Low resistance, stable ohmic contacts to silcon carbide, and method of making the same
Assignee: Wolfspeed Inc
•
Filing: 1994-06-03
•
Granted: 1995-08-15
•
Expires: 2014-06-03
Abstract
Abstract Stable, high temperature electrical contacts to silicon carbide formed using a unique silicide formation process that employs a sacrificial silicon layer between the silicon carbide and the contacting metal, which forms a metal silicide interlayer providing the resulting contact with low specific contact resistance and high electrical and structural stability. The contact interface is formed by reaction below the semiconductor surface, and thus the in-situ silicide formation process is insensitive to surface impurities and oxides and permits the controlled formation of silicides without the formation of excess carbon and carbides at the contact interface. The silicon layer may optionally be doped in situ during growth or implanted with dopants after growth, to lower the contact resistance and enhance its operational stability.
Inventors
- 👤 Michael A. Tischler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:23
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10D64/0115; H10D64/60; H10D64/62; Y; Y10; Y10S; Y10S148/00; Y10S148/148
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
22 words
An ohmic contact SiC article, comprising: a SiC base layer; and a non-carbonaceous metal silicide ohmic contact structure on the SiC layer.
Claim 2
Dependent Claim
22 words
An ohmic contact SiC article, comprising: a SiC base layer; and a non-carbonaceous metal silicide ohmic contact structure on the SiC layer.
Claim 3
Dependent Claim
20 words
An article according to claim 1, further comprising a contact metal overlayer on the non-carbonaceous metal silicide ohmic contact structure.
Claim 4
Dependent Claim
38 words
An article according to claim 1, wherein the metal constituent of the metal silicide comprises a material selected from the group consisting of the Group 4b, 5b, 6b, 7b, and 8 transition metals and their mixtures and alloys.
Claim 5
Dependent Claim
37 words
An article according to claim 1, wherein the metal constituent of the metal silicide comprises a material selected from the group consisting of nickel, chromium, palladium, titanium, tungsten, tantalum, molybdenum, cobalt, zirconium, and their mixtures and alloys.
Claim 6
Dependent Claim
29 words
An article according to claim 1, wherein the metal constituent of the metal silicide comprises a material selected from the group consisting of molybdenum, tantalum, nickel, and titanium-tungsten alloys.
Claim 7
Dependent Claim
19 words
An article according to claim 1, wherein the metal silicide has a melting point of at least 1000° C.
Claim 8
Dependent Claim
39 words
An article according to claim 1, wherein the non-carbonaceous metal silicide ohmic contact structure comprises a metal silicide selected from the group consisting of platinum silicide, palladium silicide, tungsten silicide, tantalum silicide, nickel silicide, titanium silicide and cobalt silicide.
Claim 9
Dependent Claim
67 words
An article according to claim 1, wherein the non-carbonaceous metal silicide ohmic contact structure has been formed in situ by deposition of a silicon layer on the SiC base layer and deposition of a silicide-forming metal on the silicon layer, with subsequent reaction of the silicide-forming metal with the silicon layer at sufficient temperature and for sufficient time to form said non-carbonaceous metal silicide ohmic contact structure.
Claim 10
Dependent Claim
29 words
An article according to claim 8, wherein the silicon layer comprises a dopant species, and the non-carbonaceous metal silicide ohmic contact structure is doped with a same dopant species.
Claim 11
Dependent Claim
24 words
An article according to claim 1, wherein the non-carbonaceous metal silicide ohmic contact structure comprises a material having a resistivity not exceeding 75 micro-ohms-cm.
Claim 12
Dependent Claim
24 words
An article according to claim 1, wherein the non-carbonaceous metal silicide ohmic contact structure comprises a material having a resistivity not exceeding 40 micro-ohms-cm.
Claim 13
Dependent Claim
40 words
An article according to claim 9, wherein the silicon layer is doped to a level of at least 10 18 carriers/cm 3 , with a dopant species selected from the group consisting of n-type dopant atoms and p-type dopant atoms.
Claim 14
Dependent Claim
15 words
An article according to claim 12, wherein the dopant species comprises an n-type dopant species.
Claim 15
Dependent Claim
22 words
An article according to claim 13, wherein the n-type dopant species is selected from the group consisting of phosphorus, arsenic, and antimony.
Claim 16
Dependent Claim
15 words
An article according to claim 12, wherein the dopant species comprises a p-type dopant species.
Claim 17
Dependent Claim
21 words
An article according to claim 15, wherein the p-type dopant species is selected from the group consisting of boron and aluminum.
Claim 18
Dependent Claim
30 words
An article according to claim 1, wherein the non-carbonaceous metal silicide ohmic contact structure has a specific contact resistance to SiC of less than about 5×10 -5 ohm-cm 2 .
References Cited (Backward Citations)
US4875083A
Cited
WO1994006153A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-08-14 | 1999-02-13 | 1999-08-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-08-14 | 2003-02-13 | 2003-08-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-08-14 | 2007-02-13 | 2007-08-15 | $7700.00 | Window Closed / Lapsed |