Method of manufacturing resin member
Assignee: Toyoda Gosei Co Ltd
•
Filing: 1993-10-29
•
Granted: 1995-07-04
•
Expires: 2013-10-29
Abstract
Abstract A resilient surface sheet element 14 is vacuum molded from a resilient laminate sheet member 13 including a skin sheet 10 and a foam sheet 12. The resilient surface sheet element 14 is placed in a predetermined recess 16 of a female mold 15 for molding an instrument panel. After a first thermoplastic resin 18 is fed into a space between a male mold 17 and the resilient surface sheet element 14 placed in the female mold 15, the female mold 15 and the male mold 17 are closed tightly. The first thermoplastic resin 18 then flows through a first cavity section formed on a rear face of the resilient surface sheet element 14 to be integrated with the resilient surface sheet element 14. Before the first plastic resin 18 completely hardens in the first cavity section, a second thermoplastic resin 21 is injected from an injection gate 20 into a second cavity section adjacent to the first cavity section to securely fuse and join with the first thermoplastic resin 18.
Inventors
- 👤 Norio Jogan
- 👤 Tetsuya Fujii
- 👤 Akiyoshi Nagano
- 👤 Toshihiko Mori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 07:31
CPC Classifications
B; B29; B29C; B29C45/00; B29C45/14; B29C45/14336; B29C45/16; B29C45/1671; B29C45/17; B29C45/46; B29C45/56; B29C45/561; B29C70/00; B29C70/68; B29C70/74; B29C70/76; B29C70/763; B29C70/78; B29C2045/1486; B29C2045/14901; B29C2793/00; B29C2793/0081; B29C43/00; B29C51/00; B29L; B29L2031/00; B29L2031/30; B29L2031/3005; B29L2031/3008; B29L2031/3041; B60; B60R; B60R13/00; B60R13/02; B60R13/0256
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
203 words
A method of manufacturing an article, part of which comprises a resilient surface element, using a first mold and a second mold, which mate with each other and form a cavity therebetween for molding said article, said cavity including a first cavity section corresponding to said resilient surface element and a second cavity section formed adjacent to said first cavity section, said method comprising the steps of: (a) forming a resilient surface element in a predetermined shape corresponding to the part being manufactured; (b) setting the resilient surface element in said first mold so as to be disposed at a predetermined position in said first cavity section while said first mold is separate from said second mold; (c) feeding a volume of a first thermoplastic resin into said first cavity section between said second mold and said resilient surface element set in said first mold, and closing and pressing said first mold and said second mold against each other, the volume of said first thermoplastic resin being such that it spreads out over only said resilient surface element; and (d) injecting a second thermoplastic resin into said second cavity section before said first thermoplastic resin is completely hardened in said first cavity section.
Claim 2
Independent Claim
203 words
A method of manufacturing an article, part of which comprises a resilient surface element, using a first mold and a second mold, which mate with each other and form a cavity therebetween for molding said article, said cavity including a first cavity section corresponding to said resilient surface element and a second cavity section formed adjacent to said first cavity section, said method comprising the steps of: (a) forming a resilient surface element in a predetermined shape corresponding to the part being manufactured; (b) setting the resilient surface element in said first mold so as to be disposed at a predetermined position in said first cavity section while said first mold is separate from said second mold; (c) feeding a volume of a first thermoplastic resin into said first cavity section between said second mold and said resilient surface element set in said first mold, and closing and pressing said first mold and said second mold against each other, the volume of said first thermoplastic resin being such that it spreads out over only said resilient surface element; and (d) injecting a second thermoplastic resin into said second cavity section before said first thermoplastic resin is completely hardened in said first cavity section.
Claim 3
Dependent Claim
45 words
A method in accordance with claim 1, wherein said step (d) comprises the step of: injecting said second thermoplastic resin into said second cavity section within a time period from approximately zero seconds to approximately 3.5 seconds after said mold closing in said step (d).
Claim 4
Dependent Claim
67 words
A method in accordance with claim 1, wherein said step (a) further comprises the steps of: (a-1) manufacturing a resilient laminate sheet member by laminating a skin sheet and a foam sheet; and (a-2) adjusting a shape of said resilient laminate sheet member to produce said resilient surface sheet element, where said foam sheet is to be directly in contact with and adhere to said resin member.
Claim 5
Dependent Claim
33 words
A method in accordance with claim 3, wherein said step (a-1) further comprises the step of: preparing said foam sheet by expanding foaming material at an expansion rate between fifteen and thirty times.
Claim 6
Dependent Claim
17 words
A method in accordance with claim 1, wherein said resin member is an interior member for vehicles.
Claim 7
Dependent Claim
32 words
A method in accordance with claim 3, wherein said resin member and said skin sheet and said foam sheet of said resilient surface sheet element are all composed of an olefin resin.
Claim 8
Dependent Claim
13 words
A method in accordance with claim 6, wherein said olefin resin is polypropylene.
Claim 9
Dependent Claim
34 words
A method in accordance with claim 3, wherein said step (a-2) further comprises the step of: vacuum molding said resilient laminate sheet member to form said resilient surface sheet element of said predetermined shape.
Claim 10
Dependent Claim
37 words
A method in accordance with claim 8, wherein said resilient laminate sheet member is heated to a temperature allowing an ornamental pattern on a molding surface of a vacuum mold to be transferred to said skin sheet.
Claim 11
Dependent Claim
22 words
A method in accordance with claim 1, wherein said first thermoplastic resin and said second thermoplastic resin are identical with each other.
Claim 12
Dependent Claim
37 words
A method in accordance with claim 10, wherein an injection temperature of said second thermoplastic resin injected in said step (d) is higher than a feeding temperature of said first thermoplastic resin fed in said step (c).
Claim 13
Dependent Claim
60 words
A method in accordance with claim 1, wherein said step (a) further comprises the step of: (a-3) manufacturing a sheet member having a fluffed cushion layer therein and forming said sheet member to said predetermined shape to prepare said resilient surface sheet element, where said cushion layer is to be directly in contact with and adhere to said resin member.
Claim 14
Independent Claim
122 words
A method for manufacturing a resin member, comprising the steps of: forming a resilient surface sheet element; placing said resilient surface sheet element on a first mold member; feeding a heated first thermoplastic resin to a second mold member; pressing the first and second mold members together so that said first thermoplastic resin integrated with said resilient surface sheet element on a rear cavity thereof; and injecting a heated second thermoplastic resin, between said first and second mold members into a second cavity so as to contact said first thermoplastic resin away from said rear cavity; wherein said second thermoplastic resin is heated to a temperature higher than said first thermoplastic resin so as to fuse the first and second resins together.
Claim 15
Independent Claim
122 words
A method for manufacturing a resin member, comprising the steps of: forming a resilient surface sheet element; placing said resilient surface sheet element on a first mold member; feeding a heated first thermoplastic resin to a second mold member; pressing the first and second mold members together so that said first thermoplastic resin integrated with said resilient surface sheet element on a rear cavity thereof; and injecting a heated second thermoplastic resin, between said first and second mold members into a second cavity so as to contact said first thermoplastic resin away from said rear cavity; wherein said second thermoplastic resin is heated to a temperature higher than said first thermoplastic resin so as to fuse the first and second resins together.
Claim 16
Dependent Claim
39 words
A method as claimed in claim 13, wherein said injecting step includes allowing said second thermoplastic resin to penetrate said first thermoplastic resin deeper at a center portion of said second cavity than at sides of said second cavity.
Claim 17
Dependent Claim
22 words
A method as claimed in claim 14, wherein said second thermoplastic resin is the same type resin as said first thermoplastic resin.
References Cited (Backward Citations)
JPS55156037A
Cited
JPS599054A
Cited
US4525231A
Cited
US4766025A
Cited
US4902557A
Cited
US5292465A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-07-03 | 1999-01-02 | 1999-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-07-03 | 2003-01-02 | 2003-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-07-03 | 2007-01-02 | 2007-07-04 | $7700.00 | Window Closed / Lapsed |