Metalorganic chemical vapor deposition of ferroelectric thin films

Assignee: Sharp Corp
•
Filing: 1992-12-31
•
Granted: 1995-07-11
•
Expires: 2012-12-31
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract A method to produce high quality doped and undoped lead zirconate titanate (PZT) thin films by metalorganic chemical vapor deposition is disclosed. The PZT thin films with the perovskite structure were deposited on sapphire disks, Pt/Ti/SiO 2 /Si wafers, and RuO x /SiO 2 /Si wafers by both hot-wall and cold-wall CVD reactors at deposition temperature as low as 550° C. and a reduced pressure 6 torr. The source materials include metalorganic precursors and oxidizing agent. The metalorganic precursors can be metal alkoxides, metal acetylacetonates, or metal β-diketonates. Preferably, the precursors are lead tetramethylheptadione for Pb component, zirconium tetramethylheptadione for Zr component, and titanium ethoxide for Ti component and the oxidizing agent is oxygen. The stoichiometry of the films can be easily controlled by varying the individual precursor temperature and/or the flow rate of the carrier gas. The Pb(Zr 0 .82 Ti 0 .18)O 3 film produced by the present invention shows a spontaneous polarization of 23.3 μC/cm 2 , a remanent polarization of 12.3 μC/cm 2 , and coercive field of 64.5 kV/cm.

Inventors

  • 👤 Seshu B. Desu
  • 👤 Chien-Hsiung Peng

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-03 13:06
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C23C16/40; C23C16/409

Claims Analysis

Total Claims: 10
Claim 1
Independent Claim 93 words
A method of depositing ferroelectric lead zirconate titanate thin film with perovskite structure on a substrate by MOCVD, comprising the steps of: maintaining said substrate at a pressure below about 100 torr in a CVD reactor; heating said substrate in said CVD reactor; transporting the vapors of precursors by a carrier gas and a oxidizing agent and/or a diluent gas into said CVD reactor for deposition on said substrate to form said ferroelectric lead zirconate titanate thin film with the perovskite structure wherein said precursors are lead tetramethylheptadione, zirconium tetramethylheptadione, and titanium ethoxide.
Claim 2
Independent Claim 93 words
A method of depositing ferroelectric lead zirconate titanate thin film with perovskite structure on a substrate by MOCVD, comprising the steps of: maintaining said substrate at a pressure below about 100 torr in a CVD reactor; heating said substrate in said CVD reactor; transporting the vapors of precursors by a carrier gas and a oxidizing agent and/or a diluent gas into said CVD reactor for deposition on said substrate to form said ferroelectric lead zirconate titanate thin film with the perovskite structure wherein said precursors are lead tetramethylheptadione, zirconium tetramethylheptadione, and titanium ethoxide.
Claim 3
Dependent Claim 37 words
The method of claim 1 wherein said precursor temperature for lead tetramethylheptadione is about 140° to 165° C., for zirconium tetramethylheptadione is about 180° to 230° C., and for titanium ethoxide is about 80° C. 125° C.
Claim 4
Dependent Claim 18 words
The method of claim 1 wherein said oxidizing agent is at least one of oxygen and nitrous oxide.
Claim 5
Dependent Claim 27 words
The method of claim 3 wherein said oxidizing agent flow rate is about 300 to 2000 sccm, wherein the abbreviation sccm signifies standard cubic centimeter per minute.
Claim 6
Dependent Claim 18 words
The method of claim 1 wherein said carrier gas is at least one of nitrogen and inert gas.
Claim 7
Dependent Claim 60 words
The method of claim 5 wherein said lead tetramethylheptadione is carried by the carrier gas at about 10 to 50 sccm, zirconium tetramethylheptadione is carried by the carrier gas at about 10 to 50 sccm, and titanium ethoxide is carried by the carrier gas at about 1 to 10 sccm, wherein the abbreviation sccm signifies standard cubic centimeter per minute.
Claim 8
Dependent Claim 18 words
The method of claim 1 wherein said diluent gas is at least one of nitrogen and inert gas.
Claim 9
Dependent Claim 31 words
The method of claim 1 wherein said ferroelectric lead zirconate titanate thin film has a composition of Pb(Zr x Ti 1-x )O 3 wherein x ranges from 0.0 to about 0.9.
Claim 10
Dependent Claim 56 words
The method of claim 1 wherein said ferroelectric lead zirconate titanate thin film deposited on said substrate has a composition of Pb(Zr 0 .83 Ti 0 .18)O 3 with the ferroelectric properties of the spontaneous polarization of 23.3 μC/cm 2 , the remanent polarization of 12.3 μC/cm 2 , and the coercive field of 64.5 kV/cm.

References Cited (Backward Citations)

US5006363A Cited
US5104690A Cited
US5204314A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1998-07-10 1999-01-09 1999-07-11 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 2002-07-10 2003-01-09 2003-07-11 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 2006-07-10 2007-01-09 2007-07-11 $7700.00 Window Closed / Lapsed

Assigned Categories & Tags

No categories assigned to this patent yet.

Assign Category Tag