High performance carbon filament structures
Assignee: Individual
•
Filing: 1992-09-18
•
Granted: 1995-05-09
•
Expires: 2012-09-18
Abstract
Abstract High performance carbon filaments are provided which are characterized as having; (i) a surface area from about 50 m 2 /g to 800 m 2 /g, (ii) an electrical resistivity from about 0.3 μohm.m to 0.8 μohm.m, (iii) a crystallinity from about 5% to about 100%, (iv) a length from about 1 μm to about 100 μm, and (v) a shape which is selected from the group consisting of branched, spiral, and helical. Also provided is a carbon fiber structure suitable for use in high performance composites which structure is characterized by a primary carbon fiber structure having carbon filaments grown therefrom. The carbon filaments are grown from the carbon fibers by use of an alloy catalyst comprised of a first metal selected from Group IB of the Periodic Table of the Elements, and one or more metals from a second group of metals selected from iron, nickel, cobalt, and zinc; and optionally a metal from a third group of metals selected from titanium, tungsten, tin, and tantalum.
Inventors
- 👤 R. Terry K. Baker
- 👤 Nelly M. Rodriguez
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:33
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/83; B; B82; B82Y; B82Y30/00; B01; B01D; B01D2253/00; B01D2253/30; B01D2253/302; B01D2253/304; B01D2253/306
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
67 words
Carbon filaments characterized as having; (i) a surface area from about 50 m 2 /g to 800 m 2 /g, (ii) an electrical resistivity from about 0.3 μohm.m to 0.8 μohm.m, (iii) a crystallinity from about 5% to about 100%, (iv) a length from about 1 μm to about 100 μm, and (v) a shape which is selected from the group consisting of branched, spiral, and helical.
Claim 2
Dependent Claim
67 words
Carbon filaments characterized as having; (i) a surface area from about 50 m 2 /g to 800 m 2 /g, (ii) an electrical resistivity from about 0.3 μohm.m to 0.8 μohm.m, (iii) a crystallinity from about 5% to about 100%, (iv) a length from about 1 μm to about 100 μm, and (v) a shape which is selected from the group consisting of branched, spiral, and helical.
Claim 3
Dependent Claim
22 words
The carbon filaments of claim 1 which have a surface area of about 100 m 2 /g to 700 m 2 /g.
Claim 4
Dependent Claim
15 words
The carbon filaments of claim 2 which have a crystallinity of about 50% to 100%.
Claim 5
Dependent Claim
33 words
The carbon filaments of claim 3 which have an electrical resistivity of 0.3 μohm.m to 0.5 μohm.m, a crystallinity from about 75% to 100%, and an aspect ratio from about 100 to 200.
Claim 6
Dependent Claim
82 words
A refractory structure comprised of a refractory substrate having grown therefrom carbon filaments, wherein the filaments are characterized as having; (i) a surface area from about 50 m 2 /g to 800 m 2 /g, (ii) an electrical resistivity from about 0.3 μohm.m to 0.8 μohm.m, (iii) a crystallinity from about 5% to about 100%, (iv) a length from about 1 μm to about 100 μm, and (v) a shape which is selected from the group consisting of branched, spiral, and helical.
Claim 7
Dependent Claim
82 words
A refractory structure comprised of a refractory substrate having grown therefrom carbon filaments, wherein the filaments are characterized as having; (i) a surface area from about 50 m 2 /g to 800 m 2 /g, (ii) an electrical resistivity from about 0.3 μohm.m to 0.8 μohm.m, (iii) a crystallinity from about 5% to about 100%, (iv) a length from about 1 μm to about 100 μm, and (v) a shape which is selected from the group consisting of branched, spiral, and helical.
Claim 8
Dependent Claim
26 words
The structure of claim 5 wherein the substrate is selected from the group consisting of carbon fibers, alumina, silica, silicon carbide, silicon nitride, ceramics, and metals.
Claim 9
Dependent Claim
28 words
The structure of claim 5 wherein the refractory structure is a carbon fiber structure comprised of a primary structure of carbon fibers having grown therefrom the carbon filaments.
Claim 10
Dependent Claim
25 words
The structure of claim 7 wherein the carbon filaments have a crystallinity greater than about 50% and a surface area from about 100 to 700.
Claim 11
Dependent Claim
27 words
The structure of claim 8 wherein the carbon filaments have a crystallinity greater than about 75% and which has an aspect ratio from about 100 to 200.
Claim 12
Dependent Claim
14 words
The structure of claim 9 wherein substantially all of the carbon filaments are branched.
Claim 13
Dependent Claim
11 words
The structure of claim 9 wherein the fibers are aligned unidirectionally.
Claim 14
Independent Claim
190 words
A method for producing a carbon fiber structure comprised of primary structure of carbon fibers having carbon filaments grown therefrom, wherein substantially all of the carbon filaments are characterized as having; (i) a surface area from about 50 m 2 /g to 800 m 2 /g, (ii) an electrical conductivity from about 0.3 μohm.m to 0.8 μohm.m, (iii) a crystallinity from about 5% to about 100%, (iv) a length from about 1 μm to about 100 μm, and (v) a shape which is selected from the group consisting of branched, spiral, and helical, which method comprises: (a) depositing an alloy catalyst composition onto said carbon fibers, which alloy catalyst composition is comprised of a first metal selected from the metals of Group IB, and one or more metals from a second group of metals, selected from Fe, Ni, Co, and Zn; and optionally a metal from a third group of metals selected from Ti, W, Sn, and Ta; and (b) subjecting the catalyst treated carbon fibers to a carbon-containing gas at a temperature from the decomposition temperature of the carbon containing gas to the deactivation temperature of the alloy catalyst.
Claim 15
Independent Claim
190 words
A method for producing a carbon fiber structure comprised of primary structure of carbon fibers having carbon filaments grown therefrom, wherein substantially all of the carbon filaments are characterized as having; (i) a surface area from about 50 m 2 /g to 800 m 2 /g, (ii) an electrical conductivity from about 0.3 μohm.m to 0.8 μohm.m, (iii) a crystallinity from about 5% to about 100%, (iv) a length from about 1 μm to about 100 μm, and (v) a shape which is selected from the group consisting of branched, spiral, and helical, which method comprises: (a) depositing an alloy catalyst composition onto said carbon fibers, which alloy catalyst composition is comprised of a first metal selected from the metals of Group IB, and one or more metals from a second group of metals, selected from Fe, Ni, Co, and Zn; and optionally a metal from a third group of metals selected from Ti, W, Sn, and Ta; and (b) subjecting the catalyst treated carbon fibers to a carbon-containing gas at a temperature from the decomposition temperature of the carbon containing gas to the deactivation temperature of the alloy catalyst.
Claim 16
Dependent Claim
74 words
The method of claim 12 wherein the alloy catalyst is deposited onto the carbon fibers by an incipient wetness technique which comprises: (i) treating the fibers with a salt of said alloy, which salt is soluble in water or in an organic solvent; (ii) drying the so-treated carbon fibers; and (iii) calcining the dried fibers at a temperature from about 200° C. to about 300° C., thus converting the metals to their oxide form.
Claim 17
Dependent Claim
15 words
The method of claim 13 wherein the alloy salt is soluble in an organic solvent.
Claim 18
Dependent Claim
16 words
The method of claim 14 wherein the alloy salt is selected from formates, acetates, and oxalates.
Claim 19
Dependent Claim
25 words
The method of claim 12 wherein the alloy salt is water soluble and the surface of the carbon fibers are first oxygenated prior to treatment.
Claim 20
Dependent Claim
14 words
The method of claim 16 wherein the carbon fibers are oxygenated with atomic oxygen.
Claim 21
Dependent Claim
17 words
The method of claim 17 wherein the water soluble salt is selected from nitrates, sulfates, and chlorides.
Claim 22
Dependent Claim
26 words
The method of claim 12 wherein the catalyst is comprised of a copper-nickel alloy wherein about 5 to 30 at. % of the alloy is copper.
Claim 23
Dependent Claim
26 words
The method of claim 12 wherein the catalyst is comprised of a copper-nickel alloy wherein about 70 to 95 at. % of the alloy is copper.
Claim 24
Dependent Claim
21 words
The method of claim 12 wherein the catalyst is a copper-nickel alloy which is comprised of about 50 at. % copper.
Claim 25
Dependent Claim
12 words
The method of claim 12 wherein the alloy is a copper-nickel-iron alloy.
Claim 26
Dependent Claim
36 words
The method of claim 22 wherein the copper-nickel-iron alloy is comprised of 5 to 50 at. % copper, 90 to 40 at. % nickel, and 5 to 10 at. % iron, based on the total alloy.
Claim 27
Dependent Claim
22 words
The method of claim 12 wherein the carbon-containing gas is selected from carbon monoxide, and hydrocarbons having less than 8 carbon atoms.
Claim 28
Dependent Claim
19 words
The method of claim 24 wherein the carbon-containing gas is comprised of hydrocarbons having 3 or less carbon atoms.
Claim 29
Dependent Claim
11 words
The method of claim 25 wherein the carbon-containing gas is ethylene.
Claim 30
Dependent Claim
14 words
The method of claim 12 wherein hydrogen is also present with the carbon-containing gas.
Claim 31
Dependent Claim
18 words
The method of claim 27 wherein the vol. % of hydrogen present is from about 5 to 40%.
Claim 32
Dependent Claim
18 words
The method of claim 28 wherein the vol. % of hydrogen present is from about 10 to 30%.
Claim 33
Dependent Claim
19 words
The method of claim 12 wherein the temperature of step (b) is from about 500° C. to 700° C.
Claim 34
Dependent Claim
50 words
The method of claim 13 wherein: the surface of the carbon fibers oxygenated prior to catalyst deposition; the carbon-containing gas is comprised of hydrocarbons having 3 or fewer carbon atoms; and the fibers are heat treated in step (b) to a temperature from about 500° C. to about 700° C.
Claim 35
Dependent Claim
10 words
The method of claim 31 wherein hydrogen is also present.
References Cited (Backward Citations)
FR2512076A1
Cited
US4816289A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-05-08 | 1998-11-07 | 1999-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-05-08 | 2002-11-07 | 2003-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-05-08 | 2006-11-07 | 2007-05-09 | $7700.00 | Window Closed / Lapsed |