Method for producing a metallization level having contacts and interconnects connecting the contacts
Assignee: Infineon Technologies AG
•
Filing: 1993-12-16
•
Granted: 1995-06-06
•
Expires: 2013-12-16
Abstract
Abstract An insulating layer wherein contact holes to regions to be contacted are opened is applied surface-wide onto a substrate. For producing an interconnect mask, a photoresist layer is applied, exposed and developed such that the surface of the regions to be contacted remains covered with photoresist in exposed regions, whereas the surface of the insulating layer is uncovered in the exposed regions. Using the interconnect mask as etching mask, trenches are etched into the insulating layer. Contacts and interconnects of a metallization level are finished by filling the contact holes and the trenches with metal.
Inventors
- 👤 Thomas Zettler
- 👤 Ulrich Scheler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 21:16
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/081; H10W20/084; H10W20/085; H10P; H10P50/00; H10P50/73; Y; Y10; Y10S; Y10S148/00; Y10S148/05; Y10S438/00; Y10S438/942; Y10S438/948; Y10S438/95
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
177 words
A method for producing a metallization level on a substrate comprising the steps of: applying an insulating layer surface-wide onto a substrate surface; opening contact holes in said insulating layer at selected locations corresponding to regions of said substrate surface at which a contact to said substrate surface is desired; producing an interconnect mask by covering said insulating layer with a photoresist layer which also fills said contact holes and exposing and developing said photoresist layer to leave said contact holes filled with photoresist and to uncover an area of said insulating layer adjacent to said contact holes in which an interconnect for said contact is to be produced; using said interconnect mask as a mask for etching away said insulating layer in said area of said insulating layer adjacent to said contact holes in which an interconnect for said contact is to be produced to produce a trench; and removing said photoresist and filling said trench and said contact holes with metal to produce said interconnect in each trench and a contact in each contact hole.
Claim 2
Independent Claim
177 words
A method for producing a metallization level on a substrate comprising the steps of: applying an insulating layer surface-wide onto a substrate surface; opening contact holes in said insulating layer at selected locations corresponding to regions of said substrate surface at which a contact to said substrate surface is desired; producing an interconnect mask by covering said insulating layer with a photoresist layer which also fills said contact holes and exposing and developing said photoresist layer to leave said contact holes filled with photoresist and to uncover an area of said insulating layer adjacent to said contact holes in which an interconnect for said contact is to be produced; using said interconnect mask as a mask for etching away said insulating layer in said area of said insulating layer adjacent to said contact holes in which an interconnect for said contact is to be produced to produce a trench; and removing said photoresist and filling said trench and said contact holes with metal to produce said interconnect in each trench and a contact in each contact hole.
Claim 3
Dependent Claim
45 words
Method according to claim 1, further comprising the steps of: etching through said insulating layer in one etch step for the formation of said contact holes upon employment of a contact hole mask, and removing said contact hole mask before formation of said interconnect mask.
Claim 4
Dependent Claim
21 words
Method according to claim 1, further defined by forming said photoresist layer for producing said interconnect mask of a dry-developing resist.
Claim 5
Dependent Claim
69 words
Method according to claim 3, further defined by providing said photoresist mask having a two-layer system with a bottom layer and a top layer, further comprising the steps of: after exposure, developing and silylizing said top layer, and dry-developing said bottom layer such that a quantity of photoresist remains undeveloped as a fill in said contact holes as a result of an abbreviated developing time period of said dry-developing.
Claim 6
Dependent Claim
16 words
Method according to claim 4, further defined by conducting said dry-developing in an O 2 plasma.
Claim 7
Dependent Claim
27 words
Method according to claim 4, further defined by providing said bottom layer with a planarizing, absorbent and photo-insensitive resist and said upper layer with a photo-sensitive resist.
Claim 8
Dependent Claim
36 words
Method according to claim 1, further comprising the steps of: depositing a conformal metal layer surface-wide for filling said contact holes and trenches, and subsequently removing said conformal metal layer from outside said contacts and interconnects.
Claim 9
Dependent Claim
25 words
Method according to claim 7, further defined by providing said insulating layer with an essentially planar surface, and conducting said removing step by chemical-mechanical polishing.
Claim 10
Dependent Claim
34 words
Method according to claim 7, said removing step further defined by conducting a mask-free, anisotropic etching when the width of said interconnects is less than twice the value of the depth of said trenches.
Claim 11
Dependent Claim
17 words
Method according to claim 7, further defined by conducting said depositing step by conformal deposition of tungsten.
Claim 12
Dependent Claim
21 words
Method according to claim 2, further defined by forming said photoresist layer for producing said interconnect mask of a dry-developing resist.
Claim 13
Dependent Claim
27 words
Method according to claim 5, further defined by providing said bottom layer with a planarizing, absorbent and photo-insensitive resist and said upper layer with a photo-sensitive resist.
Claim 14
Dependent Claim
36 words
Method according to claim 2, further comprising the steps of: depositing a conformal metal layer surface-wide for filling said contact holes and trenches, and subsequently removing said conformal metal layer from outside said contacts and interconnects.
Claim 15
Dependent Claim
36 words
Method according to claim 3, further comprising the steps of: depositing a conformal metal layer surface-wide for filling said contact holes and trenches, and subsequently removing said conformal metal layer from outside said contacts and interconnects.
Claim 16
Dependent Claim
36 words
Method according to claim 4, further comprising the steps of: depositing a conformal metal layer surface-wide for filling said contact holes and trenches, and subsequently removing said conformal metal layer from outside said contacts and interconnects.
Claim 17
Dependent Claim
36 words
Method according to claim 5, further comprising the steps of: depositing a conformal metal layer surface-wide for filling said contact holes and trenches, and subsequently removing said conformal metal layer from outside said contacts and interconnects.
Claim 18
Dependent Claim
36 words
Method according to claim 6, further comprising the steps of: depositing a conformal metal layer surface-wide for filling said contact holes and trenches, and subsequently removing said conformal metal layer from outside said contacts and interconnects.
Claim 19
Dependent Claim
17 words
Method according to claim 8, further defined by conducting said depositing step by conformal deposition of tungsten.
Claim 20
Dependent Claim
17 words
Method according to claim 9, further defined by conducting said depositing step by conformal deposition of tungsten.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-06-05 | 1998-12-05 | 1999-06-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-06-05 | 2002-12-05 | 2003-06-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-06-05 | 2006-12-05 | 2007-06-06 | $7700.00 | Window Closed / Lapsed |