Method for synthesis of high capacity Lix Mn2 O4 secondary battery electrode compounds
Assignee: Valence Technology Inc
•
Filing: 1993-05-19
•
Granted: 1995-06-20
•
Expires: 2013-05-19
Abstract
Abstract Lithium intercalation compounds suitable for use in high capacity secondary battery electrodes are prepared by reacting together at a temperature in the range of about 800° to 900° C. lithium and manganese compounds in a stoichiometric ratio resulting in a Li x Mn 2 O 4 compound wherein x is within the range of about 1.00 to 1.20. The resulting compound is annealed at a temperature in excess of about 800° C. and cooled to at least about 500° C. at the rate less than about 10° C. per hour before being finally cooled to ambient working temperature. Intercalation electrodes comprising these lithiated compounds are used in secondary batteries to yield stable, extended capacities in excess of 110 AHr/Kg.
Inventors
- 👤 Jean-Marie Tarascon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:42
CPC Classifications
C; C01; C01G; C01G45/00; C01G45/12; C01G45/1221; C01G45/1242; H; H01; H01M; H01M10/00; H01M10/05; H01M10/052; H01M4/00; H01M4/02; H01M4/36; H01M4/48; H01M4/50; H01M4/505; C01P; C01P2002/00; C01P2002/70; C01P2002/77; C01P2002/80; C01P2002/88; C01P2006/00; C01P2006/40; H01M4/62; H01M4/621; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
116 words
A method of synthesizing a Li x Mn 2 O 4 intercalation compound wherein x ranges from about 1.00 to 1.20 which comprises reacting a mixture of at least one each of a lithium compound and a manganese compound at a temperature of at least about 800° C. to form a product characterized in that a) said mixture comprises a mole ratio of about 1.00 to 1.20 moles of lithium per 2.00 moles of manganese; and b) the product is finally cooled, from about 800° C. to at least about 500° C. at a rate of less than about 10° C. per hour in air, thereby to obtain an a-axis parameter ≦8.23 Å for said compound.
Claim 2
Independent Claim
116 words
A method of synthesizing a Li x Mn 2 O 4 intercalation compound wherein x ranges from about 1.00 to 1.20 which comprises reacting a mixture of at least one each of a lithium compound and a manganese compound at a temperature of at least about 800° C. to form a product characterized in that a) said mixture comprises a mole ratio of about 1.00 to 1.20 moles of lithium per 2.00 moles of manganese; and b) the product is finally cooled, from about 800° C. to at least about 500° C. at a rate of less than about 10° C. per hour in air, thereby to obtain an a-axis parameter ≦8.23 Å for said compound.
Claim 3
Dependent Claim
21 words
A method according to claim 1 wherein the product is finally cooled at a rate of about 2°-3° C. per hour.
Claim 4
Dependent Claim
30 words
A method according to claim 1 wherein said lithium compound is selected from the group consisting on Li 2 CO 3 , LiOH, LiI, and Li 2 NO 3 .
Claim 5
Dependent Claim
24 words
A method according to claim 3 wherein said manganese compound is selected from the group consisting of manganese oxide, manganese acetate, and manganese hydroxide.
References Cited (Backward Citations)
US4246253A
Cited
US4567031A
Cited
GB2221213A
Cited
US5114910A
Cited
US5110696A
Cited
US5240794A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-06-19 | 1998-12-19 | 1999-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-06-19 | 2002-12-19 | 2003-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-06-19 | 2006-12-19 | 2007-06-20 | $7700.00 | Window Closed / Lapsed |