Pigment-containing polymer particles, method of production thereof
Assignee: Konica Minolta Inc
•
Filing: 1994-02-15
•
Granted: 1995-05-16
•
Expires: 2014-02-15
Abstract
Abstract A method of manufacturing pigment containing polymer particles comprises the steps of dissolving a surface active agent in a water at concentration higher than the CMC, dispersing a pigment, diluting the suspension at the concentration not higher than the CMC, and adding a monomer and a polymerization initiator for forming the pigment-containing polymer particles.
Inventors
- 👤 Kenji Hayashi
- 👤 Mikio Koyama
- 👤 Yoshiaki Koizumi
- 👤 Tomoe Kikuchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:26
CPC Classifications
G; G03; G03G; G03G9/00; G03G9/08; G03G9/09; G01; G01N; G01N33/00; G01N33/48; G01N33/50; G01N33/58; G01N33/585; G03G9/0802; G03G9/0804; G03G9/0806; Y; Y10; Y10S; Y10S526/00; Y10S526/909
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
148 words
A method of manufacturing a pigment containing polymer particle, comprising the steps of: dissolving a surface active agent in water to form a solution having a concentration higher than a critical micelle concentration; dispersing an organic or inorganic pigment into the solution to make a suspension wherein (a) an average diameter of organic pigment in the suspension is not more than 10 times an average diameter of a primary particle of the organic pigment; and (b) an average diameter of inorqanic pigment in the suspension is not more than 20 times an average diameter of a primary particle of the inorqanic pigment; diluting the suspension with water to form a diluted suspension having a concentration not higher than the critical micelle concentration; and adding a monomer comprising a hydrophobic monomer and a polymerization initiator into the diluted suspension to polymerize the monomer for forming the pigment-containing polymer particle.
Claim 2
Independent Claim
148 words
A method of manufacturing a pigment containing polymer particle, comprising the steps of: dissolving a surface active agent in water to form a solution having a concentration higher than a critical micelle concentration; dispersing an organic or inorganic pigment into the solution to make a suspension wherein (a) an average diameter of organic pigment in the suspension is not more than 10 times an average diameter of a primary particle of the organic pigment; and (b) an average diameter of inorqanic pigment in the suspension is not more than 20 times an average diameter of a primary particle of the inorqanic pigment; diluting the suspension with water to form a diluted suspension having a concentration not higher than the critical micelle concentration; and adding a monomer comprising a hydrophobic monomer and a polymerization initiator into the diluted suspension to polymerize the monomer for forming the pigment-containing polymer particle.
Claim 3
Dependent Claim
53 words
The method of claim 1, wherein the pigment is an organic pigment, and the monomer and the polymerization initiator satisfy the following formulas I and II: 0.001≦A≦0.03 I 0.004≦A/B≦0.10 II wherein A is a concentration (mol per liter) of the polymerization initiator and B is a concentration (mol per liter) of the monomers.
Claim 4
Dependent Claim
29 words
The method of claim 2 wherein the monomer further comprises a hydrophilic monomer, and a weight per cent of the hydrophilic monomer to the monomers is 0.1 to 15.0.
Claim 5
Dependent Claim
78 words
The method of claim 3, wherein the hydrophilic monomer is a polar group substitutable monomer selected from the group consisting of a monomer containing a carboxyl group, a monomer containing a sulfo group, a monomer containing a primary amine group, a monomer containing a secondary amine group, a monomer containing a tertiary amine group, and a monomer containing a quaternary ammonium salt group, all capable of introducing the polar group to the side chain of a polymer therefrom.
Claim 6
Dependent Claim
53 words
The method of claim 1, wherein the pigment is an inorganic pigment, and the monomer and the polymerization initiator satisfy the following formulas I and II: 0.001≦A≦0.03 I 0.004≦A/B≦0.10 II wherein A is a concentration (mol per liter) of the polymerization initiator and B is a concentration (mol per liter) of the monomers.
Claim 7
Dependent Claim
29 words
The method of claim 5, wherein the monomer further comprising a hydrophilic monomer, and a weight per cent of the hydrophilic monomer to the monomers is 0.1 to 15.0.
Claim 8
Dependent Claim
78 words
The method of claim 6, wherein the hydrophilic monomer is a polar group substitutable monomer selected from the group consisting of a monomer containing a carboxyl group, a monomer containing a sulfo group, a monomer containing a primary amine group, a monomer containing a secondary amine group, a monomer containing a tertiary amine group, and a monomer containing a quaternary ammonium salt group, all capable of introducing the polar group to the side chain of a polymer therefrom.
Claim 9
Dependent Claim
26 words
The method of claim 5, wherein the inorganic pigment is selected from the group consisting of a carbon black, a ferrite group, and a magnetite group.
Claim 10
Dependent Claim
15 words
The method of claim 5, wherein the inorganic pigment is processed with a surface improver.
Claim 11
Independent Claim
153 words
A method of manufacturing an immunological diagnostic reagent carrier, comprising the steps of: dissolving a surface active agent in water to form a solution having a concentration higher than a critical micelle concentration; dispersing an orqanic or inorganic pigment into the solution to make a suspension, wherein (a) an average diameter of organic pigment in the suspension is not more than 10 times an average diameter of a primary particle of the organic pigment; and (b) an average diameter of inorqanic pigment in the suspension is not more than 20 times an average diameter of a primary particle of the inorganic pigment; diluting the suspension with water to form a diluted suspension having a concentration not higher than the critical micelle concentration; and adding a monomer comprising a hydrophobic monomer and a polymerization initiator into the diluted suspension to polymerize the monomer for forming pigment-containing polymer particles as the immunological diagnostic reagent carrier.
Claim 12
Independent Claim
153 words
A method of manufacturing an immunological diagnostic reagent carrier, comprising the steps of: dissolving a surface active agent in water to form a solution having a concentration higher than a critical micelle concentration; dispersing an orqanic or inorganic pigment into the solution to make a suspension, wherein (a) an average diameter of organic pigment in the suspension is not more than 10 times an average diameter of a primary particle of the organic pigment; and (b) an average diameter of inorqanic pigment in the suspension is not more than 20 times an average diameter of a primary particle of the inorganic pigment; diluting the suspension with water to form a diluted suspension having a concentration not higher than the critical micelle concentration; and adding a monomer comprising a hydrophobic monomer and a polymerization initiator into the diluted suspension to polymerize the monomer for forming pigment-containing polymer particles as the immunological diagnostic reagent carrier.
Claim 13
Dependent Claim
26 words
The method of claim 10, wherein the pigment is an organic pigment, and the monomer and the polymerization initiator satisfy the following formulas I and II:
Claim 14
Dependent Claim
27 words
001≦A≦0.03 I 0.004≦A/B≦0.10 II wherein A is a concentration (mol per liter) of the polymerization initiator and B is a concentration (mol per liter) of the monomers.
Claim 15
Dependent Claim
27 words
001≦A≦0.03 I 0.004≦A/B≦0.10 II wherein A is a concentration (mol per liter) of the polymerization initiator and B is a concentration (mol per liter) of the monomers.
Claim 16
Dependent Claim
29 words
The method of claim 11, wherein the monomer further comprises a hydrophilic monomer, and a weight per cent of the hydrophilic monomer to the monomers is 0.1 to 15.0.
Claim 17
Dependent Claim
78 words
The method of claim 12, wherein the hydrophilic monomer is a polar group substitutable monomer selected from the group consisting of a monomer containing a carboxyt group, a monomer containing a sulfo group, a monomer containing a primary amine group, a monomer containing a secondary amine group, a monomer containing a tertiary amine group, and a monomer containing a quaternary ammonium salt group, all capable of introducing the polar group to the side chain of a polymer therefrom.
Claim 18
Dependent Claim
53 words
The method of claim 10, wherein the pigment is an inorganic pigment, and the monomer and the polymerization initiator satisfy the following formulas I and II: 0.001≦A≦0.03 I 0.004≦A/B≦0.10 II wherein A is a concentration (mol per liter) of the polymerization initiator and B is a concentration (mol per liter) of the monomers.
Claim 19
Dependent Claim
29 words
The method of claim 14, wherein the monomer further comprising a hydrophilic monomer, and a weight per cent of the hydrophilic monomer to the monomers is 0.1 to 15.0.
Claim 20
Dependent Claim
78 words
The method of claim 15, wherein the hydrophilic monomer is a polar group substitutable monomer selected from the group consisting of a monomer containing a carboxyl group, a monomer containing a sulfo group, a monomer containing a primary amine group, a monomer containing a secondary amine group, a monomer containing a tertiary amine group, and a monomer containing a quaternary ammonium salt group, all capable of introducing the polar group to the side chain of a polymer therefrom.
Claim 21
Dependent Claim
26 words
The method of claim 14, wherein the inorganic pigment is selected from the group consisting of a carbon black, a ferrite group, and a magnetite group.
Claim 22
Dependent Claim
15 words
The method of claim 14, wherein the inorganic pigment is processed with a surface improver.
Claim 23
Independent Claim
160 words
A method of manufacturing a toner for electrophotography, comprising the steps of: dissolving a surface active agent in water to form a solution having a concentration higher than a critical micelle concentration; dispersing an organic or inorganic pigment into the solution to make a suspension, wherein (a) an average diameter of organic pigment in the suspension is not more than 10 times an averaqe diameter of a primary particle of the orqanic pigment; and (b) an average diameter of inorganic pigment in the suspension is not more than 20 times an average diameter of a primary particle of the inorganic pigment; diluting the suspension with water to form a diluted suspension having a concentration not higher than the critical micelle concentration; and adding a monomer comprising a hydrophobic monomer and a polymerization initiator into the diluted suspension to polymerize the monomer for forming pigment-containing polymer particles; and coagulating or fusing the pigment-containing polymer particles to form the toner for electrophotography.
Claim 24
Independent Claim
160 words
A method of manufacturing a toner for electrophotography, comprising the steps of: dissolving a surface active agent in water to form a solution having a concentration higher than a critical micelle concentration; dispersing an organic or inorganic pigment into the solution to make a suspension, wherein (a) an average diameter of organic pigment in the suspension is not more than 10 times an averaqe diameter of a primary particle of the orqanic pigment; and (b) an average diameter of inorganic pigment in the suspension is not more than 20 times an average diameter of a primary particle of the inorganic pigment; diluting the suspension with water to form a diluted suspension having a concentration not higher than the critical micelle concentration; and adding a monomer comprising a hydrophobic monomer and a polymerization initiator into the diluted suspension to polymerize the monomer for forming pigment-containing polymer particles; and coagulating or fusing the pigment-containing polymer particles to form the toner for electrophotography.
Claim 25
Dependent Claim
53 words
The method of claim 19, wherein the pigment is an organic pigment, and the monomer and the polymerization initiator satisfy the following formulas I and II: 0.001≦A≦0.03 I 0.004≦A/B≦0.10 II wherein A is a concentration (mol per liter) of the polymerization initiator and B is a concentration (mol per liter) of the monomers.
Claim 26
Dependent Claim
29 words
The method of claim 20, wherein the monomer further comprising a hydrophilic monomer, and a weight per cent of the hydrophilic monomer to the monomers is 0.1 to 15.0.
Claim 27
Dependent Claim
78 words
The method of claim 21, wherein the hydrophilic monomer is a polar group substitutable monomer selected from the group consisting of a monomer containing a carboxyl group, a monomer containing a sulfo group, a monomer containing a primary amine group, a monomer containing a secondary amine group, a monomer containing a tertiary amine group, and a monomer containing a quaternary ammonium salt group, all capable of introducing the polar group to the side chain of a polymer therefrom.
Claim 28
Dependent Claim
53 words
The method of claim 19, wherein the pigment is an inorganic pigment, and the monomer and the polymerization initiator satisfy the following formulas I and II: 0.001≦A≦0.03 I 0.004≦A/B≦0.10 II wherein A is a concentration (mol per liter) of the polymerization initiator and B is a concentration (mol per liter) of the monomers.
Claim 29
Dependent Claim
29 words
The method of claim 23 wherein the monomer further comprising a hydrophilic monomer, and a weight per cent of the hydrophilic monomer to the monomers is 0.1 to 15.0.
Claim 30
Dependent Claim
78 words
The method of claim 24, wherein the hydrophilic monomer is a polar group substitutable monomer selected from the group consisting of a monomer containing a carboxyl group, a monomer containing a sulfo group, a monomer containing a primary amine group, a monomer containing a secondary amine group, a monomer containing a tertiary amine group, and a monomer containing a quaternary ammonium salt group, all capable of introducing the polar group to the side chain of a polymer therefrom.
Claim 31
Dependent Claim
26 words
The method of claim 23, wherein the inorganic pigment is selected from the group consisting of a carbon black, a ferrite group, and a magnetite group.
Claim 32
Dependent Claim
15 words
The method of claim 23, wherein the inorganic pigment is processed with a surface improver.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-05-15 | 1998-11-14 | 1999-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-05-15 | 2002-11-14 | 2003-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-05-15 | 2006-11-14 | 2007-05-16 | $7700.00 | Window Closed / Lapsed |