water and alcohol are removed from said pores by a process comprising: (a) extracting said water and alcohol by immersion in a volume of acetone sufficient to reduce the residual water content to less than 0.1% by weight; (b) extracting said acetone by autoclaving in a volume of liquid carbon dioxide sufficient to reduce the residual acetone content to less than 0.1% by weight with said liquid carbon dioxide at a temperature of 15° to 30° C. and at a pressure of 700 to 1,000 pounds per square inch (49.2 to 70.3 Kg/cm 2 ); (c) heating said liquid carbon dioxide to a temperature of about 40° to 60° C. for about 1 hour, thus generating supercritical carbon dioxide at a pressure of about 1,400 to 2,000 pounds per square inch (98.5 to 147 Kg/cm 2 ); and (d) depressurizing said supercritical carbon dioxide at constant temperature to atmospheric pressure over a period of at least a 1-hour, thus converting said supercritical carbon dioxide into gas, and thereby provide said aerogel foam.

Claim 19

Dependent Claim 31 words

The process of claim 14 wherein said sintering is done at a temperature ranging from about 500° to 900° C. for a period of time ranging from 1 to 120 minutes.

Claim 20

Dependent Claim 37 words

The process of claim 14 wherein following said vacuum impregnation, said aerogel is subjected to an inert gas under a pressure ranging from about 100 to 2,500 pounds per square inch (7.03 to 175.8 Kg/cm 2 ).

Claim 21

Dependent Claim 24 words

The process of claim 14 wherein said polymer is selected from the group consisting of polystyrene, polyethylene, polypropylene, fluorinated poly(ethylene-co-propylene), polycarbonate, and polyphenylene oxide.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1998-08-21	1999-02-20	1999-08-22	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	2002-08-21	2003-02-20	2003-08-22	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2006-08-21	2007-02-20	2007-08-22	$7700.00	Window Closed / Lapsed

Ferroelectric aerogel composites for voltage-variable dielectric tuning, and method for making the same

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag